226 resultados para NaYF4: 0.02Er center dot xYb-PVP nanofibers
em Chinese Academy of Sciences Institutional Repositories Grid Portal
Resumo:
NaYF4: 0.02Er center dot xYb-PVP composite nanofibers with the diameter of similar to 400 nm have been prepared by electrospinning. Field emission scanning electron microscope and X-ray diffraction have been utilized to characterize morphology and structure of the as-prepared electrospun nanofibers. Their up-conversion luminescence is investigated under a 980-nm excitation. Green (538 and 520 nm), red (6-55 nm), and blue (405 nm) emissions are observed in the up-conversion luminescence spectra, and the intensity of these three emissions changes differently with the variety of Yb content, which has been interpreted successfully in this letter. The color of NaYF4: 0.02Er center dot xYb-PVP nanolibers under a 980-nm excitation can be changed from green --> white --> yellow gradually via changing the Yb content.
Resumo:
Ag nanoparticle embedded NaYF4:0.05Tb center dot chi Ce/ PVP (PVP stands for poly(vinyl pyrrolidone)) composite nanofibers have been prepared by electrospinning. A field emission scanning electron microscope and x-ray diffraction have been utilized to characterize the size, morphology and structure of the as-prepared electrospun nanofibers. Obvious photoluminescence (PL) of NaYF4:0.05Tb center dot 0.05Ce/PVP electrospun nanofibers due to the efficient energy transfer from Ce3+ to Tb3+ ions is observed. The PL intensity of the electrospun nanofibers decreases gradually with the addition of Ag nanoparticles. No obvious surface plasmon resonance enhanced luminescence is observed. The reasons for the weakening of the emission intensity with the addition of Ag nanoparticles have also been discussed in this work.
Resumo:
A new polyoxometalate [Co(phen)(3)](2)[HPMo4V Mo-4(VI) V-6(IV) M2O44]center dot 4H(2)O (M = 0.78Mo(V)+ 0.22V(IV)) 1 was hydrothermally synthesized and characterized by IR, elemental analyses, X-ray photoelectron spectrum, ESR and single crystal X-ray diffraction. The title compound is in the triclinic space group P (1) over bar with a = 12.0953(7) angstrom, b = 14.0182(6) angstrom, c = 14.6468(7) angstrom, V=2402.55(18) angstrom(3), alpha = 105.134(2), beta = 91.841(3), gamma = 91.401(2), Z = 1, and R-1 (wR(2)) = 0.0617 (0.1701). The compound was prepared from tetra-capped pseudo-Kepin with phosphorus-centered polyoxoanions [PMo8V6M2O44](5-) , [Co(phen)(3)](2+) cations and linked through hydrogen bonds and pi-pi stacking interaction into three-dimensional supramolecular framework. Astudy of the magnetic properties of 1 demonstrates that it exhibits antiferromagnetic coupling interactions.
Resumo:
A copper-strontium heterometallic coordination polymer was synthesized and characterized by elemental analysis and IR spectra. The crystal structure was determined by single-crystal X-ray diffraction analyses. The title complex is a 2 D coordination polymer with the chemical formula [[(CuL)(2)Sr (H2O) center dot Sr-2 ((HO)-O-2)(7)]center dot 2H(2)O center dot 0.5CH(3)OH](n), where H4L = N-(2-hydroxybenzamido)-N'-(3-carboxylsalicylidene) ethylenediamine. Its structural unit is comprised of two adjacent units, which polymerized with each other to form a new layered heterometallic coordination polymer.
Resumo:
A novel organic-inorganic hybrid compound [Cu(phen)](2)[(VV4As2O19)-V-IV-As-V-O-V].0.5H(2)O 1 has been hydrothermally synthesized. Its structure, determined by single crystal X-ray diffraction, exhibits an unusual two-dimensional arsenic vanadate layered network grafted with the [Cu(phen)](2+) complex. The chelating phen ligands project perpendicularly beyond the inorganic layer. Variable temperature magnetic susceptibility studies indicate that both ferro- and antiferro-magnetic interactions exist in 1.
Resumo:
An investigation into the interactions between thiamine monophosphate (TMP) and anions has resulted in the preparation and X-ray characterization of the compounds (TMP)(Hg2Br5).0.5H(2)O (1) and (TMP)(2)(Hg3I8) (2). In each compound the TMP molecule exists as a monovalent cation in the usual F conformation. The halogenomercurate anions occur in two-dimensional (2-D) network in 1 or one-dimensional (1-D) chain in 2. In both 1 and 2, the structures consist of alternating cationic sheets of the hydrogen-bonded TMP molecules and anionic sheets of the polymeric halogenomercurate anions. The TMP molecule binds to the polymeric anions through the characteristic 'anion bridge I', C(2)-H..X...pyrimidinium (X = Br in 1 and 1 in 2), and electrostatic interactions between electropositive S(1) and halogen atoms. The 'anion bridge II' of the type N(4'1)-H...X...thiazolium (X = phosphate group) plays a role in stabilizing the molecular conformation. The biological implication of the host-guest-like complexation between TMP and polymeric anions is discussed.
