THE EFFECT OF PASSIVATION OF BORON DOPANTS BY HYDROGEN IN NANO-CRYSTALLINE AND MICROCRYSTALLINE SILICON FILMS

It is well known that the value of room-temperature conductivity sigma(RT) of boron-doped silicon films is one order lower than that of phosphorus-doped silicon films, when they are deposited in an identical plasma-enhanced chemical vapour deposition system. We use surface acoustic wave and secondary-ion mass spectrometry techniques to measure the concentration of total and electrically active boron atoms. It is shown that only 0.7% of the total amount of incorporated boron is electrically active. This is evidence that hydrogen atoms can passivate substitutional B-Si bonds by forming the neutral B-H-Si complex. By irradiating the boron-doped samples with a low-energy electron beam, the neutral B-H-Si complex converts into electrically active B-Si bonds and the conductivity can be increased by about one order of magnitude, up to the same level as that of phosphorus-doped samples.

REDUCTION OF CRYSTALLINE DISORDER IN MOLECULAR-BEAM EPITAXY GAAS ON SI BY MEV ION-IMPLANTATION AND SUBSEQUENT ANNEALING

Molecular beam epitaxy GaAs films on Si, with thicknesses ranging from 0.9-2.0-mu-m, were implanted with Si ions at 1.2-2.6 MeV to doses in the range 10(15)-10(16) cm-2. Subsequent rapid infrared thermal annealing was carried out at 850-degrees-C for 15 s in a flowing N2 atmosphere. Crystalline quality was analyzed by using Rutherfold backscattering/channeling technique and Raman scattering spectrometry. The experimental results show that the recrystallization process greatly depends on the dose and energy of implanted ions. Complete recrystallization with better crystalline quality can be obtained under proper implantation and subsequent annealing. In the improved layer the defect density was much lower than in the as-grown layer, especially near the interface.

SPECTROSCOPIC INVESTIGATION OF HYDROGEN-DOPANT COMPLEXES IN BULK P-TYPE AND IMPLANTED N-TYPE CRYSTALLINE SILICON

Infrared absorption experiments have been performed on hydrogenated and deuterated bulk boron- and aluminum-doped-Si and implanted P, As, and Sb donors in silicon. A first evidence of complex formation in bulk p-type Si is obtained and the spectra confirm the anomalous 3.3-cm-1 deuterium frequency shift with respect to boron isotopes. The ratio of the D-B-11 and D-B-10 peak areas is found to be the same as that of the two boron isotopes natural abundance. In donor-implanted silicon, a quantitative analysis of the obtained data has allowed a rough estimate of the passivating rate due to diffusing deuterium. While the frequencies of the various vibrational lines are found to be in agreement with those reported in the literature, the data on the broad line at 1660 cm-1 (H) or 1220 cm-1 (D) seem to suggest an assignment of this peak to a complex in the bulk involving some type of defect due to the implantation process.

Behavior of crystalline silicon under huge electronic excitations: A transient thermal spike description

Recent experimental works devoted to the phenomena of mixing observed at metallic multilayers Ni/Si irradiated by swift heavy ions irradiations make it necessary to revisit the insensibility of crystalline Si under huge electronic excitations. Knowing that Ni is an insensitive material, such observed mixing would exist only if Si is a sensitive material. In order to extend the study of swift heavy ion effects to semiconductor materials, the experimental results obtained in bulk silicon have been analyzed within the framework of the inelastic thermal spike model. Provided the quenching of a boiling ( or vapor) phase is taken as the criterion of amorphization, the calculations with an electron-phonon coupling constant g(300 K) = 1.8 x 10(12) W/cm(3)/K and an electronic diffusivity D-e(300 K) = 80 cm(2)/s nicely reproduce the size of observed amorphous tracks as well as the electronic energy loss threshold value for their creation, assuming that they result from the quenching of the appearance of a boiling phase along the ion path. Using these parameters for Si in the case of a Ni/Si multilayer, the mixing observed experimentally can be well simulated by the inelastic thermal spike model extended to multilayers, assuming that this occurs in the molten phase created at the Ni interface by energy transfer from Si. (C) 2009 Elsevier B. V. All rights reserved.

Surface morphology of He-implanted single-crystalline silicon

Single-crystalline Si (100) samples were implanted with 30 keV He2+ ions to doses ranging from 2.0x10(16) to 2.0x10(17) ions/cm(2) and subsequently thermally annealed at 800 degrees C for 30min. The morphological change of the samples with the increase of implantation dose was investigated using atomic force microscopy (AFM). It was found that oblate-shaped blisters with an average height around 4.0nm were found on the 2.0 x 10(16) ions /cm(2) implanted sample surface; spherical-shaped blisters with an average height wound 10.0nm were found on the 5.0 x 10(16) ions/cm(2) implanted sample surface; strip-shaped and conical cracks were observed on the sample He-implanted to a dose of 1.0 X 10(17) ions /cm(2). Exfoliations occurred on the sample surface to a dose of 2.0 x10(17) ions /cm(2). Mechanisms underlying the surface change were discussed.