Influence of substrate temperature on properties of MgF2 coatings

Thermal boat evaporation was employed to prepare MgF2 single-layer coatings upon both JGS1 and UBK7 substrates at different substrate temperatures. Microstructure, transmittance and residual stress of these coatings were measured by X-ray diffraction, spectrophotometer, and optical interferometer, respectively. Measurement of laser induced damage threshold (LIDT) of the samples was performed at 355 nm, 8 ns pulses. The results showed that high substrate temperature was beneficial to crystallization of the film. Above 244 degrees C, the refractive index increased gradually with the substrate temperature rising. Whereas, it was exceptional at 210 degrees C that the refractive index was higher than those deposited at 244 and 277 degrees C. The tensile residual stresses were exhibited in all MgF2 films, but not well correlated with the substrate temperature. In addition, the stresses were comparatively smaller upon JGS1 substrates. A tendency could be seen that the LIDTs reached the highest values at about 244 degrees C, and the films upon JGS1 had higher LIDTs than those upon UBK7 substrates at the same temperature. Meanwhile, the damage morphologies showed that the laser damage of the coating resulted from an absorbing center at the film-substrate interface. The features of the damages were displayed by an absorbing center dominated model. Furthermore, the reason of the difference in LIDT values was discussed in detail. (C) 2007 Elsevier B.V. All rights reserved.

基底对光学薄膜弱吸收测量的影响

对表面热透镜技术测量光学薄膜弱吸收低频调制时不同基底对测量的影响进行了理论分析。用Lambda-900分光光度计测量了K9和石英基底的Ti3O5单层膜的吸收值，将该组样品作为定标片；用表面热透镜装置分别测量了BK7和石英空白基底及HfO2，ZnO两组不同基底不同厚度单层膜样品的吸收。通过分析比较同一工艺条件下镀制的不同基底薄膜样品用与其同种和不同种基底定标片定标测量的结果，表明在低频测量时需要用与测量样品同种基底的定标片定标；不同厚度样品的测量结果表明，在不能严格满足热薄条件时，测量结果需引入修正值。

沉积温度对LaF3薄膜性能的影响

abstract {LaF₃ single-layer coatings were prepared by thermal boat evaporation at the deposition temperatures of 189, 255, 277 and 321°C respectively. The crystal structures of the coatings were characterized by X-ray diffraction (XRD). A spectrophotometer was employed to measure its transmittance. Moreover, refractive index, extinction coefficient and cut-off wavelength were obtained from the measured transmittance spectral curve. The residual stress was evaluated by the Stoney's equation and optical interferometer. Laser induce damage threshold (LIDT) was performed by a tripled Nd:YAG laser system. The results show that the crystallization status becomes better with the deposition temperature increasing. Correspondingly, the grain size also gets larger. Meanwhile, the coatings become more compact and the refractive index increases. However, the absorption of coatings seriously rises and the cut-off wavelength drifts to the long wave. In addition, the residual stress also increases and the intrinsic stress plays a determinant role in the coating. The LIDT of the coating also enhances at high temperature.}

沉积速率对热舟蒸发LaF3薄膜性能的影响

用热舟蒸发方法在不同的沉积速率下制备了LaF3单层膜,并对部分单层膜进行了真空退火。分别采用X射线衍射(XRD),Lambda 900 光谱仪和355 nm Nd∶YAG脉冲激光测试了薄膜的晶体结构、透射光谱和激光损伤阈值(LIDT),并通过透射光谱计算得到样品的折射率和消光系数。实验结果表明,增大沉积速率有利于LaF3薄膜的结晶和择优生长,可以提高薄膜的致密性和折射率,但薄膜的抗激光损伤能力有所下降;沉积速率太大,又会恶化薄膜的结晶性能,同时薄膜中产生大量孔洞,薄膜的机械强度降低,导致薄膜的折射率减小和

