Structural change of laser-irradiated Ge2Sb2Te5 films studied by electrical property measurement

Sheet resistance of laser-irradiated Ge2Sb2Te5 thin films prepared by magnetron sputtering was measured by the four-point probe method. With increasing laser power the sheet resistance undergoes an abrupt drop from 10(7) to 10(3) Omega/square at about 580 mW. The abrupt drop in resistance is due to the structural change from amorphous to crystalline state as revealed by X-ray diffraction (XRD) study of the samples around the abrupt change point. Crystallized dots were also formed in the amorphous Ge2Sb2Te5 films by focused short pulse laser-irradiated, the resistivities at the crystallized dots and the non-crystallized area are 3.375 x 10(-3) and 2.725 Omega m, sheet resistance is 3.37 x 10(4) and 2.725 x 10(7) Omega/square respectively, deduced from the I-V Curves that is obtained by conductive atomic force microscope (C-AFM). (C) 2008 Elsevier B.V. All rights reserved.

Passive Q-switching of short-length Tm3+-doped silica fiber lasers by polycrystalline Cr2+:ZnSe microchips

We demonstrate passive Q-switching of short-length double-clad Tm3+-doped silica fiber lasers near 2 mu m pumped by a laser diode array (LDA) at 790 nm. Polycrystalline Cr2+:ZnSe microchips with thickness from 0.3 to 1 mm are adopted as the Q-switching elements. Pulse duration of 120 ns, pulse energy over 14 mu] and repetition rate of 53 kHz are obtained from a 5-cm long fiber laser. As high as 530 kHz repetition rate is achieved from a 50-cm long fiber laser at similar to 10-W pump power. The performance of the Q-switched fiber lasers as a function of fiber length is also analyzed. (c) 2008 Elsevier B.V. All rights reserved.

High-power Nd:YAG planar waveguide laser with YAG and Al2O3 claddings

Thermal effects in Nd:YAG planar waveguide lasers with non-symmetrical claddings are discussed. The heat generated in the active core can be removed more efficiently by directly contacting the active core to the heat sink. Several cladding materials are compared to optimize the heat removal. Furthermore, uniform pumping is achieved with oblique edge-pumping technique. Using quasi-CW pumping at 1 KHz repetition rate, an average output power of 280 W with a slope efficiency of 38% is obtained with a positive unstable resonator. (C) 2008 Elsevier B.V. All rights reserved.

Efficient excitations of radially and azimuthally polarized Nd 3+:YAG ceramic microchip laser by use of subwavelength multilayer concentric gratings composed of Nb2O5/SiO2

Cylindrical vector beams were produced from laser diode end-pumped Nd:YAG ceramic microchip laser by use of two types of subwavelength multilayer gratings as the axisymmetric-polarization output couplers respectively. The grating mirrors are composed of high- and low-refractive-index (Nb2O5/SiO2) layers alternately while each layer is shaped into triangle and concentric corrugations. For radially polarized laser output, the beam power reached 610mW with a polarization extinction ratio ( PER) of 61: 1 and a slope efficiency of 68.2%; for azimuthally polarized laser output, the beam power reached 626mW with a PER of 58: 1 and a slope efficiency of 47.6%. In both cases, the laser beams had near-diffraction limited quality. Small differences of beam power, PER and slope efficiency between radially and azimuthally polarized laser outputs were not critical, and could be minimized by further optimized adjustment to laser cavity and the reflectances of respective grating mirrors. The results manifested, by use of the photonic crystal gratings mirrors and end-pumped microchip laser configuration, CVBs can be generated efficiently with high modal symmetry and polarization purity. (C) 2008 Optical Society of America.