Resumo:
The deposition of CdO center dot nH(2)O On CdTe nanoparticles was studied in an aqueous phase. The CdTe nanocrystals (NCs) were prepared in aqueous solution through the reaction between Cd2+ and NaHTe in the presence of thioglycolic acid as a stabilizer. The molar ratio of the Cd2+ to Te2- in the precursory solution played an important role in the photoluminescence of the ultimate CdTe NCs. The strongest photoluminescence was obtained under 4.0 of [Cd2+]/[Te2-] at pH similar to 8.2. With the optimum dosage of Cd(II) hydrous oxide deposited on the CdTe NCs, the photoluminescence was enhanced greatly. The photoluminescence of these nanocomposites was kept constant in the pH range of 8.0-10.0, but dramatically decreased with an obvious blue-shifted peak while the pH was below 8.0. In addition, the photochemical oxidation of CdTe NCs with cadmium hydrous oxide deposition was markedly inhibited.
Resumo:
The deposition of CdO center dot nH(2)O On CdTe nanoparticles was studied in an aqueous phase. The CdTe nanocrystals (NCs) were prepared in aqueous solution through the reaction between Cd2+ and NaHTe in the presence of thioglycolic acid as a stabilizer. The molar ratio of the Cd2+ to Te2- in the precursory solution played an important role in the photoluminescence of the ultimate CdTe NCs. The strongest photoluminescence was obtained under 4.0 of [Cd2+]/[Te2-] at pH similar to 8.2. With the optimum dosage of Cd(II) hydrous oxide deposited on the CdTe NCs, the photoluminescence was enhanced greatly. The photoluminescence of these nanocomposites was kept constant in the pH range of 8.0-10.0, but dramatically decreased with an obvious blue-shifted peak while the pH was below 8.0. In addition, the photochemical oxidation of CdTe NCs with cadmium hydrous oxide deposition was markedly inhibited.
Resumo:
The electronic structures of InSb1-xNx nanowires are investigated using the ten-band k center dot p method. It is found that nitrogen increases the Rashba coefficient of the nanowires dramatically. For thick nanowires, the Rashba coefficient may increase by more than 20 times. The semiconductor-metal transition occurs more easily in InSb1-xNx nanowires than in InSb nanowires. The electronic structure of InSb1-xNx nanowires is very different from that of the bulk material. For fixed x the bulk material is a semimetal, while the nanowires are metal-like. In InSb1-xNx bulk material and thick nanowires, an interesting decrease of electron effective mass is observed near k=0 which is induced by the nitrogen, but this phenomenon disappears in thin nanowires.
Resumo:
The crystal structures of EtEDTB.1.4C(2)H(5)OH.5H(2)O 1 and H4EtEDTB(ClO4)(4).C2H5OH 2 (EtEDTB = N, N,N',N'-tetrakis[2-(1-ethylbenzimidazolyl)methyl]-1,2-ethanediamine) have been determined by single-crystal X-ray diffraction method. Compound 1 crystallizes in the space group P(1) over bar with a = 11.489(2), b = 11.866(3), c = 12.002(3) Angstrom, alpha = 97.47(2), beta = 114.564(13), gamma = 114.11(2)degrees, V = 1266.6(5) Angstrom(3), Z = 1, M-r = 847.48, D-c = 1.111 g/cm(3), F(000) = 456 and mu(MoKalpha) = 0.076 mm(-1). A total of 5207 reflections were measured for 1, of which 4323 were independent. The structure of 1 was solved by direct methods and refined by full-matrix least-squares technique to the final R = 0.0706 and wR = 0.1802 for 1318 observed reflections with I > 2sigma(I). In the structure of 1, centrosymmetric EtEDTB molecules are linked by hydrogen bonds through water and ethanol to form 2-dimensional network. Compound 2 crystallizes in the space group C2/c with a = 24.260(5), b = 13.040(3), c = 17.680(4) Angstrom, beta = 97.50(3)degrees, V = 5545.2(2) Angstrom(3), Z = 4, M-r = 1140.80, D-c = 1.366 g/cm(3), F(000) = 2384 and mu(MoKalpha) = 0.289 mm(-1).
