The nanocomposite scaffold of poly(lactide-co-glycolide) and hydroxyapatite surface-grafted with L-lactic acid oligomer for bone repair

Nanohydroxyapatite (op-HA) surface-modified with L-lactic acid oligomer (LAc oligomer) was prepared by LAc oligomer grafted onto the hydroxyapatite (HA) surface. The nanocomposite of op-HA/PLGA with different op-HA contents of 5, 10, 20 and 40 wt.% in the composite was fabricated into three-dimensional scaffolds by the melt-molding and particulate leaching methods. PLGA and the nanocomposite of HA/PLGA with 10 wt.% of ungrafted hydroxyapatite were used as the controls. The scaffolds were highly porous with evenly distributed and interconnected pore structures, and the porosity was around 90%. Besides the macropores of 100-300 mu m created by the leaching of NaCl particles, the micropores (1-50 mu m) in the pore walls increased with increasing content of op-HA in the composites of op-HA/PLGA. The op-HA particles could disperse more uniformly than those of pure HA in PLGA matrix. The 20 wt.% op-HA/PLGA sample exhibited the maximum mechanical strength, including bending strength (4.14 MPa) and compressive strength (2.31 MPa). The cell viability and the areas of the attached osteoblasts on the films of 10 wt.% op-HA/PLGA and 20 wt.% op-HA/PLGA were evidently higher than those on the other composites.

Preparation of bioactive glass ceramic nanoparticles by combination of sol-gel and coprecipitation method

SiO2-CaO-P2O5 ternary bioactive glass ceramic nanoparticles were prepared via the combination of sol-gel and coprecipitation processes. Precursors of silicon and calcium were hydrolyzed in acidic solution and gelated in alkaline condition together with ammonium dibasic phosphate. Gel particles were separated by centrifugation, followed by freeze drying, and calcination procedure to obtain the bioactive glass ceramic nanoparticles. The investigation of the influence of synthesis temperature on the nanopartilce's properties showed that the reaction temperature played an important role in the crystallinity of nanoparticle. The glass ceramic particles synthesized at 55 degrees C included about 15% crystalline phase, while at 25 degrees C and 40 degrees C the entire amorphous nanopowder could be obtained.

Preparation and electrical properties of new oxide ion conductors Ce6-xDyxMoO15-delta (0.0 <= x <= 1.8)

Ce6-xDyxMoO15-delta (0.0 <= x <= 1.8) were synthesized by modified sol-gel method. Structural and electrical properties were investigated by means of X-ray diffraction (XRD), Raman, X-ray photoelectron spectroscopy (XPS) and electrochemical impedance spectroscopy (EIS). The XRD patterns showed that the materials were single phase with a cubic fluorite structure. Impedance spectroscopy measurement in the temperature range between 350 degrees C and 800 degrees C indicated a sharp increase in conductivity for the system containing small amount of Dy2O3. The Ce5.6Dy0.4MoO15-delta detected to be the best conducting phase with the highest conductivity (sigma(t) = 8.93 x 10(-3) S cm(-1)) is higher than that of Ce5.6Sm0.4MoO15-delta (sigma(t) = 2.93 x 10(-3) S cm(-1)) at 800 degrees C, and the corresponding activation energy of Ce5.6Dy0.4MoO15-delta (0.994 eV) is lower than that of Ce5.6Sm0.4MoO15-delta (1.002 eV).

Synthesis of Titanate-Based Nanotubes for One-Dimensionally Confined Electrical Properties

Structural tailoring for dimensionally confined electrical properties is fundamentally important for nanodevices and the relevant technologies. Titanate-based nanotubes were taken as a prototype one-dimensional material to study. First, Na0.96H1.04Ti3O7 center dot 3.42H(2)O nanotubes were prepared by a simple hydrothermal condition, which converted into Na0.036H1.964Ti3O7 center dot 3.52H(2)O nanotubes by a subsequent acidic rinsing. Systematic sample characterization using combined techniques of X-ray diffraction, field emission scanning electron microscopy, high resolution transmission electron microscopy, electron paramagnetic resonance, Fourier transform infrared spectroscopy, elemental analyses, and alternative current impedance indicated that both nanotubes possessed a scrolled trititanate-type structure with the (200) crystal face predominant on the tube surface. With increasing temperature, both nanotubes underwent a continuous dehydration process, which however imposed different impacts oil the structures and electrical properties, depending on the types of the nanotubes

Effect of the addition of YAG(Y3Al5O12) nanopowder on the mechanical properties of lanthanum zirconate

