SWAP operation in the two-qubit Heisenberg XXZ model: Effects of anisotropy and magnetic field

In this paper we study the SWAP operation in a two-qubit anisotropic XXZ model in the presence of an inhomogeneous magnetic field. We establish the range of anisotropic parameter lambda within which the SWAP operation is feasible. The SWAP errors caused by the inhomogeneous field are evaluated.

Spatial variation of optical and structural properties of ELO GaN directly grown on patterned sapphire by HVPE

A 275 mu m thick GaN layer was directly grown on the SiO2-prepatterned sapphire in a home-built vertical hydride vapour phase epitaxy (HVPE) reactor. The variation of optical and structure characteristics were microscopically identified using spatially resolved cathodeluminescence and micro-Raman spectroscopy in a cross section of the thick film. The D X-0(A) line with the FWHM of 5.1 meV and etch- pit density of 9 x 10(6) cm(-2) illustrated high crystalline quality of the thick GaN epitaxial layer. Optically active regions appeared above the SiO2 masks and disappeared abruptly due to the tapered inversion domains at 210 - 230 mu m thickness. The crystalline quality was improved by increasing the thickness of the GaN/sapphire interface, but the region with a distance of 2 mu m from the top surface revealed relatively low quality due to degenerate surface reconstruction by residual gas reaction. The x-ray rocking curve for the symmetric (0 0 2) and asymmetric (1 0 2) reflections also showed good quality and a small wing tilt of the epitaxial lateral overgrowth (ELO) GaN.

Effect of oxidation on the optical and surface properties of AlGaN

The chemical properties of AlxGa1-xN surfaces exposed to air for different time periods are investigated by atomic force microscopy (AFM), photoluminescence (PL) measurement and X-ray photoelectron spectroscopy (XPS). PL and AFM results show that AlxGa1-xN samples exhibit different surface characteristics for different air-exposure times and Al contents. The XPS spectra of the Al 2p and Ga 2p core levels indicate that the peaks shifted slightly, from an Al-N to an Al-O bond and from a Ga-N to a Ga-O bond. All of these results show that the epilayer surface contains a large amount of Ga and Al oxides. (c) 2006 Elsevier B.V. All rights reserved.

Two opposite gradients of hole density in as-grown and annealed (Ga,Mn)As layers

The depth distribution of the hole density p in 500 nm-thick (Ga,Mn)As layers is investigated. From Raman scattering spectra, it is found that the gradients of p are opposite in the as-grown and annealed layers. At the region around the free surface, with increasing etching depth, p significantly increases in the as-grown layer; however, p decreases distinctly in the annealed layer. Then, in the bulk, p becomes almost homogeneous for both cases. The etching-depth dependence of Curie temperature obtained from magnetic measurements is in agreement with the distribution characterization of p. These results suggest that annealing induces outdiffusion of Mn interstitials towards the free surface, and incomplete outdiffusion during the growth leads to an accumulation of Mn interstitials around the free surface of the as-grown (Ga,Mn)As. (c) 2006 Elsevier B.V. All rights reserved.

Electronic structure and binding energy of a hydrogenic impurity in a hierarchically self-assembled GaAs/AlxGa1-xAs quantum dot

We calculate the electronic structures and binding energy of a hydrogenic impurity in a hierarchically self-assembled GaAs/AlxGa1-xAs quantum dot (QD) in the framework of effective-mass envelope-function theory. The variation of the electronic structures and binding energy with the QD structure parameters and the position of the impurity are studied in detail. We find that (1) acceptor impurity energy levels depend more sensitively on the size of the QD than those of a donor impurity; (2) all impurity energy levels strongly depend on the GaAs quantum well (QW) width; (3) a donor impurity in the QD has only one binding energy level except when the GaAs QW is large; (4) an acceptor impurity in the QD has two binding energy levels, which correspond to heavy- and light-hole quantum states; (5) the binding energy has a maximum value when the impurity is located below the symmetry axis along the growth direction; and (6) the binding energy has a minimum value when the impurity is located at the top corner of the QD. (c) 2006 American Institute of Physics.

