Enhanced broadband near-infrared luminescence from transparent Yb 3+/Ni2+ codoped silicate glass ceramics

The near-infrared emission intensity of Ni2+ in Yb3+/Ni2+ codoped transparent MgO-Al2O3-Ga2O3-SiO2-TiO2 glass ceramics could be enhanced up to 4.4 times via energy transfer from Yb3+ to Ni2+ in nanocrystals. The best Yb2O3 concentration was about 1.00 mol%. For the Yb3+/Ni2+ codoped glass ceramic with 1.00 mol% Yb2O3, a broadband near-infrared emission centered at 1265 nm with full width at half maximum of about 300 nm and lifetime of about 220 mu s was observed. The energy transfer mechanism was also discussed. (C) 2008 Optical Society of America.

Enhanced broadband near-infrared luminescence in transparent silicate glass ceramics containing Yb3+ ions and Ni2+-doped Li Ga5 O8 nanocrystals

Spectral properties of Yb3+/Ni2+ codoped transparent silicate glass ceramics containing LiGa5O8 nanocrystals were investigated. The near-infrared emission intensity of Ni2+ was largely increased with Yb3+ codoping due to Yb3+-> Ni2+ energy transfer. The qualitative calculation of the energy transfer constant Cs-a and rate Ps-a showed that the Yb3+-> Ni2+ energy transfer was much greater than in the opposite direction. Yb3+/Ni2+ codoped glass ceramics with 0.75 mol % Yb2O3 exhibited a near-infrared emission with full width at half maximum of 290 nm and fluorescent lifetime of 920 mu s. The glass ceramics are promising for broadband optical amplification.

Yb掺杂的YAlO<3/sub>单晶体的温梯法生长和光谱性能

The dark-brown colored 5 at% Yb-doped YAlO3 (Yb:YAP) single crystal was grown successfully by temperature gradient technique (TGT) for the first time. The TGT-grown Yb:YAP crystal with the perovskite structure and excellent crystallization perfection were confirmed by the X-ray diffractions techniques. The dark-brown color of TGT-Yb:YAP crystal turned into the colorless after annealing in the air at 1200 degrees C for 10h. The absorption spectra, LD-excited infrared emission and X-ray excited luminescence spectra of the air-annealed Yb:YAP single crystal were investigated at the room temperature. The results indicate that the TGT-Yb:YAP single crystals can be used for the laser and scintillation applications. (c) 2005 Elsevier B.V. All rights reserved.

Temperature dependence of the 1.03 mu m stimulated emission cross section of Cr : Yb : YAG crystal

The fluorescence emission spectra of Cr:Yb:YAG crystal are measured and the effective stimulated emission cross section of the crystal are obtained from -80 degrees C to +80 degrees C. A linear temperature dependence between -80 degrees C and +80 degrees C is reported for the 1.03 mu m peak stimulated emission cross section of Cr:Yb:YAG crystal. (c) 2004 Elsevier B.V. All rights reserved.

Temperature dependence of the 1.064-mu m stimulated emission cross-section of Cr : Nd : YAG crystal

The fluorescence emission spectra of Cr:Nd:YAG crystal are measured and the effective stimulated emission cross-section of the crystal is obtained from -80 to +80 degrees C. A linear temperature dependence between -80 and +80 degrees C is reported for the 1.064-mu m peak stimulated emission cross-section of Cr:Nd:YAG crystal. (C) 2005 Elsevier Ltd. All rights reserved.

Cr4+在Al2O3多晶体中的光谱性能研究

Transparent polycrystalline Cr:Al2O3 ceramics were synthesized by conventional pressureless synthesis processing. The absorption and emission spectra of Cr:Al2O3 ceramics specimens before and after annealing were measured at room temperature. It was discovered that the emission spectra of Cr4+ in Al2O3 octahedral coordination site is in infrared wavelength range of 1100-1600 nm. The emission peak of Cr4+ is centered at 1223 nm, which is similar to that of Cr4+ in tetrahedral site. Al2O3 has smaller lattice constant, resulting in the larger crystal field strength, so there is a blue shift in the peak of Cr4+:Al2O3 ceramics compared to those of other Cr4+-doped crystals. And the emission band is much narrower with full width at half maximum Delta lambda 37 nm.

