Amorphous silicon nanoparticles in compound films grown on cold substrates for high-efficiency photoluminescence

Silicon nanoparticles have been fabricated in both oxide and nitride matrices by using plasma-enhanced chemical vapour deposition, for which a low substrate temperature down to 50 degreesC turns out to be most favourable. High-rate deposition onto such a cold substrate results in the formation of nanoscaled silicon particles, which have revealed an amorphous nature under transmission electron microscope (TEM) examination. The particle size can be readily controlled below 3.0 nm, and the number density amounts to over 10(12) cm(-2), as calculated from the TEM micrographs. Strong photoluminescence in the whole visible light range has been observed in the as-deposited Si-in-SiOx and Si-in-SiNx thin films. Without altering the size or structure of the particles, a post-annealing at 300 degreesC for 2 min raised the photoluminescence efficiency to a level comparable to the achievements with nanocrystalline Si-in-SiO2 samples prepared at high temperature. This low-temperature procedure for fabricating light-emitting silicon structures opens up the possibility of manufacturing integrated silicon-based optoelectronics.

Relaxation of carriers in terbium-doped ZnO nanoparticles

Terbium ions were successfully incorporated in nano-sized zinc oxide particles with a doping concentration up to 3% by using a wet chemical route. Four narrow emission peaks of Tb3+ ions and a broad emission band of the surface states on ZnO nano-hosts were observed for all Tb-doped nanoparticles. Relaxation of carriers from excited states of ZnO hosts to rare earth (RE) dopants is disclosed by the fact that the emission intensity of Tb3+ centers increases with increased Tb content at the expense of the emission from surface defect states in ZnO matrix. (C) 2001 Elsevier Science B.V. All rights reserved.

Investigations on oxide-free InGaAlAs waveguides grown by narrow stripe selective MOVPE

Oxide-free InGaAlAs waveguides have been grown on the InP substrates patterned with pairs of SiO2 mask stripes using narrow stripe selective MOVPE. The mask stripe width is varied from 0 to 40 pm, while the window region width between a pair of mask stripes is fixed at 1.5, 2.5 and 3.5 mu m, respectively. Smooth surface s and flat interfaces are obtained in the selectively grown InQaAlAs waveguides. There exhibit strong dependences of the thickness enhancement ratio and the photoluminescence (PL) spectrum on the mask stripe width and the window region width for the InGaAlAs wavegwdes. A large PL peak wavelength shift of 79 nm and a PL full width of at half maximum (FWHM) of less than 64 meV are obtained simultaneously. Some possible interpretations for our investigations are presented by considering both the migration effect from a masked region (MMR) and the lateral vapor diffusion effect (LVD).

Magnet-assisted assembly of 1-dimensional hollow PtCo nanomaterials on an electrode surface

In this work, rapid and controllable confinement of one-dimensional (1D) hollow PtCo nanomaterials on an indium tin oxide (ITO) electrode surface was simply realized via magnetic attraction. The successful assembly was verified by scanning electron microscopy (SEM) and cyclic voltammetry, which showed that a longer exposure time of the electrode to the suspension of these 1D hollow nanomaterials (magnetic suspension) led to a larger amount of attached 1D hollow PtCo nanomaterials.

Facile electrochemical approach to fabricate hierarchical flowerlike gold micro structures: Electrodeposited superhydrophobic surface

A templateless, surfactantless, electrochemical approach is proposed to directly fabricate hierarchical flowerlike gold microstructures (HFGMs) on an indium tin oxide (ITO) substrate. The as-prepared HFGMs have been characterized by scanning electron microscopy (SEM), X-ray photoelectron spectroscopy (XPS), X-ray diffraction (XRD) and cyclic voltammetry.

Facile electrochemical route to directly fabricate hierarchical spherical cupreous micro structures: Toward superhydrophobic surface

A templateless, surfactantless, electrochemical route is proposed to directly fabricate hierarchical spherical cupreous microstructures (HSCMs) on an indium tin oxide (ITO) substrate. The as-prepared HSCMs have been characterized by scanning electron microscopy (SEM), energy-dispersive X-ray (EDX) analysis, X-ray photoelectron spectroscopy (XPS) and X-ray diffraction (XRD).

Magnetic control of bioelectrocatalytic processes based on assembled iron oxide particles

A facile magnetic control system was designed in bioelectrocatalytic process based on functionalized iron oxide particles. The iron oxide particles were modified with glucose oxidase, and ferrocene dicarboxylic acid was used as electron transfer mediator. Functionalized iron oxide particles can assemble along the direction of applied magnetic field, and the directional dependence of the assembled iron oxide particles can be utilized for device purposes. We report here how such functionalized magnetic particles are used to modulate the bioelectrocatalytic signal by changing the orientation of the applied magnetic field. (C) 2008 Elsevier B.V. All rights reserved.

