应用中频感应提拉法生长出不同掺杂浓度的Yb：FAP激光晶体，运用电感耦合等离子体原子发射光谱仪（ICP-AES）测定了Yb^3＋离子存Yb：FAP晶体中的分凝系数约为0．03。随着晶体的生长，晶体中Yb^3＋离子的轴向浓度逐渐增大。研究Yb：FAP晶体在77K和300K温度下的吸收光谱发现，振动谱的变化主要是由电子-声子近共振耦合作用引起的。系统地研究了不同Yb^3＋离子掺杂浓度Yb：FAP晶体的吸收光谱和荧光光谱。通过吸收光谱的测量计算了晶体的吸收截面。Yb：FAP晶体在904nm和982nm处存在Yb

Growth and spectral properties of Yb : FAP single crystal

In this paper, single crystal of ytterbium (Yb) doped Ca-5(PO4)(3)F (FAP) has been grown along the c-axis by using the Czochralski method. The segregation coefficients of Yb3+ in the Yb:FAP crystal has been determined by ICP-AES method. The absorption spectrum, fluorescence spectrum and fluorescence lifetime of the Yb:FAP crystal has been also measured at room temperature. In the absorption spectra, there are two absorption bands at 904 and 982 nm, respectively, which are suitable for InGaAs diode laser pumping. The absorption cross-section (sigma(abs)) is 5.117 x 10(-20) cm(2) with an FWHM of 4 nm at 982 nm. The emission cross-section is (sigma(em)) 3.678 x 10(-20) cm(2) at 1042 nm. Favorable values of the absorption cross-section at about 982 nm are promising candidates for laser diode (LD) pumping. (c) 2005 Elsevier B.V. All rights reserved.

Single-photon emission from a single InAs quantum dot

Excitation power-dependent micro-photoluminescence spectra and photon-correlation measurement are used to study the optical properties and photon statistics of single InAs quantum dots. Exciton and biexciton emissions, whose photoluminescence intensities have linear and quadratic excitation power dependences, respectively, are identified. Under pulsed laser excitation, the zero time delay peak of second order correlation function corresponding to exciton emission is well suppressed, which is a clear evidence of single photon emission.

Optical properties and exciton localization in GaNas/GaAs

GaNAs/GaAs single quantum wells (SQWs) and dilute GaNAs bulk grown by molecular beam epitaxy(MBE) were studied by photoluminescence (PL), selectively-excited PL, and time-resolved PL. Exciton localization and delocalization were investigated in detail. Under short pulse laser excitation, the delocalization exciton emission was revealed in GaNAs/GaAs SQWs. It exhibits quite different optical properties from N-related localized states. In dilute GaNAs bulk, a transition of alloy band related recombination was observed by measuring the PL dependence on temperature and excitation intensity and time-resolved PL, as well. This alloy-related transition presents intrinsic optical properties. These results are very important for realizing the abnomal features of III-V-N semiconductors.

Photoluminescence degradation in GaN induced by light enhanced surface oxidation

The exponential degradation of the photoluminescence (PL) intensity at the near-band-gap was observed in heavily doped or low-quality GaN with pristine surface under continuous helium-cadmium laser excitation. In doped GaN samples, the degradation speed increased with doping concentration. The oxidation of the surface with laser irradiation was confirmed by x-ray photoemission spectroscopy measurements. The oxidation process introduced many oxygen impurities and made an increase of the surface energy band bending implied by the shift of Ga 3d binding energy. The reason for PL degradation may lie in that these defect states act as nonradiative centers and/or the increase of the surface barrier height reduces the probability of radiative recombination.

Material growth and device fabrication of highly strained InGaAs/InGaAsP long wavelength distributed feedback lasers

1.6-1.7 mu m highly strained InGaAs/InGaAsP distributed feedback lasers was grown and fabricated by low pressure mentalorganic chemical vapor deposition. High quality highly strained InGaAs/InP materials were obtained by using strain buffer layer. Four pairs of highly strained quantum wells were used in the devices and carrier blocking layer was used to improve the temperature characteristics of the devices. The uncoated 1.66 mu m and 1.74 mu m lasers with ridge wave guide 3 mu m wide have low threshold current (< 15mA) and high output power (> 14mW at 100mA). In the temperature range from 10 degrees C to 40 degrees C, the characteristic temperature T-0 of the 1.74 mu m laser is 57K, which is comparable to that of the 1.55 mu m-wavelength InGaAsP/InP-DFB laser.

