Spectroscopic properties of Ce : YAP scintillation crystal grown by temperature gradient technique

Spectroscopic properties of Ce-doped yttrium orthoaluminate (Ce:YAlO3 or Ce:YAP) crystals grown by temperature gradient technique (TGT) were investigated, and the effects of the growth conditions on the properties were analyzed.. Methods of optical absorption (OA), photoluminescence (PL), photoluminescence decay (PLD), X-ray excited luminescence (XL) and cathodeluminescence (CL) were used in these investigations. The results showed that the absorption band peak at 202, 394 and 532 nm originated from F and F+ color center induced by the weak reducing growth atmosphere, green emission band near 500 ran derived from Ce3+ -Ce3+ pairs and band at 650 similar to 850 run from some unintentional impurity in crystals.

Single crystal beta-Ga2O3: Cr grown by floating zone technique and its optical properties

beta-Ga2O3: Cr single crystals were grown by floating zone technique. Absorption spectra and fluorescence spectra were measured at room temperature. The values of field splitting parameter Dq and Racah parameter B were obtained by the peak values of absorption spectra. The value 10Dq/B=23.14 manifests that in beta-Ga2O3 crystals Cr3+ ions are influenced by low energy crystal field. After high temperature annealing in air, the Cr3+ intrinsic emission was enhanced and the green luminescence disappeared. The strong and broad 691 nm emission was obtained at 420 nm excitation due to the electron transition occurred from T-4(2) to (4)A(2). The studies manifest that the beta-Ga2O3 crystals have the potential application for tunable laser.

液相外延法制备β-BBO薄膜

采用液相外延法在掺Sr^2＋的Q—BBO（001）衬底上制备了β-BBO薄膜，研究了制备条件对薄膜质量的影响．结果表明：当生长温度为810℃时，转速为300r／min生长的外延膜具有较高的结晶质量，且随着生长时间的延长，外延膜的结晶质量有所提高．β—BBO薄膜呈C轴高度择优取向，薄膜的双晶摇摆曲线半峰宽值FWHM仅为676．6”，表明β-BBO薄膜较好的结晶质量；在不具备相位匹配的条件下，β—BBO外延膜也能够实现二次谐波输出．

气相传输平衡法在Sr^2＋：α-BBO衬底上制备β-BBO薄膜的研究

采用气相传输平衡技术在掺Sr^2＋的α-BBO（001）衬底上制备了β-BBO薄膜，研究了粉料配比、VTE处理温度以及恒温时间对薄膜质量的影响。结果表明，在适当的粉料配比、VTE处理温度以及恒温时间下，在Sr^2＋：α-BBO晶片表层制备呈c轴高度择优取向的、没有第二相物质的β-BBO薄膜，其双晶摇摆曲线半峰宽值FWHM为1000＂，显示出β-BBO薄膜较好的结晶质量。并对气相传输平衡技术制备β-BBO薄膜的机理进行了初步的探讨。

Demonstration of GaN/InGaN light emitting diodes on (100) beta-Ga2O3 substrates by metalorganic chemical vapour deposition

The growth and fabrication of GaN/InGaN multiple quantum well (MQW) light emitting diodes ( LEDs) on ( 100) beta-Ga2O3 single crystal substrates by metal-organic chemical vapour deposition (MOCVD) technique are reported. x-ray diffraction (XRD) theta-2 theta. scan spectroscopy is carried out on the GaN buffer layer grown on a ( 100) beta-Ga2O3 substrate. The spectrum presents several sharp peaks corresponding to the ( 100) beta-Ga2O3 and ( 004) GaN. High-quality ( 0002) GaN material is obtained. The emission characteristics of the GaN/InGaN MQW LED are measurement. The first green LED on beta-Ga2O3 with vertical current injection is demonstrated.

Edge-defined, film-fed growth (EFG) technique for the preparation of alpha-Al2O3 : C crystal with highly sensitive thermoluminescence response

In this work, alpha-Al2O3:C, a highly sensitive thermoluminescence dosimetry crystal, was grown by the EFG method in which a graphite heating unit and shield acted as the carbon source during the growth process. The optical, luminescent properties and dosimetric characteristics of the crystal were investigated. The as-grown crystal shows a single glow peak at 536 K, which is associated with Cr3+ ions. After annealing in H-2 at 1673 K for 80 h, the crystal shows a single glow peak at 460 K and a blue emission band at 415 nm. The thermoluminescent response of the annealed crystal shows linear-sublinear-saturation characteristics in the dose range from 5 x 10(-6) to 100 Gy.

Fabrication and spectral properties of Nd3+-doped yttrium lanthanum oxide transparent ceramics

Transparent 1 at% Nd3+:Y1.9La0.1O3 ceramics were fabricated with nanopowders prepared by carbonate coprecipitation method. The powder compacts were sintered in H-2 atmosphere at 1550 degrees C for 30 h. The Nd3+:Y1.9La0.1O3 ceramics display uniform grains of about 50 mu m and high transparency. The highest transmittance of the ceramics reaches 67%. The strongest absorption peak is in the wavelength of 820 nm with absorption cross section of 2.48 x 10(-20) cm(2). The absorption is still high at LD wavelength 806 nm with absorption cross section of 1.78 x 10(-20) cm(2) and broad full width at half maximum (FWHM) of about 6.3 nm. The strongest emission peak was centered at 1078 nm with large stimulated emission cross section of 9.63 x 10(-20) cm(2) and broad FWHM of about 7.8 nm. The broad absorption and emission bandwidth of Nd3+:y(1.9)La(0.1)O(3) transparent ceramics are favorable to achieve the miniaturized LD pumping apparatus and ultrashort modelocked pulse laser output, respectively. (c) 2007 Elsevier B.V. All rights reserved.

