Electrocatalytic properties of Cu-Zr amorphous alloy towards the electrochemical hydrogenation of nitrobenzene

The Cu-Zr amorphous alloy was studied as an electrocatalyst towards the electrochemical hydrogenation of nitrobenzene. The electrocatalyst was activated by chemical etching in HF solution. Resulted changes in the morphology, chemical composition and crystalline structure of the electrocatalyst surface were characterised by scanning electron microscopy, X-ray diffraction and Auger electron spectroscopy. The electrocatalytic properties of the Cu-Zr amorphous alloy were assessed by voltammetric measurements. Due to the formation and aggregation of Zr residue modified Cu nanocrystals on the surface caused by the selective dissolution of Zr components in the chemical etching, the activated amorphous alloy is an effective electrocatalyst for the electrochemical reduction reaction of nitrobenzene with aniline as the main product. The positive shift of the peak potential and accompanying increase in the value of peak current in voltammograms with increasing Cu content and decreasing Zr content of the alloy surface in the chemical etching are indicative of improved electrocatalytic activity. (C) 2002 Elsevier Science B.V. All rights reserved.

Adsorption of arsenite and arsenate on amorphous iron hydroxide

Adsorption isotherms in solutions with ionic strengths of 0.01 at 25°C were measured over the arsenite and arsenate concentration range 10−7−10−3 M and the pH range 4–10. At low concentrations, these isotherms obeyed equations of the Langmuir type. At higher concentrations the adsorption isotherms were linear, indicating the existence of more than one type of surface site on the amorphous iron hydroxide adsorbent. Removal of arsenite and arsenate by amorphous iron hydroxide throughout the concentration range were determined as a function of pH. By careful selection of the relative concentration of arsenic and amorphous iron hydroxide and pH, removals on the order of 92% can be achieved.

Bluish-white emission from radical carbonyl impurities in amorphous Al2O3 prepared via the Pechini-type sol-gel process

Many efforts have been devoted to exploring novel luminescent materials that do not contain expensive or toxic elements, or do not need mercury vapor plasma as the excitation source. In this paper, amorphous Al2O3 powder samples were prepared via the Pechini-type sol-gel process. The resulting samples were characterized by X-ray diffraction (XRD), Fourier transform infrared (FT-IR) spectroscopy, field emission scanning electron microscopy (FESEM), photoluminescence (PL) excitation and emission spectra, kinetic decay, and electron paramagnetic resonance (EPR).

New carbazole-based copolymers as amorphous hole-transporting materials for multilayer light-emitting diodes

New carbazole-based copolymers, which contain various concentrations of 9-alkyl-3, 6-carbazole fragments in the main chain connected via alkylene spacers, have been synthesized by Ni(0)-catalyzed Yamamoto-type aryl-aryl coupling reactions. Full characterization of the copolymer structure by NMR spectroscopy and elemental analysis is presented. These compounds represent amorphous materials of high thermal stability with glass transition temperatures of 151-162 degrees C and thermal decomposition starting at temperatures > 390 degrees C. UV-Vis absorption and photoluminescence emission of the copolymers confirmed that the effectively conjugated segment in the 3,6-linked carbazole-type copolymers is limited to dyads (dimeric units). However, copolymers with varying concentrations of the oligocarbazole chromophores demonstrate different charge injection and transport properties in multilayer light-emitting diodes with the copolymers as the hole transport and Alq(3) as the electroluminescent/electron transport layer. The device based on a copolymer composed of oligocarbazole blocks with an average length of around four carbazoles exhibited the best overall performance with a turn-on voltage of 3.5 V, a maximal photometric efficiency of 4.1 cd center dot A(-1) and maximum brightness of about 4 200 cd center dot m(-2).

Hydrogen absorption in Ti45Zr35Ni17Cu3 amorphous and quasicrystalline alloy powders

Ti45Zr35Ni17Cu3 amorphous and icosahedral quasicrystal line (I-phase) powders were synthesized by mechanical alloying (MA) and subsequent annealing, the phase structure and hydrogen absorption properties of two powders were investigated. XRD analysis indicated that the MAed powder was an amorphous phase and annealed powder was an I-phase. Two alloy exhibited excellent hydrogen adsorption property and started to absorb hydrogen without induction time. PCT measurement showed that the plateau pressure of the amorphous powders was obviously higher than that of the I-phase powders. After the first hydrogen cycling, the partial amorphous phase changed to (Zr, Ti)H-2 phases, and the I-phase was steady. Similar hydride phases Ti2ZrH4 and (Zr, Ti)H-2 were also formed after the second hydrogen cycling for the amorphous and I-phase alloy powders.

