Citrate-gel synthesis and luminescent properties of alpha-Zn-3(PO4)(2) doped with Eu3+

By using inorganic salts as raw materials and citric acid as complexing agent, alpha-Zn-3(PO4)(2) and Eu3+ doped alpha-Zn-3(PO4)(2) phosphor powders were prepared by a citrate-gel process. X-ray diffraction, (XRD), TG - DTA, FT - IR and luminescence excitation and emission spectra were used to characterize the resulting products. The results of XRD reveal that the powders begin to crystallize at 500 degreesC and pure alpha-Zn-3(PO4)(2) phase is obtained at 800 degreesC. And the results of XRD reveal that Eu3+ exists Lis EoPO(4) ill the powder. In the phosphor powders, the Eu3+ shows its characteristic red-orange (592 nm, D-5(0) - F-7(1)) emission and has no quenching concentration.

Seed-mediated synthesis of branched gold nanoparticles with the assistance of citrate and their surface-enhanced Raman scattering properties

We report an easy synthesis of highly branched gold particles through a seed-mediated growth approach in the presence of citrate. The addition of citrate in the growth solution is found to be crucial for the formation of these branched gold particles. Their size can be varied from 47 to 185 nm. The length of the thumb-like branch is estimated to be between about 5 and 20 nm, and changes slightly as the particle size increases. Owing to these obtuse and short branches, their surface plasmon resonance displays a marked red-shift with respect to the normal spherical particles. These branched gold particles exhibit stronger SERS activity than the non-branched ones, which is most likely related to these unique branching features.

Synthesis of Sr2CeO4: Eu-3 by citrate-gel method and its luminescence properties

A novel phosphor Sr2CeO4 was synthesized by the citrate-gel method. The results of XRD show that the temperature at which the crystallization starting is lowered and the soak time for complete crystallization is decreased. The values of pH of the precursor and the ratio( R) between the citrate and cation ions have an effect on the crystallization process. The host can transfer its exciting energy to rare earth ion Eu3+. The doped compound emits strong white light when the concentration of the doped Eu3+ is low. When that of Eu3+ is increased, it emits strong red light. The fluorescence from the higher excited states can be observed because the multiphonon relaxation probability between Eu3+ ions is low.

Nitrate-citrate combustion synthesis and properties of Ce1-xSmxO2-x/2 solid solutions

A nitrate-citrate combustion route to synthesize nanocrystalline samarium-doped ceria powders for solid electrolyte ceramics is presented. This route is based on the gelling of nitrate solutions by the addition of citric acid and ammonium hydroxide, followed by an intense combustion process due to an exothermic redox reaction between nitrate and citrate ions. The influence of ignition temperature on the characteristics of the powders was studied. The change of the crystal structure with the content of doped Sm was investigated. High temperature X-ray, and Raman scattering were used to characterize the sample. The lattice constant and unit volume increase with doping level and increasing temperature. Dense ceramic samples prepared by uniaxial pressing and sintering in air were also studied.

Citrate-gel synthesis and luminescent properties of ZnGa2O4 doped with Mn2+ and EU3+

By using inorganic salts as raw materials and citric acid as complexing agent, spinel oxide ZnGa2O4 and Mn2+, Eu3+-doped ZnGa2O4 phosphor powders were prepared by a citrate-gel process. X-ray diffraction (XRD), TG-DTA, FT-IR. and luminescence excitation and emission spectra were used to characterize the resulting products. The results of XRD reveal that the powders begin to crystallize at 500 degreesC and pure ZnGa2O4 phase is obtained at 700 degreesC, which agrees well with the results of TG-DTA and FT-IR. In the crystalline ZnGa2O4, the Eu shows its characteristic red (615 nm, D-5(0)-F-7(2)) emission with a quenching concentration of 5 mol% (of Ga3+), and the Mn shows green emission (505 nm, T, A,) with a quenching concentration of 0.1 mol% (of Zn2+). The luminescence mechanism of ZnGa2O4:Mn2+/Eu3+ is presented.

A new dinuclear molybdenum(V)-sulfur complex containing citrate ligand: synthesis and characterization of K2.5Na2NH4[Mo2O2S2(cit)(2)].5H(2)O

The complex, K2.5Na2NH4[Mo2O2S2(cit)(2)]. 5H(2)O (1), was obtained by crystallization from a solution of (NH4)(2)MoS4, potassium citrate (K(3)cit) and hydroxyl sodium in methanol and water under an atmosphere of pure nitrogen at ambient temperature. The crystals are triclinic, space group , a = 7.376 (3)Angstrom, b = 14.620 (2) Angstrom, c = 14.661 (1) Angstrom, alpha = 71.10 (1)degrees, beta = 81.77 (1)degrees, gamma = 78.27(2)degrees, R = 0.0584 for 2545 observed (I > 2 sigma (I)) reflections. Single crystal structure analysis reveals that citrate ligand coordinated to molybdenum atom through two carboxylato oxygens and one deprotonated hydroxyl oxygen together with two bridging sulfur atoms and a terminal oxygen atom completes distorted coordination octahedron around each molybdenum atom. Principal dimensions are: Mo = O-t, 1.707 Angstrom (av); Mo-S-b, 2.341 Angstrom (av); Mo-O-(hydroxyl), 2.021 Angstrom (av); Mo-O(alpha-carboxyl), 2.1290 Angstrom (av) and Mo-O(beta-carboxyl), 2.268(av) Angstrom. IR spectrum is in agreement with the structure.

