Investigation of optical properties of Ce3+-doped Gd2SiO5 crystal irradiated by a femtosecond laser

We report on the optical property changes for Ce3+-doped Gd2SiO5 crystal irradiated by a femtosecond (fs) laser. Absorption spectra showed that Ce-related color centers were formed in this crystal after an 800 nm fs laser irradiation. The annealing temperature-dependence of the refractive index and absorption intensity changes have been investigated. Furthermore, a new way of writing overlapped gratings inside the crystal by use of birefringence of fs laser beam in this crystal was proposed. (c) 2005 Elsevier B.V. All rights reserved.

Growth and its spectroscopic properties of Sm : YAP crystal

Sm3+-doped yttrium aluminum perovskite (YAP) single crystal was grown by Czochralski (CZ) method. The absorption and fluorescence spectra along the crystallographic axis b were measured at room temperature. Judd-Ofelt theory was used to calculate the intensity parameters (Omega(t)), the spontaneous emission probability, the branching ratio and the radiative lifetime of the state (4)G(5/2). The peak emission cross-sections were also estimated at 567, 607, and 648 nm wavelengths. (c) 2006 Elsevier B.V. All rights reserved.

Growth and properties of ZnO thin film on beta-Ga2O3(100) substrate by pulsed laser deposition

Zinc oxide (ZnO) thin films were grown on the beta-Ga2O3 (100) substrate by pulsed laser deposition (PLD). X-ray diffraction (XRD) indicated that the ZnO films are c-axis oriented. The optical and electrical properties of the films were investigated. The room temperature Photoluminescence (PL) spectrum showed a near band emission at 3.28 eV with two deep level emissions. Optical absorption indicated a visible exciton absorption at room temperature. The as-grown films had good electrical properties with the resistivities as low as 0.02 Omega cm at room temperature. Thus, beta-Ga2O3 (100) substrate is shown to be a suitable substrate for fabricating ZnO film. (c) 2006 Elsevier B.V. All rights reserved.

Growth and spectral properties of Gd2SiO5 crystal codoped with Er and Yb

Gd2SiO5 (GSO) single crystal codoped with Yb3+ and Er3+ (Abbr. as Er:Yb:GSO) was successfully grown by the Czochralski (CZ) method for the first time and the spectral characteristics were investigated. The absorption and fluorescence spectra were measured. The emission lifetime of the I-4(13/2)-Er-level was measured to be 5.84ms and the emission cross-section at 1529nm was calculated to be 1.03 x 10(-20) cm(2). The results indicate that Er:Yb:GSO is a potential laser material at similar to 1. 55 mu m wavelength region. (c) 2006 Elsevier B.V. All rights reserved.

Optical properties of ZnO thin film on gamma-LiAlO2 substrate grown by pulsed laser deposition

Optical properties were investigated of ZnO thin films grown oil (100) gamma-LiAlO2 (LAO) substrates by pulsed laser deposition method. C-axis oriented ZnO film was grown oil (100) LAO substrate at the substrate temperature of 550 degrees C. The transmittances of the films were over 85%. Peaks attributed to excitons were seen in the absorption spectra, indicating that the thin films have high crystallinity. Photoluminescence spectra were observed at room temperature; the peak at 550 urn is ascribed to oxygen vacancies in the ZnO films caused by the diffusion of Li from the substrate into the film during deposition. (c) 2005 Elsevier B.V. All rights reserved.

Effect of air annealing on the spectral properties of Ce : Y3Al5O12 single crystals grown by the temperature gradient technique

Five absorption hands, at 227, 300 340, 370 and 457nm, were observed in the optical absorption spectrum of Ce:Y3Al5O12 (Ce:YAG) crystals grown by the temperature gradient technique (TGT). The absorption bands at 227, 340, and 457 nm were identified Lis belonging to the Ce3+ -ion in the YAG crystal. A near UV optical emission band at 398nm was observed. with an excitation spectrum containing two bands, at 235 and 370nm. No fluorescence was detected under 300 nm excitation. The pair of absorption bands at 235 and 370 nm and the absorption band at 300 nm were attributed to the F- and F+-type color centers, respectively. The color centers model was also applied to explain the spectral changes in the Ce:YAG (TGT) crystal, including the reduction in the Ce 31 -ion absorption intensity, after annealing in an oxidizing atmosphere (air). (C) 2004 Elsevier B.V. All rights reserved.

Thermal, spectroscopic and laser properties of Yb3+Na+: CaF2 single crystals

The effects of Na+ doping level on the thermal conductivities, absorption and emission spectra, and fluorescence lifetimes of Yb3+ ,Na+ :CaF2 crystals were systematically studied. Sites structure, covalent force, and crystal field strength of Yb3+ :CaF2 crystals were markedly varied by codoping Na+ as charge compensator. The 2.0at% Yb3+ and 3.0at% Na+-codoped CaF2 crystal was demonstrated to operate in diode-pumped passively mode-locking scheme. Transform-limited 1 ps laser pulses were obtained, showing the crystal capable of producing ultra-short laser pulses. (c) 2006 Elsevier B.V. All rights reserved.