Correlation between optical and electrical properties in In0.52Al0.48As/InxGa1-xAs metamorphic high-electron-mobility-transistor structures on GaAs substrates

4.2 K photoluminescence (PL) and 77 K standard Hall-effect measurements were performed for In0.52Al0.48As/InxGa1-xAs metamorphic high-electron-mobility-transistor (HEMT) structures grown on GaAs substrates with different indium contents in the InxGa1-xAs well or different Si delta-doping concentrations. It was found that electron concentrations increased with increasing PL intensity ratio of the "forbidden" transition (the second electron subband to the first heavy-hole subband) to the sum of the "allowed" transition (the first electron subband to the first heavy-hole subband) and the forbidden transition. And electron mobilities decreased with increasing product of the average full width at half maximum of allowed and forbidden transitions and the electron effective mass in the InxGa1-xAs quantum well. These results show that PL measurements are a good supplemental tool to Hall-effect measurements in optimization of the HEMT layer structure. (c) 2006 American Institute of Physics.

Growth and magnetic properties of zincblende CrSb epilayers on relaxed and strained (In, Ga)As buffers

Zincblende CrSb (zb-CrSb) layers with room-temperature ferromagnetism have been grown on relaxed and strained (In,Ga)As buffer layers epitaxially prepared on (001) GaAs substrates by molecular-beam epitaxy. The structural characterizations of CrSb layers fabricated under the two cases are studied by using synchrotron grazing incidence x-ray diffraction (GID). The results of GID experiments indicate that no sign of second phase exists in all the zb-CrSb layers. Superconducting quantum interference device measurements demonstrate that the thickness of zb-CrSb layers grown on both relaxed and strained (In,Ga)As buffer layers can be increased to similar to 12 monolayers (similar to 3.6nm), compared to similar to 3 monolayers (similar to 1nm) on GaAs directly.

Structural, optical and intraband absorption properties of vertically aligned In0.32Ga0.68As/GaAs quantum dots superlattices

The self-organization growth of In0.32Ga0.68As/GaAs quantum dots (QDs) superlattices is investigated by molecular beam epitaxy. It is found that high growth temperature and low growth rate are favorable for the formation of perfect vertically aligned QDs superlattices. The aspect ratio (height versus diameter) of QD increases from 0.16 to 0.23 with increase number of bi-layer. We propose that this shape change play a significant role to improve the uniformity of QDs superlattices. Features in the variable temperature photoluminescence characteristics indicate the high uniformity of the QDs. Strong infrared absorption in the 8-12 mum was observed. Our results suggest the promising applications of QDs in normal sensitive infrared photodetectors. (C) 2001 Elsevier Science B.V. All rights reserved.

Influences of initial nitridation process on the optical and structural characterization of GaN layer grown on sapphire (0001) by metalorganic chemical vapor deposition

In this paper. we investigate the influences of the initial nitridation of sapphire substrates on the optical and structural characterizations in GaN films. Two GaN samples with and without 3 min nitridation process were investigated by photoluminescence (PL) spectroscopy in the temperature range of 12-300 K and double-crystal X-ray diffraction (XRD). In the 12 K PL spectra of the GaN sample without nitridation, four dominant peaks at 3.476, 3.409 3.362 and 3.308 eV were observed, which were assigned to donor bound exciton, excitons bound to stacking faults and extended structural defects. In the sample with nitridation, three peaks at 3.453, 3.365. and 3.308 eV were observed at 12 K, no peak related to stacking faults. XRD results at different reflections showed that there are more stacking faults in the samples without nitridation.

Fe-57 Mossbauer spectroscopic and magnetic studies of R3Fe29-xVx (R = Y, Ce, Nd, Sm, Gd, Tb, and Dy)

Mossbauer spectra for Fe atoms in the series of R3Fe29-xVx (R = Y, Ce, Nd, Sm, Gd, Tb, and Dy) compounds were collected at 4.2 K. The ratio of 14.5 T/mu(B) between the average hyperfine field B-hf and the average Fe magnetic moment mu(Fe)(MS), obtained from our data, in Y3Fe29-xVx is in agreement with that deduced from the RxTy alloys by Gubbens et al. The average Fe magnetic moments mu(Fe)(MS) in these compounds at 4.2 K, deduced from our Mossbauer spectroscopic studies, are in accord with the results of magnetization measurement. The average hyperfine field of the Fe sites for R3Fe29-xVx at 4.2 K increases with increasing values of the rare earth effective spin (g(J) - 1) J, which indicates that there exists a transferred spin polarization induced by the neighboring rare earth atom.