808 nm 抽运的Ho3+，Tm3+及Er3+掺杂的氟磷酸盐 玻璃的2.0 μm 光谱性质研究

2.0 μm spectroscopic properties of Er³⁺/Tm³⁺/Ho³⁺ triply-doped fluorophosphate glasses pumped by 808 nm and the energy transfer mechanisms between the three rare earth ions were investigated. J-O theory was used to calculate the parameters of Ho³⁺ in fluorophosphate glasses. Absorption and emission cross-sections and the gain coefficients were calculated. The obtained lifetime r and spontaneous transition probability Ar of Ho³⁺:⁵I7 level were 10.64 ms and 93.95 s^-1 respectively. The calculated maximum emission cross-section of 2.0 μm was 9.26×10^-21 cm². The energy transfer analysis indicated that the cross-relaxation of Tm³⁺ was important and the resonent energy transfer in Er³⁺&rarrHo³⁺, Tm³⁺&rarrHo³⁺, Er³⁺&rarrTm³⁺&rarrHo³⁺ process was the main channel. The study revealed that the Er³⁺/Tm³⁺/Ho³⁺ triply-doped fluorophosphate glass would be a potential material for 2.0 μm emission because of the efficient sensitization of Er³⁺ and Tm³⁺ to Ho³⁺.

Energy transfer between Cr3+ and Ni2+ in transparent silicate glass ceramics containing Cr3+/Ni2+ co-doped ZnAl2O4 nanocrystals

The emission intensity of Ni2+ at 1200 nm in transparent ZnO-Al2O3-SiO2 glass ceramics containing ZnAl2O4 nanocrystals is improved approximately 8 times by Cr3+ codoping with 532 nm excitation. This enhanced emission could be attributed to an efficient energy transfer from Cr3+ to Ni2+, which is confirmed by time-resolved emission spectra. The energy transfer efficiency is estimated to be 57% and the energy transfer mechanism is also discussed. (C) 2008 Optical Society of America.

Enhanced broadband near-infrared luminescence from transparent Yb 3+/Ni2+ codoped silicate glass ceramics

The near-infrared emission intensity of Ni2+ in Yb3+/Ni2+ codoped transparent MgO-Al2O3-Ga2O3-SiO2-TiO2 glass ceramics could be enhanced up to 4.4 times via energy transfer from Yb3+ to Ni2+ in nanocrystals. The best Yb2O3 concentration was about 1.00 mol%. For the Yb3+/Ni2+ codoped glass ceramic with 1.00 mol% Yb2O3, a broadband near-infrared emission centered at 1265 nm with full width at half maximum of about 300 nm and lifetime of about 220 mu s was observed. The energy transfer mechanism was also discussed. (C) 2008 Optical Society of America.

Enhanced luminescence from transparent Ni2+-doped MgO-Al2O3-SiO2 glass ceramics by Ga2O3 addition

Transparent Ni2+-doped MgO-Al2O3-SiO2 glass ceramics without and with Ga2O3 were synthetized. The precipitation of spinel nanocrystals, which was identified as solid solutions in the glass ceramics, could be favored by Ga2O3 addition and their sizes were about 7.6 nm in diameter. The luminescent intensity of the Ni2+-doped glass ceramics was largely enhanced by Ga2O3 addition which could mainly be caused by increasing of Ni2+ in the octahedral sites and the reduction of the mean frequency of phonon density of states in the spinel nanocrystals of solid solutions. The full width at half maximum (FWHM) of emissions for the glass ceramics with different Ga2O3 content was all more than 200 nm. The emission lifetime increased with the Ga2O3 content and the longest lifetime is about 250 mu s. The Ni2+-doped transparent glass ceramics with Ga2O3 addition have potential application as broadband optical amplifier and laser materials. (C) 2007 Elsevier Ltd. All rights reserved.

Transparent Ni2+-doped silicate glass ceramics for broadband near-infrared emission

Transparent Ni2+-doped MgO-Al2O3-Ga2O3-SiO2-TiO2 glass ceramics were fabricated. The precipitated nanocrystal phase in the glass ceramics was identified by X-ray diffraction and transmission electron microscope. Broadband near-infrared emission centered at 1220 nm with full width at half maximum of about 240 nm and lifetime of about 250 mu s was observed with 980 nm excitation. The longer wavelength emission compared with Ni2+-doped MgAl2O4 crystal was attributed to the low crystal field occupied by Ni2+ in the glass ceramics. The present Ni2+-doped transparent glass ceramics may have potential applications in broadband optical amplifiers. (c) 2007 Elsevier B.V. All rights reserved.

