Superbroadband 1310 nm emission from bismuth and tantalum codoped germanium oxide glasses

Near-infrared broadband emission from bismuth-tantalum-codoped germanium oxide glasses was observed at room temperature when the glasses were pumped by an 808 nm laser diode. The emission band covered the 0, E, S, C, and L bands (1260-1625 nm), with a maximum peak at similar to 1310 nm, a FWHM broader than 400 nm, and a lifetime longer than 200 lis. The observed broadband luminescence was attributed to bismuth clusters in the glasses. Bismuth-tantalum-codoped germanium oxide glass might be promising as amplification media for broadly tunable lasers and wideband amplifiers in optical communications. (c) 2005 Optical Society of America.

Study of crystal formation in titanate glass irradiated by 800 nm femtosecond laser pulse

The structure of the titanate glass is destroyed during irradiation by the femtosecond laser pulses, and (TiO6)(8-) and (TiO4)(4-) anion units are exsolved from the network of the titanate glass. These anion units are rearranged to form some crystals such as anatase and Ba2TiO4 crystals. By Raman spectroscopy, it is found that these crystals have a strong dependence on the intensity of the femtosecond laser pulses. The relation between the generation of these crystals and space distribution of the femtosecond laser power intensity is qualitatively explained. (c) 2005 Elsevier B.V. All rights reserved.

Generation of 210 fs laser pulses at 1093 nm by a self-starting mode-locked Yb:GYSO laser

We report the first demonstration, to our knowledge, of the femtosecond laser operation by using a new alloyed Yb:GYSO crystal as the gain medium. With a 5 at. % Yb3+-doped sample and chirped mirrors for dispersion compensation, we obtained pulses as short as 210 fs at the center wavelength of 1093 nm. The average mode-locking power is 300 mW, and the pulse repetition frequency is 80 MHz. (C) 2008 Optical Society of America

Effects of CO2 laser conditioning of the antireflection Y2O3/SiO2 coatings at 351 nm

Y2O3/SiO2 coatings were deposited on fused silica by electron beam evaporation. A continuous wave CO2 laser was used to condition parts of the prepared samples at different scanning speeds in the air. LAMBDA 900 spectrometer was used to investigate the changes of the transmittance and residual reflection spectrum. A Nomarski microscope under dark field was used to examine the changes of the micro defect density. The changes of the surface roughness and the microstructure of the film before and after conditioning were investigated by AFM and X-ray diffraction, respectively. We found that laser-induced damage threshold (LIDT) of the films conditioning at 30 mm/s scanning speed was increased by more than a factor of 3 over the thresholds of the as-deposited films. The conditioning effect was correlated with an irradiation-induced decrease of the defect density and absorption of the films. (c) 2005 Elsevier B.V. All rights reserved.

Stress, absorptance and laser-induced damage threshold properties of 355-nm HR coatings

A number of 355-nm Al2O3/MgF2 high-reflectance (HR) coatings were prepared by electron-beam evaporation. The influences of the number of coating layers and deposition temperature on the 355-nm Al2O3/MgF2 HR coatings were investigated. The stress was measured by viewing the substrate deformation before and after coating deposition using an optical interferometer. The laser-induced damage threshold (LIDT) of the samples was measured by a 355-nm Nd:YAG laser with a pulse width of 8 ns. Transmittance and reflectance of the samples were measured by a Lambda 900 spectrometer. It was found that absorptance was the main reason to result in a low LIDT of 355-nm Al2O3/MgF2 HR coatings. The stress in Al2O3/MgF2 HR coatings played an unimportant role in the LIDT, although MgF2 is known to have high tensile stress.

Study of Al2O3/MgF2 HR coatings at 355 nm

With the present work we tried to study the effective methods to improve the laser-induced damage threshold (LIDT) and reflectance of HR coatings at 355 nm. The work presented in this paper wits part of an ongoing study about vacuum annealing. It was dedicated to study the effects Of Vacuum annealing with different temperature gradients on the structure, optical properties and laser-induced damage threshold (LIDT) of 355nm Al2O3/MgF2HR coatings. A number of samples were prepared by electron beam evaporation using the same deposition process with an optimal deposition temperature of 280 degrees C. After deposition, samples were annealed in the coating chamber for 3 h with different temperature gradients. Morphologies of the samples were observed by Leica-DMRXE. Microscope, Structure of the samples had been characterized by X-ray diffraction (XRD). Transmittance and reflectance of the samples were measured by Lambda 900 Spectrometer, The LIDT of the samples was measured by a 355 nm Nd:YAG laser with a pulse width of 8 ns. It was found that the temperature gradient of vacuum annealing had significant effects on the morphology, structure, absorption, and LIDT of the samples, (c) 2005 Elsevier Ltd. All rights reserved.

Overcoat dependence of laser-induced damage threshold of 355 nm HR coatings

A series of HR coatings, with and without overcoat, were prepared by electron beam evaporation using the same deposition process. The laser-induced damage threshold (LIDT) was measured by a 355 nm Nd:YAG laser with a pulse width of 8 ns. Damage morphologies of samples were observed by Leica-DMRXE Microscope. The stress was measured by viewing the substrate deformation before and after coatings deposition using an optical interferometer. Reflectance of the samples was measured by Lambda 900 Spectrometer. The theoretical results of electric field distributions of the samples were calculate by thin film design software (TFCalc). It was found that SiO2 overcoat had improved the LIDT greatly, while MgF2 overcoat had little effect on the LIDT because of its high stress in the HR coatings. The damage morphologies were different among HR coatings with and without overcoats. (c) 2005 Elsevier B.V. All rights reserved.

