Amorphous silicon carbide films prepared by H-2 diluted silane-methane plasma

This paper reports on the preparation and characterization of hydrogenated amorphous silicon carbide films prepared by H-2 diluted silane-methane plasma. Carbon-rich a-SiC:H film with band gap of up to 3.3 eV has been achieved. IR and UV Vis spectra were employed to characterize the chemical bonding and optical properties of as-prepared films. It is shown that hydrogen dilution is crucial in obtaining these wide band gap carbon-rich films. Raman and PL measurements were performed to probe the microstructure and photoelectronic properties of these films before and after annealing. Films with intermediate carbon concentration seem more defective and exhibit stronger photoluminescence and subband absorption than others. Films with different compositions exhibit different annealing behaviours. For silicon rich and carbon rich films, high temperature annealing results in the formation of silicon crystallites and graphite clusters, respectively. (C) 2003 Elsevier B.V. All rights reserved.

Structure, stability and photoelectronic properties of transition films from amorphous to microcrystalline silicon

A series of hydrogenated silicon films near the threshold of crystallinity was prepared by very high frequency plasma enhanced chemical vapor deposition (VHF-PECVD) from a mixture of SiH4 diluted in H, The effect of hydrogen dilution ratios R-H = [H-2]/[SiH4] on microstructure of the films was investigated. Photoelectronic properties and stability of the films were studied as a function of crystalline fraction. The results show that more the crystalline volume fraction in the silicon films, the higher mobility life-time product (mu tau), better the stability and lower the photosensitivity. Those diphasic films contained 8%-31% crystalline volume fraction can gain both the fine photoelectronic properties and high stability. in the diphasic (contained 12% crystalline volume fraction) solar cell, we obtained a much lower light-induced degradation of similar to 2.9%, with a high initial efficiency of 10.01% and a stabilized efficiency of 9.72% (AM1.5, 100 mW/cm(2)). (c) 2005 Elsevier B.V. All rights reserved.

Transition films from amporphous to microcrystalline silicon and solar cells

A series of hydrogenated silicon films near the threshold of crystallinity was prepared by very high frequency plasmaenhanced chemical vapor deposition (VHF-PECVD)from a mixture of SiH4 diluted in H-2. The effect of hydrogen dilution ratios R = [H-2]/[SiH4] on the microstructure of the films was investigated. The photoelectronic properties and stability of the films were studied as a function of crystalline fraction. The results show that the diphasic films gain both the fine photoelectric properties like a-Si: H and high stability like mu w-Si:H. By using the diphasic silicon films as the intrinsic layer, p-i-n junction solar cells were prepared. Current-voltage (J-V) characteristics and stability of the solar cells were measured under an AM1.5 solar simulator. We observed a light-induced increase of 5.2% in the open-circuit voltage (V-oc) and a light-induced degradation of similar to 2.9% inefficiency.

Characterization of silicon carbide thin films and their use in colour sensor

A series of hydrogenated amorphous silicon carbide (a-Si1-xCx:H) films were prepared by plasma-enhanced chemical vapour deposition (PECVD) using a gas mixture of silane, methane, and hydrogen as the reactive source. The previous results show that a high excitation frequency, together with a high hydrogen dilution ratio of the reactive gases, allow an easier incorporation of the carbon atoms into the silicon-rich a-Si1-xCx:H film, widen the valence controllability. The data show that films with optical gaps ranging from about 1.9 to 3.6 eV could be produced. In this work the influence of the hydrogen dilution ratio of the reactive gases on the a-Si1-xCx:H film properties was investigated. The microstuctural and photoelectronic properties of the silicon carbide films were characterized by Rutherford backscattering spectrometry (RBS), elastic recoil detection analysis (ERDA), and FT-IR spectrometry. The results show that a higher hydrogen dilution ratio enhances the incorporation of silicon atoms in the amorphous carbon matrix for carbon-rich a-Si1-xCx:H films. One pin structure was prepared by using the a-Si1-xCx:H film as the intrinsic layer. The light spectral response shows that this structure fits the requirement for the top junction of colour sensor. (c) 2004 Elsevier B.V. All rights reserved.

Light-induced changes in diphasic nanocrystalline silicon films and solar cells

A series of diphasic nanocrystalline silicon films and solar cells was prepared using different hydrogen dilution ratios of silane by very high frequency plasma enhanced chemical vapor deposition (VHF-PECVD). It was observed that after light soaking the open circuit voltage (V-oc) of the diphasic solar cells increased, while that of amorphous silicon solar cells decreased. Raman scattering spectroscopy was performed on the series of diphasic silicon films before and after light soaking. It was found that after light soaking the nanostruclures in the diphasic nanocrystalline silicon films were changed. Both the grain sizes and grain volume fraction reduced, while the grain boundary components increased. These results provide experimental evidence for the conjecture that the light-induced increase in V-oc of the diphasic nanocrystalline solar cells might be induced by the changes in the nanostructure of the intrinsic layer. (c) 2006 Elsevier B.V. All rights reserved.

