Dielectric properties of Bi2Ti2O7 films grown on Si(100) substrate by APMOCVD

The growth of Bi2Ti2O7 films with (111) orientation on Si(100) substrate by atmospheric pressure metal-organic chemical vapor deposition(APMOCVD) technique at 480similar to550 degreesC is presented. The films were characterized by X-ray diffraction analysis, atomic force microscopy and electron diffraction. The results show high quality Bi2Ti2O7 films with smooth shinning surface. The dielectric properties and C-V characterization of the films were studied. The dielectric constant (epsilon) and loss tangent (tgdelta) were found to be 180 and 0.01 respectively. The charge storage density was 31.9fC/mum(2). The resistivity is higher than 1x10(12) Omega. .cm under the applied voltage of 5V. The Bi2Ti2O7 films are suitable to be used as a new insulating gate material in dynamic random access memory (DRAM).

Impact of wide bandgap p-type nc-Si on the performance of a-Si solar cells

This paper reports the impact of a wide bandgap p-type hydrogenated nanocrystalline silicon (nc-Si:H) on the performances of hydrogenated amorphous silicon (a-Si:H) based solar cells. The player consists of nanometer-sized Si crystallites and has a wide effective bandgap determined mainly by the quantum size-confinement effect (QSE). By incorporation of this p-layer into the devices we have obtained high performances of a-Si:H top solar cells with V-infinity=1.045 V and FF=70.3 %, and much improved mid and bottom a-SiGe:H cells, deposited on stainless steel (SS) substrate. The effects of the band-edge mismatch at the p/i-interface on the I-V characteristics of the solar cells arc discussed on the bases of the density-functional approach and the AMPS model.

Origin of negative differential resistance and memory characteristics in organic devices based on tris(8-hydroxyquinoline) aluminum

Negative differential resistance (NDR) and memory phenomenon have been realized in current-voltage (I-V) characteristics of indium tin oxide/tris(8-hydroxyquinoline) aluminum/aluminum devices. The I-V curves have been divided into three operational regions that are associated with different working regimes of the devices: (i) bistable region, (ii) NDR region, and (iii) monotonic region. The bistable region disappeared after a couple of voltage sweeps from zero to a positive voltage. The bistable nature can be reinstated by applying a suitable negative voltage.

Realization of negative differential resistance and switching devices based on copper phthalocyanine by the control of evaporation rate

We have observed, respectively, a negative differential resistance (NDR) and switching conduction in current-voltage (I-V) characteristics of organic diodes based on copper phthalocyanine (CuPc) film sandwiched between indium-tin-oxide (ITO) and aluminum (Al) by controlling the evaporation rate. The NDR effect is repeatable which can be well, controlled by sweep rate and start voltage, and the switching exhibits write-once-read-many-times (WORM) memory characteristics. The traps in the organic layer and interfacial dipole have been used to explain the NDR effect and switching conduction. This opens up potential applications for CuPc organic semiconductor in low power memory and logic circuits.

Investigation of sandwiched gadolinium(III) complexes with tungstosilicates as potential MRI contrast agents

Two gadolinium-sandwiched complexes with tungstosilicates, K-13[Gd(SiW11O39)(2)] (Gd(SiW11)(2)) and K11H6[Gd2O3(SiW9O34)(2)] (Gd-3(SiW9)(2)), have been investigated by in vitro and in vivo experiments as potential contrast agents for magnetic resonance imaging (MRI). T-1-relaxivity of Gd(SiW11)(2)was 6.59 mM(-1) . s(-1) in aqueous solution and 6.85 mM(-1) . s(-1) in 0.725 mmol . L-1 bovine serum albumin solution at 25degreesC and 9.39 T, respectively. The corresponding T-1-relaxivity of Gd-3(SiW9)(2) was 12.6 and 19.3 mM(-1) . s(-1) per Gd, respectively. MRI for Sprague-Dawley rats showed longer and more remarkable enhancement in rat liver after i.v. injection of these two complexes: 39.4 +/- 3.9% and 57.4 +/- 11.6% within the first 30 min after injection, 31.2 +/- 2.6% and 39.9 +/- 7.6% in the next 60 min for Gd(SiW11)(2) and Gd-3(SiW9)(2) at doses of 0.081 and 0.084 mmol Gd/kg, respectively. Our preliminary in vitro and in vivo study indicates that Gd(SiW11)(2) and Gd-3(SiW9)(2) are favorable candidates for hepatic contrast agents for MRI. However, the two complexes exhibit higher acute toxicity and need to be modified and studied further before clinical use.

Synthesis and evaluation of novel polysaccharide-Gd-DTPA compounds as contrast agent for MRI

Macromolecular conjugates of two kinds of natural polysaccharides, that from Panax quinquefolium linn (PQPS) and Ganoderma applanatum pat (GAPS), with gadolinium-diethylenetriaminepenta-acetic acid (Gd-DTPA) have been synthesized and characterized by means of FTIR, elementary analysis and ICP-AES. Their stability was investigated by competition study with Ca2+, EDTA (ethylenediaminetetraacetic acid) and DTPA. Polysaccharide-bound complexes exhibit T-1 relaxivities of 1.5-1.7 times that of Gd-DTPA in D2O at 25degreesC and 9.4T. MR imaging of Sprague-Dawley (SD) rats showed remarkable enhancement in rat liver and kidney after i.v. injection of these two complexes: liver parenchyma 60.9+/-5.6%, 57.8+/-7.4% at 65-85 min; kidney 144.9+/-14.5%, 199.9+/-25.4% at 10-30 min for PQPS-GdDTPA, GAPS-Gd-DTPA at gadolinium dose of 0.083 and 0.082 mmol/kg, respectively. Our preliminary in vivo and in vitro study indicates that the two kinds of polysaccharide-bound complexes are potential tissue-specific contrast agents for MRI.