High-reflectance 193 nm Al2O3/MgF2 mirrors

Thin-film single layers of Al2O3 and MgF2 were deposited upon super polished fused-silica by electron-beam evaporation. The subsequent optical constants n and k were reported for the spectral range of 180-230 nm. High-reflectance dense multilayer coatings for 193 nm were designed on the basis of the evaluated optical constants and produced. The spectra of the reflectance of HR coatings were compared to the theoretical calculations. HR mirrors of 27 layers with a reflectance of more than 98% were reported. (c) 2004 Elsevier B.V. All rights reserved.

Laser-induced damage of Ta2O5/S1O2 narrow-band interference filters under different 1064 nm Nd : YAG laser modes

The laser-induced damage (LID) behavior of narrow-band interference filters was investigated with a Nd:YAG laser at 1064 nm under single-pulse mode and free-running mode. The absorption measurement of such coatings was performed with surface thermal lensing (STL) technique. The damage morphologies under the two different laser modes were also studied in detail. It was found that all the filters exhibited a pass-band-center-dependent absorption and laser-induced damage threshold (LIDT) behavior, but the damage morphologies were diverse. The explanation was given with the analysis of the electric field distribution and the operational behavior of the irradiation laser. (c) 2005 Elsevier B.V. All rights reserved.

Ta2O5膜在532, 800 和 1064 nm波长的n-on-1体系下的激光损伤阈值研究

Ta2O5膜采用传统的电子束蒸发方法制备，并在氧气中673 K的条件下进行了退火12 h处理。首先在1-on-1体系下对Ta2O5膜进行了532和1064 nm波长下的激光损伤阈值（LIDT） 研究，然后在n-on-1体系下分别对532，800和1064 nm三种波长下的激光损伤阈值进行了研究。结果表明在n-on-1体系下Ta2O5膜在532和1064 nm波长下的阈值均高于1-on-1体系下的阈值。此外，在n-on-1体系下，薄膜的阈值随波长增加而增大。同时发现，在氧气中进行退火对Ta2O5膜的光学性能

Influence of vacuum organic contaminations on laser-induced damage of 1064 nm anti-reflective coatings

We investigate the influence of vacuum organic contaminations on laser-induced damage threshold (LIDT) of optical coatings. Anti-reflective (AR) coatings at 1064 nm made by Ta2O5/SiO2 are deposited by the ion beam sputtering method. The LIDTs of AR coatings are measured in vacuum and in atmosphere, respectively. It is exhibited that contaminations in vacuum are easily to be absorbed onto optical surface because of lower pressure, and they become origins of damage, resulting in the decrease of LIDT from 24.5 J/cm(2) in air to 15.7 J/cm(2) in vacuum. The LIDT of coatings in vacuum has is slightly changed compared with the value in atmosphere after the organic contaminations are wiped off. These results indicate that organic contaminations are the main reason of the LIDT decrease in vacuum. Additionally, damage morphologies have distinct changes from vacuum to atmosphere because of the differences between the residual stress and thermal decomposability of filmy materials.

三倍频分光膜在1064 nm的破斑特性研究

采用电子束蒸发方式制备了两种不同材料组合的分光膜,分别对其在波长1064 nm激光辐照下的损伤阈值进行了测试,用Alpha-Step 500台阶仪对破斑进行了深度测量。实验结果表明,破斑呈现出表面层的剥落和深坑破坏两种形态。表面层的剥落深度在一定范围内不随能量密度的变化而变化；深坑破坏深浅不一,是膜内缺陷融化、汽化及喷发的综合作用的结果,是损伤阈值降低的主要原因。

三硼酸锂晶体上1064 nm, 532 nm, 355 nm三倍频增透膜的设计

采用矢量法设计了三硼酸锂晶体上1064 nm、532 nm和355 nm三倍频增透膜,结果表明1064 nm、532 nm和355 nm波长的剩余反射率分别为0.0017％、0.0002％和0.0013％。根据误差分析,薄膜制备时沉积速率精度控制在＋5.5％时,1064 nm、532 nm和355 nm波长的剩余反射率分别增加至0.20％、0.84％和1.89％。当材料折射率的变化控制在＋3％时,1064 nm处的剩余反射率增大为0.20％,532 nm和355 nm处分别达0.88％和0.24％。与薄膜

Laser-induced damage of Ti O2 Si O2 high reflector at 1064 nm

A high laser-induced damage threshold (LIDT) TiO2/SiO2 high reflector (HR) at 1064 nm is deposited by e-beam evaporation. The HR is characterized by optical properties, surface, and cross section structure. LIDT is tested at 1064 nm with a 12 ns laser pulse in the one-on-one mode. Raman technique and scanning electron Microscope are used to analyze the laser-induced modification of HR. The possible damage mechanism is discussed. It is found that the LIDT of HR is influenced by the nanometer precursor in the surface, the intrinsic absorption of film material, the compactness of the cross section and surface structure, and the homogeneity of TiO2 layer. Three typical damage morphologies such as flat-bottom pit, delamination, and plasma scald determine well the nanometer defect initiation mechanism. The laser-induced crystallization consists well with the thermal damage nature of HR. (C) 2008 American Institute of Physics.

Temperature fields of 355 nm HR coatings based on the interface absorption model

Temperature fields of 355 nm high-reflectance (HR) coatings were investigated based on the interface absorption model. It was found that the highest temperature in the HR coatings increased with an increase in the extinction coefficient of the interface A, B, C, Al2O3 and MgF2. The highest temperature of HR coatings that can be reached increased quickly with the increase in the extinction coefficient of interface A in particular. The temperature rises of 355 nm HR coatings at different layers and different deposition temperatures were investigated based on experiments also. The damage mechanism of 355 nm HR coatings was confirmed with temperature fields and the interface absorption model.