Raman scattering in hexagonal GaN epitaxial layer grown on MgAl2O4 substrate

The room temperature Raman spectra of the hexagonal GaN epilayer grown on [111]- oriented MgAl2O4 substrate were measured in various backscattering and right angle scattering geometries. All of the symmetry-allowed optical phonon modes were observed except the E-2 (low frequency) mode. The quasitransverse and quasilongitudinal modes were also observed in the x(zx)z and x(yy)z configurations, which are the mixed modes of pure transverse and longitudinal modes with A(1) and E-1 symmetry, respectively. (C) 1999 American Institute of Physics. [S0021-8979(99)01416-4].

Improved neutron radiation hardness for Si detectors: Application of low resistivity starting material and or manipulation of N-eff by selective filling of radiation-induced traps at low temperatures

Radiation-induced electrical changes in both space charge region (SCR) of Si detectors and bulk material (BM) have been studied for samples of diodes and resistors made on Si materials with different initial resistivities. The space charge sign inversion fluence (Phi(inv)) has been found to increase linearly with the initial doping concentration (the reciprocal of the resistivity), which gives improved radiation hardness to Si detectors fabricated from low resistivity material. The resistivity of the BM, on the other hand, has been observed to increase with the neutron fluence and approach a saturation value in the order of hundreds k Omega cm at high fluences, independent of the initial resistivity and material type. However, the fluence (Phi(s)), at which the resistivity saturation starts, increases with the initial doping concentrations and the value of Phi(s) is in the same order of that of Phi(inv) for all resistivity samples. Improved radiation hardness can also be achieved by the manipulation of the space charge concentration (N-eff) in SCR, by selective filling and/or freezing at cryogenic temperatures the charge state of radiation-induced traps, to values that will give a much smaller full depletion voltage. Models have been proposed to explain the experimental data.

Comparative Raman scattering studies of GaAs/AlxGa1-xAs and AlxGa1-xAs/AlAs superlattices

The room-temperature Raman scattering studies of longitudinal optic phonons in AlAs/AlxGa1-xAs and GaAs/AlxGa1-xAs short-period superlattices with different layer thicknesses were reported. The AlAs LO modes confined in AlAs layers and GaAs-like LO modes confined in AlxGa1-xAs layers were observed in AlAs/AlxGa1-xAs superlattices under off-resonance conditions. And the GaAs LO modes confined in GaAs layers and AlAs-like LO modes confined in AlxGa1-xAs layers were observed in GaAs/AlxGa1-xAs superlattices. In addition, the AlAs interface mode in AlAs/AlxGa1-xAs was also observed under near-resonance conditions. Based on the linear chain mode, the frequencies of confined LO modes measured by Raman scattering were unfolded according to q=m/(n+1)(2 pi/a(0)) by which the dispersion curves of AlAs-like and GaAs-like LO phonons in AlxGa1-xAs mixed crystal were obtained.

First charge collection and position-precision data on the medium-resistivity silicon strip detectors before and after neutron irradiation up to 2x10(14) n/cm(2)

Test strip detectors of 125 mu m, 500 mu m, and 1 mm pitches with about 1 cm(2) areas have been made on medium-resistivity silicon wafers (1.3 and 2.7 k Ohm cm). Detectors of 500 mu m pitch have been tested for charge collection and position precision before and after neutron irradiation (up to 2 x 10(14) n/cm(2)) using 820 and 1030 nm laser lights with different beam-spot sizes. It has been found that for a bias of 250 V a strip detector made of 1.3 k Ohm cm (300 mu m thick) can be fully depleted before and after an irradiation of 2 x 10(14) n/cm(2). For a 500 mu m pitch strip detector made of 2.7 k Ohm cm tested with an 1030 nm laser light with 200 mu m spot size, the position reconstruction error is about 14 mu m before irradiation, and 17 mu m after about 1.7 x 10(13) n/cm(2) irradiation. We demonstrated in this work that medium resistivity silicon strip detectors can work just as well as the traditional high-resistivity ones, but with higher radiation tolerance. We also tested charge sharing and position reconstruction using a 1030 nm wavelength (300 mu m absorption length in Si at RT) laser, which provides a simulation of MIP particles in high-physics experiments in terms of charge collection and position reconstruction, (C) 1999 Elsevier Science B.V. All rights reserved.

