Influence of interface modification on the performance of polymer/Bi2S3 nanorods bulk heterojunction solar cells

In this paper, bulk heterojunction photovoltaic devices based on the poly[2-methoxy-5-(3',7'-dimethyloctyloxy)- 1,4-phenylenevinylene] (MDMO-PPV):Bi2S3 nanorods hybrid material were present. To optimize the performance of the devices, the interface modification of the hybrid material that has a significant impact on the exciton dissociation efficiency was studied. An improvement in the device performance was achieved by modifying the Bi2S3 surface with a thin dye layer. Moreover, modifying the Bi2S3 surface with anthracene-9-carboxylic acid can enhance the performance further. Compared with the solar cells with Bi2S3 nanorods hybrid with the MDMO-PPV as the active layer, the anthracene-9carboxylic acid modified devices are better in performance, with the power conversion efficiency higher by about one order in magnitude.

Internal quantum efficiency analysis of solar cell by genetic algorithm

To investigate factors limiting the performance of a GaAs solar cell, genetic algorithm is employed to fit the experimentally measured internal quantum efficiency (IQE) in the full spectra range. The device parameters such as diffusion lengths and surface recombination velocities are extracted. Electron beam induced current (EBIC) is performed in the base region of the cell with obtained diffusion length agreeing with the fit result. The advantage of genetic algorithm is illustrated.

EFFECTS OF 1-MEV-ELECTRON IRRADIATION ON A-SI SOLAR-CELLS

In this report we present the effects of 1 MeV-electron irradiation on i a-Si:H films and solar cells. It is observed that in the dose range of 1.4-8.4 x 10(15) cm(-2) the defect creation has not reached its saturation level and the metastable defects caused by the irradiation cannot be completely removed by a two hour annealing at 200 degrees C for i a-Si:H films or at 130 degrees C for a-Si:H solar cells. The results may be understood in terms of a model based on two kinds of metastable defects created by 1 MeV-electron irradiation.

A COMPARATIVELY LOW-QUALITY SILICON MATERIAL IMPROVED FOR SOLAR-CELL FABRICATION

A comparatively low-quality silicon wafer (with a purity of almost-equal-to 99.9%) was adopted to form a silicon-on-defect-layer (SODL) structure featuring improved crystalline silicon near the defect layer (DL) by means of proton implantation and subsequent annealing. Thus, the SODL technique provides an opportunity to enable low-quality silicon wafers to be used for fabrication of low-cost solar cells.