Synthesis and properties of cerium oxide nanometer powders by pyrolysis of amorphous citrate

CeO2 nanometer powders of different sizes were prepared at low temperature by pyrolysis of amorphous citrate. XRD patterns show that CeO2 is cubic in structure, space group O-h(5)-F-M3M. TEM indicates that the prepared CeO2 is spherical in shape, and the particle size distribution is in narrow range. It was found that calcination temperature is a more important factor affecting the crystallite size of CeO2 than calcining time, the smaller the particle, the bigger the crystal lattice distortion, the worse the crystal growth. Solubility test of CeO2 in nitric acid reveals that the surface activity of CeO2 decreases with the increasing particle sizes. IR spectra analysis shows that the absorption of Ce-O bond is shifted to higher energy with the decrease of CeO2 particle sizes.

C-13 NMR study on the aqueous structure of lanthanide citrate complexes

The aqueous complexation of lanthanide complexes of citrate in pH 7.4 solutions has been studied by using lanthanide-induced shift and relaxation times measurement methods. These results indicate that citrate coordinate via 3-hydroxyl and 3-carboxylate groups with lanthanide ions and form 1:2 (Ln/cit) isostructural complexes through lanthanide series. We suggest a new coordination geometry which is different from that described in literature.

LANTHANIDE-INDUCED SHIFT AND RELAXATION RATE STUDIES OF THE AQUEOUS COMPLEXATION OF CITRATE

The aqueous complexation of lanthanide ions with citrate in pH 7.4 solution has been investigated with use of the lanthanide-induced shift and paramagnetic relaxation rate enhancement methods. The results show that citrate coordinates via hydroxyl and central carboxylate groups with lanthanide ions and forms 1:2 (Ln/cit) isostructural complexes through the lanthanide series. A new possible coordination geometry deduced from our experimental data is suggested and discussed.

Large Scale Fabrication Of Periodical Bowl-Like Micropatterns Of Single Crystal Zno

Nanostructured ZnO materials are of great significance for their potential applications in photoelectronic devices, light-emitting displays, catalysis and gas sensors. In this paper, we report a new method to produce large area periodical bowl-like micropatterns of single crystal ZnO through aqueous-phase epitaxial growth on a ZnO single crystal substrate. A self-assembled monolayer of polystyrene microspheres was used as a template to confine the epitaxial growth of single crystal ZnO from the substrate, while the growth morphology was well controlled by citrate anions. Moreover, it was found that the self-assembled monolayer of colloidal spheres plays an important role in reduction of the defect density in the epitaxial ZnO layer. Though the mechanism is still open for further investigation, the present result indicates a new route to suppress the dislocations in the fabrication of single crystal ZnO film. A predicable application of this new method is for the fabrication of two-dimensional photonic crystal structures on light emitting diode surfaces.

Direct synthesis and intense luminescence of Y2O3 : Eu nanophosphors by complexation combustion

In this paper, we report the synthesis of high-luminance Y2O3:Eu nanocrystal through a citrate-nitrate complexation combustion method at a low temperature of 200-280 degrees C. The as-combusted Y2O3:Eu phosphors are almost equiaxed crystallites with an average size of 30-40 run, and have an intense red luminescence. The present fuel-deficient method suggests that by control of the ratio of citric acid to nitrates, it is valuable for the fabrication of Y2O3 nanoparticles without heat treatment. This process should be applicable to a wide range of nanocrystal oxides.

Synthesis of CaCu3Ti4O12 ceramic via a sol-gel method

The novel nano-ultrafine powders for the preparation of CaCu3Ti4O12 ceramic were prepared by the sol-gel method and citrate auto-ignition method. The obtained precursor powders were pressed, sintered at 1000 degrees C to fabricate microcrystal CaCu3Ti4O12 ceramic. The microcrystalline phase of CaCu3Ti4O12 was confirmed by X-ray powder diffraction (XRD). The morphology and size of the grains of the powders and ceramics under different heat treatments were observed using scanning electron microscopy (SEM). The relative dielectric constant of the ceramic sintered at 1000 degrees C was measured with a magnitude of more than 10(4) at room temperature, which was approaching to those of Pb-containing complex perovskite ceramics, and the loss tangent was less than 0.20 in a broad frequency region. The relative dielectric constant and loss tangent were also compared with that of CaCu3Ti4O12 ceramic prepared by other reported methods. (c) 2006 Elsevier B.V. All rights reserved.