Growth of highly sensitive thermoluminescent crystal alpha-Al2O3 : C by the temperature gradient technique

In this work, an alpha-Al2O3:C crystal with highly sensitive thermoluminescence was directly grown by the temperature gradient technique (TGT) using Al2O3 and graphite powders as raw materials. The optical and luminescent properties and the dosimetric characteristics of the crystal were investigated. An as-grown alpha-Al2O3:C crystal shows a single glow peak at 462 K and a blue emission peak at 415 nm. The thermoluminescence (TL) response of the crystal shows a linear-sublinear-saturation characteristic. In the dose range from 5 x 10(-6) to 10Gy, the alpha-Al2O3:C crystal shows excellent linearity, and saturation was observed at about 30Gy. The sensitivity of the crystal decreases as the heating rate increases. (c) 2008 Elsevier B.V. All rights reserved.

Design and fabrication of color filters for projection display system

Color filters are key components in an optical engine projection display system. In this paper, a new admittance-matching method for designing and fabricating the high performance filters is described, in which the optimized layers are limited to the interfaces between the stack (each combination of quarter-wave-optical-thickness film layers is called a stack) and stack, or between stack and substrate, or between stack and incident medium. This method works well in designing filters containing multiple stacks such as UV-IR cut and broadband filters. The tolerance and angle sensitivity for the designed film stacks are analyzed. The thermal stability of the sample color filters was measured. A good result in optical performance and thermal stability was obtained through the new design approach. (c) 2006 Society of Photo-Optical Instrumentation Engineers.

Design and fabrication of color filters for projection display system

Color filters are key components in an optical engine projection display system. In this paper, a new admittance-matching method for designing and fabricating the high performance filters is described, in which the optimized layers are limited to the interfaces between the stack (each combination of quarter-wave-optical-thickness film layers is called a stack) and stack, or between stack and substrate, or between stack and incident medium. This method works well in designing filters containing multiple stacks such as UV-IR cut and broadband filters. The tolerance and angle sensitivity for the designed film stacks are analyzed. The thermal stability of the sample color filters was measured. A good result in optical performance and thermal stability was obtained through the new design approach. (c) 2006 Society of Photo-Optical Instrumentation Engineers.

1064nm倍频波长分离膜的制备与性能研究

通过对主膜系添加匹配层并借助计算机对膜系进行优化，设计出结构规整、性能优良的1064ilm倍频波长分离膜。用电子束蒸发及光电极值监控技术在K9玻璃基底上沉积薄膜，将样品置于空气中在260℃温度下进行3h热退火处理。然后用Lambda 900分光光度计测量了样品的光谱性能；用表面热透镜(STL)技术测量了样品的弱吸收值；用调Q脉冲激光装置测试了样品的抗激光损伤阈值(LIDT)。实验结果发现，样品的实验光谱性能与理论光谱性能有很好的一致性。退火前后其光谱性能几乎没有发生温漂，说明薄膜的温度稳定性好；同时退火使

渐变反射率镜的设计与制备

按照高斯型渐变反射率镜(GRM)的参数要求,采用了中间层厚度渐变的方案对膜系和掩模板形状进行设计.根据薄膜的实际需求和具体的沉积设备,设计了掩模和掩模切换装置.在一次高真空环境下镀制了渐变反射率镜的所有膜系.采用直接测量的方法,测量了高斯型渐变反射率镜反射率的径向分布.测试结果表明,用这种技术制备的样品,与设计要求基本一致.分析得出,掩模板形状与精度对镀制结果有影响.随着设计尺寸减小,掩模板对膜料分子的散射作用增强,使样品中心反射率小于设计要求,边缘出现旁瓣.提出了减小基片与掩模板之间的距离和提高膜厚监控的精度的改善方案.

Effects of process on microstructure and properties of translucent Dy-alpha-SiAlON sintered at lower temperatures

Hot pressing (HP) at higher sintering temperature has been a traditional and prevalent technique for the fabrication of alpha-SiAlON. In order to prepare translucent SiAlON more easily, LiF was used as a non-oxide sintering additive to lower the sintering temperature to <= 1650 degrees C. As a result, all of the samples possessed a good hardness and fracture toughness. At the same time, the lower temperature sintered samples showed a higher optical transmittance in the range of 2.5-5.5 mu m wavelength (0.5 mm in thickness). The maximum infrared transmission reached 68% at a wavelength of 3.3 mu m. The present work shows that the sintering process has a strong effect on microstructure and property of alpha-SiAlON. To be exact, a lower sintering temperature and longer holding time can produce some fully-developed microstrcture, which is beneficial for the optical transmittance. (C) 2008 The Ceramic Society of Japan. All rights reserved.

Compensation of reflectance response deviations of guided-mode resonant filters induced by overetching fabrication

Unless the fabrication error control is well treated, it easily causes overetched fabrication errors, which causes the resonant peak value deviation during the fabrication process of guided-mode resonant filters (GMRFs). Hence, the fabrication error control becomes a key point for improving the performance of GMRF. We find that, within the range of the groove depth from 93 to 105 nm, the relationship between the overetched error and the resonant peak value deviation is nearly linear, which means that we can compensate the reflectance response deviation and reduce the resonant peak value deviation by the method of covering the layer film on the GMRF. Simulation results show that the deviation is compensated perfectly by this way. (C) 2008 Optical Society of America