Heterojunction solar cells with n-type nanocrystalline silicon emitters on p-type c-Si wafers

Hydrogenated nanocrystalline silicon (nc-Si:H) n-layers have been used to prepare heterojunction solar cells on flat p-type crystalline silicon (c-Si) wafers. The nc-Si:H n-layers were deposited by radio-frequency (RF) plasma enhanced chemical vapor deposition (PECVD), and characterized using Raman spectroscopy, optical transmittance and activation energy of dark-conductivity. The nc-Si:H n-layers obtained comprise fine grained nanocrystallites embedded in amorphous matrix, which have a wider bandgap and a smaller activation energy. Heterojunction solar cells incorporated with the nc-Si n-layer were fabricated using configuration of Ag (100 nm)/1T0 (80 nm)/n-nc-Si:H (15 nm)/buffer a-Si:H/p-c-Si (300 mu m)/Al (200 nm), where a very thin intrinsic a-Si:H buffer layer was used to passivate the p-c-Si surface, followed by a hydrogen plasma treatment prior to the deposition of the thin nanocrystalline layer. The results show that heterojunction solar cells subjected to these surface treatments exhibit a remarkable increase in the efficiency, up to 14.1% on an area of 2.43 cm(2). (c) 2006 Elsevier B.V. All rights reserved.

Strain accommodation of 3C-SiC grown on hydrogen-implanted Si (001) substrate

The hydrogen-implanted Si substrate has been used for the fabrication of the "compliant substrate", which can accommodate the mismatch strain during the heteroepitaxy. The compliance of the substrate can be modulated by the energy and dose of implanted hydrogen. In addition, the defects caused by implantation act as the gettering center for the internal gettering of the harmful metallic impurities. Compared with SiC films growth on substrate without implantation. all the measurements indicated that the mismatch strains in the SiC films grown on this substrate have been released and the crystalline qualities have been improved. It is a practical technique used for the compliant substrate fabrication and compatible with the semiconductor industry. (C) 2003 Elsevier B.V. All rights reserved.

Microstructure characterization of transition films from amorphous to nanocrocrystalline silicon

Hydrogenated silicon (Si:H) films near the threshold of crystallinity were prepared by very high-frequency plasma-enhanced chemical vapor deposition (VHF-PECVD) using a wide range of hydrogen dilution R-H = [H-2]/[SiH4] values of 2-100. The effects of H dilution R-H on the structural properties of the films were investigated using micro-Raman scattering and Fourier transform infrared (FTIR) absorption spectroscopy. The obtained Raman spectra show that the H dilution leads to improvements in the short-range order and the medium-range order of the amorphous network and then to the morphological transition from amorphous to crystalline states. The onset of this transition locates between R-H = 30 and 40 in our case, and with further increasing R-H from 40 to 100, the nanocrystalline volume fraction increases from similar to23% to 43%, and correspondingly the crystallite size enlarges from similar to2.8 to 4.4 nm. The FTIR spectra exhibit that with R-H increasing, the relative intensities of both the SiH stretching mode component at 2100 cm(-1) and wagging mode component at 620 cm(-1) increase in the same manner. We assert that these variations in IR spectra should be associated with the formation of paracrystalline structures in the low H dilution films and nanocrystalline structures in the high H dilution films. (C) 2003 Elsevier Science B.V. All rights reserved.

Role of amorphous silicon domains on Er3+ emission in the Er-doped hydrogenated amorphous silicon suboxide film

An investigation on the correlation between amorphous Si (a-Si) domains and Er3+ emission in the Er-doped hydrogenated amorphous silicon suboxide (a-Si:O:H) film is presented. On one hand, a-Si domains provide sufficient carriers for Er3+ carrier-mediated excitation which has been proved to be the highest excitation path for Er3+ ion; on the other hand, hydrogen diffusion from a-Si domains to amorphous silicon oxide (a-SiOx) matrix during annealing has been found and this possibly decreases the number of nonradiative centres around Er3+ ions. This study provides a better understanding of the role of a-Si domains on Er3+ emission in a-Si:O:H films.

Micro-Raman study on hydrogenated protocrystalline silicon films

Good quality hydrogenated protocrystalline silicon films were successfully prepared by radio frequency plasma enhanced chemical vapor deposition (PECVD) with various hydrogen dilution ratios (R = ([H-2]/[SiH4]) from 10 to 100). The photosensitivity of the films is up to 10(6) under the light intensity of 50mW.cm(-2). The microstructure of the films was studied by micro-region Raman scattering spectra at room temperature. The deconvolution of the Raman spectra by Gaussion functions shows that the films deposited under low hydrogen dilution ratios (R < 33) exhibit typical amorphous properties, while the films deposited under high hydrogen dilution ratios (R > 50) possess a diphasic structure, with increasing crystalline volume fraction with R. The size of the crystallites in the diphasic films is about 2.4 mm, which was deduced from the phonon confinement model. The intermediate range order of the silicon film increases with increasing hydrogen dilution ratio.