Thickness dependence of mobility in CuPc thin film on amorphous SiO2 substrate

Hole mobility in a copper-phthalocyanine (CuPc)-based top-contact transistor has been studied with various organic layer thicknesses. It is found that the transistor performance depends on the thickness of the CuPc layer, and the mobility increases with the increase in the CuPc layer and saturated at the thickness of 6 ML. The upper layers do not actively contribute to the carrier transport in the organic films. The morphology of the organic layer grown on the bare SiO2/Si substrate is also presented. The analysis of spatial correlations shows that the CuPc films grow on the SiO2 according to the mixed-layer mode.

Crystallization of mechanically alloyed amorphous W-Mg alloy under high pressure

Pure metal powder mixtures of W and Mg at the desired composition were milled in conventional high-energy ball mill, and amorphous alloy W50Mg50 was obtained after milling for 20 h. The structure evolution of elemental powder mixtures was studied following milling and subsequent high pressure and high temperature treatment. The amorphous alloy transform into a nanocrystalline material below 1050 degreesC at 4.0 GPa. On increasing the temperature, it transforms into a mixture of several new crystal phases under high-pressure condition. It also found that both mechanical alloying and high pressure treatment are the two necessary processes to form the nanocrystalline and the new phases.

Properties of a nanocomposite polymer electrolyte from an amorphous comb-branch polymer and nanoparticles

Three fully amorphous comb-branch polymers based on poly(styrene-co-maleic anhydride) as a backbone and poly(ethylene glycol) methyl ether of different molecular weights as side chains were synthesized. SiO2 nanoparticles of various contents and the salt LiCF3SO3 were added to these comb-branch polymers to obtain nanocomposite polymer electrolytes. The thermal and transport properties of the samples have been characterized. The maximum conductivity of 2.8x10(-4) S cm(-1) is obtained at 28 degreesC. In the system the longer side chain of the comb-branch polymer electrolyte increases in ionic conductivity after the addition of nanoparticles. To account for the role of the ceramic fillers in the nanocomposite polymer electrolyte, a model based on a fully amorphous comb-branch polymer matrix in enhancing transport properties of Li+ ions is proposed.

Electrochemical properties of amorphous and icosahedral quasicrystalline Ti45Zr35Ni17Cu3 powders

Ti45Zr35Ni17Cu3 amorphous and single icosahedral quasicrystalline powders were synthesized by mechanical alloying and subsequent annealing at 855 K. Microstructure and electrochemical properties of two alloy electrodes were characterized. When the temperature was enhanced from 303 to 343 K, the maximum discharge capacities increased from 86 to 329 mAh g(-1) and 76 to 312 mAh g(-1) for the amorphous and quasicrystalline alloy electrodes, respectively. Discharge capacities of two electrodes decrease distinctly with increasing cycle number. The I-phase is stable during charge/discharge cycles, and the main factors for its discharge capacity loss are the increase of the charge-transfer resistance and the pulverization of alloy particles. Besides the factors mentioned above, the formation of TiH2 and ZrH2 hydrides is another primary reason for the discharge capacity loss of the amorphous alloy electrode.

Well defined carbazole-based hole-transporting amorphous molecular materials

Monodisperse carbazole-based oligomers have been synthesized via C-N bonds formation by the modified Ullmann reaction. The full characterization of their structure is presented. These derivatives are highly thermally stable amorphous compounds with glass transition temperatures of 167-171 degrees C and thermal decomposition temperatures of ca. 400 degrees C. Amorphous films of the materials were fabricated and their hole-transporting properties were tested in a light emitting device with Alq(3) as an electroluminescent and electron-transporting material.

Crystallization and melting behavior of amorphous poly(iminosebacoyl iminodecamethylene)

Multiple melting behavior was observed in the differential scanning calorimetry (DSC) scans for the isothermally crystallized poly(iminosebacoyl iminodecamethylene) (PA1010) samples. Coexistence of crystal populations with different lamellar thickness in PA1010 was discussed by means of DSC, wide-angle X-ray diffraction (WAXD), and small-angle X-ray scattering techniques. During crystallization of the polymer, a major lamellar crystal population developed first, which possessed a higher melting temperature. However, a small fraction of the polymer formed minor crystal population with thinner lamellae, which was metastable and, upon post-annealing, could grow into more stable and thicker lamellae through melting and recrystallization process. Lamellae insertion or stacks would develop during the post-annealing at a lower temperature for the isothermally crystallized samples; thus, multiple crystal populations with different thickness could be produced. It is the multiple distribution of lamella thickness that gives rise to multiple melting behavior of crystalline polymers. (C) 2000 John Wiley & Sons, Inc.