Radiation effects on the immiscible polymer blend of nylon1010 and high-impact polystyrene (HIPS) I: Gel/dose curves, mathematical expectation theorem and thermal behaviour

This paper studies the radiation properties of the immiscible blend of nylon1010 and HIPS. The gel fraction increased with increasing radiation dose. The network was found mostly in nylon1010, the networks were also found in both nylon1010 and HIPS when the dose reaches 0.85 MGy or more. We used the Charleby-Pinner equation and the modified Zhang-Sun-Qian equation to simulate the relationship with the dose and the sol fraction. The latter equation fits well with these polymer blends and the relationship used by it showed better linearity than the one by the Charleby-Pinner equation. We also studied the conditions of formation of the network by the mathematical expectation theorem for the binary system. Thermal properties of polymer blend were observed by DSC curves. The crystallization temperature decreases with increasing dose because the cross-linking reaction inhibited the crystallization procession and destroyed the crystals. The melting temperature also reduced with increasing radiation dose. The dual melting peak gradually shifted to single peak and the high melting peak disappeared at high radiation dose. However, the radiation-induced crystallization was observed by the heat of fusion increasing at low radiation dose. On the other hand, the crystal will be damaged by radiation. A similar conclusion may be drawn by the DSC traces when the polymer blends were crystallized. When the radiation dose increases, the heat of fusion reduces dramatically and so does the heat of crystallization. (C) 1999 Elsevier Science Ltd. All rights reserved.

Effects of pressure and molecular weight on the miscibility of polystyrene and cyclohexane

With the aid of Sanchez-Lacombe lattice fluid theory (SLLFT), the phase diagrams were calculated for the system cyclohexane (CH)/polystyrene (PS) with different molecular weights at different pressures. The experimental data is in reasonable agreement with SLLFT calculations. The total Gibbs interaction energy, g*(12) for different molecular weights PS at different pressures was expressed, by means of a universal relationship, as g(12)* =f(12)* + (P - P-0) nu*(12) demixing curves were then calculated at fixed (near critical) compositions of CH and PS systems for different molecular weights. The pressures of optimum miscibility obtained from the Gibbs interaction energy are close to those measured by Wolf and coworkers. Furthermore, a reasonable explanation was given for the earlier observation of Saeki et al., i.e., the phase separation temperatures of the present system increase with the increase of pressure for the low molecular weight of the polymer whereas they decrease for the higher molecular weight polymers. The effects of molecular weight, pressure, temperature and composition on the Flory Huggins interaction parameter can be described by a general equation resulting from fitting the interaction parameters by means of Sanchez-Lacombe lattice fluid theory.

Preparation and characterization of nanometer-sized CeO2/polystyrene hybrid material

Nanometer-sized CeO2/polystyrene hybrid material was prepared using reversed micelles microemulsion method. XRD analysis revealed that the CeO2 nanoparticles in polystyrene were amorphous. XPS patterns indicated that the hybrid material was not a simply physical mixture, but a certain strength of chemical bond between CeO2 nanoparticles and polystyrene existed. FTIR patterns revealed that the absorption of Ce-O bond in hybrid material was blue-shifted.

Radiation effects on the immiscible polymer blend of nylon1010 and high-impact strength polystyrene (II): mechanical properties and morphology

The paper studies the morphology and mechanical properties of immiscible binary blends of the nylon 1010 and HIPS through the radiation crosslinking method. In this blend, the HIPS particles were the dispersed phases in the nylon 1010 matrix. With increasing of dose, the elastic modulus increased, However, the tensile strength. elongation at bleak and the energy of fracture increased to a maximum at a dose of 0.34 MGy, then reduced with the increasing of dose. SEM photographs show that the hole sizes are not changed obviously at low dose and at high dose, remnants that cannot be dissolved in formic acid and THF can be observed in the holes and on the surface. TEM photographs showed that radiation destroys the rubber phases in the polymer blend. (C) 2001 Elsevier Science Ltd. All rights reserved.

Blends of polyamide 1010 with ungrafted and maleic anhydride grafted high impact polystyrene

The crystallization, dynamic mechanical properties, tensile properties and morphology features of polyamidel 1010(PA1010) blends with the high impact polystyrere (HIPS) and maleic anhydride (MA) grafted HIPS(HIPS-g-MA) were examined at a wide composition range. By comparison the PA1010/HIPS-g-MA and PA1010/HIPS binary blends, it was found that the size of the domains of HIPS-g-MA was much smaller than that of HIPS at the same compositions. It was found that the mechanical properties of PA1010/HIPS-g-MA blends were obviously higher than those of PA1010/HIPS blends. When the content of PA1010 is more than 50wt% in the blends, the crystallization temperatures, T-cs, of PA1010 increase with increasing the content of HIPS-g-MA. On the other hand, when the content of PA1010 in the blends is less than 35wt% the fraction crystallization is observed. The same result is not obtained for the blends of PA1010/HIPS. These behaviors could be attributed to the chemical interactions between the two components and good dispersion in PA1010/HIPS-g-MA blends.

