The induced flow fields by internal solitary waves and its actions on cylindrical piles in density stratified ocean with a basic density profile and a basic velocity profile are investigated. Some results, such as the time evolution of flow fields and hydrodynamic forces on the piles are yielded both by theoretical analysis and numerical calculation for general and specific cases. Several kinds of ambient sea conditions of the South China Sea are specified for numerical simulation. Moreover, the effects of relative density difference, depth ratio and wave steepness on maximal total force and total torque are analyzed.

In situ synthesis of ZrO2/ZrW2O8 composites with near-zero thermal expansion

In this paper, ZrO2 and WO3 were used as the raw materials to prepare ZrO2/ZrW2O8 composites by in situ reaction method and the thermal expansion property of the composites was studied. This novel method included a heating step up to 1473 K for 24 h, which combines the synthesizing and sintering of ZrW2O8. The result indicates that ZrO2/ZrW2O8 composite shows near-zero thermal expansion when the weight ratio of ZrO2 and WO3 is 2.5:1. Compared with composites prepared previously by non-reactive sintering of ZrO2 and ZrW2O8, the composites show higher relative density and lower porosity.

Study on the Cell Structure and Compressive Behavior of Biodegradable Poly(epsilon-caprolactone) Foam

Biodegradable poly(e-caprolactone) (PCL) foams with a series of controlled structures were prepared by using chemical foaming method. The cell morphology was detected by scanning electron microscope (SEM). The compressive behavior of the foams was investigated by uniaxial compression test. The effect of density and structural parameters on the foam compressive behavior was analyzed. It was found that the relative compressive modulus has a power law relationship with relative density. Increasing of both the cell wall thickness and the cell density lead to higher compressive modulus of the foam; however, the cell size has no distinct effect on compressive behavior.

Bulk ultrafine binderless (W0.4Al0.6)C prepared by high pressure sintering

Pure (W0.4Al0.6)C powder of about 1 mu m in diameter was sintered by the high pressure sintering (HPS) process without the addition of any binder phase. The microstructure, Vickers micro hardness and density versus the sintering time and temperature are well described. The most suitable sintering condition under pressure of 4.5 GPa is 1873 K for 8 min. Under this sintering condition, the hardness can reach 2295 kg mm(-2) and the relative density can reach 98.6%.

Lanthanum zirconate ceramic toughened by BaTiO3 secondary phase

La2Zr2O7 (LZ) is a promising thermal barrier coating material for the high-temperature applications, which could be significantly toughened by the BaTiO3 piezoelectric phase incorporated into the matrix. The composites of xBaTiO(3)/(l-x)LZ (x=5, 10, 15, 20 vol%, LZ-x-BaTiO3) were densified by means of high-pressure sintering (HPS) under a pressure of 4.5 GPa at 1450 degrees C for 10 min, by which a high relative density above 93% could be obtained.

Synthesis and high-pressure sintering of lanthanum magnesium hexaaluminate

Lanthanum magnesium hexaaluminate is a very important ceramic material for high temperature applications. In this paper lanthanum magnesium hexaaluminate has been synthesized directly by solid-state reaction. The forming mechanism was investigated by XRD. The SEM photographs show that the prepared powders are made of hexagonal plates. These powders can be well sintered at the high temperature (1600 degrees C) under the high pressure (4.5 GPa), and the relative density reaches 94.8%.

High-pressure sintered yttria stabilized zirconia ceramics

Fast densification of 8YSZ ceramics under a high pressure of 4.5 GPa was carried out at different temperatures (800, 1000, 1450 degrees C), by which a high relative density above 92% could be obtained. FT-Raman spectra indicate that the 8YSZ underwent a phase transition from partially tetragonal to partially cubic phase as temperatures increase from 1000 to 1450 degrees C when sintering under high pressure. The electrical properties of the samples under different high-pressure sintering conditions were measured by complex impedance method. The total conductivity of 0.92 x 10(-2) S cm(-1) at 800 degrees C has been obtained for 8YSZ under high pressure at 1450 degrees C, which is about 200 degrees C lower than that of the samples prepared by conventional pressureless sintering.

High-pressure sintering the novel light (W0.25Al0.75)C hard material without binder phase

A novel hard material of (W0.25Al75)C has been successfully prepared by the high-pressure sintering process without the addition of any binder phase. The high-pressure is a suitable and powerful technique for sintering the binderless hard material, the relative density of the hard material can reach 99.6% under high-pressure sintering. The density of the novel light hard material is only 6.2371 g cm(-3), which is much lighter than the normal hard material. The hardness of the light hard material can reach 18.89 GPa even the aluminum content get the astonished 75%.

Effect of the addition of YAG(Y3Al5O12) nanopowder on the mechanical properties of lanthanum zirconate

La2Zr2O7 (LZ) is a promising thermal barrier coating material for the high-temperature applications, which could be significantly toughened by the YAG nanopowder incorporated into the matrix. The composites of xYAG/(1-x)LZ (Y=10, 15, 20 vol. %, LZ-x-YAG) were densified by means of high-pressure sintering (HPS) under a pressure of 4.5 GPa at 1650 degrees C for 5 min, by which a high-relative density above 93% could be obtained. The morphologies of the fractured surfaces were investigated by the scanning electron microscope, and the fracture toughness and Vicker's-hardness of the composites were evaluated by the microindentation. The grain size of the LZ matrix drops significantly with the addition of YAG nanoparticles and the fracture type changes from the intergranular to a mixture type of the transgranular and intergranular in the nanocomposites. The LZ-20-YAG nanocomposite has a fracture toughness of 1.93 MPa m(1/2), which is obviously higher than that of the pure LZ (1.57 MPa m(1/2)), and the toughening mechanism is discussed in this paper.