Photoluminesfcence of Er-doped SiO2 films containing Si nanocrystals and Er

Correlations between Si nanocrystal (nc-Si) related photoluminescence (PL), Er3+ emission and nonradiative defects in the Er-doped SiO2 films containing nc-Si (SRSO) are studied. Upon 514.5 nm laser excitation the erbium-doped SRSO samples exhibit PL peaks at around 0.8 and 1.54 mum, which can be assigned to the electron-hole recombination in nc-Si and the intra-4f transition in Er3+, respectively. With increasing Er3+ content in the films, Er3+ emission becomes intense while the PL at 0.8 mum decreases, suggesting a strong coupling of nc-Si and Er 31 ions. Hydrogen plasma treatment for the samples improve the PL intensities of the 0.8 and 1.54 mum bands, indicating H passivation for the nonradiative defects existing in the samples. Further-more, from the effect of hydrogen treatment for the samples, we observe variation of the number of nonradiative defects with annealing temperatures. (C) 2003 Elsevier Science B.V. All rights reserved.

Influence of coupling between Er3+, nc-Si and nonradiative centers on photoluminescence from Er3+-doped nc-Si/SiO2 films

Con-elation between nc-Si, Er3+ and nonradiative defects in Er-doped nc-Si/SiO2 films is studied. Upon the 514.5 run laser excitation, the samples exhibit a nanocrystal-related spectrum centered at around 750 nm and an Er3+ luminescence line at 1.54mum. With increasing Er3+ content in the films,the Er3+ emission becomes intense while the photoluminescence at 750 nm decreases. Hydrogen passivation of the samples is shown to result in increases of the two luminescence peaks. However, the effect of hydrogen treatment is different for the samples annealed at different temperatures. The experimental results show that the coupling between Er3+, nc-Si and noradiative centers has a great influence on photoluminescence from nc-Si/SiO2 < Er > films.

Lasing of CdSexS1-x quantum dots in a glass spherical microcavity

A glass spherical microcavity only a few microns in diameter embedded with CdSexS1-x quantum dots (QDs) was fabricated using a physical method; it exhibited good optical stability under continuous-wave laser excitation with high power. We investigated the excitation power dependences of the emission intensity and the linewidth of both transverse electric and transverse magnetic resonance peaks of whispering gallery modes. Stimulated emission behaviour of multi-frequency modes is observed at room temperature. The low threshold value and large mode separation makes QD-containing microspheres promising for visible microlaser applications.

Radiative recombination characteristics in GaAs multilayer n(+)-i interfaces

In this communication, we have carried out a detailed investigation of radiative recombination in n-GaAs homojunction far-infrared detector structures with multilayer emitter (n(+))-intrinsic (i) interfaces by temperature-dependent steady-state photoluminescence measurements. The observation of the emitter-layer luminescence structures has been identified from their luminescence characteristics, in combination with high density theoretical calculation. A photogenerated carrier transferring model has been proposed, which can well explain the dependencies of the luminescence intensities on the laser excitation intensity and temperature. Furthermore, the obtained radiative recombination behavior helps us to offer a proposal to improve the operating temperature of the detector. (C) 2001 American Institute of Physics.

Broad-spectrum and long-lifetime emissions of Nd3+ ions in lead fluorosilicate glass

A novel Nd3+-doped lead fluorosilicate glass (NPS glass) is prepared by a two-step melting process. Based on the absorption spectrum a Judd-Ofelt theory analysis is made. The emission line width of NPS glass is 44.2nm. The fluorescence decay lifetime of the 4F3/2 level is 586±20μsec, and the stimulated emission cross-section is 0.87×10-20cm2 at 1056nm. A laser oscillation is occurred at 1062nm when pumped by 808nm Diode Laser. The slope efficiency is 23.7% with a 415mJ threshold. It is supposed that NPS glass is a good candidate for using in ultra-short pulse generation and amplification by the broad emission bandwidth and long fluorescence lifetime.