Preparation of nanoparticles of bipyridineruthenium and silicotungstate and application as electrochemiluminescence sensor

The novel nanoparticles, [Ru(bPY)(3)](2)SiW12O40 center dot 2H(2)O(2) were firstly synthesized and characterized by elemental analysis, IR, and TEM. The nanoparticles were used to fabricate a chemically modified carbon paste electrode (CPE) by dispersing nanoparticles and graphite powder in silicone grease. Thus-prepared CPE shows bifunctional electrocatalytic activities towards the reduction of nitrite and the oxidation of oxalate, and exhibits sensitive electrochemiluminescence (ECL).

Hydrothermal synthesis and photoluminescent properties of stacked indium sulfide superstructures

Unusual hierarchical stacked superstructures of cubic beta-In2S3 were fabricated via a facile hydrothermal process in the presence of a surfactant cetyltrimethylammonium bromide CTAB; the 3D superstructures were developed by helical propagation of surface steps from microflakes of 10-20 nm thickness.

[Ru(bpy)(3)](2+)-doped silica nanoparticles within layer-by-layer biomolecular coatings and their application as a biocompatible electrochemiluminescent tag material

[Ru(bpy)(3)](2+)-doped silica (RuSi) nanoparticles were synthesized by using a water/oil microemulsion method. Stable electrochemiluminescence (ECL) was obtained when the RuSi nanoparticles were immobilized on a glassy carbon electrode by using tripropylamine (TPA) as a coreactant. Furthermore, the ECL of the RuSi nanoparticles with layer-by-layer biomolecular coatings was investigated. Squential self-assembly of the polyelectrolytes and biomolecules on the RuSi nanoparticles gave nanocomposite suspensions, the ECL of which decreased on increasing the number of bilayers.

The role of molybdenum oxide as anode interfacial modification in the improvement of efficiency and stability in organic light-emitting diodes

It has been experimentally found that molybdenum oxide (MoO3) as the interfacial modification layer on indium-tin-oxide (ITO) in organic light-emitting diodes (OLEDs) significantly improves the efficiency and lifetime. In this paper, the role of MoO3 and MoO3 doped N,N '-di(naphthalene-1-yl)-N,N '-diphenyl-benzidine (NPB) as the interface modification layer on ITO in improvement of the efficiency and stability of OLEDs is investigated in detail by atomic force microscopy (AFM), polarized optical microscopy, transmission spectra, ultraviolet photoemission spectroscopy (UPS) and X-ray photoemission spectroscopy (XPS).

Pd nanoparticles supported on WO3/C hybrid material as catalyst for oxygen reduction reaction

Pd nanoparticles supported on WO3/C hybrid material have been developed as the catalyst for the oxygen reduction reaction (ORR) in direct methanol fuel cells. The resultant Pd-WO3/C catalyst has an ORR activity comparable to the commercial Pt/C catalyst and a higher activity than the Pd/C catalyst prepared with the same method. Based on the physical and electrochemical characterizations, the improvement in the catalytic performance may be attributed to the small particle sizes and uniform dispersion of Pd on the WO3/C, the strong interaction between Pd and WO3 and the formation of hydrogen tungsten bronze which effectively promote the direct 4-electron pathway of the ORR at Pd.

Facile Synthesis and Optical Property of Porous Tin Oxide and Europium-Doped Tin Oxide Nanorods through Thermal Decomposition of the Organotin

Porous SnO2 and SnO2-Eu3+ nanorods have been facilely prepared using triphenyltin hydroxide microrods as precursors. The porous structure of SnO2 nanorods, which was aggregated by small SnO2 nanocrystallites, has been confirmed by TEM images and nitrogen adsorption-desorption isotherms. The optical property of the porous SnO2-Eu3+ nanorods was investigated by UV-vis absorption and photoluminescence spectra.

A strategy to prepare ultrafine dispersed Fe2O3 nanoparticles

In this article, a novel strategy was applied to prepare dispersed ultrafine alpha-Fe2O3 nanoparticles. The initial Fe(OH)(3) nanoparticles were synthesized by the reaction of NaOH and FeCl3 in alcohol. With the new-formed nanoparticles as nuclei, NaCl crystallized and encapsulated the particles into solid cages. As a result, the nanoparticles were prevented from aggregating and growing. The composite of Fe(OH)(3) and NaCl was calcined and then washed by water to obtain the pure alpha-Fe2O3 nanoparticles.

The synthesis of perylene-coated graphene sheets decorated with Au nanoparticles and its electrocatalysis toward oxygen reduction

Chemically converted graphene (CCG)/3,4,9,10-perylene tetracarboxylic acid (PTCA)/Au-ionic liquid (Au-IL) composites (CCG/PTCA/Au-IL) have been prepared by a chemical route that involves functionalization of CCG with PTCA followed by deposition of Au-IL. Transmission electron microscopy revealed well-distributed Au with a high surface coverage. The identity of the hybrid material was confirmed through X-ray diffraction and X-ray photoelectron spectroscopy. The CCG/PTCA/Au-IL composites exhibited good electrocatalytic behavior toward oxygen reduction. The results indicate that modification of CCG with Au-IL could play an important role in increasing the electrocatalytic activity of CCG.