碳纳米管-Mg_(65)Cu_(25)Gd_(10)非晶复合材料玻璃转变的动力学性质

制备了Mg65Cu25Gd10大块非晶合金及其碳纳米管(CNTs)复合材料,对两种材料进行了不同扫描速率下的差热扫描量热分析,研究了加入CNTs对材料玻璃转变和晶化动力学效应的影响。结果表明:加入CNTs后,复合材料的玻璃转变和晶化行为仍然具有动力学效应,但加入的CNTs减小了材料晶化行为对升温速率的依赖程度;同时,加入CNTs加大了材料发生玻璃转变时需要克服的能量势垒,增大了峰值温度时的晶化反应速率常数,从而降低了材料的玻璃形成能力(GFA);对CNTs降低GFA的原因也进行了探讨。

微重力落管法制备Nd_(60)Al_(10)Fe_(20)Co_(10)非晶薄片的磁性能研究

采用微重力落管法制得了Nd6 0 Al1 0 Fe2 0 Co1 0 非晶薄片 .利用X衍射 (XRD)分析了Nd6 0 Al1 0 Fe2 0 Co1 0 非晶薄片的结构特征 .用振动样品磁强计 (VSM)研究了其磁性能 .结果表明微重力落管法制得的非晶薄片具有硬磁性 ,与快速非平衡凝固(如甩带法 )试样的XRD相比 ,尽管其曲线还是较为典型的非晶相漫散衍射峰 ,但已有少量的不规则的类似晶化的突起小峰 ,表明该非晶片中已经有微量晶态合金或者细小晶粒析出 ,初步分析可能是生成了类似于亚稳A1 相的短程有序原子团簇或者是较大尺寸的纳米晶 ,这种短程有序原子团簇或纳米晶是Nd6 0 Al1 0 Fe2 0 Co1 0 非晶薄片显示硬磁性的主要原因

激光熔覆大厚度Fe_(57)Co_8Ni_8Zr_(10)Si_4B_(13)非晶表层及其微结构研究

利用激光熔覆制备出1.2mm厚的Fe_(57)Co_8Ni_8Zr_(10)Si_4B_(13)大厚度非晶表层。用XRD,ES,TEM,DSC及硬度对获得的非晶表层进行了多种分析，研究了非晶合金表层的微结构与非晶形成能力。初步探讨了大厚度非晶表层的形式机制。

Nd_(60)Al_(10)Fe_(20)Co_(10)大块金属玻璃的玻璃转变和晶化过程

本文利用DSC、X射线衍射和动态力学分析以及扫描电子显微镜研究了Nd_(60)Al_(10)Fe_(20)Co_(10)大块金属玻璃(BMG)的玻璃转变和晶化过程。结果表明,合金的动态力学分析结果清楚地反映出材料的玻璃转变和晶化过程。由此确定材料的玻璃转变温度为493K,初始晶化温度为590K。X射线衍射和组织分析表明合金的晶化过程为:非晶α→非晶α’+未知亚稳NdFeAl相→非晶α’+初晶δ相→初晶δ相+共晶δ相+Nd_3Co+Nd_3Al。

Influence of HCl on CO and NO emissions in combustion

The influence of HCl on CO and NO emissions was experimentally investigated in an entrained flow reactor (EFR) and an internally circulating fluidized bed (ICFB). The results in EFR show the addition of HCl inhibits CO oxidation and NO formation at 1073 K and 1123 K. At the lower temperature (1073 K) the inhibition of HCl becomes more obvious. In ICFB, chlorine-containing plastic (PVC) was added to increase the concentration of HCl during the combustion of coal or coke. Results show that HCl is likely to enhance the reduction of NO and N2O. HCl greatly increases CO and CH4 emission in the flue gas. A detailed mechanism of CO/NO/HCl/SO2 system was used to model the effect of HCl in combustion. The results indicate that HCl not only promotes the recombination of radicals O, H, and OH, but also accelerates the chemical equilibration of radicals. The influence of HCl on the radicals mainly occurs at 800-1200 K. (C) 2009 Elsevier Ltd. All rights reserved.

