大尺寸高质量γ-LiAlO2晶体的制备研究

采用提拉法快速（6mm／h）生长了透明、φ45mm×50mm完整的铝酸锂晶体，但晶体中下部出现了一个树状、乳白色的核芯．分别从透明和乳白色核芯部位取样，研磨作粉末X射线衍射测试，发现两个样品所有的衍射峰均可以用γ-LiAlO2指标化．双晶摇摆曲线显示晶体透明和乳白色部位的半高宽分别为116．9arcsec和132．0axcsec，结晶质量较差．通过三步气相传输平衡法（简称VTE）处理后，透明部位半高宽值（FWHM）降至44．2arcsec，乳白色部位FWHM值降至53．3arcsec．结合快速生长和VTE

提拉法生长大尺寸γ-LiAlO2单晶的研究(英文)

由于与GaN晶格失配小(约1．4％)，γ-LiAlO2单晶有望成为一种很有希望的GaN外延衬底材料。本文使用提拉法生长出了尺寸达Ф5×50mm^3的γ-LiAlO2单晶。对该晶体毛坯的各个有代表性的位置作了X射线粉末衍射(XRPD)分析，结果表明仅仅在晶体毛坯的底部生成了一种缺锂相(LiAl5O8)。γ-LiAlO2晶体化学稳定性差，在室温时轻微水解。当在空气中于1100℃退火70h，γ-LiAlO2晶体挥发出锂组分，在表面产生缺锂相(LiAl5O8)。值得注意的是，在γ-LiAlO2晶体的红外光谱区不存

Judd-Ofelt analysis of spectra and experimental evaluation of laser performance of Tm3+ doped Lu2SiO5 crystal

This paper reports that the TM3+:Lu2SiO5 (Tm:LSO) crystal is grown by Czochralski technique. The room-temperature absorption spectra of Tm:LSO crystal are measured on a b-cut sample with 4 at.% thulium. According to the obtained Judd-Ofelt intensity parameters Omega(2)=9.3155 x 10(-20) cm(2), Omega(4)=8.4103 x 10(-20) cm(2), Omega(6)=1.5908 x 10(-20) cm(2), the fluorescence lifetime is calculated to be 2.03 ms for F-3(4) -> H-3(6) transition, and the integrated emission cross section is 5.81 x 10(-18) cm(2). Room-temperature laser action near 2 mu m under diode pumping is experimentally evaluated in Tm:LSO. An optical-optical conversion efficiency of 9.1% and a slope efficiency of 16.2% are obtained with continuous-wave maximum output power of 0.67 W. The emission wavelengths of Tm:LSO laser are centred around 2.06 mu m with spectral bandwidth of similar to 13.6 nm.

倾斜角沉积技术制备ZnS双折射雕塑薄膜

使用倾斜角沉积（GLAD）的电子束蒸发技术，制备了倾斜角度在60°～85°之间的ZnS双折射雕塑薄膜（STF）。使用X射线衍射（XRD）和扫描电镜（SEM）检测了ZnS薄膜的结晶状态和断面形貌，使用Lamda-900分光光度计测量了薄膜在不同的偏振光入射时的透过率。研究发现，室温下倾斜沉积ZnS薄膜断面为倾斜柱状结构，且薄膜的结晶程度不高。在相同的监控厚度时，随倾斜角度增大，沉积到基片上的薄膜厚度逐渐变小，但仍然大于余弦曲线显示的理论厚度。根据偏振光垂直入射时薄膜的透过光谱计算了不同角度沉积的薄膜的折射率

MULTIPLE GENOTYPES OF MITOCHONDRIAL-DNA WITHIN A HORSE POPULATION FROM A SMALL REGION IN YUNNAN PROVINCE OF CHINA

mtDNA genotypes of six domestic horses (three adult short horses whose heights are under 1 m and three common domestic horses) from a small region of 15 km(2) in Malipo county of Yunnan province of China were investigated by the technique of restriction fragment length polymorphism (RFLP) with restriction endonucleases which recognize 6-bp sequences. An average of fragments for an individual was obtained. Unlike other domestic animals, this population of horses exhibits high mtDNA genetic diversity. Each of the six horses has a specific mtDNA genotype showing a pattern of multiple maternal origins, as suggested by fossil and literature records. We think the population of horses is an amazing seed-resource pool of horses and hence deserves to be paid more attention from the view of conservation genetics. However it is also remarkable that we did not find any typical mtDNA genetic markers which would discriminate between short horses and common domestic horses.

