Stress reduction in GaN films on (111) silicon-on-insulator substrate grown by metal-organic chemical vapor deposition

The GaN film was grown on the (111) silicon-on-insulator (SOI) substrate by metal-organic chemical vapor deposition and then annealed in the deposition chamber. A multiple beam optical stress sensor was used for the in-situ stress measurement, and X-ray diffraction (XRD) and Raman spectroscopy were used for the characterization of GaN film. Comparing the characterization results of the GaN films on the bulk silicon and SOI substrates, we can see that the Raman spectra show the 3.0 cm(-1) frequency shift of E-2(TO), and the full width at half maximum of XRD rocking curves for GaN (0002) decrease from 954 arc see to 472 are sec. The results show that the SOI substrates can reduce the tensile stress in the GaN film and improve the crystalline quality. The annealing process is helpful for the stress reduction of the GaN film. The SOI substrate with the thin top silicon film is more effective than the thick top silicon film SOI substrate for the stress reduction. (C) 2007 Elsevier B.V. All rights reserved.

Stress evolution influenced by oxide charges on GaN metal-organic chemical vapor deposition on silicon-on-insulator substrate

GaN epilayers have been deposited on silicon-on-insulator (SOI) and bulk silicon substrates. The stress transition thickness and the initial compressive stress of a GaN epilayer on the SOI substrate are larger than those on the bulk silicon substrate, as shown in in situ stress measurement results. It is mainly due to the difference of the three-dimensional island density and the threading dislocation density in the GaN layer. It can increase the compressive stress in the initial stage of growth of the GaN layer, and helps to offset the tensile stress generated by the lattice mismatch.

Chemical trends of defect formation in Si quantum dots: The case of group-III and group-V dopants

Using first-principles methods, we have systematically calculated the defect formation energies and transition energy levels of group-III and group-V impurities doped in H passivated Si quantum dots (QDs) as functions of the QD size. The general chemical trends found in the QDs are similar to that found in bulk Si. We show that defect formation energy and transition energy level increase when the size of the QD decreases; thus, doping in small Si QDs becomes more difficult. B-Si has the lowest acceptor transition energy level, and it is more stable near the surface than at the center of the H passivated Si QD. On the other hand, P-Si has the smallest donor ionization energy, and it prefers to stay at the interior of the H passivated Si QD. We explained the general chemical trends and the dependence on the QD size in terms of the atomic chemical potentials and quantum confinement effects.

Al compositional inhomogeneity of AlGaN epilayer with a high Al composition grown by metal-organic chemical vapour deposition

The A1 compositional distribution of A1GaN is investigated by cathodoluminescence (CL). Monochromatic CL images and CL spectra reveal a lateral A1 compositional inhomogeneity, which corresponds to surface hexagonal patterns. Cross-sectional CL images show a relatively uniform Al compositional distribution in the growth direction, indicating columnar growth mode of A1GaN films. In addition, a thin A1GaN layer with lower Al composition is grown on top of the buffer A1N layer near the bottom of the A1GaN epilayer because of the larger lateral mobility of Ga adatoms on the growth surface and their accumulation at the grain boundaries.

Growth of a novel periodic structure of SiC/AlN multilayers by low pressure chemical vapour deposition

A novel 10-period SiC/AlN multilayered structure with a SiC cap layer is prepared by low pressure chemical vapour deposition (LPCVD). The structure with total film thickness of about 1.45 mu m is deposited on a Si (111) substrate and shows good surface morphology with a smaller rms surface roughness of 5.3 nm. According to the secondary ion mass spectroscopy results, good interface of the 10 period SiC/AlN structure and periodic changes of depth profiles of C, Si, Al, N components are obtained by controlling the growth procedure. The structure exhibits the peak reflectivity close to 30% near the wavelength of 322 nm. To the best of our knowledge, this is the first report of growth of the SiC/AlN periodic structure using the home-made LPCVD system.

Unveiling the morphology of buried In(Ga)As nanostructures by selective wet chemical etching: From quantum dots to quantum rings

The three-dimensional morphology of In(Ga)As nanostructures embedded in a GaAs matrix is investigated by combining atomic force microscopy and removal of the GaAs cap layer by selective wet etching. This method is used to investigate how the morphology of In(Ga)As quantum dots changes upon GaAs capping and subsequent in situ etching with AsBr3. A wave function calculation based on the experimentally determined morphologies suggests that quantum dots transform into quantum rings during in situ etching. (c) 2007 American Institute of Physics.

Growth of AlGaN epitaxial film with high Al content by metalorganic chemical vapour deposition

A high-Al-content AlGaN epilayer is grown on a low-temperature-deposited AlN buffer on (0001) sapphire by low pressure metalorganic chemical vapour deposition. The dependence of surface roughness, tilted mosaicity, and twisted mosaicity on the conditions of the AlGaN epilayer deposition is evaluated. An AlGaN epilayer with favourable surface morphology and crystal quality is deposited on a 20 nm low-temperature-deposited AlN buffer at a low V/III flow ratio of 783 and at a low reactor pressure of 100 Torr, and the adduct reaction between trimethylaluminium and NH3 is considered.

Depth dependence of structural quality in InN grown by metalorganic chemical vapor deposition

Rutherford backscattering and channeling is combined with X-ray diffraction to study the depth dependence of crystalline quality in InN layers grown by metalorganic chemical vapor deposition on sapphire substrate. The poorest crystalline quality in InN layer is produced at the intermediate region over 100 nm away from the InN/sapphire interface. With increasing layer thickness the crystalline quality improves to a certain degree dependent on the growth temperature. The InN sample grown at 450 degrees C is found to be more homogeneous than the sample grown at 550 degrees C. The difference in the defect profile is explained by the temperature-dependent growth modes. The inhomogeneity of structural quality and related properties such as carrier concentration and strain field is possibly the reason to observe a high energy wing in PL spectrum of the InN sample grown at 550 degrees C. (c) 2006 Elsevier B.V All rights reserved.

