Temperature Dependence of Surface Composition and Morphology in Polymer Blend Film

Thin films of poly(methyl methacrylate) (PMMA) and poly(styrene-ran-acrylonitrile) (SAN) blend can phase separate upon heating to above its critical temperature. Temperature dependence of the surface composition and morphology in the blend thin film upon thermal treatment was studied using in situ X-ray photoelectron spectroscopy (XPS) and in situ atomic force microscopy (AFM). It was found that in addition to phase separation, the blend component preferentially diffused to and aggregated at the surface of the blend film, leading to the variation of surface composition with temperature. At 185 degrees C, above the critical temperature, the amounts of PMMA and SAN phases were comparable.

WATER-SOLUBLE AND AMPHIPHILIC POLYMERS .6. A STUDY ON THE SURFACE-COMPOSITION OF CAST FILMS OF PST/PMAA AND PEO-PST-PEO BLOCK POLYMERS BY XPS

Thin films of PSt/PMAA and PEO-PSt-PEO block polymers were deposited on a polystyrene substrate by solution adsorption (with or without solvent treatment), and the film surfaces were characterized by means of XPS. Direct solvent - casting of PEO-PSt-PEO from benzene solutions resulted in PSt-rich surfaces, whereas PMAA richer surfaces were obtained for PSt/PMAA films cast from DMF solutions. Moreover, solvent treatment after casting had profound effect on the film surface composition. Treatment with water markedly increased the surface concentration of polar PEO segments. In the case of PSt-PMAA block polymers, the PSt content on the surface increased in the order of water < ethanol < cyclohexane < petroleum ether, the last-named giving films with almost pure PSt surface. It is well worth noticing that the bulk composition had little to do with the surface composition for both PSt/PMAA and PEO-PSt-PEO block polymers within the composition range investigated when subsequent solvent treatment was applied.

Stress corrosion studies of ion implanted austenitic steel

Stress corrosion studies of 50 Mn18Cr4 austenitic steel implanted with 120 keV N+, 100 keV Cr+, 200 keV and 400 keV Er+ ions were carried out by constant strain method in the nitrate solution. Surface composition and depth profiles of the implanted material were measured by AES sputter etching technique. The results exhibit that nitrogen implantation has no significant affection to the stress corrosion, but the chromium and erbium implantation has prolonged the incubation period of the stress corrosion cracking. (C) 1999 Kluwer Academic Publishers.

Phase separation of PS/PVME blend films induced by capillary force

The phase behavior of a miscible PS/PVME (80/20, w/w) blend film in a confined geometry has been investigated at the annealing temperature much lower than the low critical solution temperature (LCST) of the blend. When the annealing temperature (52degreesC) is near the glass transition temperature of the blend (51.2degreesC), PVME-rich phase at the air-film surface under a microchannel forms smaller protrusion. When the annealing temperature is increased to 70degreesC, the protruding stripes, which are almost developed, are mainly composed of the mobile PVME-rich phase. These results reveal that the capillary force lead to the enrichment of PVME-rich phase at the air-polymer interface of a PDMS microchannel, that is, the capillary force lithography (CFL) can induce the phase separation of PS/PVME blend films.

X-Ray Photoelectron Spectroscopy Study of LaMn1-xFexO3 (x=0-1) Oxides

The redox potential, surface composition and oxygen species of a series of complex oxides LaMn1-xFexO3 (x=0-1) having perovskite structure (ABO(3)) have been investigated by means of XI'S. The variation of binding energies referring to Mn2p and Fe 2p under different treatment offerred an obvious evidence of redox between Mn and Fe, which could be expressed as Mn4+ + Fe(3-delta)+ Mn(4-delta)+ Fe3+ Feat Through computer fit three kinds of adsorbed oxygen species (O-I, O-II, O-III) have been evaluated based on the XPS spectra of O1s. From the variation of contents of different oxygen species, it could be concluded that. the redox occuring in the surface might be related with the adsorbed oxygen species O-I and O-II, furthermore the possibility of transfer of electron between adsorption site and oxygen was also discussed.

XPS STUDY OF CORROSION BEHAVIOUR OF TITANIUM IN H2C2O4 SOLUTION

The corrosion behaviour of titanium substance and the XPS characterization of Ti surface in the H2C2O4 solution have been first studied by X-ray photoelectron spectroscopy, The experimental results show that there am mile Ti-2 and Ti2+ on sample surface in 10% H2C2O4 solution for two boars corrosion at 80 degrees C, but if corrosion is extended to 4 hones, the surface composition is mainly TiO2 with a small amount of Ti2+. This result corresponds to the structure of TiH1.642 composion in sample surface found by XRD analysis. Since bath TiO2 and the surface coating RuO2 are of Gald-Redstone structure, therefore electrode materials of Ti-Ru are stable in chemical industry.