Spectroscopic properties of Nd3+-doped high silica glass prepared by sintering porous glass

A new kind of Nd3+, -doped high silica glass (SiO2 > 96% (mass fraction)) was obtained by sintering porous glass impregnated with Nd3+, ions. The absorption and luminescence properties of high silica glass doped with different Nd3+, concentrations were studied. The intensity parameters Omega(t) (t = 2, 4, 6), spontaneous emission probability, fluorescence lifetime, radiative quantum efficiency, fluorescence branching ratio, and stimulated emission cross section were calculated using the Judd-Ofelt theory. The optimal Nd3+ concentration in high silica glass was 0.27% (mole fraction) because of its high quantum efficiency and emission intensity. By comparing the spectroscopic parameters with other Nd3+ doped oxide glasses and commercial silicate glasses, the Nd3+-doped high silica glasses are likely to be a promising material used for high power and high repetition rate lasers.

Study on growth and properties of novel gamma-LiAlO2 substrate

Transparent gamma-LiAlO2 single crystal has been grown by Temperature Gradient technique. The surface of the wafer annealed in O-2-atmosphere at 1100 degrees C for 70 h became opaque and Li-poor phase (LiAl5O8); while, that annealed in Li-rich atmosphere kept transparent and smooth. The full-width at half maximum value dropped to 30 arcsecs when the wafer was annealed in Li-rich atmosphere. That annealed in O-2-atmosphere increased to 78 arcsec. Compared with absorption spectra, we can conclude that the 196 nm absorption peak was caused by Li vacancies and the 736 nm peak was caused by O vacancies.

Spectral properties and charge transfer luminescence of Yb3+ : Gd3Ga5O12 (Yb : GGG) crystal

The Yb (10%):GGG and Yb (30%): GGG crystals have been grown by the Czochralski method. The chemical compositions are: Yb1.07Gd1.74Ga5.19O12 and Yb0.33Gd1.47Ga5.2O12. The absorption and emission spectra of Yb:GGG crystal at room temperature have been measured. The spectroscopic parameters of Yb:GGG and Yb:YAG have been compared. Optical absorption spectra of Yb:GGG show 4f-4f transitions related to Gd3+ ion around 300 nm, and also an onset of charge transfer (CT) transitions from oxygen ligands to Gd3+ or Yb3+ cations below 240nm. The CT absorption of Yb3+ is largely overlapped by that of Gd3+ ions. (c) 2005 Elsevier B.V. All rights reserved.

Sites structure and spectroscopic properties of Yb-doped and Yb, Na-codoped CaF2 laser crystals

For the first time, the effect of Na+ on crystal structure, valence state of Yb ions, spectroscopic properties of YbF3-doped CaF2 system was systematically studied. Na+ can greatly suppress the deoxidization of Yb3+ to Yb2+. Absorption and emission spectra showed codoping Na+ with different Na:Yb ratios can modulate the spectroscopy and photoluminescence properties of Yb3+ ions in CaF2 lattice in a large scope. The emission lifetime and quantum efficiency of Yb3+ in CaF2 were greatly enhanced by the codopant of Na+. The potential laser performances of the new Yb, Na-codoped CaF2 crystals were predicted. (c) 2005 Elsevier B.V. All rights reserved.

Effect of gamma-irradiation on spectral properties of undoped Y2SiO5 crystals

The absorption spectra of undoped Y2SiO5 crystals were studied before and after gamma-irradiation. After gamma-irradiation, the additional absorption peaks at 260-270 and 320nm were observed in as-grown and H,annealed Y2SiO5 crystal, but it did not occur in air-annealed Y2SiO5 crystal. These absorption peaks were attributed to F color centers and O- hole centers, respectively. Owing to more oxygen vacancies and color centers in H-2-annealed Y2SiO5 crystal than that in as-grown Y2SiO5 crystal after gamma-irradiation, the additional absorption peaks were more intense in the former than that in the latter. With the irradiation dose increasing from 20 to 220kGy, the intensity of additional absorption peaks increased.

Preparation and optical properties of silicate glasses containing Pd nanoparticles

We report the space selective precipitation of Pd nanoparticles in Pd2+ -doped silicate glass by ultrashort laser pulses irradiation and further annealing. Absorption spectra, transmission electron microscopy, refractive index measurement and Z-scan technique demonstrated that metallic Pd nanoparticles were precipitated in the glass sample after irradiation by an 800-nm femtosecond laser and subsequent annealing at 600 degrees C. We discuss a refractive index change and nonlinear absorption that combines the precipitation of Pd nanoparticles. Crown Copyright (c) 2005 Published by Elsevier B.V. All rights reserved.

Spectral properties of Ho : GdVO4 single crystal

Absorption and emission spectral properties of GdVO4 single crystal doped with Ho3+ ions were investigated at room temperature. Polarized absorption cross section is calculated in the range of 400-2200nm. Results were analyzed and parameters were calculated based on Judd-Ofelt theory, the emission spectrum shows that the emission intensity around the wavelength of 546 nm associated with transition S-5(2) -> I-5(8) is much stronger than other bands in the observed range and potentially enable the green light output around this emission band in this crystal. (c) 2006 Elsevier B.V. All rights reserved.

Spectroscopic properties of Ce : YAP scintillation crystal grown by temperature gradient technique

Spectroscopic properties of Ce-doped yttrium orthoaluminate (Ce:YAlO3 or Ce:YAP) crystals grown by temperature gradient technique (TGT) were investigated, and the effects of the growth conditions on the properties were analyzed.. Methods of optical absorption (OA), photoluminescence (PL), photoluminescence decay (PLD), X-ray excited luminescence (XL) and cathodeluminescence (CL) were used in these investigations. The results showed that the absorption band peak at 202, 394 and 532 nm originated from F and F+ color center induced by the weak reducing growth atmosphere, green emission band near 500 ran derived from Ce3+ -Ce3+ pairs and band at 650 similar to 850 run from some unintentional impurity in crystals.