A Raman scattering study of GaAs: As films lifted off GaAs substrate

We performed Raman scattering investigations on low-temperature-grown (LTG) films of GaAs that had been lifted off the GaAs substrate. The Raman measurements unambiguously show the effects of excess arsenic on phonon scattering from LTG films of GaAs. The larger downwards shift of the LO phonon frequency for unannealed free-standing films is explained by invoking the elimination of mismatch strain. The Raman signal due to precipitates of elemental arsenic in the annealed GaAs : As films is determined. It is confirmed that the arsenic clusters formed by rapid thermal annealing are mainly amorphous, giving rise a broad Raman peak in the range 180-260 cm(-1).

Neutron irradiation-infrared based measurement method for interstitial oxygen in heavily boron-doped silicon

A novel method, based on an infrared absorption and neutron irradiation technique, has been developed for the determination of interstitial oxygen in heavily boron-doped silicon. The new procedure utilizes fast neutron irradiated silicon wafer specimens. On fast neutron irradiation, the free carriers of high concentration in silicon can be trapped by the irradiated defects and the resistivity increased. The resulting calibration curve for the measurement of interstitial oxygen in boron-doped silicon has been established on the basis of the annealing behaviour of irradiated boron-doped CZ silicon.

Study of microstructure of high stability hydrogenated amorphous silicon films by Raman scattering and infrared absorption spectroscopy

The microstructure, hydrogen bonding configurations and hydrogen content of high quality and stable hydrogenated amorphous silicon (a-Si:H) films prepared by a simple ''uninterrupted growth/annealing" plasma enhanced chemical vapor deposition technique have been investigated by Raman scattering and infrared absorption spectroscopy. The high stability a-Si:H films contain small amounts of a microcrystalline phase and not less hydrogen (10-16 at. %), particularly, the clustered phase hydrogen, Besides, the hydrogen distribution is very inhomogeneous. Some of these results are substantially distinct from those of conventional device-quality n-Si:H film or stable cr-Si:H films prepared by the other techniques examined to date. The stability of n-Si:H films appears to have no direct correlation with the hydrogen content or the clustered phase hydrogen concentration. The ideal n-Si:H network with high stability and low defect density is perhaps not homogeneous. (C) 1998 American Institute of Physics.

Electronic and vibrational Raman scattering in resonance with yellow luminescence transitions in GaN on sapphire substrate

We analyze low-temperature Raman and photoluminescence spectra of MBE-grown GaN layers on sapphire. Strong and sharp Raman peaks are observed in the low frequency region. These peaks, which are enhanced by excitation in resonance with yellow luminescence transitions, are attributed to electronic transitions related to shallow donor levels in hexagonal GaN. It is proposed that a low frequency Raman peak at 11.7 meV is caused by a pseudo-local vibration mode related to defects involved in yellow luminescence transitions. The dependence of the photoluminescence spectra on temperature gives additional information about the residual impurities in these GaN layers.

Raman scattering from In1-x-yGaxAlyAs quaternary alloys

Raman scattering studies were reported of In1-x-yGaxAlyAs/InP lattice matched quaternary alloys. The quaternary alloys a.ere grown on (100) oriented InP substrates by MBE method. The composition and intensity dependence of optical phonon mode frequencies show that the quaternary alloys exhibit three-mode behavior, i.e. InAs-like, GaAs-like and AlAs-like modes. Polarization analysis of the Raman spectra shows that the LO phonon modes are Raman active in the depolarized configuration and Raman inactive in the polarized configuration. TO phonon modes were also observed due to disorder effects, resulting in the asymmetrical shapes of the Raman peaks of the optical phonons.

Raman scattering and photoluminescence of ZnSxTe1-x mixed crystals

We have investigated the Raman scattering and the photoluminescence (PL) of ZnSxTe1-x mixed crystals grown by MBE, covering the entire composition range (0 less than or equal to x < 1). The results of Raman studies show that the ZnSxTe1-x mixed crystals display two-mode behaviour. In addition, photoluminescence spectra obtained in backscattering and edge-emission geometries, reflectivity spectra and the: temperature dependence of the photoluminescence of ZnSxTe1-x have been employed to find out the origin of PL emissions in ZnSxTe1-x with different x values. The results indicate that emission bands, for the samples with small x values, can be related to the band gap transitions or a shallow-level emission centre, while as x approaches 1, they are designated to strong radiative recombination of Te isoelectronic centres (IECs).