Optical Pr operties of GaNAs and GaAsSb Semiconductors

Under short pulse laser excitation, it has been observed, for the first time, a new high-energy photoluminescence emission from GaNx As1- x/GaAs SQWs. This new emission has totally different optical properties compared with the localized exciton transition in GaNx As1-x, and is attributed to the recombination of delocalized excitons in QWs. At the same time, a competition process between localized and delocalized exciton emissions in GaNx As1-x/GaAs quantum wells is observed in the temperaturedependent PL spectra under the short pulse excitation. This competition process for the first time, reveals the physical origin of the temperature-induced S-shaped PL peak shift, which was often reported in the disordered alloy semiconductor system under continuous-wave excitation and puzzled people for a long time. We have also investigated a set of GaNx As1- x samples with small nitrogen composition( x ＜ 1% )by PL, and time-resolved PL. After the PL dependence on temperature and excitation power and PL dynamics were measured, the new PL peak was identified as an intrinsic transition of alloy, rather than N-related bound states. This is the first observation in PL, showing that alloy state exists in GaNx As1- x materials even when N composition is smaller than 0.1%. Finally by selective excitation,both type-Ⅰ and type-Ⅱ transitions were observed simultaneously in GaAs1-xSbx/GaAs SQWs for the first time.

Exciton Localization and Delocalization in GaNAs/GaAs Quantum Wells

We have studied exciton localization and delocalization effect in GaNAs/GaAs quantum wells (QWs) grown by molecular beam epitaxy (MBE) using photoluminescence (PL) and timeresolved PL measurements. Studied results suggest that, at low temperature and under a conventional CW excitation, measured PL spectra were dominated by localized exciton (LE) emission caused by potential fluctuations in GaNAs layer. However, under short pulse laser excitation, it is different. An extra high-energy PL peak comes out from GaNAs/GaAs QWs and dominates the PL spectra under high excitation and/or at high temperature. By investigation, we have attributed the new PL peak to the recombination of delocalized excitons in QWs. This recombination process competes with the localized exciton emission, which, we believe, constitutes the "S-shaped" temperature-dependent emission shift often reported in ternary nitrides of InGaN and AlGaN in the literature.

Design of side-pumped Nd : YAG lasers

Design of the typical laser diode side-pumped Nd:YAG rod system has been discussed using the conventional ray tracing method in this paper. Firstly introduce two basic matrices, refractional and translational matrix, described the transmission of nonparaxial light ray in the medium without concerning the absorption of light. And then, using those matrices, analyze the distribution of pump light in the crystal respectively under the condition of directly pumped system and indirectly pumped system with a cylindrical quartz rod as focusing lens. From the result of simulation, we compare the advantage and disadvantage of the two pumped method, and mainly consider how to select the diameter of the focus lens and cooling tube, indicate the effect of deionized water and cooling tube have on the pump light distribution in the active material. At last, make some conclusions about the side-pumped Nd:YAG laser system.

Synthesis and Upconversion Luminescence Properties of GdF3:Er3+, Yb3+

GdF3:Er3+,Yb-3 with Er3+ ion of 3% and Yb3+ ion concentration of 10%, 20% have been prepared by a hydrothermal method. The results of XRD show that all the samples are of an orthorhombic structure. The average crystallite sizes estimated by Scherrer formula are 28 and 26 nm for Gd0.87Yb0.10Er0.03F3 and Gd0.77Yb0.20Er0.03F3, respectively. The Upconversion luminescence spectra of the samples have been studied under 980 run laser excitation. The results show that the green and red upconversion emission can be attributed to the H-2(11/2),S-4(3/2) -> 4I(15/2) and 4F(9/2) -> 4I(15/2) transitions of Er3+, respectively.