The effects of substrate temperature on the structure and properties of ZnO films prepared by pulsed laser deposition

ZnO thin films were prepared by pulsed laser deposition (PLD) on glass substrates with growth temperature from room temperature (RT) to 500 degrees C. The effects of substrate temperature on the structural and optical properties of ZnO films have been investigated by X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission spectra, and RT photoluminescence (PL) measurements. The results showed that crystalline and (0 0 2)-oriented ZnO films were obtained at all substrate temperatures. As the substrate temperature increased from RT to 500 degrees C, the ratio of grain size in height direction to that in the lateral direction gradually decreased. The same grain size in two directions was obtained at 200 degrees C, and the size was smallest in all samples, which may result in maximum E, and E-0 of the films. UV emission was observed only in the films grown at 200 degrees C, which is probably because the stoichiometry of ZnO films was improved at a suitable substrate temperature. It was suggested that the UV emission might be related to the stoichiometry in the ZnO film rather than the grain size of the thin film. (c) 2007 Elsevier Ltd. All rights reserved.

Role of edge dislocation and Si impurity in linking the blue luminescence and yellow luminescence in n-type GaN films

A close relationship is found between the blue and yellow luminescence bands in n-type GaN films, which are grown without intentional acceptor doping. The intensity ratio of blue luminescence to yellow luminescence (I-BL/I-YL) decreases with the increase in edge dislocation densities as demonstrated by the (102) full width at half maximum of x-ray diffraction. In addition, the I-BL/I-YL ratio decreases with the increase in Si doping. It is suggested that the edge dislocation and Si impurity play important roles in linking the blue and yellow luminescence.

Electron spin quantum beats and room temperature g factor in GaAsN

We report on the investigation of electron spin quantum beats at room temperature in GaAsN thin films by time-resolved Kerr rotation technique. The measurement of the quantum beats, which originate from the Larmor precession of electron spins in external transverse magnetic field, yields an accurate determination of the conduction electron g factor. We show that the g factor of GaAs1-xNx thin films is significantly changed by the introduction of a small nitrogen fraction.

Growth behavior of AlInGaN films

The structural and surface properties of AlInGaN quaternary films grown at different temperatures on GaN templates by metalorganic chemical vapor deposition are investigated. Formation of two quaternary layers is confirmed and the difference between them is pronounced when the growth temperature is increased. The surface is featured with V-shaped pits and cracks, whose characteristics are further found to be strongly dependent on the growth temperature of AlInGaN layers. The two-layer structure is interpreted by taking into account of the strain status in AlInGaN layers. (C) 2008 Elsevier B.V. All rights reserved.

Valence band offset of InN/4H-SiC heterojunction measured by x-ray photoelectron spectroscopy

The valence band offset (VBO) of InN/4H-SiC heterojunction has been directly measured by x-ray photoelectron spectroscopy. The VBO is determined to be 0.55 +/- 0.23 eV and the conduction band offset is deduced to be -2.01 +/- 0.23 eV, indicating that the heterojunction has a type-I band alignment. The accurate determination of the valence and conduction band offsets is important for applications of InN/SiC optoelectronic devices.

Structural and optical properties of ZnO thin films on glass substrate grown by laser-ablating Zn target in oxygen atmosphere

C-axis-orientated ZnO thin films were prepared on glass substrates by pulsed-laser deposition (PLD) technique in an oxygen-reactive atmosphere, using a metallic Zn target. The effects of growth condition such as laser energy and substrate temperature on the structural and optical properties of ZnO films had been investigated by X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission spectra and room-temperature (RT) photoluminescence (PL) measurements. The results showed that the thickness, crystallite size, and compactness of ZnO films increased with the laser energy and substrate temperature. Both the absorption edges and the UV emission peaks of the films exhibited redshift, and UV emission intensity gradually increased as the laser energy and substrate temperature increased. From these results, it was concluded that crystalline quality of ZnO films was improved with increasing laser energy and substrate temperature. (c) 2007 Elsevier B.N. All rights reserved.

Improved field emission properties from metal-coated diamond films

Diamond films were prepared by microwave plasma chemical vapor deposition (MWPCVD). In order to obtain better field emission properties, the samples coated with different metals were prepared. The results showed that the field emission properties of diamond coated with metals could be greatly improved in comparison to pure diamond film and the different kinds of coated metals have different influences on the field emission properties. The possible reasons of effects on the field emission properties are discussed, which were probably due to the reduced effective surface work function by metal coatings; but the detail of the mechanism should be studied further. The surface morphology and microstructure of the sample were characterized by Atomic Force Microscope (AFM), X-ray photoelectron spectroscopy (XPS), X-ray Diffraction (XRD) and Raman spectrum tests. (c) 2006 Elsevier B.V. All rights reserved.

Photoluminescence of Mg-doped GaN grown by metalorganic chemical vapor deposition

Two Mg-doped GaN films with different doping concentrations were grown by a metalorganic chemical vapor deposition technique. Photoluminescence (PL) experiments were carried out to investigate the optical properties of these films. For highly Mg-doped GaN, the PL spectra at 10 K are composed of a blue luminescence (BL) band at 2.857 eV and two excitonic luminescence lines at 3.342 eV and 3.282 eV, in addition to a L2 phonon replica at 3.212 eV. The intensity of the L1 line decreases monotonously with an increase,in temperature. However, the intensity of the L2 line first slowly increases at first, and then decreases quickly with an increase in temperature. The two lines are attributed to bound excitonic emissions at extended defects. The BL band is most likely due to the transition from deep donor Mg-V-N complex to Mg shallow acceptor. From the temperature dependence of the luminescence peak intensity of the BL band, the activation energy of acceptor Mg was found to be 290 meV. (C) 2003 American Vacuum Society.

