Effects of grain size on the mosaic tilt and twist in InN films grown on GaN by metal-organic chemical vapor deposition

The structural property of InN films grown on Ga-face GaN layers by metal-organic chemical vapor deposition has been studied by high-resolution x-ray diffraction. The mosaic tilt and twist are found to be strongly dependent on the surface lateral grain size. The twist decreases with increasing grain size and finally approaches to a constant level. On the other hand, the mosaic tilt increases substantially when the grain size becomes large enough and exceeds the width of step terraces on the GaN surface, showing an important mechanism for the defect generation in the InN/GaN system with large out-of-plane lattice mismatch. (c) 2006 American Institute of Physics.

New insight into the origin of twin and grain boundary in InP

X-ray reflectivity curves show bi-crystal (twin) characteristics. Defect segregations at the twin boundary can be seen, whereas stress is relaxed at the edge of the boundary. Relaxation of the stress resulted in the formation of twins and other defects. As a result of the formation of such defects, a defect-free and stress-free zone or low defect density and small stress zone is created around the defects. Stress, chemical stoichiometry deviation and non-homogeneous distribution of impurities are the key factors that cause twins in LEC InP crystal growth. (C) 1999 Elsevier Science Ltd. All rights reserved.

Twin and grain boundary in InP: A synchrotron radiation study

Experimentally observed X-ray reflectivity curves show bi-crystal(twin) characteristics. The study revealed that there was defect segregation at the twin boundary. Stress was relaxed at the edge of the boundary. Relaxation of the stress resulted in formation of twin and other defects. As a result of formation of such defects, a defect-free and stress-free zone or low defect density and small stress zone is created around the defects. So a twin model was proposed to explain the experimental results. Stress(mainly thermal stress), chemical stoichiometry deviation and impurities nonhomogeneous distributions are the key factors that cause twins in LEC InP crystal growth. Twins on (111) face in LEC InP crystal were studied. Experimental evidence of above mentioned twin model and suggestions on how to get twin-free LEC InP single crystals will be discussed.