Blends of polyamide 1010 with ungrafted and maleic anhydride grafted high impact polystyrene

The crystallization, dynamic mechanical properties, tensile properties and morphology features of polyamidel 1010(PA1010) blends with the high impact polystyrere (HIPS) and maleic anhydride (MA) grafted HIPS(HIPS-g-MA) were examined at a wide composition range. By comparison the PA1010/HIPS-g-MA and PA1010/HIPS binary blends, it was found that the size of the domains of HIPS-g-MA was much smaller than that of HIPS at the same compositions. It was found that the mechanical properties of PA1010/HIPS-g-MA blends were obviously higher than those of PA1010/HIPS blends. When the content of PA1010 is more than 50wt% in the blends, the crystallization temperatures, T-cs, of PA1010 increase with increasing the content of HIPS-g-MA. On the other hand, when the content of PA1010 in the blends is less than 35wt% the fraction crystallization is observed. The same result is not obtained for the blends of PA1010/HIPS. These behaviors could be attributed to the chemical interactions between the two components and good dispersion in PA1010/HIPS-g-MA blends.