Electron diffraction and photoemission studies of clean and water-covered Si(5,5,12) and Si(112) surfaces

The structure of silicon surfaces in the orientation range (113)-(5,5,12)-(337)-(112) has been investigated using high resolution LEED and photoemission both on a spherical and on flat samples. We find that Si(5,5,12) [5.3 degrees from (113) and 0.7 degrees from (937)] is the only stable orientation between (113) and (111) and confirm the result of Baski et al. [Science 269, 1556 (1995)] that it has a 2 x 1 superstructure with a very large unit cell of 7.68 x 53.5 Angstrom(2). Adsorption measurements of water on Si(5,5,12) yield a mobile precursor kinetics with two kinds of regions saturating at 0.25 and 0.15 ML which are related to adsorption on different sites. Using these results, a modified structure model is proposed. Surfaces between (113) and (5,5,12) separate into facets of these two orientations; between (5,5,12) and (112), they separate into (5,5,12) and (111) facets. (337) facets in this range may be considered as defective (5,5,12) facets.

Morphology Evolution of (331)A High-Index Surfaces During Atomic Hydrogen Assisted Molecular Beam Epitaxy (MBE)

Step like morphology of (331)A high-index surfaces during atomic hydrogen assisted molecular beam epitaxy (MBE) growth has been investigated. Atomic Force Microscope (AFM) measurements show that in conventional MBE, the step heights and terrace widths of GaAs layers increase monotonically with increasing substrate temperatures. The terrace widths and step densities increase with increasing the GaAs layer thickness and then saturates. And, in atomic hydrogen assisted MBE, the terrace width reduces and density increases when depositing the same amount of GaAs. It attributes this to the reduced surface migration length of Ga adatoms with atomic hydrogen. Laterally ordered InAs self-aligned nano-wires were grown on GaAs (331)A surfaces and its optical polarization properties were revealed by photoluminescence measurements.

Fabrication of Novel Superhydrophobic Surfaces and Water Droplet Bouncing Behavior - Part 1: Stable ZnO-PDMS Superhydrophobic Surface with Low Hysteresis Constructed Using ZnO Nanoparticles

A superhydrophobic surface has many advantages in micro/nanomechanical applications, such as low adhesion, low friction and high restitution coefficient, etc. In this paper, we introduce a novel and simple route to fabricate superhydrophobic surfaces using ZnO nanocrystals. First, tetrapod-like ZnO nanocrystals were prepared via a one-step, direct chemical vapor deposition (CVD) approach. The nanostructured ZnO material was characterized by scanning electron microscope (SEM) and X-ray diffraction (XRD) and the surface functionalized by aminopropyltriethoxysilane (APS) was found to be hydrophobic. Then the superhydrophobic surface was constructed by depositing uniformly ZnO hydrophobic nanoparticles (HNPs) on the Poly(dimethylsiloxane) (PDMS) film substrate. Water wettability study revealed a contact angle of 155.4 +/- 2 degrees for the superhydrophobic surface while about 110 degrees for pure smooth PDMS films. The hysteresis was quite low, only 3.1 +/- 0.3 degrees. Microscopic observations showed that the surface was covered by micro- and nano-scale ZnO particles. Compared to other approaches, this method is rather convenient and can be used to obtain a large area superhydrophobic surface. The high contact angle and low hysteresis could be attributed to the micro/nano structures of ZnO material; besides, the superhydrophobic property of the as-constructed ZnO-PDMS surface could be maintained for at least 6 months. (C) Koninklijke Brill NV, Leiden, 2010