Growth mode and strain evolution during InN growth on GaN(0001) by molecular-beam epitaxy

Epitaxial growth of InN on GaN(0001) by plasma-assisted molecular-beam epitaxy is investigated over a range of growth parameters including source flux and substrate temperature. Combining reflection high-energy electron diffraction (RHEED) and scanning tunneling microscopy (STM), we establish a relationship between film growth mode and the deposition condition. Both two-dimensional (2D) and three-dimensional (3D) growth modes of the film are observed. For 2D growth, sustained RHEED intensity oscillations are recorded while STM reveals 2D nucleation islands. For 3D growth, less than three oscillation periods are observed indicating the Stranski-Krastanov (SK) growth mode of the film. Simultaneous measurements of (reciprocal) lattice constant by RHEED suggest a gradual relaxation of the strain in film, which commences during the first bilayer (BL) deposition and almost completes after 2-4 BLs. For SK growth, 3D islanding initiates after the strain has mostly been relieved, presumably by dislocations, so the islands are likely strain free. (C) 2002 American Institute of Physics.

Exciton localization in In0.15Ga0.85As/GaAs quantum wire structures grown on (553)B-oriented GaAs substrate

Using time-resolved photoluminescence (PL) measurements, we have studied the exciton localization effect in InGaAs/GaAs quantum wire (QWR) structures formed in corrugated narrow InGaAs/GaAs quantum wells (QWs) grown on (553)B GaAs substrate. The PL decay time in the QWR structure was found to be independent of the temperature for T < 70 K, showing a typical dynamical behavior of the localized excitons. This result is in striking contrast to the corresponding quantum well structures, where a linear increase of the PL decay time was observed. In addition, an increase of the exciton lifetime was observed at low temperature for the QWR structure as compared to a reference InGaAs/GaAs quantum well sample (1200 vs 400 ps). The observed longer decay time was attributed to the reduction in the spatial coherence of excitons in the QWR-like structure. In PL measurements, a significant polarization anisotropy was also found in our narrow InGaAs/GaAs QWs grown on (553)B GaAs. (C) 2001 American Institute of Physics.

Experimental investigation of photoluminescence dynamics of cavity polaritons under nonresonant excitation

Low-temperature time-resolved photoluminescence (PL) experiments have been performed on a semiconductor planar microcavity, which contains two sets of three In0.13Ga0.87As/GaAs quantum wells embedded in a 3 lambda /2 GaAs cavity. The spontaneous emission dynamics of both lower- and upper-branch polaritons is investigated as a function of exciton-cavity detuning under nonresonant optical excitation. It is found that the PL decay times of both branches are independent of cavity detuning while the PL rising kinetics of the lower- and upper-branch polaritons exhibits a significant difference. The rise time of the upper polarition branch shows a strong dependence on cavity detuning, while the rise time of the lower polarition branch is less sensitive to cavity detuning. Our results can be well understood in the framework of the theoretical prediction of Tassone et al.

Annealing-induced evolution of defects in low-temperature-grown GaAs-related materials

Infrared absorption spectroscopy, optical transient current spectroscopy (OTCS), and photoluminescence (PL) spectroscopy are used to investigate the annealing induced evolution of defects in low-temperature (LT)-grown GaAs-related materials. Two LT samples of bulk GaAs (sample A) and GaAs/AlxGa1-xAs multiple-quantum-well. (MQW) structure (sample B) were grown at 220 and 320 degreesC on (001) GaAs substrates, respectively. A strong defect-related absorption band has been observed in both as-grown samples A and B. It becomes weaker in samples annealed at temperatures above 600 degreesC. In sample A, annealed in the range of 600-800 degreesC, a large negative decay signal of the optical transient current (OTC) is observed in a certain range of temperature, which distorts deep-level spectra measured by OTCS, making it difficult to identify any deep levels. At annealing temperatures of 600 and 700 degreesC, both As-Ga antisite and small As cluster-related deep levels are identified in sample B. It is found that compared to the As cluster, the As-Ga antisite has a larger activation energy and carrier capture rate. At an annealing temperature of 800 degreesC, the large negative decay signal of the OTC is also observed in sample B. It is argued that this negative decay signal of the OTC is related to large arsenic clusters. For sample B, transient PL spectra have also been measured to study the influence of the, defect evolution on optical properties of LT GaAs/AlxGa1-xAs MQW structures. Our results clearly identify a defect evolution from AS(Ga) antisites to arsenic clusters after annealing.

Strong temperature dependence of photoluminescence properties in visible InAlAs quantum dots

Strong temperature dependence of optical properties has been studied in visible InAlAs/AlGaAs quantum dots, by employing photoluminescence (PL) and time-resolved photoluminescence (TRPL) measurements. The fast redshift of the exciton emission peak was observed at much lower temperature range compared to that observed in the InAs/GaAs QDs. In TRPL we did not observe the constant decay time even at low temperature. Instead, the observed decay time increases quickly with increasing temperature, showing 2D properties in the transient dynamic process. We attributed our results to the strong lateral coupling effect, which results in the formation of the local minibands or extended states from the discrete energy levels. (C) 2000 Elsevier Science B.V. All rights reserved.

Steady and transient optical properties of cubic InGaN epilayers

Photoluminescence (PL) and time-resolved PI, were employed to study the steady and transient optical properties of cubic InxGa1-xN epilayers grown by MBE. The results suggest that the PL transitions in InGaN epilayers are mainly from localized exciton states. The localization energies are estimated to be 60 meV, independent of In composition. The PL decay is characterized by a hi-exponential dependence. The fast process (50 ps at 12K) is related to the fast relaxation of excitons, while a slower contribution (200-270 ps at 12K) is attributed to the decay process of localized excitons.