THE FORMATION MECHANISM OF THE VITRIFIED SLAG IN A PLASMA ARC REACTOR FOR HAZARDOUS WASTE TREATMENT

Various hazardous wastes with additives have been vitrified to investigate the formation mechanism of the glassy slag by a 30 kW DC plasma-arc reactor developed by the Institute of Mechanics, Chinese Academy of Sciences. The average temperature in the reaction area is controlled at 1500°C. The chemical compositions of three sorts of fly ashes are analyzed by XRF (X-Ray Fluorescence). Fly ashes with vitrifying additives can be vitrified to form glassy slag, which show that the ratio of the whole oxygen ions to the whole network former ions in glass (R) is appropriate in the range of 2~3 to form durable vitrified slag. In this experiment, the arc power is controlled below 5 kW to inhibit waste evaporation. To enhance the effects of heat transfer to wastes, ferrous powder has been added into the graphite crucible, which aggregates as ingot below the molten silicate after vitrification. The slag fails to form glass if the quenching rate is less than 1 K/min. Therefore, the slag will break into small chips due to the sharp quenching rate, which is more than 100 K/sec.

Generation of 17-TW 23-fs pulses with a two-stage Ti : Sapphire amplifier at repetition rate 10 Hz

We have developed a two-stage Ti:sapphire amplifier system which can produce 17-TW/23-fs pulses at a repetition rate 10 MHz. A birefringent plate is used in the regenerative amplifier to alleviate gain narrowing, while an all-reflective cylindrical-mirror-based pulse stretcher and an acousto-optic programmable dispersive filter (AOPDF) are used to compensate for the higher order dispersion of the system.

Femtosecond optical Kerr effect study of Ge(10)AS(40)S(30)Se(20) film

The results of the femtosecond optical heterodyne detection of optical Kerr effect at 805 nm with the 80 fs ultrafast pulses in amorphous Ge10As40S30Se20 film is reported in this paper. The film shows an optical non-linear response of: 200 fs under ultrafast 80 fs-pulse excitation and the values of real and imaginary parts of non-linear susceptibility chi((3)) were 9.0 X 10(-12) and -4.0 X 10(-12) esu, respectively. The large third-order non-linearity and ultrafast response are attributed to the ultrafast distortion of the electron orbits surrounding the average positions of the nucleus of Ge, As, S and Se atoms. This Ge10As40S30Se20 chalcogenide glass would be expected as a promising material for optical switching technique. (c) 2005 Elsevier Ltd. All rights reserved.

Preparation, characterization and gas sensing properties of lead tetra-(tert-butyl)-5,10,1 5,20-tetraazaporphyrin spin-coating films

A spin-coated film of lead tetra-(tert-butyl)-5,10,15,20-tetraazaporphyrin complex (PbTAP(t-Bu)(4)) was obtained and characterized by IR spectra, absorption spectra and atomic force microscopy. The response and recovery characteristics of the film to NH3, NO2 and C2H5OH vapor were investigated at room temperature. In addition, the reversibility and stability of the film to NH3 were also studied. The results indicate that the PbTAP(t-Bu)(4) derivative can be exploited as an NH3 sensor at room temperature. (c) 2007 Elsevier B.V. All rights reserved.

Yb：Y2O3陶瓷薄片激光器获得10．5W连续激光输出

室温下采用中心波长约970nm准直输出的大功率激光二极管模块作为抽运源，端面抽运双程吸收的腔型结构，抽运原子数分数为8％的Yb：Y2O3多晶透明陶瓷片获得连续激光输出。抽运阈值功率为7W，当抽运功率达到35W时，获得优化连续激光输出功率为10．5W，光光转换效率为30％，斜率效率为37．5％。激光输出功率随抽运功率基本呈线性增长。采用更高功率抽运源、优化谐振腔结构和减小热效应的影响，Yb：Y2O3陶瓷激光器的输出功率和效率将会得到进一步提高。