Silicon nanowires grown on a pre-annealed Si substrate

Polycrystalline Si nanowires (poly SiNWS) were successfully synthesized by plasma-enhanced chemical vapor deposition (PECVD) at 440degreesC using silane as the Si source and Au as the catalyst. The diameters of Si nanowires range from 15 to 100nm. The growth process indicates that to fabricate SiNWS by PECVD, pre-annealing at high temperature is necessary. A few interesting nanowires with Au nanoclusters uniformly distributed in the body of the wire were also produced by this technique. (C) 2002 Elsevier Science B.V. All rights reserved.

Influence of mode symmetry on quality factors of degenerate states in microlasers with an equilateral triangle resonator

Modes in equilateral triangle resonator (ETR) are analyzed and classified according to the irreducible representations of the point group C-3v., Both the analytical method based on the far field emission and the numerical method by FDTD technique are used to calculate the quality factors (Q-factors) of the doubly degenerate states in ETR. Results obtained from the two methods are in reasonable agreement. Considering the different symmetry properties of the doubly degenerate eigenstates, we also discuss the ETR joined with an output waveguide at one of the vertices by FDTD technique and the Pade approximation. The variation of Q-factors versus width of output waveguide is analyzed. The numerical results show that doubly degenerate eigenstates of TM0.36 and TM0.38 whose wavelengths are around 1.5 mu m in the resonator with side-length of 5 mu m have the Q-factors larger than 1000 when the width of the output waveguide is smaller than 0.4 mu m. When the width of the output waveguide is set to 0.3 mu m, the symmetrical states that are more efficiently coupled to output waveguide have Q-factors about 8000, which are over 3 times larger than those of asymmetric state.

Structural characterization, stability and electrical properties of strontium niobate ceramic

The double perovskite oxide Sr2CrNbO6 has a cubic structure according to powder X-ray diffraction. After reducing in CO, Sr2CrNbO6 still exhibited a cubic structure refined by Rietveld technique. The TG analysis indicated that Sr2CrNbO6 loses 0.127 oxygen per formula unit from 400 to 700 degrees C in H-2. The morphology and compositions of this ceramic did not significantly change on reduction

Electrochemical Detection of Hydrazine Based on Electrospun Palladium Nanoparticle/Carbon Nanofibers

In this work, we developed an electrochemical method for the detection of hydrazine based oil palladium nanoparticle/carbon nanofibers (Pd/CNFs). Pd/CNFs were prepared by electrospinning technique and subsequent thermal treatments. The electrocatalytic behaviors of Pd/CNFs modified glassy carbon electrode (Pd/CNF-GCE) for hydrazine oxidation were evaluated by cyclic voltammetry (CV), an obvious and well-defined oxidation peak appeared at -0.32 V (vs. Ag/AgCl). The mechanism of the oxidation of hydrazine at Pd/CNF-GCE was also studied, which demonstrated an irreversible diffusion-controlled electrode process and a four-electron transfer involved in the overall reaction. Furthermore, the wide linear range, low detection limit, good reproducibility and excellent storage stability were obtained utilizing differential pulse voltammetry (DPV).

Direct electron transfer and electrocatalysis of glucose oxidase immobilized on glassy carbon electrode modified with Nafion and mesoporous carbon FDU-15

In this paper, it was found that glucose oxidase (GOD) has been stably immobilized on glassy carbon electrode modified with mesoporous carbon FDU-15 (MC-FDU-15) and Nafion by simple technique. The sorption behavior of GOD immobilized on MC-FDU-15 matrix was characterized by transmission electron microscopy (TEM), ultraviolet-visible (UV-vis), FTIR, respectively, which demonstrated that MC-FDU-15 could facilitate the electron exchange between the active center of GOD and electrode. The direct electrochemistry and electrocatalysis behavior of GOD on the modified electrode were characterized by cyclic voltammogram (CV) which indicated that GOD immobilized on Nafion and MC-FDU-15 matrices display direct, reversible and surface-controlled redox reaction with an enhanced electron transfer rate constant of 4.095 s(-1) in 0.1 M phosphate buffer solution (PBS) (pH 7.12).