La2Zr2O7 (LZ) is a promising thermal barrier coating material for the high-temperature applications, which could be significantly toughened by the YAG nanopowder incorporated into the matrix. The composites of xYAG/(1-x)LZ (Y=10, 15, 20 vol. %, LZ-x-YAG) were densified by means of high-pressure sintering (HPS) under a pressure of 4.5 GPa at 1650 degrees C for 5 min, by which a high-relative density above 93% could be obtained. The morphologies of the fractured surfaces were investigated by the scanning electron microscope, and the fracture toughness and Vicker's-hardness of the composites were evaluated by the microindentation. The grain size of the LZ matrix drops significantly with the addition of YAG nanoparticles and the fracture type changes from the intergranular to a mixture type of the transgranular and intergranular in the nanocomposites. The LZ-20-YAG nanocomposite has a fracture toughness of 1.93 MPa m(1/2), which is obviously higher than that of the pure LZ (1.57 MPa m(1/2)), and the toughening mechanism is discussed in this paper.

Phase conversion and spectral properties of long lasting phosphor Zn-3 (PO4)(2): Mn2+, Ga3+

A red long lasting phosphor Zn-3(PO4)(2): Mn2+ Ga3+ (ZPMG) was prepared by ceramic method, and phase conversion and spectral properties were investigated. Results indicated that the phase conversion from alpha-Zn-3(PO4), beta-Zn-3(PO4)(2) to gamma-Zn-3(PO4)(2) occurs with different manganese concentration incorporated and sinter process. The structural change induced by the phase transformation results in a remarkable difference in the spectral properties. The possible luminescence mechanism for this red LLP with different forms has been illustrated.

Grain boundary conductivity of high purity neodymium-doped ceria nanosystem with and without the doping of molybdenum oxide

Solid solutions of Ce1-xNdxO2-x/2 (0.05 <= x <= 0.2) and (Ce1-xNdx)(0.95)MO0.05O2-delta (0.05 <= x <= 0.2) have been synthesized by a modified sol-gel method. Both materials have very low content of SiO2 (similar to 27 ppm). Their structures and ionic conductivities were characterized by X-ray diffraction (XRD), field-emission scanning electron microscopy (FESEM) and electrochemical impedance spectroscopy (M). The XRD patterns indicate that these materials are single phases with a cubic fluorite structure. The powders calcined at 300 degrees C with a crystal size of 5.7 nm have good sinterability, and the relative density could reach above 96% after being sintered at 1450 degrees C. With the addition Of MoO3, the sintering temperature could be decreased to 1250 degrees C. Impedance spectroscopy measurement in the temperature range of 250-800 degrees C indicates that a sharp increase of conductivity is observed when a small amount of Nd2O3 is added into ceria, of which Ce0.85Nd0.15O1.925 (15NDC) shows the highest conductivity. With the addition of a small amount Of MoO3, the grain boundary conductivity of 15NDC at 600 degrees C increases from 2.56 S m(-1) to 5.62 S m(-1).

Ceramic materials for thermal barrier coatings

This paper summarizes the basic properties of ceramic materials for thermal barrier coatings. Ceramics, in contrast to metals, are often more resistant to oxidation, corrosion and wear, as well as being better thermal insulators. Except yttria stabilized zirconia, other materials such as lanthanum zirconate and rare earth oxides are also promising materials for thermal barrier coatings.

Synthesis, structural characterization and electrical property of new oxide ion conductors: La3MMo2O12 (M = In, Ga and Al)

New series of oxides, La3MMo2O12 (M = In, Ga and Al), have been prepared by the solid-state reaction. The composition and elemental distribution were analyzed by the energy-dispersive X-ray (EDX) analysis. As determined by the X-ray diffraction (XRD), these compounds have similar crystal structures that can be indexed on a monoclinic cell at room temperature. AC impedance spectra and the DC electrical conductivity measurements in various atmospheres indicate that they are oxide ion conductors with ionic conductivities between 10(-2) and 10(-3) S/cm at 800 degrees C. The conductivity decreases in the order of La3GaMo2O12 > La3AlMo2O12 > La3InMo2O12, implying that the effect of cell volume and polarization associated with In3+, Ga3+ and Al3+ play an important role in the anion transport of these materials. The reversible phase transition was observed in all these compounds as confirmed by the differential thermal analysis (DTA) and dilatometric measurements.