Effect of Al incorporation on the AlGaN growth by metalorganic chemical vapor deposition

The effect of Al incorporation on the AlGaN growth by metalorganic chemical vapor deposition is investigated. With the increase of trimethylalluminum (TMAl) flux, the crystal quality becomes worse, and the epilayer surface becomes rougher. An interesting phenomenon is that the growth rate of AlGaN decrease with increasing TMAl flux, which is opposite to the AlN growth rate dependence on the TMAl flux. All these effects are attributed to the different properties of At atoms due to the higher bond strength of Al-N compared with Ga-N, which lead to lower surface mobility and stronger competitive ability of Al atoms during the growth. The enhancement of the surface mobility of Al is especially important for improving the quality of AlGaN. (c) 2006 Elsevier B.V. All rights reserved.

Chemical composition and elastic strain in AlInGaN quaternary films

High-quality AlInGaN quaternary layers were grown on c-Al2O3 using a thick GaN template. A full width at half maximum of 0.075 degrees from AlInGaN(0004) rocking curve and a minimum yield of 5.6% from Rutherford backscattering/channelling spectrometry (RBS) prove the AlInGaN layer of a comparable crystalline quality with GaN layers. The chemical compositions (both of Al and In contents) of AlInGaN layers are directly obtained from RBS and elastic recoil detection analysis. The lattice parameters both in perpendicular and parallel directions are deduced from X-ray diffraction. The AlInGaN layer is found to process a compressive strain in parallel direction and a tensile strain in perpendicular direction. (c) 2006 Elsevier B.V. All rights reserved.

Growth of single crystalline ZnxCd1-xS nanocombs by metallo-organic chemical vapor deposition

Single crystalline ternary ZnxCd1-xS nanocombs, which have 'comb' shaped' teeth on one side, have been synthesized by a one-step metallo-organic chemical vapor deposition process at a low temperature of 420 degrees C. The asymmetric, growth behavior of the nanocombs is likely to be induced by the polarization of the c-ptane. Because of the uniform structure and perfect geometrical shape, the nanoteeth could be potentially useful as nanocantilever arrays for nanosensors and, nanotweezers. (c) 2006 Elsevier B.V. All rights reserved.

Effects of grain size on the mosaic tilt and twist in InN films grown on GaN by metal-organic chemical vapor deposition

The structural property of InN films grown on Ga-face GaN layers by metal-organic chemical vapor deposition has been studied by high-resolution x-ray diffraction. The mosaic tilt and twist are found to be strongly dependent on the surface lateral grain size. The twist decreases with increasing grain size and finally approaches to a constant level. On the other hand, the mosaic tilt increases substantially when the grain size becomes large enough and exceeds the width of step terraces on the GaN surface, showing an important mechanism for the defect generation in the InN/GaN system with large out-of-plane lattice mismatch. (c) 2006 American Institute of Physics.

Measurement of threading dislocation densities in GaN by wet chemical etching

We demonstrate a technique based on wet chemical etching that enables quick and accurate evaluation of edge- and screw/mixed-type threading dislocations (TDs) in GaN. Large and small etch pits are formed by phosphoric acid on the etched surfaces. The large etch pits are attributed to screw/mixed TDs and the small ones to edge TDs, according to their locations on the surface and Burgers vectors of TDs. Additionally, the origin of small etch pits is confirmed by a transmission electron microscopy. The difference in the size of etch pits is discussed in view of their origin and merging. Overetching at elevated temperatures or for a long time may result in merging of individual etch pits and underestimating of the density of TDs. Wet chemical etching has also been proved efficient in revealing the distribution of TDs in epitaxial lateral overgrowth GaN.

Evolution of mosaic structure in InN grown by metalorganic chemical vapor deposition

Mosaic structure in InN layers grown by metalorganic chemical vapor deposition at various temperatures has been investigated by X-ray diffraction (XRD). With a combination of Williamson-Hall measurement and fitting of twist angles, it was found that variation of growth temperature from 450 to 550 degrees C leads to the variation of the lateral coherence length, vertical coherence length, tilt and twist of mosaic blocks in InN films in a, respectively, monotonic way. In particular, mosaic tilt increases whereas mosaic twist decreases with elevating temperature. Atomic force microscopy shows the morphological difference of the InN nucleation layers grown at 450 and 550 degrees C. Different coalescence thickness and temperature-dependent in-plane rotation of InN nuclei are considered to account for the XRD results. (c) 2006 Elsevier B.V. All rights reserved.

InN nanoflowers grown by metal organic chemical vapor deposition

Hexangular indium nitride nanoflower pattern is observed from scanning electron microscopy and atomic force microscopy. The sample is grown on c-plane (0001) sapphire by metal organic chemical vapor deposition with intentional introduction of hydrogen gas. With the aid of hydrogen, a stable existence of metallic indium is achieved. This will induce the growth of InN nanoflowers via self-catalysis vapor-liquid-solid (VLS) process. It is found that the VLS process is modulated by the interface kinetics and thermodynamics among the sapphire substrate, indium, and InN, which leads to the special morphology of the authors' InN nanoflower pattern. (c) 2006 American Institute of Physics.