Ultrabroad infrared luminescence from Bi-doped aluminogermanate glasses

We report ultrabroad infrared luminescence from Bi-doped aluminogermanate glasses. The infrared luminescence almost covers the whole low loss wavelength region (1200-1650 nm) of silica glass fiber when excited by a diode laser at 980 nm. The full width at half maximum (FWHM) of the luminescence is 510 nm. The luminescence peak can be divided into three Gaussian peaks, and the fluorescence lifetime of the three emissions are 297 mu s, 470 mu s and 1725 mu s, respectively. These fluorescence properties indicate that the glasses are promising material for broadband optical amplifiers. (C) 2007 Elsevier Ltd. All rights reserved.

Effects of thermal treatment on broadband near-infrared emission from Bi-doped chalcohalide glasses

GeGaSKBr glass with Bi ions as emission centers were fabricated. An intense emission centered at around 1230 nm with the width of more than 175 nm was observed by 808 nm photo-excitation of the glass. Lower quenching rate and thermal treatment promote micro-crystallization process, thus strengthening the emission. Crown Copyright (c) 2008 Published by Elsevier Ltd. All rights reserved.

Enhanced broadband near-infrared luminescence and optical amplification in Yb-Bi codoped phosphate glasses

Yb-Bi codoped phosphate glass was prepared and its properties were compared with Bi-doped phosphate glass. The broadband infrared luminescence intensity from Yb-Bi codoped glass was similar to 32 times stronger than that of Bi-doped glass. The single-pass optical amplification was measured on a traditional two-wave mixing configuration. No optical amplification was observed in Bi-doped glass, while apparent broadband optical amplification between 1272 and 1336 nm was observed from Yb-Bi codoped glass with 980 nm laser diode excitation. The highest gain coefficient at 1272 nm of Yb-Bi codoped glass reached to 2.62 cm(-1). Yb-Bi codoped phosphate glass is a promising material for broadband optical amplification. (C) 2008 American Institute of Physics.

Novel Bi-doped glasses for broadband optical amplification

Broadband infrared luminescence is observed in various Bi-doped oxide glasses prepared by conventional melting-quenching technique. The absorption spectrum of the Bi-doped germanium oxide glass consists of five broad peaks at below 370, 500, 700, 800 and 1000 nm. The fluorescence spectrum exhibits a broad peak at about 1300 nm with full width at half maximum (FWHM) of more than 300 nm when excited by an 808 nm laser diode. The fluorescence lifetime at room temperature decreases with increasing Bi2O3 concentration. Influence of the glass composition and melting atmosphere on the fluorescence lifetime and luminescent intensity is investigated. The mechanism of the broadband infrared luminescence is suggested. The product of stimulated emission cross-section and lifetime of the Bi-doped aluminophosphate glass is about 5.0 X 10(-24) cm(2) s. The glasses might be promising for applications in broadband optical fiber amplifiers and tunable lasers. (c) 2007 Elsevier B.V. All rights reserved.

GeO2 : Bi, M (M = Ga, B) glasses with super-wide infrared luminescence

Broadband infrared luminescence covering the optical telecommunication wavelength region of 0, E and S bands was observed in GeO2: Bi, M (M = Ga, B) glasses prepared by conventional melting-quenching technique. The luminescence with a maximum at around 1320 nm possesses a full width at half maximum larger than 300 nm and mean fluorescent lifetime longer than 500 mus when excited by an 808 nm-laser. These glasses may have potential applications in widely tunable laser and super-broadband optical amplifier for the optical communications. (C) 2005 Elsevier B.V. All rights reserved.

Nd：（La，Sr）（Al，Ta）O3晶体的生长及光谱性能的研究

应用中频感应提拉法生长了新型的Nd：（La，Sr）（Al，Ta）O3（Nd^3＋：LSAT）晶体。运用电感耦合等离子体原子发射光谱仪（ICPAES）测定Nd^3＋离子在Nd^3＋：LSAT晶体中的分凝系数为0．587。X射线粉末衍射（XRPD）测试结果表明Nd^3＋：LSAT晶体与LSAT晶体同构。研究了不同退火条件对晶体光谱性能的影响。分析了Nd^3＋：LSAT晶体的光谱性能，Nd^3＋：LSAT晶体的荧光寿命为290μs。比较了Nd^3＋：LSAT和Nd^3＋：YAG，Nd^3＋：YVO3等晶体的光谱

在Sr～2+α_BBO单晶衬底上生长β_BBO薄膜的研究

Crystalline beta-BBO thin films were successfully prepared on (001)-oriented Sr2+-doped alpha-BBO substrates by using liquid phase epitaxy, pulsed laser deposition and vapor transport equilibration techniques. The films were characterized by X-ray diffraction and X-ray rocking curve. The present results manifest that the beta-BBO thin films grown on Sr2+-doped alpha-BBO substrates have larger degree of orientation f value and smaller X-ray rocking curve FWHM than the ones grown on other reported substrates. Compared with other substrates, alpha-BBO has the similar structure, the same UV cutoff and the same chemical properties to beta-BBO. These results reveal that Sr2+-doped alpha-BBO single crystal may be a promising substrate proper to the growth of beta-BBO films.

Spectroscopic properties of Nd3+:(La,Sr)(Al,Ta)O-3 crystal

A new laser crystal Nd3+:(La, Sr)(Al, Ta)O-3 (abbreviated as Nd3+:LSAT) has been grown by the conventional Czochralski method. The absorption and luminescence spectra of trivalent neodymium in Nd3+:LSAT crystal were measured at room temperature. The value of absorption and emission cross-section was calculated. The Judd-Ofelt analysis was applied to the crystal to get the phenomenological parameters (Omega(i), i = 2,4,6), the line strengths, the radiative transition rates, the branching ratios and the radiative lifetime. (C) 2006 Elsevier B.V. All rights reserved.

气相传输平衡法在Sr^2＋：α-BBO衬底上制备β-BBO薄膜的研究

采用气相传输平衡技术在掺Sr^2＋的α-BBO（001）衬底上制备了β-BBO薄膜，研究了粉料配比、VTE处理温度以及恒温时间对薄膜质量的影响。结果表明，在适当的粉料配比、VTE处理温度以及恒温时间下，在Sr^2＋：α-BBO晶片表层制备呈c轴高度择优取向的、没有第二相物质的β-BBO薄膜，其双晶摇摆曲线半峰宽值FWHM为1000＂，显示出β-BBO薄膜较好的结晶质量。并对气相传输平衡技术制备β-BBO薄膜的机理进行了初步的探讨。