Up-conversion spectrum properties of the oxy-fluoride glass co-doped with Er3+ and Yb3+

Up-conversion of 45PbF(2)-45GeO(2)-10WO(3) oxy-fluoride glasses co-doped with Yb3+ and Er3+ ions were prepared by fusion method through melting at 1223 K and then annealing at 653 K for 4 h. Transmittance of the undoped host glass was beyond 73% in a range of 0.6-2.5 mu m and the co-doped glasses still provided good transmittance beyond 50%. Refractive indices of the host and co-doped glasses were 1.517 and 1.650, respectively. Blue, green and red fluorescence spectra were observed in a range of 400-700 nm under 980 nm diode laser excitation. Up-conversion spectra at about 410, 518, 530and 650 nm were assigned to the 4f electron transitions of H-2(9/2) -> I-4(15)/(2), H-2(15/2) -> I-4(15/2) S-4(3/2) -> I-4(15/2) and F-4(9/2) -> I-4(15/2) of Er3+ ion, respectively. The mechanism of energy transfer between Yb3+ and Er3+ ions in the glass was analyzed. Raman shift shows the non-radiative relaxation of the glass sample is low.

Nitrate-citrate combustion synthesis and properties of Ce1-xSmxO2-x/2 solid solutions

A nitrate-citrate combustion route to synthesize nanocrystalline samarium-doped ceria powders for solid electrolyte ceramics is presented. This route is based on the gelling of nitrate solutions by the addition of citric acid and ammonium hydroxide, followed by an intense combustion process due to an exothermic redox reaction between nitrate and citrate ions. The influence of ignition temperature on the characteristics of the powders was studied. The change of the crystal structure with the content of doped Sm was investigated. High temperature X-ray, and Raman scattering were used to characterize the sample. The lattice constant and unit volume increase with doping level and increasing temperature. Dense ceramic samples prepared by uniaxial pressing and sintering in air were also studied.

Synthesis, characterization and electrical properties of the new solid electrolyte materials Ce6-xErxMoO15-delta (0.0 < x < 1.5)

A new series of oxides, Ce6-xErxMoO15-delta (0.0 less than or equal to x less than or equal to 1.5), was synthesized using wet-chemistry techniques. The precursors and resultant oxide powders were characterized by differential thermal analysis/thermogravimetry, x-ray diffraction, and IR, Raman and x-ray photoelectron spectroscopy. The formation temperature of the powders was found to be as low as 350degreesC. Ce6-xErxMoO15-delta crystallized to a fluorite-related cubic structure. The electrical conductivity of the samples was investigated by using ac impedance spectroscopy. This showed that the presence of Er was related to the oxygen-ion conductivity, and that the highest oxygen-ion conductivity was found in Ce6-xErxMoO15-delta (x = 0.4), ranging from 5.9 x 10(-5) S cm(-1) at 300degreesC to 1.26 x 10(-2) S cm(-1) at 700degreesC, respectively. This kind of material shows a potential application in intermediate-temperature solid oxide fuel cells.

Preparation of Y3Al5O12 : Eu phosphors by citric-gel method and their luminescent properties

By using metal nitrates as starting materials and citric acid as complexing agent, Y3Al5O12 (YAG) and Y3Al5O12:Eu (1 mol%) (YAG:Eu) powder phosphors were prepared by a citrate-gel method. The formation process of YAG and YAG:Eu were investigated by means of XRD, TG-DTA and FT-IR spectra. The purified crystalline phases of YAG and YAG:Eu were obtained at 800 degreesC. The crystalline YAG:Eu phosphors showed an orange-red emission with D-5(0)-F-7(1) (591 nm) as the most prominent group, whose intensity was dependent on the pH value of the starting solution, citric acid content and firing temperature. It has been found that the suitable pH and citric acid/metal ratio are 3 and 2 for obtaining the highest emission intensity, respectively. The emission intensity increases steadily with increasing the annealing temperature from 800 to 1200 degreesC, and nearly remains constant after 1200 degreesC. Furthermore, great differences were observed for the lifetimes and the charge transfer band of Eu3+ in crystalline and amorphous states of YAG.

Preparation and characteristics of polyimide-TiO2 nanocomposite film

A sol-gel approach has been developed to prepare polyimide-TiO2, hybrid films fi om soluble polyimides and a modified titanium precursor. The rate of the hydrolysis reaction of titanium alkoxide can be controlled by using acetic acid as a modifier. FTIR and XPS indicated that TiO2, particles were well distributed in polyimide matrixes with particle size small per than 60 nm. Polyimide hybrid films having the TiO2, component less than or equal to 10% exhibited high thermal stability, high optical transparency and good mechanical properties and possessed higher dielectric constants than correspondingly polyimides. (C) 2000 Society of Chemical Industry.