Synthesis of a novel graft-like copolymer of syndiotactic polystyrene with polybutadiene

A novel graft-like copolymer of syndiotactic polystyrene (sPS) with polybutadiene (PB) was synthesized by polymerization of styrene in a toluene solution of PB using the cyclopentadiene titanium trichloride (CpTiCl3)/methylaluminoxane (MAO) catalytic system. The effect of PB on the crystallization behavior of the copolymer was investigated by differential scanning calorimetry and wide angle X-ray diffraction. Hydrogenation of the sPS/PB copolymer with p-toluenesulfonyl hydrazide afforded a PE-like copolymer.

Blends of polyamide1010 with unmodified and maleic-anhydride-grafted high-impact polystyrene

The crystallization behaviors, dynamic mechanical properties, tensile, and morphology features of polyamide1010 (PA1010) blends with the high-impact polystyrene (HIPS) were examined at a wide composition range. Both unmodified and maleicanhydride-(MA)-grafted HIPS (HIPS-g-MA) were used. It was found that the domain size of HIPS-g-MA was much smaller than that of HIPS at the same compositions in the blends. The mechanical performances of PA1010-HIPS-g-MA blends were enhanced much more than that of PA1010-HIPS blends. The crystallization temperature of PA1010 shifted towards higher temperature as HIPS-g-MA increased from 20 to 50% in the blends. For the blends with a dispersed PA phase (less than or equal to 35 wt %), the T-c of PA1010 shifted towards lower temperature, from 178 to 83 degrees C. An additional transition was detected at a temperature located between the T-g's of PA1010 and PS. It was associated with the interphase relaxation peak. Its intensity increased with increasing content of PA1010, and the maximum occurred at the composition of PA1010-HIPS-g-MA 80/20. (C) 1999 John Wiley & Sons, Inc. J Appl Polym Sci 74: 857-865, 1999.

Syndiotactic polystyrene/thermoplastic polyurethane blends using poly(styrene-b-4-vinylpyridine) diblock copolymer as a compatibilizer

The effect of adding diblock copolymer poly(styrene-b-4-vinylpyridine) (P(S-b-4VPy), to immiscible blends of syndiotactic polystyrene (sPS)/thermoplastic polyurethane (TPU) on the morphology, thermal transition, crystalline structure, and rheological and mechanical properties of the blends has been investigated. The diblock copolymer was synthesized by sequential anionic copolymerization and was melt-blended with sPS and TPU. Scanning electron microscopy (SEM) showed that the added block copolymer reduced the domain size of the dispersed phase in the blends. Differential scanning calorimetry (DSC) and wide-angle X-ray diffraction (WAXD) revealed that the extent of compatibility between sPS and TPU affected the crystallization of the sPS in the blends. Tensile strength and elongation at break increased, while the dynamic modulus and complex viscosity decreased with the amount of P(S-b-4VPy) in the blend. The compatibilizing effect of the diblock copolymer is the result of its location at the interface between the sPS and the TPU phases and penetration of the blocks into the: corresponding phases, i.e. the polystyrene block enters the noncrystalline regions of the sPS, and the poly(4-vinylpyridine) block interacts with TPU through intermolecular hydrogen bonding. (C) 1999 Elsevier Science Ltd. All rights reserved.

Compatibilization of blends of polystyrene and zinc salt of sulfonated polystyrene by poly(styrene-b-4-vinylpyridine) diblock copolymer

The compatibilizing effect and mechanism of poly(styrene-b-4-vinylpyridine) diblock copolymer, P(S-b-4VPy), on the immiscible blend of polystyrene (PS)/zinc salt of sulphonated polystyrene (Zn-SPS) were studied. SEM results show that the domains of the dispersed phase in the blend become finer. DSC experiments reveal that the difference between the two T-g's corresponding to the phases in the blends becomes larger on addition of P(S-b-4VPy), mainly resulting from dissolving of the poly(4-vinylpyridine (P4VPy) block in the Zn-SPS phase. FTIR analysis shows that compatibility of P4VPy and Zn-SPS arises from the stoichiometric coordination of the zinc ions of Zn-SPS and pyridine nitrogens of P4VPy. SAXS analysis indicates the effect of the P(S-b-4VPy) content on the structure of the compatibilized blends. When the content of the block copolymer is lower than 4.1 wt%, the number of ion pairs in an aggregate in the Zn-SPS becomes smaller, and aggregates in ionomer in the blend become less organized with increasing P(S-b-4VPy). When the P(S-b-4VPy) content in the blend is up to 7.4 wt%, a fraction of P(S-b-4VPy) form a separate domain in the blend. (C) 1999 Elsevier Science Ltd. All rights reserved.

