Fluorescent Ag nanoclusters in glass induced by an infrared femtosecond laser

We report a method for the selective introduction of fluorescent Ag nanoclusters in glass. Extinction and photoluminescence spectra show that a fraction of the Ag atoms are generated through femtosecond laser induced multiphoton reduction and then aggregate to form Ag nanoclusters after heat treatment. Red luminescence from the irradiated region is observed under blue or green laser excitation. The fluorescence can be attributed to interband transitions within Ag nanoclusters. This method provides a novel route to fabricate fluorescent nanomaterials in 3D transparent materials. (c) 2007 Elsevier B.V. All rights reserved.

Effect of cerium oxide on the precipitation of silver nanoparticles in femtosecond laser irradiated silicate glass

We investigated the effect of cerium oxide on the precipitation of Ag nanoparticles in silicate glass via a femtosecond laser irradiation and successive annealing. Absorption spectra show that Ce3+ ions may absorb part of the laser energy via multiphoton absorption and release free electrons, resulting in an increase of the concentration of Ag atoms and a decrease of the concentration of hole-trapped color centers, which influence precipitation of the Ag nanoparticles. In addition, we found that the formed Ag-0 may reduce Ce4+ ions to Ce3+ ions during the annealing process, which inhibits the growth of the Ag nanoparticles.

Theoretical study of interaction between atoms of Au, Ag, Cu and clean Si(111) surface

To evaluate the interactions between the atoms of An, Ag and Cu and clean Si(111) surface, two types of silicon clusters Si4H7 and Si16H20 together with their metal complexes were studied by using hybrid (U)B3LYP density functional theory method. Optimized geometries and energies on different adsorption sites indicate that: (1) the binding energies at different adsorption sites are large (ranging from similar to 1.2 to 2.6 eV depend on the metal atoms and adsorption sites), suggesting a strong interaction between metal atom and silicon surface; (2) the most favorable adsorption site is the on top (T) site. Mulliken population analysis indicated that in the system of on top (T) site, a covalent bond is formed between metal atom and dangling bond of surface Si atom. (c) 2006 Elsevier B.V. All rights reserved.

Cu原子簇触发形核下的深过冷Ag-Ge合金组织演变研究

采用玻璃包覆的方法获得具有较大过冷度的亚共晶、共晶以及过共晶Ag-Ge合金熔体,并通过高能离子束轰击Cu箔产生Cu原子团簇溅射到过冷合金熔体中来触发非均质形核过程.凝固后合金显微组织的分析结果表明:在深过冷合金熔体中引入Cu原子团簇,它对亚共晶、共晶以及过共晶Ag-Ge合金的显微组织演变有着不同的影响效果,分析了显微组织的演变规律与形成机制. The Ag-Ge alloy melts with deeply undercooled hypoeutectic, eutectic and hypereutectic were obtained via glass fluxing technique. The nucleation of the deeply undercooled alloy melts were triggered by atoms cluster sputtering on the surface of the melts. The atoms clusters were generated by an ion beam bombarding on the Cu foil fixed above the alloy melts. The resultant microstructure reveals that the induced atom clusters exert great influence on the microstructural evolution of the highly undercooled eutectic and hypereutectic Ag-Ge alloys, but no obvious influence on the highly undercooled hypoeutectic alloy. The microstructural evolution and formation mechanism were analyzed and discussed.

Cu原子簇触发形核下的深过冷Ag-Ge合金组织演变研究

采用玻璃包覆的方法获得具有较大过冷度的亚共晶、共晶以及过共晶Ag-Ge合金熔体，并通过高能离子束轰击Cu箔产生Cu原子团簇溅射到过冷合金熔体中来触发非均质形核过程。凝固后合金显微组织的分析结果表明：在深过冷合金熔体中引入Cu原子团簇，它对亚共晶、共晶以及过共晶Ag-Ge合金的显微组织演变有着不同的影响效果，分析了显微组织的演变规律与形成机制。

Photoreduction of Ag+ in aluminoborate glasses induced by irradiation of a femtosecond laser

We report on photoreduction of Ag+ in aluminoborate glasses induced by irradiation of a femtosecond laser. Novel fluorescence was observed in the femtosecond laser irradiated glass when excited by a 365 nm ultraviolet lamp. Optical absorption, emission, and electron spin resonance spectra of the glass samples demonstrated that after the laser irradiation, portions of silver ions near the focused part of the laser beam inside the glass were reduced to silver atoms, which resulted in the formation of the characteristic fluorescence. The observed phenomenon may have promising applications in the fabrication of functional optical devices.

Al2O3和Cr过渡层对Ag膜光学性质及其附着力的影响

研究了在玻璃基底上镀制Al2O3和Cr过渡层对Ag膜反射率及附着力的影响.分光光度计测试了Ag膜的反射率,结果表明,与Cr过渡层相比,Al2O3过渡层对Ag膜反射率的降低相对较小;而且,随着Al2O3厚度的增加,Ag膜的反射率先增大后减小.XRD与AES测试表明,引入Al2O3或Cr可明显细化Ag晶粒,减弱Ag膜（111）织构;Al2O3作过渡层时,Al原子向Ag层中扩散显著;而Cr作过渡层时,只有少量Cr原子扩散进入Ag层.因此,Al2O3作过渡层能显著增强薄膜与玻璃基体之间的附着力.