A biodegradable triblock copolymer poly(ethylene glycol)-b-poly(L-lactide)-b-poly(L-lysine): Synthesis, self-assembly and RGD peptide modification

A novel biodegradable triblock copolymer poly(ethylene glycol)-b-poly(L-lactide)-b-poly(L-lysine) (PEG-PLA-PLL) was synthesized by acidolysis of poly(ethylene glycol)-b-poly(L-lactide)-b-poly(F-benzyloxycarbonyl-L-lysine) (PEG-PLA-PZLL) obtained by the ring-opening polymerization (ROP) of epsilon-benzyloxycarbonyl-L-lysine N-carboxyanhydride (ZLys NCA) with amino-terminated PEG-PLA-NH2 as a macro-initiator, and the pendant amino groups of the lysine residues were modified with a peptide known to modulate cellular functions, Gly-Arg-Gly-Asp-Ser-Tyr (GRGDSY, abbreviated as RGD) in the presence of 1,1'-carbonyldiimidazole (CDI). The structures of PEG-PLA-PLL/RGD and its precursors were confirmed by H-1 NMR, FT-IR, amino acid analysis and XPS analysis. The cell adhesion and cell spread on the PEG-PLA-PLL/RGD film were enhanced compared to those on pure PLA film. Therefore, the novel RGD-grafted triblock copolymer is promising for cell or tissue engineering applications. Both copolymers PEG-PLA-PZLL and PEG-PLA-PLL showed an amphiphilic nature and could self-assemble into micelles of homogeneous spherical morphology. The micelles were determined by fluorescence technique, dynamic light scattering (DLS), and field emission scanning electron microscopy (ESEM) and could be expected to find application in drug and gene delivery systems.

Lanthanum zirconate nanofibers with high sintering-resistance

The PVP/lanthanum nitrate/zirconium oxychloride (PVP-precursor) nanofiber was prepared by electrospinning technique. Lanthanum zirconate (La2Zr2O7, LZ) in the nanofiber is formed after calcination at 800 degrees C and the nanofiber with pyrochlore structure and a diameter of 100-500 nm can be obtained by calcination of the above precursor fiber at 1000 degrees C for 12 h. The surface of the fiber is rough but the continuous microstructure is still maintained after calcination. LZ fibers stack randomly, resulting in a structure with a low contact area between the fibers. This special structure makes the fiber to have a high resistance to sintering at elevated temperatures. The BET (Brunauer-Emmett-Teller) specific surface areas of the LZ fiber and powder calcined at different temperatures are shown in this paper, and the fiber was characterized by TG-DTA (thermal gravimetry-differential thermal analysis), XRD (X-ray diffraction), N-2 absorption-desorption porosimetry and SEM (scanning electron microscopy).

Effective energy transfer and luminescence of LB films based on europium-substituted heteropolytungstate

The europium-substituted heteropolytungstate K13Eu(SiW11O39)(2) was successfully assembled into two lipids by LB technique for the first time. X-ray diffraction has shown a well defined lamellar for the LB films. The LB films have been characterized by fluorescence spectra and the characteristic luminescence behaviors were discussed. The ligand-metal charge transfer band could be observed in the spectra of the LB films, which could not be found in that of heteropolytungstate solid. The results of fluorescence spectra indicate the energy could be effectively transferred from ligands to the Eu3+ ions in the LB films and the luminescence efficiency was increased greatly. The influences of various lipids on the luminescence of polyoxometalates were investigated. The various interactions between monolayer and polyanions have different effect on the luminescence properties of europium-substituted heteropolytungstate.

The LB films of dansyl chloride labeled octadecylamine and its fluorescence lifetime

Octadecylamine was derivatized with dansyl chloride (5-dimethylaminonaphthalene-1-sulfonyl chloride) In order to simplify and understand the LB films of fluorescent probe labeling proteins. its monolayer and multilayers in the absence and presence of stearic acid were deposited by LB technique. Fluorescence spectra and lifetimes of the fluorescent products were studied to elucidate the microenvironment of molecules in the LB films.

Electrostatic layer-by-layer assembly of polycation and DNA multilayer films by real-time surface plasmon resonance technique

The assembly of alternating DNA and positively charged poly(dimethyldiallylammonium chloride) (PDDA) multilayer films by electrostatic layer-by-layer adsorption has been studied. Real time surface plasmon resonance (BIAcore) technique was used to characterize and monitor the formation of multilayer films in solution in real time continuously. The results indicate that the uniform multilayer can be obtained on the poly(ethylenimine) (PEI) coated substrate surface. The kinetics of the adsorption of DNA on PDDA surface was also studied by real-time BIAcore technique, and the observed rate constant was calculated using a Langmuir model (k(obs) = (1.28 +/- 0.08) x 10(-2) s(-1)).