Frequency upconversion properties of Er3+/Yb3+-codoped lead-germanium-bismuth oxide glasses

The frequency upconversion properties of Er3+/Yb3+-codoped heavy metal oxide lead-germanium-bismuth oxide glasses under 975 mn excitation are investigated. Intense green and red emission bands centered at 536, 556 and 672 run, corresponding to the H-2(1/2) --> I-4(15/2), S-4(3/2) --> I-4(15/2) and F-4(9/2) -->I-4(15/2) transitions of Er3+, respectively, were simultaneously observed at room temperature. The influences of PbO on upconversion intensity for the green (536 and 556 nm) and red (672 nm) emissions were compared and discussed. The optimized rare earth doping ratio of Er3+ and Yb3+, is 1:5 for these glasses, which results in the stronger upconversion fluorescence intensities. The dependence of intensities of upconversion emission on excitation power and possible upconversion mechanisms were evaluated and analyzed. The structure of glass has been investigated by means of infrared (IR) spectral analysis. The results indicate that the Er3+/Yb3+-codoped heavy metal oxide lead-germanium-bismuth oxide glasses may be a potential materials for developing upconversion fiber optic devices. (C) 2006 Published by Elsevier Ltd.

Primary and secondary threshold intensities of ultraviolet-laser-induced domain nucleation in nearly stoichiometric LiTaO3

The primary and secondary threshold intensities of ultraviolet-laser-induced preferential domain nucleation in nearly stoichiometric LiTaO3 is observed. The primary threshold is the minimum intensity to achieve the instantaneous preferential domain nucleation within the focus by the combined action of irradiation and electric fields. The secondary threshold is the minimum intensity to achieve the memory effect without any irradiation within the original focus. The space charge field created by the photoionization carriers is thought to be responsible for the instantaneous effect. The explanation based on the formation and transformation of extrinsic defect is presented for the memory effect. (c) 2008 American Institute of Physics.

Effects of Yb3+ in Er3+/Yb3+ codoped fluorophosphate glasses

For the Er3+/Yb3+ codoped fluorophosphate glasses, Judd-Ofelt theory is used to analyse the influence of YbF3 as not a sensitizer but an average component on the spectroscopic properties around 1530 nm emission. The double roles of Yb3+, as a sensitizer and as an average component, are discussed. It is found that Yb3+ as an average component contributes to the increase of fluorescence lifetime, and Yb3+ as a sensitizer has the best sensitization when its concentration is 2.4 mol%.

Near infrared broadband emission from bismuth-dysprosium codoped chalcohalide glasses

We investigate the broadband infrared emission of bismuth doped and bismuth/dysprosium codoped chalcohalide glasses. It is found that the bismuth/dysprosium codoping can drastically enhance the fluorescence as compared with either bismuth or dysprosium doped glasses. Meanwhile, the full width at half maximum of bismuth/dysprosium codoped glasses is over 170 nm, which is the largest value among all the reported rare-earth doped chalcohalide glasses. An ideal way for energy consumption between bismuth and dysprosium ions is supposed. Such improved gain spectra of both bismuth and dysprosium ions may have potential applications in developing broadband fibre amplifiers.

Spectroscopic properties and Judd-Ofelt theory analysis of Dy3+ doped oxyfluoride silicate glass

Dy3+ doped oxyfluoride silicate glass was prepared and its optical absorption, 1.3 mu m emission, and upconversion luminescence properties were studied. Furthermore, the Judd-Ofelt [Phys. Rev. 127, 750 (1962); J. Chem. Phys. 37, 511 (1962)] intensity parameters, oscillator strengths, spontaneous transition probability, fluorescence branching ratio and radiative lifetime were calculated by Judd-Ofelt theory, while stimulated emission cross section of H-6(9/2)+F-6(11/2)-> H-6(15/2) transition was calculated by McCumber theory [Phys. Rev. A. 134, 299 (1964)]. According to the obtained Judd-Ofelt intensity parameters Omega(2)=2.69x10(-20) cm(2), Omega(4)=1.64x10(-20) cm(2), and Omega(6)=1.64x10(-20) cm(2), the radiative lifetime was calculated to be 810 mu s for 1.3 mu m emission, whose full width at half maximum and sigma(e) were 115 nm and 2.21x10(-20)cm(2), respectively. In addition, near infrared to visible upconversion luminescence was observed and evaluated. The results suggest that Dy3+ doped oxyfluoride silicate glass can be used as potential host material for developing broadband optical amplifiers and laser applications.

