Time-resolved photoluminescence spectra of self-assembled InAs/GaAs quantum dots

Two types of InAs self-assembled Quantum dots (QDs) were prepared by Molecular beam epitaxy. Atomic force microscopy (AFM) measurements showed that, compared to QDs grown on GaAs substrate, QDs grown on InGaAs layer has a significantly enhanced density. The short spacing (several nanometer) among QDs stimulates strong coupling and leads to a large red-shift of the 1.3 mu m photoluminescence (PL) peak. We study systematically the dependence of PL lifetime on the QDs size, density and temperature (1). We found that, below 50 K, the PL lifetime is insensitive to temperature, which is interpreted from the localization effects. As T increases, the PL lifetime increases, which can be explained from the competition between the carrier redistribution and thermal emission at higher temperature. The increase of carriers in QDs migrated from barriers and wetting layer (WL), and the redistribution of carriers among QDs enhance the PL lifetime as T increases. The thermal emission and non-radiative recombination have effects to reduce the PL lifetime at higher T. As a result, the radiative recombination lifetime is determined by the wave function overlapping of electrons and holes in QDs, and QDs with different densities have different PL lifetime dependence on the QDs size. (c) 2005 Elsevier B.V. All rights reserved.

Mutual passivation of donors and isovalent nitrogen in GaAs

We study the mutual passivation of shallow donor and isovalent N in GaAs. We find that all the donor impurities, Si-Ga, Ge-Ga, S-As, and Se-As, bind to N in GaAsN, which has a large N-induced band-gap reduction relative to GaAs. For a group-IV impurity such as Si, the formation of the nearest-neighbor Si-Ga-N-As defect complex creates a deep donor level below the conduction band minimum (CBM). The coupling between this defect level with the CBM pushes the CBM upwards, thus restoring the GaAs band gap; the lowering of the defect level relative to the isolated Si-Ga shallow donor level is responsible for the increased electrical resistivity. Therefore, Si and N mutually passivate each other's electrical and optical activities in GaAs. For a group-VI shallow donor such as S, the binding between S-As and N-As does not form a direct bond; therefore, no mutual passivation exists in the GaAs(S+N) system.