基于IGES的卷曲类工件结构光测量路径规划研究

本文通过对卷曲类工件IGES文件的分析,本文提出了一种新的基于IGES文件的测量路径规划策略。根据张量积曲面的性质,提出了一种曲面组合算法,运用了张量积曲面的性质,将曲面操作转化为多次曲线操作,将IGES文件中存储的多片曲面片组合为一整片曲面,从而为自由曲面测量路径的提取提供了数学模型。运用二次逼近原理,提出了一种B样条曲线上的等距采样算法。通过在实际系统进行实验,上述策略及算法得到了验证,并在自主开发的智能测量建模加工一体化装备中得到了应用。

An in-situ modified sol-gel process for monolith catalyst preparation used in the partial oxidation of methane

An in-situ modified sol-gel method for the preparation of a Ni-based monolith-supported catalyst is reported. With the presence of a proper amount of plasticizer and binder, and at an optimized pH value, the stable boehmite sol was modified with metal ions (Ni, Li, La) successfully without distinct growth of the particle size. Monolith-supported Ni-based/gamma-Al2O3 catalysts were obtained using the modified sol as the coating medium with several cycles of dip-coating and calcination. Combined BET, SEM-EDS, XRD and H-2-TPR investigations demonstrated that the derived monolith catalysts had a high specific surface area, a relatively homogeneous surface composition, and a high extent of interaction between the active component and the support. These catalysts showed relatively stable catalytic activities for partial oxidation of methane (POM) to syngas under atmospheric pressure. The monolith catalysts prepared by this sol-gel method also demonstrated an improved resistance to sintering and loss of the active component during the reaction process.

XPS and XRD studies of fresh and sulfided Mo2N

Mo surface species of molybdenum nitride and their changes under sulfiding conditions were investigated by XRD and XPS. Mo2N was synthesized by temperature-programmed reaction of MoO3, with NH3. The decomposition of the Mo3d spectra gave a Mo3d doubler which corresponded to Modelta+ (2 less than or equal to delta < 4), Mo4+ and Mo5+ Or Mo6+ species. The BE of the Mo species of passivated Mo2N shifted to higher energy level compared with the freshly prepared Mo2N due to the oxidation of Mo nitride during passivation. When Mo2N was contacted for 4 h with a 15% H2S-H-2 mixture at 400 degrees C, the XRD spectra did not reveal any new phase, which indicates a high stability of Mo2N against sulfidation, but XPS data showed the presence of sulfur, including S-0 and S2- species, and a decrease of the N/Mo atomic ratio revealed some changes in surface composition. More than one monolayer of Mo2N was transformed to sulfide. It is probable that the oxygen incorporated during passivation reacted with sulfur and formed a thin layer of molybdenum sulfide on the Mo2N surface. (C) 1998 Elsevier Science B.V. All rights reserved.

Preparation and characterization of multi-walled carbon nanotubes supported PtRu catalysts for proton exchange membrane fuel cells

A series of PtRu nanocomposites supported on H2O2-oxidized multi-walled carbon nanotubes (MWCNTs) were synthesized via two chemical reduction methods - one used aqueous formaldehyde (HCHO method) and the other used ethylene glycol (EG method) as the reducing agents. The effects of the solvents (water and ethylene glycol) and the surface composition of the MWCNTs on the deposition and the dispersion of the metal particles were investigated using N-2 adsorption. TEM. ICP-AES. FTIR and TPD. The wetting heats of the MWCNTs in corresponding solvents were also measured. The characterizations suggest that combination of the surface chemistry of the MWCNTs with the solvents decides the deposition and the dispersion of the metal nanoparticles. These nanocomposites were evaluated as proton exchange membrane fuel cell anode catalyts for oxidation of 50 ppm CO contaminated hydrogen and compared with a commercial PtRu/C catalyst. The data reveal superior performances for the nanocomposites prepared by the EG method to those by the HCHO method and even to that for tile Commercial analogue. Structure performance relationship of the nanocomposites was also studied. (C) 2005 Elsevier Ltd. All rights reserved.

Influence of indium composition on the surface morphology of self-organized InxGa1-xAs quantum dots on GaAs substrates

InxGa1-xAs self-organized quantum dots with x=1.0, 0.5, and 0.35 have been grown by molecular beam epitaxy. The areal density, distribution, and shapes have been found to be dependent on x. The dot shape changes from a round shape for x=1.0 to an elliptical shape for x less than or equal to 0.5. The major axis and minor axis of the elliptical InxGa1-xAs dots are along the [(1) over bar 10] and [110] directions, respectively. The ordering phenomenon is also discussed. It is suggested that the dot-dot interaction may play important roles in the self-organization process. (C) 2000 American Institute of Physics. [S0021-8979(00)10701-7].

A topography/chemical composition gradient polystyrene surface: Toward the investigation of the relationship between surface wettability and surface structure and chemical composition

In this paper, we have prepared of a topography/chemical composition gradient polystyrene (PS) surface, i.e., an orthogonal gradient surface, to investigate the relationship between surface wettability and surface structure and chemical composition. The prepared surface shows a one-dimensional gradient in wettability in the x, y, and diagonal directions, including hydrophobic to hydrophilic, superhydrophobic to hydrophobic, superhydrophobic to superhydrophilic gradients, and so forth.

STRUCTURAL EVOLUTION AND COMPOSITION CHANGE IN THE SURFACE REGION OF POLYPROPYLENE/CLAY NANOCOMPOSITES ANNEALED AT HIGH TEMPERATURES

A model experiment was done to clear the formation mechanism of protective layers during combustion of polypropylene (PP)/organically modified montmorillonite (OMMT) nanocomposites. The investigation was focused on the effects of annealing temperature on the structural changes and protective layer formation. The decomposition of OMMT and degradation of PP/OMMT nanocomposites were characterized by means of thermogravimetric analysis (TGA). The structural evolution and composition change in the surface region of PP/OMMT nanocomposites during heating were monitored by means of X-ray photoelectron spectroscopy (XPS), ATR-FTIR and field emission scanning electron microscopy (FESEM).