YAG激光诱导放电通道伏安特性研究

研究了在空气、油膜和绝缘树脂薄膜这三种放电介质中的伏安特性,得出了在同一介质中,通道电极间电压不随其它初始条件改变而变化,只与放电介质对通道箍缩能力成正比,在本实验中薄膜的通道电压最高80.4V,空气中最低26.0V。通道中电流波形与放电介质有关,同样的高低压组合、相同放电脉宽下在空气和油膜中为矩形波,而在薄膜中为三角波,峰值电流变化不大。电流波形不随脉宽的改变而变化,当增大初始高压端或低压端输入时,电流随之增加,并且低压端输入对提高峰值电流更有效果。

YAG激光毛化技术进展

二十世纪八十年代，当比利时冶金研究中心(CRM)开发出CO_2激光毛化冷轧辊技术后，尝试用YAG激光进行轧辊毛化一直吸引着众多的研究者，这是因为YAG(1.06μm)激光波长比CO_2(10.6μm)激光波长短一个量级，材料对YAG激光有更高的吸收率，并用YAG激光可以聚焦到更小的光斑尺寸，同时使用电信号驱动的声光开关技术便于对毛化分布进行可设定控制。但是用传统声光调制的YAG激光虽然可以碇以很高的脉冲频率(>30kHz)，但单脉冲有量仅为10mJ左右，难以达到辊面毛化粗糙度的要求，因此人们认为YAG激光用于毛化的主要困难是脉冲能量太小。

Research on Q-Switched Nd : YAG laser engraving

IN this paper, the engraving process with Q-Switched Nd:YAG laser is investigated. High power density is the pre- requisition to vapor materials, and high repetition rate makes the engraving process highly efficient. An acousto- optic Q-Switch is applied in the cavity of CW 200 W Nd:YAG laser to achieve the high peak power density and the high pulse repetition rate. Different shape craters are formed in a patterned structure on the material surface when the laser beam irradiates on it by controlling power density, pulse repetition rate, pulse quantity and pulse interval. In addition, assisting oxygen gas is used for not only improving combustion to deepen the craters but also removing the plasma that generated on the top of craters. Off-focus length classified as negative and positive has a substantial effect on crater diameters. According to the message of rotating angle positions from material to be engraved and the information of graph pixels from computer, a special graph is imparted to the material by integrating the Q- Switched Nd:YAG laser with the computer graph manipulation and the numerically controlled worktable. The crater diameter depends on laser beam divergence and laser focal length. The crater diameter changes from 50 micrometers to 300 micrometers , and the maximum of crater depth reaches one millimeter.

Investigations of cohesive zone properties of the interface between metal film and ceramic substrate at nano- and micro-scales

Cohesive zone characterizations of the interface between metal film and ceramic substrate at micro- and nano-scales are performed in the present research. At the nano-scale, a special potential for special material interface (Ag/MgO) is adopted to investigate the interface separation mechanism by using MD simulation, and stress-separation relationship will be obtained. At the micro-scale, peeling experiment is performed for the Al film/Al2O3 substrate system with an adhesive layer at the interface. Adhesive is a mixture of epoxy and polyimide with mass ratio 1:1, by which a brittle cohesive property is obtained. The relationships between energy release rate, the film thickness and the adhesive layer thickness are measured during the steady-state peeling. The experimental result has a similar trend as modeling result for a weak adhesion interface case.

Interface cracking and particulate size effect in particle-reinforced metal-matrix composites

The mechanical behaviors of the ceramic particle-reinforced metal matrix composites are modeled based on the conventional theory of mechanism-based strain gradient plasticity presented by Huang et al. Two cases of interface features with and without the effects of interface cracking will be analyzed, respectively. Through comparing the result based on the interface cracking model with experimental result, the effectiveness of the present model can be evaluated. Simultaneously, the length parameters included in the strain gradient plasticity theory can be obtained.

Determination Of Interfacial Properties Between Metal Film And Ceramic Substrate With An Adhesive Layer

Peel test measurements and inverse analysis to determine the interfacial mechanical parameters for the metal film/ceramic system are performed, considering that there exist an epoxy interface layer between film and ceramic. In the present investigation, Al films with a series of thicknesses between 20 and 250 mu m and three peel angles of 90, 135 and 180 degrees are considered. A finite element model with the cohesive zone elements is used to simulate the peel test process. The finite element results are taken as the training data of a neural network in the inverse analysis. The interfacial cohesive energy and the separation strength can be determined based on the inverse analysis and peel experimental result. (C) 2008 Elsevier Ltd. All rights reserved.