Intense upconversion and infrared emissions in Er3+;Yb3+ codoped Lu2 Si O5 and (Lu0.5 Gd0.5)2 Si O5 crystals

High optical quality Lu2SiO5 (LSO) and (Lu0.5Gd0.5)(2)SiO5 (LGSO) laser crystals codoped with Er3+ and Yb3+ have been fabricated by the Czochralski method. Intense upconversion (UC) and infrared emission (1543 nm) are observed under excitation of 975 nm. The luminescence processes are explained and the emission efficiencies are quantitatively obtained by measuring the UC efficiency and calculating the emission cross section. The temperature-dependent optical properties of the crystals are also investigated. Our study indicates that Er3+-Yb3+ : LSO and Er3+-Yb3+: LGSO crystals are promising gain media for developing the solid-state 1.5 mu m optical amplifiers and tunable UC lasers. (c) 2008 American Institute of Physics.

Role of Bi3+ ions for Er3+ ions efficient 1.54 mu m light emission in Er/Bi codoped SiO2 thin film prepared by sol-gel method

Er/Bi codoped SiO2 thin films were prepared by sol-gel method and spin-on technology with subsequent annealing process. The bismuth silicate crystal phase appeared at low annealing temperature while vanished as annealing temperature exceeded 1000 degrees C, characterized by X-ray diffraction, and Rutherford backscattering measurements well explained the structure change of the films, which was due to the decrease of bismuth concentration. Fine structures of the Er3+-related 1.54 mu m light emission (line width less than 7 nm) at room temperature was observed by photoluminescence (PL) measurement. The PL intensity at 1.54 gm reached maximum at 800 degrees C and decreased dramatically at 1000 degrees C. The PL dependent annealing temperature was studied and suggested a clear link with bismuth silicate phase. Excitation spectrum measurements further reveal the role of Bi3+ ions for Er3+ ions near infrared light emission. Through sol-gel method and thermal treatment, Bi3+ ions can provide a perfect environment for Er3+ ion light emission by forming Er-Bi-Si-O complex. Furthermore, energy transfer from Bi3+ ions to Er3+ ions is evidenced and found to be a more efficient way for Er3+ ions near infrared emission. This makes the Bi3+ ions doped material a promising application for future erbium-doped waveguide amplifier and infrared LED

Upconversion emission of a Er3+-doped glass microsphere under 633 nm excitation

In this work, The TBS glass microspheres doped with Er3+ for morphology-dependent resonances of upconversion emission were designed. The glass sample components are 25TiO(2)-27BaCO(3)-8Ba(NO3)(2)-6ZnO(2)-9CaCO(3)-5H(3)BO(3)-10SiO(2)-7water glass-3Er(2)O(3) (wt%), and the emission spectra of TBS glass and a TBS glass microsphere (about 48 mum in diameter) were measured under 633 nm excitation and discussed. The strong morphology-dependent resonances of upconversion luminescences in the microsphere were observed. The observed resonances could be assigned by using the well-known Lorenz-Mie Formalism. (C) 2003 Elsevier Ltd. All rights reserved.

Photoluminescence enhancement of porous silicon by organic cyano compounds

A pronounced photoluminescence enhancement on chemically oxidized porous silicon was induced by a series of organic cyano compounds including 1,2-dicyanoethylene (CE), 1,3-dicyanobenzene (1,3-CB), 1,4-dicyanobenzene (1,4-CB), 1-cyanonaphthalene (1-CN), and 9-cyanoanthracene (9-CA). Photoluminescence enhancement effects were reversible for all compounds studies in this work. A dependence of photoluminescence enhancement on the steric effect and the electronic characteristics of these compounds and the structure of the porous silicon substrates were analyzed in terms of the photoluminescence enhancing factors. Surface chemical composition examined by Fourier transform infrared (FTIR) spectra demonstrated that the surface Si-H bonds were not changed and no new luminescent compounds were formed on porous silicon surface during adsorption of cyano compounds. A mechanism based on induced surface states acting as radiative recombination centers by cyano compounds adsorption was suggested.