Structural evaluation of polycrystalline silicon thin films by hot-wire-assisted PECVD

Tungsten wires were introduced into a plasma-enhanced chemical vapor deposition (PECVD) system as a catalyzer: we name this technique 'hot-wire-assisted PECVD' (HW-PECVD). Under constant deposition pressure (p(g)), gas flow ratio and catalyzer position, the effects of the hot wire temperature (T-f) on the structural properties of the poly-Si films have been characterized by X-ray diffraction (XRD), Raman scattering and Fourier-transform infrared (FTIR) spectroscopy. Compared with conventional PECVD, the grain size, crystalline volume fraction (X-e) and deposition rate were all enhanced when a high T-f was used. The best poly-Si film exhibits a preferential (220) orientation, with a full width at half-maximum (FWHM) of 0.2 degrees. The Si-Si TO peak of the Raman scattering spectrum is located at 519.8 cm(-1) with a FWHM of 7.1 cm(-1). The X-c is 0.93. These improvements are mainly the result of promotion of the dissociation of SiH4 and an increase in the atomic H concentration in the gas phase. (C) 2001 Elsevier Science B.V. All rights reserved.

Gap states of hydrogenated amorphous silicon near and above the threshold of microcrystallinity with subtle boron compensation

The effects of hydrogen dilution, subtle boron compensation, and light-soaking on the gap states of hydrogenated amorphous silicon films (a-Si:H) near and above the threshold of microcrystallinity have been investigated in detail by the constant photocurrent method and the improved phase-shift analysis of modulated photocurrent technique. It is shown that high hydrogen dilution near the threshold of microcrystallinity leads to a more ordered network structure and to the redistribution of gap states; it gives rise to a small peak at about 0.55 eV and a shoulder at about 1.2 eV below the conduction band edge, which are associated with the formation of microcrystallites embedded in the amorphous silicon host matrix. A concurrent subtle boron compensation is demonstrated to prevent excessive formation of microcrystallinity, and to help promote the growth of the ordered regions and reduce the density of gap defect states, particularly those associated with microcrystallites. Hydrogen-diluted and appropriately boron-compensated a-Si:H films deposited near the threshold of microcrystallinity show the lowest density of the defects in both the annealed and light-soaked states, and hence, the highest performance and stability. (C) 2001 American Institute of Physics.

Hydrogenated amorphous silicon films with significantly improved stability

A new regime of plasma-enhanced chemical-vapor deposition (PECVD), referred to as "uninterrupted growth/annealing" method, has been proposed for preparation of high-quality hydrogenated amorphous silicon (a-Si:H) films. By using this regime, the deposition process no longer needs to be interrupted, as done in the chemical annealing or layer by layer deposition, while the growing surface is continuously subjected to an enhanced annealing treatment with atomic hydrogen created in the hydrogen-diluted reactant gas mixture at a relatively high plasma power. The intensity of the hydrogen plasma treatment is controlled at such a level that the deposition conditions of the resultant films approach the threshold for microcrystal formation. In addition, a low level of B-compensation is used to adjust the position of the Fermi level close to the midgap. Under these conditions, we find that the stability and optoelectronic properties of a-Si:H films have been significantly improved. (C) 2001 Elsevier Science B.V. All rights reserved.

Hydrogen-dependent lattice dilation in GaN

Using Raman spectroscopy we have analysed the strain status of GaN films grown on sapphire substrates by NH3 source molecular beam epitaxy (MBE). In addition to the expected compressive biaxial strain, in some cases GaN films grown on c-face sapphire substrates suffer from serious tensile biaxial strain. This anomalous behaviour has been well interpreted in terms of interstitial hydrogen-dependent lattice dilation. The hydrogen concentration in the films is measured by nuclear reaction analysis (NRA). With increasing hydrogen incorporation, the residual compressive biaxial strain is first further relaxed, and then turns into tensile strain when the hydrogen contaminant exceeds a critical concentration. The hydrogen incorporation during the growth process is found to be growth-rate dependent, and is supposed to be strain driven. We believe that the strain-induced interstitial incorporation is another way for strain relaxation during heteroepitaxy, besides the two currently well known mechanisms: formation of dislocations and growth front roughening.

The new exploration for proton-implanted silicon: the conversion of a surface-region-purification-induced p-n junction into a p-i-n electrical structure approaching silicon on insulator

A surface-region-purification-induced p-n junction, a puzzle discovered at Brookhaven National Laboratory, in a silicon-on-defect-layer (SODL) material has been explored by carrying out various annealing conditions and subsequent measurements on electrical properties. The origin of the pn junction has been experimentally investigated. Furthermore, the p-n junction has been transformed into a p-i-n electrical structure by adding a high temperature annealing process to the previously used SODL procedure, making the SODL material approach silicon on insulator (SOI). The control of the initial oxygen amount in the silicon material is suggested to be critical for the experimental results.