4H-SiC基底Al_2O_3/SiO_2双层减反射膜的设计和制备

在4H-SiC基底上设计并制备了Al2O3/SiO2紫外双层减反射膜,通过扫描电镜(SEM)和实测反射率谱来验证理论设计的正确性。利用编程计算得到Al2O3和SiO2的最优物理膜厚分别为42.0nm和96.1nm以及参考波长λ=280nm处最小反射率为0.09%。由误差分析可知,实际镀膜时保持双层膜厚度之和与理论值一致有利于降低膜系反射率。实验中应当准确控制SiO2折射率并使Al2O3折射率接近1.715。用电子束蒸发法在4H-SiC基底上淀积Al2O3/SiO2双层膜,厚度分别为42nm和96nm。SEM截面图表明淀积的薄膜和基底间具有较强的附着力。实测反射率极小值为0.33%,对应λ=276nm,与理论结果吻合较好。与传统SiO2单层膜相比,Al2O3/SiO2双层膜具有反射率小,波长选择性好等优点,从而论证了其在4H-SiC基紫外光电器件减反射膜上具有较好的应用前景。

单脉冲飞秒脉冲激光对单层和高反光学薄膜的损伤

用电子柬蒸发的方法在BK7玻璃上制备了ZrO2单层膜和ZrO2／SiO2高反膜，利用掺Ti：sapphire飞秒激光系统输出的中心波长为800nm，脉宽为50fs的激光脉冲对这两种样品进行了激光损伤阈值测试．实验结果表明，ZrO2单层膜的阂值比ZrO2／SiO2高反膜的高；这与传统的纳秒脉冲激光的损伤情况相反．利用光离化和碰撞离化激发电子到导带，形成电子等离子体基本模型并对此现象进行了解释．同时，用显微镜对样品的损伤形貌进行了观测，对损伤的特点进行了表征．

Al2O3/SiO2 films prepared by electron-beam evaporation as UV antireflection coatings on 4H-SiC

Al2O3/SiO2 films have been deposited as UV antireflection coatings on 4H-SiC by electron-beam evaporation and characterized by reflection spectrum, scanning electron microscopy (SEM) and X-ray photoelectron spectroscopy (XPS). The reflectance of the Al2O3/SiO2 films is 0.33% and 10 times lower than that of a thermally grown SiO2 single layer at 276 nm. The films are amorphous in microstructure and characterize good adhesion to 4H-SiC substrate. XPS results indicate an abrupt interface between evaporated SiO2 and 4H-SiC substrate free of Si-suboxides. These results make the possibility for 4H-SiC based high performance UV optoelectronic devices with Al2O3/SiO2 films as antireflection coatings. (C) 2007 Elsevier B.V. All rights reserved.

SiO_2薄膜折射率的准确拟合分析

精确的光学常数对于设计和制备高品质的光学薄膜非常重要,尤其是那些光学性能对折射率变化敏感的薄膜。SiO_2是一种常用的低折射率材料,因与常用基底折射率相近使其准确拟合有一定难度。实验通过离子束溅射制备了SiO_2单层膜。考虑测量时的误差和基底折射率的影响,采用透射率包络和反射率包络得到了SiO_2的折射率,并用所得折射率进行反演来对这两种途径在实际测量拟合过程中的准确性进行比对。分析表明,剩余反射率在实际的测量过程中误差更小,直接用测量镀膜前后基片的剩余反射率值可以更简便更准确地得到SiO_2的折射率,能达到10~(-2)的精度。

HfO2的纯度对紫外多层膜反射率的影响

用辉光放电质谱法和二次离子质谱仪测定了两种HfO2材料及它们相应的单层膜中的杂质含量，结果发现，无论是在体材料中还是在用电子束蒸发技术沉积的材料单层薄膜中，ZrO2都是这两种HfO2材料中最主要的杂质。而且，这两种HfO2材料中Zr含量的差别远远大于Ti、Fe含量的差别，这说明Zr含量的差别正是引起两种HfO2膜层光学性能差别的原因。用这两种不同纯度的HfO2材料与同一纯度的SiO2材料组合，沉积形成266nm的紫外反射镜，实验结果表明这两种反射镜的反射率分别在99.85% 和 99.15%左右。这个结果与依据单层膜得出的光学常数所设计的结果符合的很好。

Influence of ZrO2 in HfO2 on reflectance of HfO2/SiO2 multilayer at 248 nm prepared by electron-beam evaporation

