Compatibilization of blends of polybutadiene and poly(methyl methacrylate) with poly(butadiene-block-methyl methacrylate)

Compatibilization of blends of polybutadiene and poly(methyl methacrylate) with butadiene-methyl methacrylate diblock copolymers has been investigated by transmission electron microscopy. When the diblock copolymers are added to the blends, the size of PB particles decreases and their size distribution gets narrower. In PB/PMMA7.6K blends with P(B-b-MMA)25.2K as a compatibilizer, most of micelles exist in the PMMA phase. However, using P(B-b-MMA)38K as a compatibilizer, the micellar aggregation exists in PB particles besides that existing in the PMMA phase. The core of a micelle in the PMMA phase is about 10 nm. In this article the influences of temperature and homo-PMMA molecular weight on compatibilization were also examined. At a high temperature PB particles in blends tend to agglomerate into bigger particles. When the molecular weight of PMMA is close to that of the corresponding block of the copolymer, the best compatibilization result would be achieved. (C) 1998 John Wiley & Sons, Inc.

Residual properties of an injection-molded poly(phenylene ether ketone) carbon composite during flexural fatigue

The present work investigates the effects of cyclic fatigue loading on the residual properties of an injection-molded composite, carbon-fiber-reinforced poly(phenylene ether ketone) (CF/PEK-C), and damage development in this material under fatigue lending. Test specimens, which had been conditioned to various preselected fatigue damage stages, were measured for their residual properties. The results indicated that cyclic fatigue loading alters the constitutive behavior of the injection-molded composite, especially in the non-linear portion of the stress/strain curve. The residual strength decreases with increase in the number of fatigue cycles as a consequence of the accumulation of fatigue damage, which is dominated by the growth of microcracks. While the residual modulus increases slightly with cyclic fatigue loading, this is probably due to the oriented hardening resulting from creep deformation which is induced during cyclic loading. (C) 1997 Elsevier Science Limited.

The crystal structure and drawing-induced polymorphism in poly(aryl ether ketone)s .1. Poly(oxybiphenyl-4-4'-diyloxy-1,4-phenylenecarbonyl-1,3-phenylenecarbonyl-1,4-phenylene)

Crystal structure and polymorphism induced by uniaxial drawing of a poly(aryl ether ketone) [PEDEKmK] prepared from 1,3-bis(4-fluorobenzoyl)benzene and biphenyl-4,4'-diol have been investigated by means of transmission electron microscopy (TEM), electron diffraction (ED), wide-angle X-ray diffraction (WAXD), and differential scanning calorimetry (DSC) techniques. The melting and recrystallization process in the temperature range of 250-260 degrees C, far below the next melting temperature (306 degrees C), was identified and found to be responsible for the remarkable changes in lamellar morphology. Based on WAXD and ED patterns, it was found that crystal structure of isotropic-crystalline PEDEKmK obtained under different crystallization conditions (melt-crystallization, cold-crystallization, solvent-induced crystallization, melting-recrystallization, and crystallization from solution) keeps the same mode of packing, i.e., a two-chain orthorhombic unit cell with the dimensions a = 0.784 nm, b = 0.600 nm, and c = 4.745 nm (form I). A second crystal modification (form II) can be induced by uniaxial drawing above the glass transition temperature, and always coexists with form I. This form also possesses an orthorhombic unit cell but with different dimensions, i.e., a = 0.470 nm, b = 1.054 nm, c = 5.064 nm. The 0.32 nm longer c-axis of form II as compared with form I is attributed to an overextended chain conformation due to the expansion of ether and ketone bridge bond angles during uniaxial drawing. The temperature dependence of WAXD patterns for the drawn PEDEKmK suggests that form II can be transformed into the more stable form I by relaxation of overextended chains and relief of internal stress at elevated temperature in absence of external tension.