Broadband near-infrared emission from transparent Ni2+-doped silicate glass ceramics

Transparent Ni2+-doped MgO-Al2O3-TiO2-SiO2 glass ceramics were prepared, and the optical properties of Ni2+-doped glass ceramics were investigated. Broadband emission centered at 1320 nm was observed by 980 nm excitation. The longer wavelength luminescence compared with Ni2+-doped Li2O-Ga2O3-SiO2 glass ceramics is ascribed to the low crystal field hold by Ni2+ in MgO-Al2O3-TiO2-SiO2 glass ceramics. The change in optical signals at the telecommunication bands with or without 980 nm excitation was also measured when the seed beam passes through the bulk gain host.(C) 2007 American Institute of Physics.

Upconversion emissions in Yb3+-Tm3+-doped tellurite glasses excited at 976 nm

Intense Tm3+ blue upconversion emission has been observed in Tm3+-Yb3+ codoped oxyfluoride tellurite glass under excitation with a diode laser at 976 nm. Three emission bands centered at 475, 650 and 796 nm corresponding to the transitions (1)G(4) -> H-3(6), (1)G(4) -> H-3(4) and F-3(4) -> H-3(6), respectively, simultaneously occur. The dependence of upconversion intensities on Tm3+ ions concentration and excitation power are investigated. For fixed Yb2O3 concentrations of 5.0 mol%, the maximum upconversion intensity was obtained with Tm2O3 concentration of about 0.1 mol%. The blue upconversion luminescence lifetimes of the Tm3+ transitions (1)G(4) -> H-3(6) are measured. The results are evaluated by the possible upconversion mechanisms.

980 nm 抽运下Yb-Tm-Ho 三掺氟磷酸盐玻璃的2 μm 荧光性质

The thermal stability, 2 μm fluorescence properties and energy transfer mechanism in Ho³⁺ doped fluorophosphate glass sensitized by Yb³⁺ and Tm³⁺ were investigated. The characteristic temperatures, absorption spectrum and fluorescence spectrum of the glass sample were measured. ΔT calculated from the characteristic temperatures shows that the thermal stability of fluorophosphate glass is better than fluoride glass. According to the absorption spectrum, several spectroscopic parameters of the glass sample, such as Judd-Ofelt parameters and spontaneous transition probability were calculated and compared with other glass hosts. The largest spontaneous transition probability for Ho³⁺:⁵ I7&rarr⁵I8 transition in fluorophosphate glass which is 78.48 s^-1 indicates that fluorophosphate glass is an appropriate base glass to achieve 2 m fluorescence. From the fluorescence spectrum of the glass sample, the extremely strong 2.0 μm fluorescence intensity is observed, which is higher than the intensity of 1.8 μm fluorescence, showing that Ho³⁺ ions sensitized by Yb³⁺ and Tm³⁺ is efficient. Meanwhile, the absorption sections and emission sections of Yb³⁺, Tm³⁺ and Ho³⁺ were calculated and the pumping scheme and energy transfer mechanism among Yb³⁺, Tm³⁺ and Ho³⁺ are discussed. The study indicates that Yb-Tm-Ho tri-doped fluorophosphate glass is a significant sensitization glass system under 980 nm excitation for 2 μm applications.

Host dependent thermal stability and frequency upconversion of Er3+-doped heavy metal oxyfluoride germanate glasses

The upconversion properties of Er3+-doped heavy metal oxyfluoride germanate glasses under 975 nm excitation have been investigated. The intense green (551 and 529 nm) and relatively weak red (657 nm) emissions corresponding to the transitions S-4(3/2) -> I-4(15/2), H-2(11/2) -> I-4(15/2) and F-4(9/2) -> I-4(15/2), respectively, were simultaneously observed at room temperature. The content of PbF2 has an important influence on the upconversion luminescence emission. With increasing content of PbF2, the intensities of green (529 nm) and red (657 nm) emissions increase slightly, while the green emission (551 nm) increases markedly. These results suggest that PbF2 has an influence on the green (551 nm) emission more than on the green (529 nm) and red (657 nm) emissions.