Raman scattering study on diluted magnetic semiconductor Ga1-xMnxAs prepared by Mn-ion implantation

Raman scattering measurements have been performed in diluted magnetic semiconductor Ga1-xMnxAs prepared by Mn-ion implantation, deposition, and post-annealing technique. It is found that the Raman spectrum measured from the implanted surface of the sample shows some new weak modes in addition to the GaAs-like modes which are observed from the unimplanted surface. The new vibrational modes observed are assigned to MnAs-like modes. The coupled LO-phonon plasmon mode, and Mn and As related vibrational modes caused by Mn-ion implantation, deposition, and post-annealing are also observed. Furthermore, the GaAs-like modes are found to be shifted by approximately 4 cm(-1) in the lower frequency side, compared with those observed from the unimplanted surface.

Raman scattering study on vibrational modes in Ga1-xMnxN prepared by Mn-ion implantation

Raman scattering measurements have been carried out on ferromagnetic semiconductor Ga1-xMnxN prepared by Mn-ion implantation and post annealing. The Raman results obtained from the annealed and un-annealed Ga1-xMnxN demonstrate that crystalline quality has been improved in Ga1-xMnxN after annealing. Some new vibrational modes in addition to GaN-like modes are found in the Raman spectra measured from the Ga1-xMnxN where the GaN-like modes are found to be shifted in the higher frequency side than those measured from the bulk GaN. A new vibrational mode observed is assigned to MnN-like mode. Other new phonon modes observed are assigned to disorder-activated modes and Mn-related vibrational modes caused by Mn-ion implantation and post-annealing. (c) 2006 Elsevier Ltd. All rights reserved.

Photoluminescence and Raman scattering correlated study of boron-doped silicon nanowires

Boron-doped (B-doped) silicon nanowires (SiNWS) have been prepared and characterized by Raman scattering and photoluminescence (PL). B-doped SiNWS were grown by plasma enhanced chemical vapor deposition (PECVD), using diborane (B2H6) as the dopant gas. Raman spectra show a band at 480cm(-1),which is attributed to amorphous silicon. Photoluminescence at room temperature exhibits three distinct emission peaks at 1.34ev, 1.42ev, 1.47ev. Possible reason for these is suggested.

Raman scattering study of vibrational modes and hole concentration in GaxMn1-xSb

The Raman scattering study of vibrational modes and hole concentration in a ferromagnetic semiconductor Ga1-xMnxSb grown by Mn ion implantation, deposition and post-annealing has been presented. The experiments are performed both in implanted and unimplanted regions before and after etching the samples. The Raman spectra measured from the unimplanted region show only GaSb-like phonon modes. On the other hand, the spectra measured from the implanted region show additional phonon modes approximately at 115, 152, 269, 437 and 659 cm(-1). The experimental results demonstrate that the extra modes are associated with surface defects, crystal disorder and blackish layer that is formed due to Mn ion implantation, deposition and annealing processes. Furthermore, we have determined the hole concentration as a function of laser probing position by modeling the Raman spectra using coupled mode theory. The contributions of GaSb-like phonon modes and coupled LO-phonon plasmon mode are taken into consideration in the model. The hole-concentration-dependent CLOPM is resolved in the spectra measured from the implanted and nearby implanted regions. The hole concentrations determined by Raman scattering are found to be in good agreement with those measured by the electrochemical capacitance-voltage technique.

Short range scattering mechanism of type-II GaSb/GaAs quantum dots on the transport properties of two-dimensional electron gas

We have studied the scattering process of AlGaAs/GaAs two-dimensional electron gas with the nearby embedded GaSb/GaAs type-II quantum dots (QDs) at low temperature. Quantum Hall effect and Shubnikov-de Haas oscillation were performed to measure the electron density n(2D), the transport lifetime tau(t) and the quantum lifetime tau(q) under various biased gate voltage. By comparing measured results of QDs sample with that of reference sample without embedded QDs, mobilities (transport mobility mu(t) and quantum mobility mu(q)) dominated by GaSb QDs scattering were extracted as functions of n(2D). It was found that the ratios of tau(t) to tau(q) were varying within the range of 1-4, implying the scattering mechanism belonging to the sort of short-range interaction. In the framework of Born approximation, a scattering model considering rectangular-shaped potential with constant barrier height was successfully applied to explain the transport experimental data. In addition, an oscillating ratio of tau(t)/tau(q) with the increasing n(2D) was predicted in the model.