Crystallographic and magnetic properties of the hydrides R3Fe29-xCrxHy (R = Y, Ce, Nd, Sm, Gd, Tb, and Dy)

A systematic study of the structural and intrinsic magnetic properties of the hydrides R3Fe29-xCrxHy (R = Y, Ce, Nd, Sm, Gd, Tb, and Dy) has been performed. Hydrogenation lends to a relative volume expansion of the unit cell and a decrease in x-ray density for each compound. Anisotropic expansions mainly along the n- and b-axes rather than along the c-axis for all of the compounds upon hydrogenation are observed. The lattice constants and the unit-cell volume of R3Fe29-xCrx and R3Fe29-xCrxHy decrease with increasing R atomic number from Nd to Dy, except for Ce, reflecting the lanthanide contraction. Hydrogenation results in an increase in the Curie temperature and a corresponding increase in the saturation magnetization at room temperature for each compound. After hydrogenation a decrease of 0.34 mu(B)/Fe in the average Fe atomic magnetic moment and a slight increase in the anisotropy field for Y3Fe27.2Cr1.8 are achieved at 4.2 K. First-order magnetization processes (FOMP) occur in magnetic fields of around 1.5 T and 4.0 T at 4.2 K for Nd3Fe24.5Cr4.5H5.0 and TD3Fe27.0Cr2.0H2.8, and around 1.4 T at room temperature for Gd3Fe28.0Cr1.0H4.2. The abnormal crystallographic and magnetic properties of Ce3Fe25.0Cr4.0 and Ce3Fe25.0Cr4.0H5.4 suggest that the Ce ion non-triply ionized.

Crystallographic and magnetic properties of nitride R3Fe29-xCrxN4 (R = Y, Ca, Nd, Sm, Gd, Tb, and Dy)

A systematic investigation of crystallographic and magnetic properties of nitride R3Fe29-xCrxN4 (R=Y, Ce, Nd, Sm, Gd, Tb, and Dy) has been performed. The lattice constants and unit cell volume decrease with increasing rare earth atomic number from Nd to Dy, reflecting the lanthanide contraction. After nitrogenation the relative volume expansion of each nitride is around between 5% and 7%. The nitrogenation results in a good improvement in the Curie temperature, the saturation magnetization and anisotropy fields at 4.2 K, and room temperature for R3Fe29-xCrxN4. Magnetohistory effects of R3Fe29-xCrxN4 and R3Fe29-xCrx (R=Nd and Sm) are observed in a low field of 0.04 T. First order magnetization process occurs in Sm3Fe24.0Cr5.0N4 in magnetic fields of 2.8 T at 4.2 K. After nitrogenation, the easy magnetization direction of Sm3Fe24.0Cr5.0 is changed from the easy-cone structure to the uniaxial. The good intrinsic magnetic properties of Sm3Fe24.0Cr5.0N4 make this compound a hopeful candidate for new high-performance hard magnets. (C) 1998 American Institute of Physics.

Crystallographic and magnetic properties of R3Fe29-xVxN4 (R = Y, Ce, Nd, Sm, Gd, Tb, and Dy)

A systematic investigation of crystallographic and magnetic properties of nitride R3Fe29-xVxN4 (R = Y, Ce, Nd, Sm, Gd, Tb, and Dy) has been performed. Nitrogenation leads to a relative volume expansion of about 6%. The lattice constants and unit cell volume decrease with increasing rare-earth atomic number from Nd to Dy, reflecting the lanthanide contraction. On average, the Curie temperature increases due to the nitrogenation to about 200 K compared with its parent compound. Generally speaking, nitrogenation also results in a remarkable improvement of the saturation magnetization and anisotropy fields at 4.2 K and room temperature for R3Fe29-xVxN4 compared with their parent compounds. The transition temperature indicates the spin reorientations of R3Fe29-xVxN4 for R = Nd and Sm are at around 375 and 370 K which are higher than that of R3Fe29-xVx, for R = Nd and Sm 145 and 140 K, respectively. The magnetohistory effects of R3Fe29-xVxN4 (R = Ce, Nd, and Sm) are observed in low fields of 0.04 T. After nitrogenation the easy magnetization direction of Sm3Fe26.7V2.3 is changed from an easy-cone structure to the b-axis. As a preliminary result, a maximum remanence B-r of 0.94 T, an intrinsic coercivity mu(0)H(C) of 0.75 T, and a maximum energy product (B H)(max) of 108.5 kJ m(-3) for the nitride magnet Sm3Fe26.7V2.3N4 are achieved by ball-milling at 293 K.