半金属zb-CrAs 和稀磁半导体(Ga,Cr)As 薄膜分子束外延生长和磁性质研究

Submitted by zhangdi (zhangdi@red.semi.ac.cn) on 2009-04-13T11:45:31Z

Growth parameter dependence of magnetic property of CrAs thin film

This paper has systematically investigated the substrate temperature and thickness dependence of surface morphology and magnetic property of CrAs compound films grown on GaAs by molecular-beam epitaxy. It finds that the substrate temperature affects the surface morphology and magnetic property of CrAs thin film more potently than the thickness.

Room-temperature ferromagnetism in zinc-blende and deformed CrAs thin films

We try to clarify the controversy about the origin of room-temperature ferromagnetism in a CrAs compound. Two kinds of CrAs thin films were grown on GaAs by molecular-beam epitaxy. Structural analyses confirm that the as-grown CrAs film is a pure zinc-blende phase. Magnetic measurements suggest that room-temperature ferromagnetism exists in zinc-blende CrAs. In contrast, the CrAs film turns into a mixture of zinc-blende and deformed CrAs after annealing. A ferromagnetic signal measured at room temperature demonstrates that zinc-blende CrAs remains room-temperature ferromagnetism even when it is partly deformed into a non-zinc-blende phase. (c) 2006 American Institute of Physics.

Growth of thicker zinc-blende CrSb layers by using (In,Ga)As buffer layers

Zinc-blende CrSb (zb-CrSb) layers with room-temperature ferromagnetism have been grown on (In,Ga)As buffer layers epitaxially prepared on (001) GaAs substrates by molecular-beam epitaxy. Compared with the typical thickness [2-3 ML (ML denotes monolayers)] of zb-CrSb grown directly on GaAs, the thickness of zb-CrSb grown on (In,Ga)As has been increased largely; the maximum can be up to similar to 9 ML. High-resolution cross sectional transmission electron microscopy images show that the zb-CrSb layer is combined with (In,Ga)As buffer layer without any dislocations at the interface. (C) 2006 American Institute of Physics.

Growth and magnetic properties of zincblende CrSb epilayers on relaxed and strained (In, Ga)As buffers

Zincblende CrSb (zb-CrSb) layers with room-temperature ferromagnetism have been grown on relaxed and strained (In,Ga)As buffer layers epitaxially prepared on (001) GaAs substrates by molecular-beam epitaxy. The structural characterizations of CrSb layers fabricated under the two cases are studied by using synchrotron grazing incidence x-ray diffraction (GID). The results of GID experiments indicate that no sign of second phase exists in all the zb-CrSb layers. Superconducting quantum interference device measurements demonstrate that the thickness of zb-CrSb layers grown on both relaxed and strained (In,Ga)As buffer layers can be increased to similar to 12 monolayers (similar to 3.6nm), compared to similar to 3 monolayers (similar to 1nm) on GaAs directly.