Resumo:
An organic-inorganic hybrid molybdenum phosphate, Na-2[{Mn(phen)(2)(H2O)} {Mn(phen)(2)}(3){(MnMo12O24)-O-v (HPO4)(6)(PO4)(2) (OH)(6)}] . 4H(2)O (phen=1,10-phenanthroline), involving molybdenum present in V oxidation state and covalently bonded transition metal coordination complexes, has been hydrothermally synthesized and structurally characterized by single-crystal X-ray diffraction. Deep brown-red crystals are formed in the triclinic system, space group P (1) over bar, a=16.581(l)Angstrom, b=18.354(1)Angstrom, c=24.485(2)Angstrom, alpha=80.589(l)degrees, beta=71.279(1)degrees, gamma=67.084(1)degrees, V=6493.8(8)Angstrom(3), Z=2, lambda(MoKalpha)=0.71073Angstrom (R(F)=0.0686 for 29,053 reflections). Data were collected on a Bruker Smart Apex CCD diffractometer at 293 K in the range of 1.76 < theta < 28.06degrees using omega-2theta scans technique. The structure of the title compound may be considered to be based on {Mo6O12(HPO4)(3)(PO4)(OH)(3)} units bonded together with {Mn(phen)(2)} subunits into a two-dimensional network. Two types of tunnels are observed in the solid of the title compound.
Resumo:
The hydrothermal reactions of vanadium oxide starting materials with divalent transition metal cations in the presence of nitrogen donor chelating ligands yield the bimetallic cluster complexes with the formulae [{Cd(phen(2))(2)V4O12].5H(2)O (1) and [Ni(phen)(3)](2)[V4O12] . 17.5H(2)O (2). Crystal data: C48H52Cd2N8O22V4 (1), triclinic. P (1) over bar, a = 10.3366(10), b = 11.320(3), c = 13.268(3) Angstrom, alpha = 103.888(17)degrees, beta = 92.256(15)degrees, gamma = 107.444(14)degrees, Z = 1; C72H131N12Ni2O29.5V4 (2), triclinic. P (1) over bar, a = 12.305(3), b = 13.172(6), c = 15.133(4), alpha = 79.05(3)degrees, beta = 76.09(2)degrees, gamma = 74.66(3)degrees, Z = 1. Data were collected on a Siemens P4 four-circle diffractometer at 293 K in the range 1.59degrees < theta < 26.02degrees and 2.01degrees < 0 < 25.01degrees using the omega-scan technique, respectively. The structure of 1 consists of a [V4O12](4-) cluster covalently attached to two {Cd(phen)(2)}(2+) fragments, in which the [V4O12](4-) cluster adopts a chair-like configuration. In the structure of 2, the [V4O12](4-) cluster is isolated. And the complex formed a layer structure via hydrogen bonds between the V4O12](4-) unit and crystallization water molecules.
Resumo:
In this paper, we will report the preparation of a mixed-valence polyoxometalate compound (Bu4N)(4)[PMo12O40].2DMF.H2O (TBA = tetrabutylammonium; DMF = N,N-dimethyl formamide). The title compound has been photochemically synthesized and characterized by using elemental analysis, IR, solid diffusion reflectance electronic spectra, ESR spectra, XPS, CV and X-ray single-crystal analysis. The crystal lographic data are as follows: monoclinic, P2(1)/c, a = 14.124(3), b = 17.481(4), c = 22.744(5) Angstrom, beta = 101.66(3)degrees, V = 5500(2) Angstrom(3), C70H160Mo12N6O43P, M-r = 2956.29, Z = 2, D-c = 1.785 g/cm(3), F(000) = 2970 and mu(MoKalpha) = 1.412 mm(-1). The structure has been refined to R = 0.0638 and wR = 0.1975 by full-matrix least-squares methods. The title compound is composed of four tetrabutylammonium cations, one [(PMoMo11O40)-Mo-V](4-) heteropoly anion, two N,N-dimethyl formamide and one H2O molecule.
Resumo:
A new compound, [Ni(en)(3)](2)[Ni(en)(2)(H2O)(2)][As6V15O42] . 4H(2)O, was first prepared by hydrothermal synthesis and characterized by elemental analysis, IR, TGA-DSC, ESR and single crystal X-ray diffraction. Crystal data: monoclinic, space group C-c, a = 1. 523 6(3) nm, b = 2. 051 8(4) nm, c = 2.395 9(5) nm, beta = 97. 41(3)degrees, V = 7.427(3) nm(3), Z = 4, R = 0. 057 0, wR(2) = 0.135 7. The polyanion consists of six AsO3 pyramids and fifteen VO5 pyramids. Counterions are complex ions with octahedral structure, which consist of NH2CH2CH2NH2 and Ni2+.