The nanocomposite scaffold of poly(lactide-co-glycolide) and hydroxyapatite surface-grafted with L-lactic acid oligomer for bone repair


Autoria(s): Cui Y; Liu Y; Cui Y; Jing XB; Zhang PBA; Chen XS
Data(s)

2009

Resumo

Nanohydroxyapatite (op-HA) surface-modified with L-lactic acid oligomer (LAc oligomer) was prepared by LAc oligomer grafted onto the hydroxyapatite (HA) surface. The nanocomposite of op-HA/PLGA with different op-HA contents of 5, 10, 20 and 40 wt.% in the composite was fabricated into three-dimensional scaffolds by the melt-molding and particulate leaching methods. PLGA and the nanocomposite of HA/PLGA with 10 wt.% of ungrafted hydroxyapatite were used as the controls. The scaffolds were highly porous with evenly distributed and interconnected pore structures, and the porosity was around 90%. Besides the macropores of 100-300 mu m created by the leaching of NaCl particles, the micropores (1-50 mu m) in the pore walls increased with increasing content of op-HA in the composites of op-HA/PLGA. The op-HA particles could disperse more uniformly than those of pure HA in PLGA matrix. The 20 wt.% op-HA/PLGA sample exhibited the maximum mechanical strength, including bending strength (4.14 MPa) and compressive strength (2.31 MPa). The cell viability and the areas of the attached osteoblasts on the films of 10 wt.% op-HA/PLGA and 20 wt.% op-HA/PLGA were evidently higher than those on the other composites.

Identificador

http://202.98.16.49/handle/322003/11837

http://www.irgrid.ac.cn/handle/1471x/148300

Idioma(s)

英语

Fonte

Cui Y;Liu Y;Cui Y;Jing XB;Zhang PBA;Chen XS.The nanocomposite scaffold of poly(lactide-co-glycolide) and hydroxyapatite surface-grafted with L-lactic acid oligomer for bone repair,ACTA BIOMATERIALIA,2009,5 (7 ):2680-2692

Palavras-Chave #IN-VITRO #PART I #COMPOSITES #TISSUE #POLY(L-LACTIDE) #POLYMERIZATION #OSTEOGENESIS #ATTACHMENT #PARTICLES #CERAMICS
Tipo

期刊论文