LIQUID-PHASE EPITAXY GROWTH AND PROPERTIES OF GAINASSB/ALGAASSB/GASB HETEROSTRUCTURES

The GaInAsSb/AlGaAsSb/GaSb heterostructures were grown by the liquid phase epitaxy (LPE) technique. The materials were characterized by means of optical microscopy, electroprobe microanalysis (EPMA), double-crystal X-ray diffraction, capacitance-voltage (C-V) and Van der Pauw measurments, infrared absorption spectra, photoluminescence and laser Raman scattering. The results show that the materials have fine surface morphology, low lattice mismatch and good homogeneity. Room-temperature light-emitting diodes with an emission wavelength of 2.2-mu-m were obtained by using the GaInAsSb/AlGaAsSb DH structures.

Application of step-scan FTIR to the research of quantum cascade lasers

The principle of step-scan Fourier transform infrared （FTIR） spectroscopy is introduced. Double modulation step-scan FTIR technique is used to obtain the quantum cascade laser＇s stacked emission spectra in the time domain. Optical property and thermal accumulation of devices due to large drive current are analyzed.

Upconversion emission of a Er3+-doped glass microsphere under 633 nm excitation

In this work, The TBS glass microspheres doped with Er3+ for morphology-dependent resonances of upconversion emission were designed. The glass sample components are 25TiO(2)-27BaCO(3)-8Ba(NO3)(2)-6ZnO(2)-9CaCO(3)-5H(3)BO(3)-10SiO(2)-7water glass-3Er(2)O(3) (wt%), and the emission spectra of TBS glass and a TBS glass microsphere (about 48 mum in diameter) were measured under 633 nm excitation and discussed. The strong morphology-dependent resonances of upconversion luminescences in the microsphere were observed. The observed resonances could be assigned by using the well-known Lorenz-Mie Formalism. (C) 2003 Elsevier Ltd. All rights reserved.

Photoluminescence character of Xe ion irradiated sapphire

In the present work the photoluminescence (PL) character of sapphire implanted with 180 keV Xe and irradiated with 308 MeV Xe ions was studied. The virgin, implanted and irradiated samples were investigated by PL and Fourier transform infrared (FTIR) spectra measurements. The obtained PL spectra showed the maximum emission bands at 2.75, 3.0 and 3.26 eV for the implanted fluence of 1.0 x 10(15) ions/cm(2) and at 2.4 and 3.47 eV for the irradiated fluence of 1.0 x 10(13) ions/cm(2). The FTIR spectra showed a broaden absorption band between 460 and 630 cm(-1), indicating that strong damaged region formed in Al2O3.

DFT/TDDFT Studies on the Electronic Structures and Spectral Properties of Rhenium(I) Pyridinybenzoimidazole Complexes

The electronic structures and spectral properties of three Re(I) complexes [Re(CO)(3)XL] (X = Br, Cl; L = 1-(4-5 '-phenyl-1.3,4-oxadiazolylbenzyl)-2-pyridinylbenzoimidazole (1), 1-(4-carbazolylbutyl)-2-pyridinylbenzoimidazole (2), and 2-(1-ethyl benzimidazol-2-yl)pyridi ne (3)) were investigated theoretically. The ground and the lowest lying triplet excited states were full optimized at the B3LYP/LANL2DZ and CIS/LANL2DZ levels, respectively. TDDFT/PCM calculations have been employed to predict the absorption and emission spectra starting from the ground and excited state geometries, respectively.