Tension-tension fatigue failure behaviour of poly(phenylene ether ketone) (PEK-C)

Tension-tension fatigue tests were conducted on unnotched injection moulded poly(phenylene ether ketone) (PEK-C) specimens with two stress ratios, R. The fatigue behaviour of this material is described. The S-N curves (S = alternating stress, N = number of cycles to failure) for different R values have the same general shape, but the curve for bigger R is shifted to long cycles. A fatigue lifetime inversion is observed from constructed S-N curves. Examinations of failure surfaces and analyses of the fatigue data reveal that the fatigue failure mechanism of the material studied is crack growth dominated. But the manner of the fatigue crack initiation and propagation depends on the maximum cyclic stress applied. At higher stresses, the fatigue crack originates at the corner of the specimen and propagates inward; at lower stresses, the fatigue crack nucleates at an internal flaw of the specimen and propagates outward. The fatigue lifetime inversion corresponds to the transition of crack initiation and propagation from one mode to the other. Copyright (C) 1996 Elsevier Science Ltd.

SYNTHESIS OF A POLYETHYLENE-GRAFT-POLYSTYRENE COPOLYMER AND ITS COMPATIBILIZATION FOR LINEAR LOW-DENSITY POLYETHYLENE/POLY(PHENYLENE OXIDE) BLENDS

Based on unsteady diffusion kinetics, polyethylene(PE)-graft-polystyrene (PS) copolymers were designed and synthesized with a heterogeneous high yield titanium-based catalyst by copolymerization of ethylene with a PS-macromonomer using 1-hexene as a short chain agent to promote the incorporation of the PS-macromonomer. The presence of 1-hexene facilitated the diffusion of the PS-macromonomer, giving rise to the significantly increased incorporation of the PS-macromonomer. Compatibilization of blends of linear low density polyethylene (LLDPE)/poly(phenylene oxide) (PPO) with the PE-g-PS copolymer were investigated using scanning electron microscopy (SEM) and dynamic mechanical analysis (DMA).

STUDIES ON THE SULFONATION OF POLY(PHENYLENE OXIDE) (PPO) AND PERMEATION BEHAVIOR OF GASES AND WATER-VAPOR THROUGH SULFONATED PPO MEMBRANES .3. SORPTION BEHAVIOR OF WATER-VAPOR IN PPO AND SULFONATED PPO MEMBRANES

Water vapor absorption and desorption by poly (phenylene oxide) (PPO) and sulfonated PPO (SPPO) membranes were studied at a constant temperature of 30-degrees-C and over a broad range of water activity (0.05 less-than-or-equal-to a < 0.8) by the weighing

STUDIES ON THE SULFONATION OF POLY(PHENYLENE OXIDE) (PPO) AND PERMEATION BEHAVIOR OF CASES AND WATER-VAPOR THROUGH SULFONATED PPO MEMBRANES .1. SULFONATION OF PPO AND CHARACTERIZATION OF THE PRODUCTS

Poly(2,6-dimethylphenylene oxide) (PPO) was sulfonated to varying degrees using different sulfonating agents. Physical properties such as solubility, density, and thermal properties were studied for both PPO and sulfonated PPO (SPPO) with different degree

STUDIES ON THE SULFONATION OF POLY(PHENYLENE OXIDE) (PPO) AND PERMEATION BEHAVIOR OF CASES AND WATER-VAPOR THROUGH SULFONATED PPO MEMBRANES .2. PERMEATION BEHAVIOR OF CASES AND WATER-VAPOR THROUGH SULFONATED PPO MEMBRANES

The permeation behaviors of water vapor and gases were studied for both PPO and SPPO of different sulfonation degree. It was found that the permeability of water vapor increased, and those of oxygen and nitrogen decreased; thus the selectivity for water v

A HIGH-RESOLUTION SOLID-STATE NMR-STUDY OF THE MISCIBILITY, MORPHOLOGY, AND TOUGHENING MECHANISM OF POLYSTYRENE WITH POLY(2,6-DIMETHYL-1,4-PHENYLENE OXIDE) BLENDS

An extended Goldman-Shen pulse sequence was used to observe indirectly the proton spin diffusion in the blends of polystyrene (PS) with poly(2,6-dimethyl-1,4-phenylene oxides) (PPO). The results indicate that the average distance between PS and PPO is less than 5 angstrom in the intimately mixed phase, but there are heterogeneous domains on a 100-angstrom scale. The data of spin relaxation of carbons, T1(C), for homopolymers and their blends suggest that there is a strong pi-pi electron conjugation interaction between the aromatic rings of PS and those of PPO, while the aromatic rings of PPO drive the aromatic rings of PS to move cooperatively. It is the cooperative motion that markedly improves the impact strength of PS.

