Write-once blue laser recording using silicon doped SbOx thin films prepared by reactive dc-magnetron sputtering

Si:SbOx films have been deposited by reactive dc-magnetron sputtering from a Sb target with Si chips attached in Ar + O-2 with the relative O-2 content 7%. The as-deposited films contained Sb metal, Sb2O3, SiO, Si2O3 and SiO2. The crystallization of Sb was responsible for the changes of optical properties of the films. The results of the blue laser recording test showed that the films had good writing sensitivity for blue laser beam (406.7 nm), and the recording marks were still clear even if the films were deposited in air 60 days, which demonstrated that doping silicon in SbOx films can improve the stability of SbOx films. High reflectivity contrast of about 36% was obtained at a writing power 6 mW and writing pulse width 300 ns. (c) 2007 Elsevier B.V. All rights reserved.

SbOx thin films used for write-once blue laser recording

SbOx thin films are deposited by reactive dc-magnetron sputtering from all antimony metal target in Ar+O-2 with the relative O-2 content 7%. It is found that the as-deposited films call represent a two-component system comprising amorphous Sb and amorphous Sb2O3. The crystallization of Sb is responsible for the changes of optical properties of the films. The results of the static, test show that the SbOx thin films have good writing sensitivity for blue laser beams and the recording marks are very clear and circular. High reflectivity contrast of about 41% is obtained at a writing power 6 mW and writing pulse width 300 ns. In addition, the films show a good stability after reading 10000 times.

Structural and photoluminescent properties of ZnO films deposited by radio frequency reactive sputtering

Zinc oxide films with c-axis preferred orientation were deposited on silicon (100) substrates by radio frequency (RF) reactive sputtering. The properties of the samples were characterized by X-ray diffractometer, X-ray photoelectron spectroscopy and fluorescent-spectrophotometer. The effect of sputtering power and substrate temperature on the structural and photoluminescent (PL) properties of the ZnO films was investigated. The results indicated that when the sputtering power is 100 W and the substrate temperature is 300-400 degrees C, it is suitable for the growth of high c-axis orientation and small strain ZnO films. A violet peak at about 380 nm and a blue band at about 430 nm were observed in the room temperature photoluminescence spectra, and the origin of blue emission was investigated.

Mapping Closure Approximation for Reactive Scalars in Random Flows

The Mapping Closure Approximation (MCA) approach is developed to describe the statistics of both conserved and reactive scalars in random flows. The statistics include Probability Density Function (PDF), Conditional Dissipation Rate (CDR) and Conditional Laplacian (CL). The statistical quantities are calculated using the MCA and compared with the results of the Direct Numerical Simulation (DNS). The results obtained from the MCA are in agreement with those from the DNS. It is shown that the MCA approach can predict the statistics of reactive scalars in random flows.

Thermal, structural and optical properties of NiOx thin films deposited by reactive dc-magnetron sputtering

The NiOx thin films were deposited by reactive dc-magnetron sputtering from a nickel metal target in Ar + O-2 with the relative O-2 content 5%. The as-deposited NiOx, thin films could represent a two-component system comprising crystalline NiO particles dispersed in an amorphous Ni2O3. Decomposition temperature of the as-deposited NiO, thin films was at about 263 degrees C. After annealed at 400 degrees C for 30 min in air, the surface morphology of the films became very rough due to the decomposition of the Ni2O3, leading to the changes of the optical properties of the NiO, thin films. The reflectivity of the films annealed at 400 degrees C was lower than that of the as-deposited one and the optical contrast was 52% at 405 nm. (c) 2006 Elsevier B.V. All rights reserved.

Rare earth doped beta-diketone complexes as promising high-density optical recording materials for blue optoelectronics

Some kinds of rare earth beta-diketone complexes with blue-violet light absorption edge were synthesized using the ligands of thenoyltrifluoroacctone (HTTA), 2, 2'-dipyridyl (BIPY) and different metal ions (Gd3+, Sm3+ and La3+). Their contents, structures and optoelectronic parameters were monitored by elemental analysis, MS, IR and UV spectra. The solubility of rare earth beta-diketone complexes in 2, 2, 3, 3-tetrafluoro-1-propanol (TFP) and absorption properties of their films in the region 300-800 nm were measured. The influence on the difference of absorption maximum from rare earth beta-diketone complexes to beta-diketone ligand by different metal ions was studied. In addition, the thermal stability of rare earth beta-diketone complexes was also reported. (C) 2005 Elsevier B.V. All rights reserved.

Design and construction of a static tester for blue ray optical storage

Blue ray optical storage is one of the important trends in the area of information storage, and attracts a number of researchers. Static tester for blue ray optical storage plays an important role in storage media research. We designed and constructed a static tester, in which modularization makes it very convenient to expand function. Employment of modulation/demodulation technique weakens test error so as to increase test precision. Focus move mode and the nano-positioners facilitate the relocation of recording marks. Only one laser with wavelength 406.7 nm is used. In this paper, system design and characteristics are represented in detail, and some experimental results are also given to show that the static tester can perform successfully, acting as research platform for blue ray optical storage. (c) 2005 Elsevier GmbH. All rights reserved.

