Effect of nucleating agent on the isothermal crystallization kinetics of PHBV

The crystallization behavior of PHBV, poly(beta -hydroxybutyrate-co-beta -hydrxyvalerate), with nucleating agents under isothermal conditions was investigated. A differential scanning calorimeter was used to monitor the crystallization process from the melt. During isothermal crystallization, the dependence of relative degree of crystallinity on time was described by the Avrami equation. It has been shown that the addition of BN and Tale causes a considerable increase in the overall crystallization rate of PHBV but does not influence the Avrami exponent n, mechanism of nucleation and spherulite growth mode of PHBV. A little of nucleating agent will increase the crystallization rate and decrease the fold surface free energy sigma (e), remarkably. The effect of BN is more significant than that of Talc.

Reactive reinforcement of the interface of high performance polymer blends by PMR-POI

The effect of PMR-polyimide(POI) as the interfacial agent on the interface characteristics, morphology features and crystallization of poly (ether sulfone) /poly (phenylene sulfide) (PES/PPS) and poly(ether ether ketone)/poly (ether sulfone) (PEEK/PES) partly miscible blends were investigated by means of the scanning electron microscopy, WAXD and XPS surface analysis. It is found that the interfacial adhesion was enhanced remarkably, the size of the dispersed phase particles was reduced significantly and the miscibility was improved by the addition of POI. During melt blending cross-link and/or grafting reaction of POI with PES, PEEK and PPS homopolymers was detected, however the reaction activity of POI with PPS was much higher than that of PES and PEEK. It was also found that POI was an effective nucleation agent of the crystallization of PPS.

Study of the mechanism for controlled crystallization of BaF2 under two kinds of monolayers

Controlled crystallization of BaF2 under two different kinds of monolayers, octadecylamine [CH3(CH2)(17)NH2] and hexadecanol [CH3(CH2)(14)CH2OH], has been studied by using x-ray diffraction (XRD) and scanning electron microscope. It was found that the monolayer headgroup, the degree of ionization of the headgroup, etc., had a complicated effect on the selectivity of monolayers for crystal and on the morphology and orientation of crystals grown under the compressed monolayers. At pH = 7.0, XRD analysis showed that (100)-oriented BaF2 crystals were formed under the octadecylamine monolayer, while several kinds of crystals were found under the hexadecanol monolayer. In comparison, at pH = 8.5, both (100)-oriented BaF2 and (111)-oriented Ba(NO3)(2) crystals were obtained under the monolayer of octadecylamine. However, crystals formed under hexadecanol monolayer consist of BaF2, Ba(NO3)(2), etc. The detailed mechanism for crystallization was discussed in terms of the specific interaction and lattice matching between the monolayer headgroup and the nucleating species.

Organic template-directed crystallization of the complex fluoride NH4MnF3 with perovskite structure

(100)-oriented NH4MnF3 perovskite with different morphologies have been obtained in situ via an organic template; experimental results can be rationalized in terms of electrostatic interactions and lattice matching between the organic template and the ions undergoing nucleation.

Formation of mesophase mono-domains and micro-structures in thin films of a series of copolyethers containing both odd-numbered methylene units

The structural and morphological evolution of mono-domains in thin films has been investigated for a series of liquid crystalline (LC) copolyethers. The copolyethers studied were synthesized by the reaction of 1-(4-hydroxy-4 ' -biphenylyl)-2-(4-hydroxyl-phenyl)propane (TPP) with 1,7-dibromoheptane and 1,11-undecane at different compositions (coTPPs-7/11). In contrast to the solution-cast thin films without annealing, which exhibit the isotropic homogeneous molecular orientation, mono-domains with a homeotropic alignment were found in coTPP-7/11(5/5) after the thin films were annealed in the high-temperature columnar phase (Phi '). Similar to the nucleation process in polymer crystallization, transmission electron microscopic observations show that small mono-domains appear in the initial stage of annealing, where molecules form a uniaxial in-plane chain orientation. With increasing annealing time, the molecular orientation gradually became tilted with respect to the substrate surface, and finally, a uniaxial homeotropic molecular orientation was achieved after a prolonged annealing time. The lateral size of mono-domains was found to increase continuously with annealing time and grew into a circular shape, indicating an isotropic lateral growth scheme which implies a hexagonal molecular packing proved by the electron diffraction experiments.

Influence of the size of ultrafine CaCO3 powder on PP crystallization

The effects of CaCO3 on the crystallization behavior of polypropylene (PP) were studied by means of DSC and WAXD. The average sizes of the CaCO3 powders used were 0.1 mum (UC) and 0.5 mum (GC), respectively. The PP/CaCO3 composites at compositions of 1 phr and 10 phr were investigated. The results showed that the addition of CaCO3 reduced the supercooling, the rate of nucleation and the overall rate of crystallization (except for the 10 phr UC/PP sample). The crystallinity of PP was increased and the size distribution of the crystallites of alpha -PP; was: broadened. On the other hand,the crystallization rate of 10 phr UC/PP is 1.5 times higher than that of neat PP. It has an overall rate of crystallization 2 times as much as that of the neat PP and has the maximum crystallinity. The sizes of crystallites and the unit cell parameters of alpha -PP were varied by the addition of CaCO3. beta -PP was formed by addition of Ge and was not detected by addition of UC. The differences of crystallization behaviors of PP might be attributed to the combined effects of the content and size of CaCO3 filled.

