DETERMINATION OF THE SUBBAND ENERGY IN THE V-SHAPED POTENTIAL WELL OF DELTA-DOPED GAAS BY DEEP-LEVEL TRANSIENT SPECTROSCOPY

Using deep level transient spectroscopy (DLTS) the conduction-subband energy levels in a V-shaped potential well induced by Si-delta doping in GaAs were determined. Self-consistent calculation gives four subbands in the well below the Fermi level. Experimentally, two DLTS peaks due to electron emission from these subbands were observed. Another two subbands with low electron concentration are believed to be merged into the adjacent DLTS peak. A good agreement between self-consistent calculation and experiment was obtained. (C) 1994 American Institute of Physics.

CHARACTERIZATION OF HIGH FLUENCE NEUTRON-INDUCED DEFECT LEVELS IN HIGH-RESISTIVITY SILICON DETECTORS USING A LASER DEEP-LEVEL TRANSIENT SPECTROSCOPY (L-DLTS)

Neutron irradiated high resistivity (4-6 kOMEGA-cm) silicon detectors in the neutron fluence (PHI(n)) range of 5 X 10(11) n/cm2 to 1 X 10(14) n/cm2 have been studied using a laser deep level transient spectroscopy (L-DLTS). It has been found that the A-center (oxygen-vacancy, E(c) = 0.17 eV) concentration increases with neutron fluence, reaching a maximum at PHI(n) almost-equal-to 5 X 10(12) n/cm2 before decreasing with PHI(n). A broad peak has been found between 200 K and 300 K, which is the result of the overlap of three single levels: the V-V- (E(c) = 0.38 eV), the E-center (P-V, E(c) = 0.44 eV), and a level at E(c) = 0.56 eV that is probably V-V0. At low neutron fluences (PHI(n) < 5 X 10(12) n/cm2), this broad peak is dominated by V-V- and the E-centers. However, as the fluence increases (PHI(n) greater-than-or-equal-to 5 X 10(12) n/cm2), the peak becomes dominated by the level of E(c) = 0.56 eV.

DETERMINATION OF THE CONDUCTION-BAND OFFSET OF A SINGLE ALGAAS BARRIER LAYER USING DEEP-LEVEL TRANSIENT SPECTROSCOPY

The tunneling from an AlGaAs confined thin layer to a GaAs layer in the GaAs/Al0.33Ga0.67As/GaAs structure during the trapped electron emission from deep level in the AlGaAs to its conduction band has been observed by deep level transient spectroscopy. With the aid of the tunneling effect, the conduction-band offset DELTAE(c) was determined to be 0.260 eV, corresponding to 63% of DELTAE(g). A calculation was also carried out based on this tunneling model by using the experimental value of DELTAE(c) = E2 - E1 = 0. 260 eV, and good agreement between the experimental and calculated curves is obtained.

INVESTIGATION OF NEGATIVE TRANSIENT CURRENT OF ARGON-IMPLANTED GAAS USING PHOTOINDUCED TRANSIENT-CURRENT SPECTROSCOPY

The investigation of deep levels of argon-implanted LEC-grown semi-insulating GaAs with implantation dosages ranging from 1 x 10(11) to 1 x 10(15) cm-2 has been performed. Using a photoinduced transient-current spectroscopy (PITCS) it was demonstrated that, for implantation dosages below 1 X 10(13) cm-2, a negative peak or negative transient current (NTC) was observed in the temperature range from 330 to 350 K. The magnitude of this negative peak increased with dosage up to a level of 1 X 10(12) cm-2, beyond which it decreased with dosage. The dosage dependence of the EL3 peak height and the resistance of the specimen have also been investigated. It was observed that the variation of the EL3 peak height with dosage was similar to the variation of the magnitude of the negative peak, that is the EL3 peak height likewise increased with dosage up to 1 X 10(12) cm-2, and then decreased. The resistance of the original high-resistivity specimen dropped abruptly when the dosage reached 1 X 10(12) cm-2. This critical dosage (1 X 10(12) cm-2) was found to be a threshold for the generation of a highly disordered state.

A NEW RESULT IN TRANSIENT CURRENT EXPERIMENT ON A-SI-H P/I/N AND N/I/N DEVICES

The transient current response of a-Si:H in both p/i/n and n/i/n structures has been measured as a function of pulse intermittence and pulse amplitude. The results are consistent with the picture that in p/i/n samples the peculiar current response is caused by the competing contributions of electrons and holes which show themselves in different time scales.