Blue emission from Eu2+ -doped high silica glass by near-infrared femtosecond laser irradiation

Eu2+-doped high silica glass (HSG) is fabricated by sintering porous glass which is impregnated with europium ions. Eu2+-doped HSG is revealed to yield intense blue emission excited by ultraviolet (UV) light and near-infrared femtosecond laser. The emission profile obtained by UV excitation can be well traced by near-infrared femtosecond laser. The upconversion emission excited by 800 nm femtosecond laser is considered to be related to a two-photon absorption process from the relationship between the integrated intensity and the pump power. A tentative scheme of upconverted blue emission from Eu2+-doped HSG was also proposed. The HSG materials presented herein are expected to find applications in high density optical storage and three-dimensional color displays. (c) 2008 American Institute of Physics.

Effect of Al(PO3)(3) content on physical, chemical and optical properties of fluorophosphate glasses for 2 mu m application

The effect of Al(PO3)(3) content on physical, chemical and optical properties of fluorophosphate glasses for 2 mu m application, such as thermal stability, chemical durability, surface hardness, absorption spectra and emission spectra, is investigated. With the increment of Al(PO3)(3) content, the thermal stability characterized by the gap of T-g and T,, increases first and then decreases, and reaches the maximum level containing 5 mol% Al(PO3)(3) content. The density and chemical durability decrease monotonously with the introduction of Al(PO3)(3) content increasing, while the refractive index and surface hardness increase. Above properties of fluorophosphate glasses are also compared with fluoride glasses and phosphate glasses. The Judd-Ofelt parameters, absorption and emission cross sections are discussed based on the absorption spectra of Tm-doped glasses. The emission spectra are also measured and the 1.8 mu m fluorescence of the sample is obvious indicating that it is suitable to 2 mu m application. (c) 2008 Elsevier B.V. All rights reserved.

Growth, etching morphology and spectra of LiAlO2 crystal

gamma-LiAlO2 single crystal was successfully grown by Czochralski method. The crystal quality was characterized by X-ray rocking curve and chemical etching. The effects of air-annealing and vapor transport equilibration (VTE) on the crystal quality, etch pits and absorption spectra of LiAlO2 were also investigated in detail. The results show that the as-grown crystal has very high quality with the full width at half maximum (FWHM) of 17.7-22.6 arcsec. Dislocation density in the middle part of the crystal is as low as about 3.0 x 10(3) cm(-2). The VTE-treated slice has larger FWHM value, etch pits density and absorption coefficient as compared with those of untreated and air-annealed slices, which indicates that the crystal quality became inferior after VTE treatment. (C) 2008 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

气相传输平衡法在Sr^2＋：α-BBO衬底上制备β-BBO薄膜的研究

采用气相传输平衡技术在掺Sr^2＋的α-BBO（001）衬底上制备了β-BBO薄膜，研究了粉料配比、VTE处理温度以及恒温时间对薄膜质量的影响。结果表明，在适当的粉料配比、VTE处理温度以及恒温时间下，在Sr^2＋：α-BBO晶片表层制备呈c轴高度择优取向的、没有第二相物质的β-BBO薄膜，其双晶摇摆曲线半峰宽值FWHM为1000＂，显示出β-BBO薄膜较好的结晶质量。并对气相传输平衡技术制备β-BBO薄膜的机理进行了初步的探讨。

7.3 W of single-frequency output power at 2.09 μm from an Ho:YAG monolithic nonplanar ring laser

Single-frequency output power of 7.3 W at 2.09 mu m from a monolithic Ho:YAG nonplanar ring oscillator (NPRO) is demonstrated. Resonantly pumped by a Tm-doped fiber laser at 1.91 mu m, the Ho:YAG NPRO produces 71% of slope efficiency with respect to absorbed pump power and nearly diffraction-limited output with a beam quality parameter of M-2 approximate to 1.1. (c) 2008 Optical Society of America

Eu:Y2O3 nano-phosphor prepared by novel energy-saving solution combustion method

A novel energy- and time-saving solution combustion method has been developed to prepare Eu:Y2O3 nano-crystal line phosphor. This novel method employs anhydrous ethanol as solvent and fuel. The prepared nano-crystals after heat-treatment own narrow size distribution, well dispersibility and sinterability, confirmed by XRD, TEM and FTIR. The emission spectra of nano-Eu:Y2O3 Samples show clear nano-size related phenomena. (c) 2007 Elsevier B.V. All rights reserved.