Mechanisms of thermal shock failure for ultra-high temperature ceramic

The materials considered in our analysis were ZrB2 ceramic matrix composites. Effect of two different additives (graphite and AlN) on thermal shock stability for the materials was measured by water quench test. It showed that it may provide more stable thermal shock properties with additives of graphite. It was explained by different thermal properties and crack resistance of the two materials in detail. Surface oxidation was one of main reasons for strength degradation of ceramic with additives of graphite after quenched in water, and surface crack was one of main reasons for strength degradation of ceramic with additives of AlN after quenched in water. It was presented that it was a potential method for improving thermal shock stability of ZrB2 ceramic matrix composites by introducing proper quantities of graphite.

Experimental Study Of Multi-Hole Cooling For Integrally-Woven, Ceramic Matrix Composite Walls For Gas Turbine Applications

In this paper, multi-hole cooling is studied for an oxide/oxide ceramic specimen with normal injection holes and for a SiC/SiC ceramic specimen with oblique injection holes. A special purpose heat transfer tunnel was designed and built, which can provide a wide range of Reynolds numbers (10(5)similar to 10(7)) and a large temperature ratio of the primary flow to the coolant (up to 2.5). Cooling effectiveness determined by the measured surface temperature for the two types of ceramic specimens is investigated. It is found that the multi-hole cooling system for both specimens has a high cooling efficiency and it is higher for the SiC/SiC specimen than for the oxide/oxide specimen. Effects on the cooling effectiveness of parameters including blowing ratio, Reynolds number and temperature ratio, are studied. In addition, profiles of the mean velocity and temperature above the cooling surface are measured to provide further understanding of the cooling process. Duplication of the key parameters for multi-hole cooling, for a representative combustor flow condition (without radiation effects), is achieved with parameter scaling and the results show the high efficiency of multi-hole cooling for the oblique hole, SiC/SiC specimen. (C) 2008 Elsevier Ltd. All rights reserved.

YAG激光诱导放电表面离散强化形貌实验研究

实验研究了YAG激光诱导放电(LGD)表面离散强化形貌,包括强化点的表面形貌和横截面形貌.利用放电过程中的电弧压力,对强化点表面进行造型.大电流、倾斜放电容易将熔凝物吹起形成凹坑和突起,表面起伏更加明显,而小电流、垂直放电则能得到平坦的表面,有利于增大强化深度.随脉冲宽度的增加,强化点的径深比逐渐变小,在相同强化深度下,小电流、长脉冲宽度可以获得小径深比、厚深状的强化点,而大电流、短脉冲宽度可以获得大径深比、扁平状的强化点.在现有实验条件下,在电流150 A,脉冲宽度9.83 ms下得到最大强化深度为 0.479 mm,径深比为3.9

Femtosecond laser ablation of crystals SiO2 and YAG

Damage threshold of crystals SiO2 and YAG against 60-900 fs, 800 nm laser pulses are reported. The breakdown mechanisms were discussed based on the double-flux model and Keldysh theory. We found that impact ionization plays the important role in the femtosecond laser-induced damage in crystalline SiO2, while the roles of photoionization and impact ionization in YAG crystals depend on the laser pulse durations. (C) 2007 Elsevier B.V. All rights reserved.

Gamma-ray induced color centers in Yb : YAG crystals grown by Czochralski method

20 at.% Yb:YAG single crystals have been grown by the CZ method and gamma-ray irradiation induced color centers and valence change of Fe3+ and Yb3+ ions in Yb:YAG have been studied. One significant 255 nm absorption band was observed in as-grown crystals and was attributed to Fe3+ ions. Two additional absorption (AA) bands located at 255 nm and 345 nm, respectively, were produced after gamma irradiation. The changes in the AA spectra after gamma irradiation and air annealing are mainly related to the charge exchange of the Fe3+, Fe2+, oxygen vacancies and F-type color centers. Analysis shows that the broad AA band is associated with Fe2+ ions and F-type color centers. The transition Yb3+ Yb2+ takes place as an effect of recharging of one of the Yb3+ ions from a pair in the process of gamma irradiation. (C) 2006 Elsevier Ltd. All rights reserved.

Experimental investigation of optical beam deflection based on PLZT electro-optic ceramic

Based on the optical characteristics of PLZT electro-optic ceramic, two kinds of electro-optic deflectors, triangular electrode structure and optical phased array technology, are studied in detail by using transverse electro-optic effect. Theoretically, the electro-optic deflection characteristics and mechanisms of the deflectors are analyzed. Experimentally, the optical characteristics of ceramic wafer, such as the phase modulation, the hysteresis and the electro-induced loss characteristics, are measured firstly, and then the beam deflection experiments are designed to verify the theoretical results. Moreover, the effect of temperature on the performance of triangular electrode deflector is investigated. The characteristics of both deflectors are also compared and illuminated. (c) 2007 Optical Society of America.