Preparation and optical properties of silicate glasses containing Pd nanoparticles

We report the space selective precipitation of Pd nanoparticles in Pd2+ -doped silicate glass by ultrashort laser pulses irradiation and further annealing. Absorption spectra, transmission electron microscopy, refractive index measurement and Z-scan technique demonstrated that metallic Pd nanoparticles were precipitated in the glass sample after irradiation by an 800-nm femtosecond laser and subsequent annealing at 600 degrees C. We discuss a refractive index change and nonlinear absorption that combines the precipitation of Pd nanoparticles. Crown Copyright (c) 2005 Published by Elsevier B.V. All rights reserved.

Edge-defined, film-fed growth (EFG) technique for the preparation of alpha-Al2O3 : C crystal with highly sensitive thermoluminescence response

In this work, alpha-Al2O3:C, a highly sensitive thermoluminescence dosimetry crystal, was grown by the EFG method in which a graphite heating unit and shield acted as the carbon source during the growth process. The optical, luminescent properties and dosimetric characteristics of the crystal were investigated. The as-grown crystal shows a single glow peak at 536 K, which is associated with Cr3+ ions. After annealing in H-2 at 1673 K for 80 h, the crystal shows a single glow peak at 460 K and a blue emission band at 415 nm. The thermoluminescent response of the annealed crystal shows linear-sublinear-saturation characteristics in the dose range from 5 x 10(-6) to 100 Gy.

斜角入射沉积法制备渐变折射率薄膜的折射率分析

斜角入射沉积法是一种制备薄膜的新颖方法，它可以用来制备渐变折射率薄膜．本文首先探讨了膜料的沉积入射角为α，薄膜柱状生长倾斜角为β时的薄膜的填充系数；之后利用drude理论，分析研究了斜角入射沉积法制备渐变折射率薄膜的折射率与薄膜的入射角和生长方向的关系．

Preparation of high laser induced damage threshold antireflection film using interrupted ion assisted deposition

Single layers and antireflection films were deposited by electron beam evaporation, ion assisted deposition and interrupted ion assisted deposition, respectively. Antireflection film of quite high laser damage threshold (18J/cm(2)) deposited by interrupted ion assisted deposition were got. The electric field distribution, weak absorption, and residual stress of films and their relations to damage threshold were investigated. It was shown that the laser induced damage threshold of film was the result of competition of disadvantages and advantages, and interrupted ion assisted deposition was one of the valuable methods for preparing high laser induced damage threshold films. (c) 2007 Optical Society of America

Preparation and characterization of nanostructured ZrO2 thin films by glancing angle deposition

ZrO2 films were prepared by electron beam evaporation with glancing angle deposition (GLAD) technique. The as-deposition and annealed ZrO2 films are all amorphous, different from that deposited at normal incidence. Due to the shadowing effect, a highly orientated structure composed of slanted columns formed, and the obtained films became the mixture of slanted columns and voids. The relationship among the effective refractive index, packing density and flux incident angle was investigated. The refractive index and packing density of ZrO2 films decrease with the increase of the incident angle. The in-plane birefringence of GLAD ZrO2 films was calculated. At the packing density of 0.576, the maximum birefringence is 0.037. (c) 2006 Elsevier B.V. All rights reserved.