Analysis on a new type magneto-optical disk for blue lasers

The conventional TbFeCo magneto-optical (MO) medium has a relatively smaller Kerr rotation angle in the blue region than in the red. With the recording wavelength gradually moving to the short wavelength, if TbFeCo is still used as recording medium, the conventional MO disk structure must be optimized to get a larger carrier to noise ratio (CNR). Sabi et al. have found that adding a metal layer attached to the TbFeCo film as thermal control layer is a useful way to get a high CNR. In this paper, we proved this through calculation, and carried out optimization of the new type of disk. Calculation results showed that the new structure is useful in preventing an excessive temperature increase, and has a better thermal response. (c) 2005 Elsevier B.V. All rights reserved.

Synthesis, spectroscopic and thermal properties of nickel (II)-azo complexes with blue-violet light wavelength

A novel azo dye containing isoxazole ring and beta-diketone derivative (TIAD) and its two nickel (II) complexes (Ni (II)-ETIAD and Ni (II)-HTIAD) were synthesized in order to obtain a blue-violet light absorption and better thermal stability as a promising organic storage material for next generation of high density digital versatile disc-recordable (HD-DVD-R) systems that uses a high numerical aperture of 0.85 at 405 nm wavelength. Their structures were confirmed on the basis of elemental analysis, MS, FT-IR, UV-Vis and magnetic data. Their solubility in 2,2,3,3-tetrafluoro-1-propanol (TFP) and absorption properties of thin film were measured. The difference of absorption maximum from the complexes to their ligands was discussed. In addition, the TG analysis of the complexes was also determined, and their thermal stability was evaluated. (C) 2004 Elsevier Ltd. All rights reserved.

热致NiOx薄膜的结构和光学性质变化

利用直流磁控反应溅射技术制备了氧气和氩气的分压比为5:100的NiOx薄膜。利用X射线衍射仪(XRD)、扫描电镜(SEM)、原子力显微镜(AFM)和光谱仪研究了热处理对薄膜的微观结构和光学性质的影响, 并对沉积态薄膜的粉末进行了热分析。沉积态的NiOx薄膜在262 ℃时开始分解, 导致NiOx薄膜的透过率增加和反射率降低。X射线衍射和示差扫描量热曲线(DSC)分析表明, 在热处理过程中并无物相的变化, 光学性质的变化是由于NiOx薄膜热分解引起薄膜表面形貌发生变化而引起的。通过Kissinger公式计算出

氧化铋薄膜用于蓝光可录存储的研究

利用直流磁控溅射法在不同氧氩分压比条件下制备了BiOx薄膜。通过对薄膜在蓝光作用前后的反射率对比度变化的研究发现，氧氩分压比为50％时制备的薄膜具有最佳的光学对比度。利用X射线衍射仪(XRD)、X光电子能谱(XPS)和光谱仪研究了薄膜热处理前后的结构和光谱性质的变化。研究结果表明薄膜光学性质变化主要由薄膜中氧化铋的相变引起。蓝光静态测试结果显示氧氩分压比为50％条件下制备的BiOx薄膜具有很好好的记录敏感度，在11mW的记录功率和800ns的记录脉宽条件下，得到了52％的反射率对比度。此外，BiOx薄膜表现出了非常好的读出稳定性。

Write-once medium with Fe-Doped BiOx thin films for blue laser recording

Fe:BiOx films are fabricated on K9 glass substrates by rf-magnetron sputtering of a BiFeO target under argon atmosphere with increasing sputtering power from 80 to 200 W at room temperature. It is found that the thin films grown at the sputtering power of 160W can be formed at an appropriate deposition rate and have an improved surface morphology. The XPS result reveals that the films investigated are comprised of Bi, Fe and O elements. A typical XRD pattern shows that no phase transition occurs in the films up to 400 degrees C. The results of the blue laser recording test demonstrate that the Fe:BiOx films have good writing sensitivity for blue laser beam (406.7 nm) and good stability after reading 10000 times. The recording marks of 200nm or less are obtained. These results indicate that the introduction of Fe into BiOx films can reduce the mark size and improve the stability of the films.

Compact continuous-wave blue lasers by direct frequency doubling of laser diodes with periodically poled lithium niobate waveguide crystals

A compact continuous-wave blue laser has been demonstrated by direct frequency doubling of a laser diode with a periodically poled lithium niobate (PPLN) waveguide crystal. The optimum PPLN temperature is near 28 degreesC, and the dependence of waveguide crystals on crystal temperature is less sensitive than that of bulk crystals. A total of 14.8 mW of 488-nm laser power has been achieved. (C) 2005 Optical Society of America.

Mechanisms of Yb3+ sensitization to Tm3+ for blue upconversion luminescence in fluorophosphate glass

The sensitization mechanisms of Yb3+ to Tm3+ for the blue upconversion luminescence in fluorophosphate glass were studied. Two different mechanisms exist in the sensitization. One is the sequential sensitization that Tm3+ is excited from H-3(6) to (1)G(4) through absorbing three photons transferred from Yb3+ one by one. Another is the cooperative sensitization that two Yb3+ ions form a couple cluster firstly, and then the couple cluster Yb3+ ions transfer their energy to Tm3+ and excite it to (1)G(4). With the increment of the concentration of Yb3+ ions, the sequential sensitization becomes weak and the cooperative sensitization becomes intense, and the transformation trend of sensitization mechanism with the increment of Yb3+ concentration can be clarified by the introduction of Th3+ ions in the glass. (c) 2006 Elsevier B.V. All rights reserved.