Influence of structure and lonic radius on solubility limit in the Mg-Re systems

The relationship between structure, ionic radius and electronegativity and solubility of the various rare-earth elements in Mg was studied. It is found that light RE(La-Sm, Eu, Yb) have more complicated phase relation with Mg but the heavy RE(Gd-Lu, Sc) have the similar crystal structure with magnesium. Also it is found that the less electronegativity difference between Mg and RE is, the more solubility limit of RE in Mg is. The fact of the RE solubility decreased in magnesium with lowering temperature suggests that there is a possibility of Mg supersaturated solid solution formation and it will decomposition during aging. According to the rule, an megnesium alloy with higher strength feature was developed. Their mechanical properties are UTS 347MPa, YTS 290MPa and elongation 12.5% at room temperature.

基质晶体的真空紫外光谱研究

初步总结了基质晶体中吸收带位置的规律 ,即氧化物 (CaO∶Eu ,Y2 O3∶Eu ,≈ 2 0 0nm) >多铝酸盐 (BaMgAl1 0 O1 7∶Eu ,≈ 175nm)≥硅酸盐 (Ca2 SiO4 ∶Tb ,160～ 170nm) >硼酸盐 [(Y ,Gd)BO3∶Eu ,15 0～ 160nm]≥钒酸盐 (YVO4 ∶Eu ,≈ 15 5nm)≈正磷酸盐 [(La,Gd)PO4 ∶Eu ,≈ 15 5nm] >五磷酸盐 (TbP5O1 4∶Eu ,≈ 13 5nm) >二磷酸盐 [Sr3(PO4 ) 2 ∶Eu或K3Tb(PO4 ) 2 ∶Eu ,≈ 12 5nm] >氟化物 (LaF3∶Eu或LiYF4 ∶Eu ,≈ 12 0nm)。基质吸收带的位置主要取决于基质的阴离子、阴离子基团 ,以及基质的组成、结构和键能 ,也受基质中阳离子的影响。这一初步规律将有助于人们寻找优质的新型紫外晶体和新型等离子体平板显示器件用的荧光粉。

液相法在Gd2O3:Eu表面包覆SiO2的研究

采用液相法成功的在球形Gd2O3:Eu 荧光粉颗粒表面包覆一层纳米SiO2 保护膜。扫描电镜分析可见包覆SiO2 后颗粒粒径略微变大说明表面包覆一层纳米级的包覆层。XPS 分析表明：SiO2 包覆层与Gd2O3:Eu颗粒表面以Gd(Eu)-O-Si 化学键的方式键合在一起的。荧光光谱分析表明：包覆后的Gd2O3:Eu3+颗粒仍旧是一种很好的发光材料。

Synthesis and characterization of SiO2/Gd2O3 : Eu core-shell luminescent materials

Europium-doped Gd2O3 with an average size of similar to15 nm was coated on the surface of preformed silica nanospheres by the wet chemical method. SEM and TEM photographs showed that SiO2/Gd2O3:Eu core-shell submicrospheres are obtained. XRD patterns indicated that the Gd2O3:Eu shell is crystalline after heat treatment. FTIR and XPS spectra showed that the Gd2O3:Eu shell is linked to the silica surface by forming a Si-O-Gd bond. Photoluminescence studies showed that the luminescent properties are still retained after coating on an inert silica core; additionally, we noted that the emitting peaks are broadened, which results from size effects and interface effects of nanocrystal.

Fabrication, structure and conductivity of hybrid organic/inorganic Langmuir-Blodgett films of polyquinoline/octadecylamine/rare earth-substituted heteropolyanion

Three kinds of hybrid organic/inorganic Langmuir-Blodgett films are obtained by the compact organization of poly (1, 2-dihydro-2,2,4-trimethyl)quinoline (abridged as PQ), octadecylamine(abridged as OA) and rare earth-substituted heteropolyanions [abridged as RE(PW11,)(2), RE=Ce-II, Eu-II, Gd-II] using the Langmuir-Blodgett technique. They are characterized by the pi-A isotherms, the absorption spectra, the fluorescence spectra and the atomic force microscope. The scanning tunneling microscopy shows that the conductivity of the hybrid LB films is much better after heteropolyanions having been incorporated in the films.

Solvent extraction of scandium(III), yttrium(III), lanthanum(III) and gadolinium(III) using Cyanex 302 in heptane from hydrochloric acid solutions

The extractions of the selected rare earths (Sc, Y, La and Gd) from hydrochloric acid solutions have been investigated using bis(2,4,4-trimethylpentyl)-mono thiophosphinic acid (Cyanex 302, HL) in heptane as an extractant. The results demonstrate that the extractions of rare earths occur via the following reaction: Sc(OH)(2+) + 2[(HL)(2)]((O)) double left right arrow [Sc(OH)L-2 (.) 2(HL)]((O)) + 2H(+) Y3+ + 3[(HL)(2)]((O)) double left right arrow [Y(HL2)(3)]((O)) + 3H(+) La(OH)(2)(+) + 3[(HL)(2)](O) double left right arrow [La(OH)(2)L (.) 5(HL)]((O)) + H+ Gd(OH)(2+) + 3[(HL)(2)]((O)) double left right arrow [Gd(OH)L-2 (.) 4(HL)]((O)) + 2H(+) The pH(1/2) values and equilibrium constants of the extracted complexes have been deduced by taking into account the aqueous phase complexation of the metal ion with hydroxyl ligands and plausible complexes extracted into the organic phase. According to the pH(1/2) values, it is possible to realize mutual separation among Sc(III), Y(III), La(III) and Gd(III) with Cyanex 302 by controlling aqueous acidity.