Effects of the morphologies and structures of light-emitting layers on the performance of organic electroluminescent devices

Organic electroluminescent devices with a structure of ITO/ploy (9-vinylcarbazole)/tris (8-hydroxyquinoline) aluminum (Alq3)/Mg:Ag are fabricated at different substrate temperatures (77, 298, and 438 K) during Alq3 deposition. It is found that the surface morphologies of Alq3 thin films greatly affect the I-V characteristics of the devices by the contact area between metal cathode and light-emitting layer. There is an increase in the luminous efficiency of the devices in the order 77 K < 298 K < 438 K. We attribute this trend to different structures of Alq3 thin films. (C) 2001 American Institute of Physics.

Effects of La3+ and Gd3+ on Ca2+ influx in rat hepatoma H-35 cells

Effects of La3+ and Gd3+ on Ca2+ influx were investigated in rat hepatoma H-35 cells by measuring the initial rate of Ca-45(2+) uptake. It was found that the maximum initial rate of Ca2+ uptake was increased six- to ten-fold at low concentrations of La3+ and Gd3+. Kinetic analyses by measuring the initial rate of Ca2+ influx at different external Ca2+ concentrations indicated the existence of two intracellular exchangeable components in the basal Ca2+ system, with low and high affinities for Ca2+, and only one class of Ca2+ binding sites was observed in the La3+- or Gd3+-treated cells. For high affinity, La3+ and Gc(3+) increased both kinetic parameters K-m and V-max of basal Ca2+ influx. La3+ and Gd3+ compete directly with Ca2+ for Ca2+ binding site for low affinity. The kinetics is competitive.

Electrochemical preparation of microelectrodes modified with non-stoichiometric mixed-valent molybdenum oxides

A compact non-stoichiometric molybdenum (VI, V) oxide of blue film was grown on carbon fiber (CF) microelectrode surface be cycling the potential between + 0.2V and - 0.70V in a freshly prepared Na2MoO4 solution containing 5 x 10(-3) mol/L H2SO4. The quantity-of the oxide is controlled by the charge passing the electrode. The electrochemical pretreatment of CF microelectrode not only mises the deposition velocity of molybdenum oxide on CF surface, but also improves greatly the cyclic voltammetric behavior of the molybdenum oxide film prior to the electrodeposition. The cathodic processes are believed to yield the hydrogen molybdenum oxide bronzes HxMoO3(0 < x < 2), or substoichiometric lower molybdenum oxides with the formula MoO3-y(0 < y < 1). The anodic response results from the reversible oxidation of molybdenum bronze/Mo(V) centers [or perhaps Mo(IV) in more reduced coatings], to Mo(VI). Further information was gained about the chemical composition and valent state of Mo from XPS and SEM.

One step isolation and purification of liquiritigenin and isoliquiritigenin from Glycyrrhiza uralensis Risch using high-speed counter-current chromatography

High-speed counter-current chromatography (HSCCC) technique in semi-preparative scale has been successfully applied to the separation of bioactive flavonoid compounds, liquiritigenin and isoliquiritigenin in one step from the crude extract of Glycyrrhiza uralensis Risch. The HSCCC was performed using a two-phase solvent system composed of n-hexane-ethyl acetate-methanol-acetonitrile-water (2:2:1:0.6:2, v/v). Yields of liquiritigenin (98.9% purity) and isoliquiritigenin (98.3% purity) obtained were 0.52% and 0.32%. Chemical structures of the purified liquiritigenin and isoliquiritigenin were identified by electrospray ionization-MS (ESI-MS) and NMR analysis. (c) 2005 Published by Elsevier B.V.

The study of oxygen spillover and back spillover on Pt/TiO2 by a potential dynamic sweep method

Oxygen spillover and back spillover on Pt/TiO2 catalysts have been studied by a potential dynamic sweep method. The characteristics of I-V profiles of Pt/TiO2 electrodes in the three potential sweep regions are different from those of Pt and TiO2 electrodes. The catalytic role of Pt/TiO2 in oxygen spillover and back spillover is identified. It decreases, and the electrochemical oxygen adsorption (or desorption) increases with elevating temperature of hydrogen post-treatment of Pt/TiO2; to a certain extent (hydrogen post-treatment of Pt/TiO2 at 700 degrees C), the control step of oxygen electrode process (anodic oxidation or cathodic reduction) changes from oxygen diffusion to electrochemical oxygen adsorption or desorption, respectively. Increasing the amount of Pt supported on TiO2 enhances the processes of oxygen spillover and back spillover. (C) 1999 Elsevier Science B.V. All rights reserved.