COMPATIBILIZING EFFECT OF POLY(ETHYLENE OXIDE)-B-POLYSTYRENE-B-POLY(ETHYLENE OXIDE) IN PHENOLPHTHALEIN POLY(ETHER ETHER KETONE) POLY(2,6-DIMETHYL-1,4-PHENYLENE OXIDE) BLENDS

The morphology and mechanical behaviour of phenolphthalein poly(ether ether ketone) (PEK-C)/poly(2,6-dimethyl-1,4-phenylene oxide) (PPO) blends has been investigated. A poly(ethylene oxide)-b-polystyrene-b-poly(ethylene oxide) (PEO-PS-PEO) triblock copolymer was used as compatibilizer. It was found that PEO-PS-PEO has a compatibilizing effect on the PEK-C/PPO blends. The addition of PEO-PS-PEO to the blends greatly improves phase dispersion and interfacial interfacial adhesion and also enhances the ultimate tensile strength and Young's modulus at compositions ranging from 30 to 70% PEK-C. However, all the values of the ultimate tensile strength within the whole composition range are lower than those expected by simple additivity, probably owing to the poor mechanical properties of PEO-PS-PEO copolymer.

The Heterogeneous Growth of P(3MeTh)--An Ellipsometric Study

Successive thicker P(3MeTh) layers are analysed by ex situ conventional and imaging ellipsometry. Thin films display a smooth surface, are compact and homogeneous while for a growth charge above 20 mC cm(-2) the polymer structure modifies to a still uniform but less dense layer. A two-layer model is used and a mathematical procedure is developed to obtain, simultaneously, from the experimental ellipsometric parameters, Delta and Psi, the thickness and the complex refractive index of P(3MeTh) films grown up to 80 mC cm(-2). Thicker polymer layers are disordered and present a high degree of surface roughness. 

Hybrid bulk heterojunction solar cells from a blend of poly(3-hexylthiophene) and TiO2 nanotubes

Hybrid bulk heterojunction solar cells based on blend of poly(3-hexylthiophene) (P3HT) and TiO2 nanotubes or dye(N719) modified TiO2 nanotubes were processed from solution and characterized to research the nature of organic/inorganic hybrid materials. Compared with the pristine polymer P3HT and TiO2 nanoparticles/P3HT solar cells, the TiO2 nanotubes/P3HT hybrid solar cells show obvious performance improvement, due to the formation of the bulk heterojunction and charge transport improvement. A further improvement in the device performance can be achieved by modifying TiO2 nanotube surface with a standard dye N719 which can play a role in the improvement of both the light absorption and charge dissociation. Compared with the non-modified TiO2 nanotubes solar cells, the modified ones have better power conversion efficiency under 100 mW/cm(2) illumination with 500W Xenon lamp. (C) 2008 Elsevier B. V. All rights reserved.

Electropolymerized poly(3,4-ethylenedioxythiophene):poly(styrene sulfonate) (PEDOT:PSS) film on ITO glass and its application in photovoltaic device

Poly(3,4-ethylenedioxythiopliene):poly(styrene sulfonate) (PEDOT:PSS) films have been electrochemically polymerized in situ on ITO glass substrate in boron trifluoride diethyl etherate electrolyte (BFEE). Cyclic voltammograms show good redox activity and stability of the PEDOT films. These films had been directly used to fabricate organic-inorganic hybrid solar cells with the structure of ITO/PEDOT/ZnO:MDMC-PPV/Al. The solar cells made of electrochemically polymerized films exhibit higher energy conversion efficiencies compared with that prepared by the spin-coating method, and the highest value is 0.33%. This in-situ electropolymerized method effectively simplifies fabricating procedures and may blaze a facile and economical route for producing high-efficiency solar cells.