Investigation of sandwiched gadolinium(III) complexes with tungstosilicates as potential MRI contrast agents

Two gadolinium-sandwiched complexes with tungstosilicates, K-13[Gd(SiW11O39)(2)] (Gd(SiW11)(2)) and K11H6[Gd2O3(SiW9O34)(2)] (Gd-3(SiW9)(2)), have been investigated by in vitro and in vivo experiments as potential contrast agents for magnetic resonance imaging (MRI). T-1-relaxivity of Gd(SiW11)(2)was 6.59 mM(-1) . s(-1) in aqueous solution and 6.85 mM(-1) . s(-1) in 0.725 mmol . L-1 bovine serum albumin solution at 25degreesC and 9.39 T, respectively. The corresponding T-1-relaxivity of Gd-3(SiW9)(2) was 12.6 and 19.3 mM(-1) . s(-1) per Gd, respectively. MRI for Sprague-Dawley rats showed longer and more remarkable enhancement in rat liver after i.v. injection of these two complexes: 39.4 +/- 3.9% and 57.4 +/- 11.6% within the first 30 min after injection, 31.2 +/- 2.6% and 39.9 +/- 7.6% in the next 60 min for Gd(SiW11)(2) and Gd-3(SiW9)(2) at doses of 0.081 and 0.084 mmol Gd/kg, respectively. Our preliminary in vitro and in vivo study indicates that Gd(SiW11)(2) and Gd-3(SiW9)(2) are favorable candidates for hepatic contrast agents for MRI. However, the two complexes exhibit higher acute toxicity and need to be modified and studied further before clinical use.

Structure and electrochemical characteristics of RENi3 alloy

The RENi3 (RE = La, Ce, Pr, Nd, Sm, Gd, Tb, Dy, Ho, Er, Y) series compounds have been prepared by arc melting constituent elements under Ar atmosphere. X-ray diffraction (XRD) analysis reveals that the as-prepared alloys have different lattice parameters and cell volumes, depending on different rare earth (RE) element. The electrochemical characteristics, including the electrochemical capacity, P-C isotherms, high rate chargeability (HRC) and high-rate dischargeability (HRD), of these alloys have been studied through the charge-discharge recycle testing at different temperatures, charge currents and discharge currents. The results show that YNi3 has the largest cell volume, smallest density, and moreover, it shows more satisfactory electrochemical characteristics than other alloys, including discharge capacity, HRC, HRD and low temperature dischargeablity.

Redshift phenomenon of the excitation light of long life emission phosphor

We observed that the SrMg2(PO4)(2):Eu phosphor could emit long life phosphorescence with the excitation light whose wavelength was shorter than 420 nm, however, when La, Ce, or Gd was codoped, the wavelength of the excitation light to cause the phosphorescence had a redshift of 40 nm. A possible mechanism and related discussion for this redshift phenomenon of the excitation light was given. It was suggested that the threshold between the trap and valence band was decreased with the addition of the codopants.

Structure and catalytic properties of magnesia-supported copper salts of molybdovanadophosphoric acid

The structure and stability of magnesia-supported copper salts of molybdovanadophosphoric acid (Cu2PMo11VO40) were characterized by different techniques. The catalyst was prepared in ethanol by impregnation because this solvent does not hurt texture of the water-sensitive MgO and Cu2PMo11VO40. The Keggin-type structure compound may be degraded partially to form oligomerized polyoxometalate when supported on MgO. However, the oligomers can rebuild as the Keggin structure again after thermal treatment in air or during the reaction. Meanwhile, the V atoms migrate out of the Keggin structure to form a lacunary structure, as observed by Fourier transform IR spectroscopy. Moreover, the presence of Cu2+ as a countercation showed an affirmative influence on the migration of V atoms, and the active sites derived from the lacunary species generated after release of V from the Keggin anion. The electron paramagnetic resonance data imply that V5+ autoreduces to V4+ in the fresh catalyst, and during the catalytic reaction a large number of V4+ ions are produced, which enhance the formation of O2- vacancies around the metal atoms. These oxygen vacancies may also improve the reoxidation function of the catalyst. This behavior is correlated to higher catalytic properties of this catalyst. The oxidative dehydrogenation of hexanol to hexanal was studied over this catalyst.