Influence of ZrO2 in HfO2 on the reflectance of HfO2/SiO2 multilayer at 248 nm was investigated. Two kinds of HfO2 with different ZrO2 content were chosen as high refractive index material and the same kind of SiO2 as low refractive index material to prepare the mirrors by electron-beam evaporation. The impurities in two kinds of HfO2 starting coating materials and in their corresponding single layer thin films were determined through glow discharge mass spectrum (GDMS) technology and secondary ion mass spectrometry (SIMS) equipment, respectively. It showed that between the two kinds of HfO2, either the bulk materials or their corresponding films, the difference of ZrO2 was much larger than that of the other impurities such as Ti and Fe. It is the Zr element that affects the property of thin films. Both in theoretical and in experimental, the mirror prepared with the HfO2 starting material containing more Zr content has a lower reflectance. Because the extinction coefficient of zirconia is relatively high in UV region, it can be treated as one kind of absorbing defects to influence the optical property of the mirrors. (C) 2008 Elsevier B.V. All rights reserved.

Spin relaxation in submonolayer and monolayer InAs structures grown in a GaAs matrix

Electron-spin dynamics in InAs/GaAs heterostructures consisting of a single layer of InAs (1/3-1 monolayer) embedded in (001) and (311)A GaAs matrix was studied by means of time-resolved Kerr rotation spectroscopy. The spin-relaxation time of the submonolayer InAs samples is significantly enhanced, compared with that of the monolayer InAs sample. The electron-spin-relaxation time and the effective g factor in submonolayer samples were found to be strongly dependent on the photogenerated carrier density. The contribution from both the D'yakonov-Perel' mechanism and Bir-Aronov-Pikus mechanism are discussed to interpret the temperature dependence of spin decoherence at various carrier densities.

The fabrication and properties of InAs/GaAs columnal islands

A columnal islands system, which was composed of three layers of self-assembled InAs/GaAs quantum dots (QDs), has been fabricated by solid-source molecular beam epitaxy (MBE) through S-K mode on a (100) semi-insulating GaAs substrate. The effects of the thickness of GaAs space layer, the growth interruption time and the amount of InAs deposition on the emission wavelength of columnal islands were presented. The image of atomic force microscopy (AFM) indicated the columnal islands with high uniformity in size and shape. At room temperature, the emission wavelength of columnal islands with different effective heights was achieved 1.32 and 1.4 mum; however, the emission wavelength of single-layer QDs with normal height was just 1. l mum. It provides a useful and intuitive approach to artificially control the emission wavelength of a QD material system.

Fabrication of metallic air bridges using multiple-dose electron beam lithography

The techniques of fabricating metallic air bridges using different resists in a one-step electron beam lithography are presented. The exposure process employed a single-layer polymethyl methacrylate (PMMA) or photoresists with either different doses in the span and feet areas or with varying acceleration voltage of the electron beam. The process using photoresists with different doses has produced air bridges more stable than what the PMMA method using various acceleration voltages would achieve. Using this method, air bridges up to 12 mu m long have been fabricated. The length and height of these metallic air bridges vary with the photoresist thickness. (c) 2006 American Institute of Physics.

Stretchable Graphene: A Close Look at Fundamental Parameters through Biaxial Straining

Tunable biaxial stresses, both tensile and compressive, are applied to a single layer graphene by utilizing piezoelectric actuators. The Gruneisen parameters for the phonons responsible for the D, G, 2D and 2D' peaks are studied. The results show that the D peak is composed of two peaks, unambiguously revealing that the 2D peak frequency (omega(2D)) is not exactly twice that of the D peak (omega(D)). This finding is confirmed by varying the biaxial strain of the graphene, from which we observe that the shift of omega(2D)/2 and omega(D) are different. The employed technique allows a detailed study of the interplay between the graphene geometrical structures and its electronic properties.

Self-formed InGaAs/GaAs quantum dot superlattice and direct observation on strain distribution in the capped superlattice

We have demonstrated a 20 period dislocation-free InGaAs/GaAs quantum dot superlattice which is self-formed by the strain from the superlattice taken as a whole rather than by the strain from the strained single layer. The island formation does not take place while growing the corresponding strained single layer. From the variation of the average dot height in each layer, the strain distribution and relaxation process in the capped superlattice have been examined. It is found that the strain is not uniformly distributed and the greatest strains occur at two interfaces between the superlattice and the substrate and the cap layer in the capped superlattice. (C) 1997 American Institute of Physics.