Formation of high reflective Ni/Ag/Ti/Au contact on p-GaN

A metallization scheme of Ni/Ag/Ti/Au has been developed for obtaining high reflective contacts on p-type GaN. In order to find optimal conditions to get a high reflectivity, we studied samples with various Ni thicknesses, annealing temperatures and annealing times. By annealing at 500 degrees C for 5 min in an O-2 ambient, a reflectivity as high as 94% was obtained from Ni/Ag/Ti/Au (1/120/120/50 nm). The effects of Ti layers on the suppression of Ag agglomeration were investigated by using Auger electron spectroscopy (AES). From AES depth profiles, it is clear that Ti acts as a diffusion barrier to prevent Au atoms from diffusing into the Ag layer, which is important in the formation of high reflectivity.

Enhanced nucleation of Ag nanoparticles by vacancy-type defects in Ar-ions implanted spinel

Vacancy-type defects are introduced into magnesium aluminate spine] (MgAl2O4 (1 1 0)) by Ar-ions implantation, and then Ag-ions are implanted into the depth rich in vacancy-type defects. The ultraviolet-visible spectrometry (UV-VIS) and positron annihilation spectroscopy (PAS) are used to study the influence of vacancy-type defects on nucleation of Ag nanoparticles. After introduction of vacancy-type defects the pronounced increase of surface plasmon resonance (SPR) absorbance intensity indicates that defects enhance the nucleation of Ag nanoparticles. The PAS results reveal that vacancy-type defects provide pre-nucleating centers for Ag nanoparticles nucleation and growth. (C) 2010 Elsevier B.V. All rights reserved.

Electrochemical Metalloimmunoassay Based on Enlargement of Gold Nanoparticle Label Treated with Ag Enhancement System

A novel sensitive electrochemical immunoassay with colloidal gold as the antibody labeling tag and subsequent signal amplification by silver enhancement is described. Colloidal gold was treated by a light-sensitive silver enhancement system which made silver deposit on the surface of colloidal gold(form Au/Ag core-shell structure), followed by the release of the metallic silver atoms anchored on the antibody by oxidative dissolution of them in an acidic solution and the indirect determination of the dissolved Ag+ ions by anodic stripping voltammetry(ASV) at a carbon fiber microelectrode. The electrochemical signal is directly proportional to the amount of analyte(goat IgG) in the standard or a sample. The method was evaluated by means of a noncompetitive heterogeneous immunoassay of immunoglobulin G(IgG) with a concentration as low as 0.2 ng/ mL. The high performance of the method is related to the sensitive ASV determination of silver(I) at a carbon fiber microelectrode and to the release of a large number of Ag+ ions from each silver shell anchored on the analyte(goat IgG).

A new alpha-Keggin type polyoxometalate coordinated to four silver complex moieties: {PW9V3O40[Ag(2,2 '-bipy)](2)[Ag-2(2,2 '-bipy)(3)](2)}

A new polyoxometalate derivative {PW9V3O40[Ag(2,2'-bipy)](2)[Ag-2(2,2'-bipy)(3)](2)} 1 has been hydrothermally synthesized and structurally characterized by the single crystal X-ray diffraction. X-Ray analysis showed that both [Ag(2,2'-bipy)](+) and [Ag-2(2,2'-bipy)(3)](2+) units are supported on the alpha-Keggin polyoxoanion [PW9V3O40](6-) via the surface bridging oxygen atoms. 1 represents the first alpha-Keggin type polyoxoanion coordinated with four transition metal complex moieties, which further acts as a neutral molecular units for the construction of an interesting three-dimensional supramolecular framework.

EXTENDED SOLUBILITY AND SPIN-GLASS BEHAVIOR IN A AG-GD SOLID-SOLUTION PREPARED BY MECHANICAL ALLOYING

The effects of mechanical alloying on the solubility in a Ag-Gd solid solution have been investigated. The study shows that the solubility of Gd in Ag can be extended to about 5 at. % Gd by mechanical alloying from the equilibrium solubility of less than 0.95 at. % Gd. Ag85Gd15 prepared by mechanical alloying exhibits a spin-glass-type transition at similar to 5 K. A Curie-Weiss behavior at higher temperatures and x-ray patterns of the material indicate that Gd atoms are either dissolved in the Ag matrix or in the form of small clusters of diameters of a few nanometers;

Ab initio pair potentials at metal-ceramic interfaces

A systematic approach is proposed to obtain the interfacial interatomic potentials. By inverting ab initio adhesive energy curves for the metal-MgO ceramic interfaces, We derive interfacial potentials between Ag and O2-, Ag and Mg2+, Al and O2-, Al and Mg2+. The interfacial potentials, obtained from this method, demonstrate general features of bondings between metal atoms and ceramic ions.

The inner Pressure of the Atoms in a Solid in Refined TFD Theory

The relation between the inner pressure of an atom in a solid and the density of energy of electrons under Refined TFD theory is given.