Synergistic extraction of rare earths by mixture of bis(2,4,4-trimethylpentyl)phosphinic acid and Sec-nonylphenoxy acetic acid

Synergistic extraction of trivalent rare earths (RE=Sc, Y, La, Gd, Yb) from hydrochloride medium using mixture of bis(2,4,4-trimethylpentyl)phosphinic acid (HL, Cyanex272) and Sec-nonylphenoxy acetic acid (HA, CA-100) in n-heptane has been studied. The synergistic enhancement coefficients were observed for La (1.30), Gd (1.97), Y (3.59), Yb (8.21) and Sc (14.41). The results indicated yttrium was extracted into n-heptane as YH(5)A(4)L(4) mixed species instead of Y(HL2)(3), Y(OH)(2)A(HA)(3) which were extracted by Cyanex272 and CA-100, respectively. A cation exchange mechanism was proposed and further clarified by IR spectra. The equilibrium constants, formation constants and thermodynamic functions such as Delta G, Delta H and Delta S were determined. The Cyanex272 + CA-100 system not only enhanced the extraction efficiency of RE but also improved the selectivities significantly. The mutual separation factors of these ions suggested the mixture system would be of practical value in extraction and separation of rare earths.

Studies on the synergistic extraction of rare earths with a combination of 2-ethylhexylphosphonic mono-2-ethylhexyl ester and trialkylphosphine oxide

The synergistic extraction of rare earths (La, Nd, Gd, Y and Yb) with a mixture of 2-ethylhexyl 2-ethylhexylphosphonate (EHEHPA) (HA) and trialkylphosphine oxide (Cyanex 923) (B) from a hydrochloride medium was investigated. The mixed system significantly enhances the extraction efficiency for lighter lanthanides and the synergistic enhancement coefficients for La (4.52), Nd (3.35), Gd (2.08), Y (1.31) and Yb (1.08) decrease with decreasing ionic radius of the rare earths. The extraction equilibrium of La, Nd and Gd indicate that La and Nd were extracted as MA(3)(.)B, whereas Gd was extracted as Gd(OH)A(2)(HA)(2)B-.. The equilibrium constants, thermodynamic functions such as Delta G, Delta H and Delta S and formation constants of the extracted species were determined. The stripping properties were also studied.

A new oxide ion conductor: La3GaMo2O12

A new oxide ion conductor, La3GaMo2O12, with a bulk conductivity of 2.7 X 10(-2) S.cm(-1) at 800 degrees C in air atmosphere was prepared by the traditional solid-state reaction. The room temperature X-ray diffraction data could be indexed on a monoclinic cell with lattice parameters of a=0.5602(2) nm, b=0.3224(1) nm, c= 1.5741(1) nm, beta= 102.555(0)degrees, V=0.2775(2) nm(3) and space group Pc(7). Ac impedance measurements in various atmospheres further support that it is an oxide ion conductor. This material was stable in various atmospheres with oxygen partial pressure P(O-2) ranging from 1.0 X 10(5) to 1.0 X 10(-7) Pa at 800 degrees C. A reversible polymorphic phase transition occurred at elevated temperatures as confirmed by the differential thermal analysis and dilatometric measurement.

Microstructures and properties of melt-spun and as-cast Mg-20Gd binary alloy

Mg-20Gd(%, mass fraction) samples were prepared using melt-spinning and copper mold casting techniques. Microstructures and properties of the Mg-20Gd were investigated. Results show that the melt-spun ribbon is mainly composed of supersaturated alpha-Mg solid solution phase and the as-east ingot mainly contains alpha-Mg solid solution and Mg5Gd phase. The differential scanning calorimeter (DSC) curve of the ribbon exhibits a small exothermic peak in the temperature range from 630 to 680 K, which indicates that the ribbon contains a metastable phase (amorphous). Tensile strength at room temperature of the melt-spun ribbon and as-cast specimen are 308 and 254 MPa, respectively. The elongations of the two samples are less than 2%. The fracture surfaces demonstrate that the fracture mode of the as-cast Mg-20Gd is a typical cleavage fracture and that of the melt-spun sample is a combination of brittle fracture and ductile fracture.

From dissymmetrical mononuclear entities to centrosymmetrical heterotrinuclear complex with 2D supramolecular structure: synthesis, characterization, crystal structure, and magnetic properties

A new centrosymmetrical heterotrinuclear complex, {[Cu(oxbe)](2)Co(H2O)(2)}.2DMF.DMA with 2D supramolecular structure, has been obtained by the self-assembly of a dissymmetrical building block [Cu(oxbe)](-) with bivalent metal ion Co2+, where H(3)oxbe is dissymmetrical ligand N-benzoato-N'-(2-aminoethyl)oxamido, DMF = dimethylformamide, DMA = dimethylamine. Its structure was determined by single crystal X-ray analysis. The molecular structure is centrosymmetrical with the cobalt atom lying on an inversion center. Through the hydrogen bonds and d-pi stacking interactions, a 2D supramolecular structure is formed. This study exemplifies a new method for the assembly of supramolecular structure using a dissymmetrical brick. Magnetic susceptibility measurements (5-300 K) indicate that the central cobalt and terminal copper metal ions are antiferromagnetically coupled with J = -23.1 cm(-1).