Fast densification and electrical conductivity of yttria-stabilized zirconia nanoceramics

Nanocrystalline 8YSZ (8 mol% yttria stabilized zirconia) bulk samples with grain sizes of 20-30 nm were synthesized by Sol-Gel method and then densified under a high pressure of 4.5 GPa at 1273 K for 10 min. The method led to the densification of 8YSZ to a relative density higher than 92% without grain growth. Fourier transmission Raman spectroscopy suggested that 8YSZ underwent a phase transition from the cubic phase to a phase mixture (tetragonal plus a trace of monoclinic) after the densification, which decreased the electrical conductivity to a certain degree as concluded from the impedance spectroscopy.

High-pressure sintering study of a novel hard material (W0.5Al0.5)C-0.5 without binder metal

A novel hard material of (W0.5Al0.5)C-0.5 has been successfully sintered under high-pressure (4.5 GPa). The influence of sintering time and temperature on the microstructure, Vickers microhardness and density of the as-prepared specimens are well described. Interestingly, sintering temperature has an amazing influence on the hardness, density and microstructure of the specimen while the sintering time does not. It is found that the most suitable sintering condition from our work is 1600 degrees C and 10 min under pressure of 4.5 GPa. The hardness and relative density of the as-prepared sample can reach 2340 kg mm(-2) and 98.62%, respectively. The cell parameters of the sintered specimen is found to be little smaller than that of the powder, which we propose is related to the high pressure.

Grain boundary conductivity of high purity neodymium-doped ceria nanosystem with and without the doping of molybdenum oxide

Solid solutions of Ce1-xNdxO2-x/2 (0.05 <= x <= 0.2) and (Ce1-xNdx)(0.95)MO0.05O2-delta (0.05 <= x <= 0.2) have been synthesized by a modified sol-gel method. Both materials have very low content of SiO2 (similar to 27 ppm). Their structures and ionic conductivities were characterized by X-ray diffraction (XRD), field-emission scanning electron microscopy (FESEM) and electrochemical impedance spectroscopy (M). The XRD patterns indicate that these materials are single phases with a cubic fluorite structure. The powders calcined at 300 degrees C with a crystal size of 5.7 nm have good sinterability, and the relative density could reach above 96% after being sintered at 1450 degrees C. With the addition Of MoO3, the sintering temperature could be decreased to 1250 degrees C. Impedance spectroscopy measurement in the temperature range of 250-800 degrees C indicates that a sharp increase of conductivity is observed when a small amount of Nd2O3 is added into ceria, of which Ce0.85Nd0.15O1.925 (15NDC) shows the highest conductivity. With the addition of a small amount Of MoO3, the grain boundary conductivity of 15NDC at 600 degrees C increases from 2.56 S m(-1) to 5.62 S m(-1).

Preparation and characterization of nanocrystalline CeO2 by precipitation method

CeO2 nanocrystalline particulates with different sizes were prepared by precipitation method using ethanol as dispersive and protective reagent. XRD spectra show that the synthesized CeO2 has cubic crystalline structure of space group O-H(5)-F-M3M, when calcination temperature is in the range of 250 similar to 800 degreesC. TEM images reveal that CeO2 particles are spherical in shape. The average size of the particles increases with the increase of calcination temperature. Thermogravimetric analysis indicates that the weight loss of precursor mainly depends on the calcination temperature, and little depends on the calcination time. Measurements of CeO2 relative density show that the relative density of CeO2 nanocrystalline powders increases with increasing CeO2 particle size.

Sintering of nanopowders of amorphous silicon nitride under ultrahigh pressure

Nanopowders of amorphous silicon nitride were densified and sintered without additives under ultrahigh pressure (1.0-5.0 GPa) between room temperature and 1600 degrees C. The powders had a mean diameter of 18 nm and contained similar to 5.0 wt% oxygen that came from air-exposure oxidation, Sintering results at different temperatures were characterized in terms of sintering density, hardness, phase structure, and grain size. It was observed that the nanopowders can be pressed to a high density (87%) even at room temperature under the high pressure. Bulk Si3N4 amorphous and crystalline ceramics (relative density: 95-98%) were obtained at temperatures slightly below the onset of crystallization (1000-1100 degrees C and above 1420 degrees C, respectively. Rapid grain growth occurred during the crystallization leading to a grain size (>160 nm) almost 1 order of magnitude greater than the starting particulate diameters, With the rise of sintering temperature, a final density was reached between 1350 and 1420 degrees C, which seemed to be independent of the pressure applied (1.0-5.0 GPa), The densification temperature observed under the high pressure is lower by 580 degrees C than that by hot isostatic pressing sintering, suggesting a significantly enhanced low-temperature sintering of the nanopowders under a high external pressure.

Application of forecasting structural cracks technique of 3D move in Chengdao buried hill

3DMove software, based on the three-dimension structural model of geologic interpretation, can forecast reservoir cracks from the point of view of formation of the structural geology, and analyze the characteristics of the cracks. 3DMove software dominates in forecasting cracks. We forecast the developments and directions of the cracks in Chengbei buried hill with the application of forecasting technique in 3DMove software, and obtain the chart about strain distributing on top in buried hill and the chart about relative density and orientation and the chart about the analysis of crack unsealing. In Chengbei 30 buried hill zone, north-west and north-east and approximately east-west cracks in Cenozoic are very rich and the main directions in every fault block are different. Forecasting results that are also verified by those of drilling approximately accord with the data from well logging, the case of which shows that the technique has the better ability in forecasting cracks, and takes more effects on exploration and exploitation of crack reservoir beds in ancient buried hill reservoirs.