SPECTROSCOPIC INVESTIGATION OF HYDROGEN-DOPANT COMPLEXES IN BULK P-TYPE AND IMPLANTED N-TYPE CRYSTALLINE SILICON

Infrared absorption experiments have been performed on hydrogenated and deuterated bulk boron- and aluminum-doped-Si and implanted P, As, and Sb donors in silicon. A first evidence of complex formation in bulk p-type Si is obtained and the spectra confirm the anomalous 3.3-cm-1 deuterium frequency shift with respect to boron isotopes. The ratio of the D-B-11 and D-B-10 peak areas is found to be the same as that of the two boron isotopes natural abundance. In donor-implanted silicon, a quantitative analysis of the obtained data has allowed a rough estimate of the passivating rate due to diffusing deuterium. While the frequencies of the various vibrational lines are found to be in agreement with those reported in the literature, the data on the broad line at 1660 cm-1 (H) or 1220 cm-1 (D) seem to suggest an assignment of this peak to a complex in the bulk involving some type of defect due to the implantation process.

ELECTRICAL CHARACTERS OF OXYGEN DEFECTS IN SILICON SUBJECTED TO INTRINSIC GETTERING TREATMENT

The influence of oxygen defects on the resistivity and mobility of silicon wafers is discussed. Grinding processes were performed on the surfaces of samples in order to obtain the information on interior defects of the samples. Spreading resistivity and Hall measurements prove that SiO(x) complexes alone result in resistivity increase and mobility decrease. Deep level transient spectroscopy experiments prove that SiO(x) complexes alone are electrically active. A mechanism of carrier scattering by electrically active SiO(x) complex is proposed to explain the changes of resistivity and mobility.

SHEAR-DEFORMATION-POTENTIAL CONSTANT OF THE CONDUCTION-BAND MINIMA OF SI - EXPERIMENTAL-DETERMINATION BY THE DEEP-LEVEL CAPACITANCE TRANSIENT METHOD

The shear-deformation-potential constant XI-u of the conduction-band minima of Si has been measured by a method which we called deep-level capacitance transient under uniaxial stress. The uniaxial-stress (F) dependence of the electron emission rate e(n) from deep levels to the split conduction-band minima of Si has been analyzed. Theoretical curves are in good agreement with experimental data for the S0 and S+ deep levels in Si. The values of XI-u obtained by the method are 11.1 +/- 0.3 eV at 148.9 K and 11.3 +/- 0.3 eV at 223.6 K. The analysis and the XI-u values obtained are also valuable for symmetry determination of deep electron traps in Si.

DETERMINATION OF THE X-CONDUCTION-SUBBAND ENERGIES IN TYPE-II GAAS/ALAS/GAAS QUANTUM-WELL BY DEEP-LEVEL TRANSIENT SPECTROSCOPY

Using deep level transient spectroscopy (DLTS) the X conduction-subband energy levels in an AlAs well sandwiched by double GaAs layers were determined. Calculation gives eight subbands in the well with well width of 50 Angstrom. Among them, five levels and the other three remainders are determined by using the large longitudinal electron effective mass m(1)(1.1m(0)) and transverse electron effective mass m(t)(0.19m(0)) at X valley, respectively. Two subbands with the height energies were hardly detectable and the other six ones with lower energies are active in the present DLTS study. Because these six subbands are close to each other, we divided them into three groups. Experimentally, we observed three signals induced from the three groups. A good agreement between the calculation and experiment was obtained. (C) 1995 American Institute of Physics.

Transient photocurrent investigation of photo-processes of lattice-matched MQW GaAs/AlxGa1-xAs electrode

Transient photocurrents induced by short light pulses at lattice-matched GaAs/AlxGa1-xAs multiple quantum well (MQW) electrodes were studied as a function of electrode potential. Dual exponential photocurrent decay transients were observed at various potentials. By analysis of the dual exponential decay transients, information on steady state photocurrents (I-s), surface collection of photoexcited minority carriers (G(0)) and lifetimes of surface states (T-s) was obtained. The kinetic behaviors of photoprocesses at illuminated MQW/electrolyte interface were discussed.

Theoretical studies of the C60 and alkali metal-containing complexes C60 M