Compatibilizing effect of polystyrene-block-poly(4-vinylpyridine) for poly(2,6-dimethyl-1,4-phenyleneoxide) chlorinated polyethylene blends

The compatibilizing effect and mechanism of compatibilization of the diblock copolymer polystyrene-block-poly(4-vinylpyridine) P(S-b-4VPy) on immiscible blends of poly(2,6-dimethyl-1,4-phenylene oxide) (PPO)/chlorinated polyethylene (CPE) were studied by means of scanning electron microscopy (SEM), differential scanning calorimetry (DSC), mechanical properties and FTIR measurements. The block copolymer was synthesized by sequential anionic polymerization and melt-blended with PPO and CPE. The results show that the P(S-b-4VPy) added acts as an effective compatibilizer, located at the interface between the PPO and the CPE phase, reducing the interfacial tension, and improving the interfacial adhesion. The tensile strength and modulus of all blends increase with P(S-b-4VPy) content, whereas the elongation at break increases for PPO-rich blends, but decreases for CPE-rich blends. The polystyrene block of the diblock copolymer is compatible with PPO, and the poly(4-vinylpyridine) block and CPE are partially miscible.

Molecular dynamics simulation of polystyrene-block-poly(methyl methacrylate)

Molecular dynamics is applied to the system of polystyrene-block-poly(methyl methacrylate). The simulation shows that for the block copolymer system, a layered structure, which reflects microphase separation, is obtained and this structure is stable. In order to elucidate that the formation of the layered structure is reasonable, some static properties such as the radial distribution function and the dipole moment are analyzed in some detail.

Synthesis of isotactic polystyrene with a rare-earth catalyst

Polymerization of styrene with the neodymium phosphonate Nd(P-507)/H2O/Al(i-Bu)(3) catalytic system has been examined. The polymer obtained was separated into a soluble and an insoluble fraction by 2-butanone extraction. C-13-NMR spectra indicate that the insoluble fraction is isotactic polystyrene and the soluble one is syndiotactic-rich atactic polystyrene. The polymerization features are described and discussed. The optimum conditions for the polymerization are as follows: [Nd] = (3.5-5.0) x 10(-2) mol/L; [styrene] = 5 mol/L; [Al]/[Nd] = 6-8 mol/mol; [H2O]/[Al] = 0.05-0.08 mol/mol; polymerization temperature around 70 degrees C. The percent yield of isotactic polystyrene (TY) is markedly affected by catalyst aging temperature. With increase of the aging temperature from 40 to 70 degrees C, TY increases from 9% to 48%. Using AlEt3 and Al(i-Bu)(2)H instead of Al(i-Bu)(3) decreases the yield of isotactic polystyrene. Different neodymium compounds give the following activity order: Nd(P-507)(3) > Nd(P-204)(3) > Nd(OPri)(3) > NdCl3 + C2HF5OH > Nd(naph)(3). With Nd(naph)(3) as catalyst, only atactic polystyrene is obtained. (C) 1998 John Wiley & Sons, Inc.

Effects of molecular weight and interaction parameter on the glass transition temperature of polystyrene mixtures and its blends with polystyrene/poly(2,6-dimethyl-p-phenylene oxide)

The glass transition temperature (T-g) of mixtures of polystyrene (PS) with different molecular weight and of blends of poly(2,6-dimethyl-p-phenylene oxide) (PPO) and polystyrene with different molecular weight (DMWPS) was studied by a DSC method. For the whole range of composition, the curves of T-g vs composition obtained by experiment were compared with predictions from the Fox, Gordon-Taylor, Couchman and Lu-Weiss, equations. It was found that the experimental results were not in agreement with those from the Fox, Gordon-TayIor and Couchman equations for the binary mixtures of DMWPS, where the interaction parameter chi was approximately zero. However, for the blends PPO/DMWPS (chi < 0), with an increase of molecular weight of PS, it was shown that the experimental results fitted well with those obtained from the Couchman, Gordon-Taylor and Fox equations, respectively. Furthermore, the Gordon-Taylor equation was nearly identical to the Lu-Weiss equation when \chi\ was not very large. Further, the dependence of the change of heat capacity associated with the glass transition (Delta C-p) on the molecular weight of PS was investigated and an empirical equation was presented. (C) 1997 Elsevier Science Ltd.

Compositional dependence of the microphase separation transition in styrene-butadiene-styrene triblock copolymer/polystyrene blends

The change in the microphase separation transition (MST) temperature of a styrene-butadiene-styrene (SBS) triblock copolymer induced by the addition of polystyrene (PS) was investigated by small-angle X-ray scattering. It was found that the transition temperature was determined from the molecular weight (M(H)) Of the added PS in relation to that of the corresponding blocks (M(A)) in the copolymer. The MST temperature decreased with added PS if M(H)/M(A) < 1/4, while it increased with added PS when M(H)/M(A) > 1/4 Analysis of the theoretical expression based on the random phase approximation showed exactly the same tendency of change in the transition temperatures as that observed experimentally. The interaction parameter, chi(SB), obtained by nonlinear fitting of the scattering profiles of SBS/PS blends in the disordered state, was found to be a function of temperature and composition. Composition fluctuations were found to exist in SBS/PS blends, increasing with increasing addition of PS but diminishing with increasing molecular weight of the added PS.