Melting crystallization behavior of nylon 66

Analysis of isothermal and nonisothermal crystallization kinetics of nylon 66 was carried out using differential scanning calorimetry (DSC). The commonly used Avrami equation and that modified by Jeziorny were used, respectively, to fit the primary stage of isothermal and nonisothermal crystallizations of nylon 66. In the isothermal crystallization process, mechanisms of spherulitic nucleation and growth were discussed. The lateral and folding surface free energies determined from the Lauritzen-Hoffman treatment are sigma = 9.77 erg/cm(2) and sigma (e) = 155.48 erg/cm(2), respectively; and the work of chain folding is q = 33.14 kJ/mol. The nonisothermal crystallization kinetics of nylon 66 was analyzed by using the Mo method combined with the Avrami and Ozawa equations. The average Avrami exponent (n) over bar was determined to be 3.45. The activation energies (DeltaE) were determined to be -485.45 kJ/mol and -331.27 kJ/mol, respectively, for the isothermal and nonisothermal crystallization processes by the Arrhenius and the Kissinger methods.

Selective crystallization of BaF2 under a compressed Langmuir monolayer of behenic acid

Selective crystallization of BaF2 crystals under a compressed Langmuir monolayer of behenic acid [CH3(CH2)(20)COOH] has been studied by using X-ray diffraction, X-ray photoelectron spectroscopy, scanning electron microscopy, and energy-dispersive X-ray analysis. It was found that, in the absence of a monolayer, three kinds of crystals (Ba2ClF3, BaClF, and BaF2) can be obtained by mixing BaCl2 with a NH4F solution. However, in the presence of the monolayer of behenic acid, only BaF2 crystals appear at the monolayer-subphase interface and crystals have a special crystal face (100). During this process of crystallization, the monolayer plays a very important role and acts as a template that can preferentially select a special crystal and a special crystal face. The above results can be explained in terms of a specific molecular interaction between ions and the headgroups of the monolayer and specific electrostatic, geometric, and stereochemical interactions at the organic-inorganic interface.

Enhanced crystallization and phase transformation of amorphous silicon nitride under high pressure

The crystallization and phase transformation of amorphous Si3N4 ceramics under high pressure (1.0-5.0 GPa) between 800 and 1700 degreesC were investigated. A greatly enhanced crystallization and alpha-beta transformation of the amorphous Si3N4 ceramics were evident under the high pressure, as characterized by that, at 5.0 GPa, the amorphous Si3N4, began to crystallize at a temperature as low as 1000 degreesC (to transform to alpha modification). The subsequent alpha-beta transformation occurred completed between 1350 and 1420 degreesC after only 20 min of pressing at 5.0 GPa. In contrast, under 0.1 MPa N-2, the identical amorphous materials were stable up to 1400 degreesC without detectable crystallization, and only a small amount of a phase was detected at 1500 degreesC. The crystallization temperature and the alpha-beta transformation temperatures are reduced by 200-350 degreesC compared to that at normal pressure. The enhanced phase transformations of the amorphous Si3N4, were discussed on the basis of thermodynamic and kinetic consideration of the effects of pressure on nucleation and growth.

Isothermal and non-isothermal crystallization kinetics of syndiotactic polypropelene

Isothermal and non-isothermal crystallization kinetics of a syndiotactic polypropylene(sPP) sample synthesized by new metallocene catalyst at different annealing temperatures and different cooling rates have been investigated by using differential scanning calorimetry(DSC) and density analysis. The equilibrium melting temperature( T-m(0)) is 158 degrees C by Hoffman-Weeks method. The equilibrium heat of fusion(Delta H-m(0)) is 88J/g in terms of the density analysis and DSC methods. The lateral and end surface free energies derived from the Lauritzen-Hoffman spherulitic growth rate equation are sigma = 5.2erg/cm(2) and sigma(e) = 69erg/cm(2), respectively. The work of chain folding is determined to be q = 33.75kJ/mol. Modified Avrami equation and Ozawa equation can be used to describe the non-isothermal crystallization behavior. And a new and convenient approach by combining the Avrami equation and Ozawa equation in a same crystallinity is used to describe the non-isothermal behavior as well. The crystallization activation energies are evaluated to be 73.7kJ/mol and 73.1kJ/mol for isothermal crystallization and non-isothermal crystallization, respectively. The Avrami exponent n is 1.5 similar to 1.6 for isothermal crystallization procedure, while the Avrami exponent n,is 2.5 similar to 3.5 for non-isothermal crystallization procedure. This indicated the difference of nucleation and growth between the two procedures.

Study on the interface structure: Diamond thin film epitaxy on (001) silicon substrate

An interesting interface structure between diamond film and silicon substrate has been observed. That is, according to the deformation of the diamond film crystal sturcture, a strictly 3:2 matching of the two lattices across the interface is obtained. This result clearly indicates that misfit dislocations at the interface and "epitaxial tilting" are not the only two ways to overcome the 1.5% residual misfit.

Isothermal crystallization kinetics and melting behavior of poly(beta-hydroxybutyrate)/poly(vinyl acetate) blends

The overall isothermal crystallization kinetics and melting behavior of poly(beta-hydroxybutyrate) (PHB)/poly(vinyl acetate) (PVAc) blends were studied by using differential scanning calorimetry(DSC). The Avrami analysis indicates that the addition of PVAc into PHB results in the decrease in the overall crystallization rate of the PHB phase, but does not affect PHB's nucleation mechanism and geometry of crystal growth. The activation energy of the overall process of crystallization increases with the increasing PVAc content in the blends. The phenomenon of multiple melting endotherms is observed, which is caused by melting and recrystallization during the DSC heating run. (C) 1998 Elsevier Science Ltd. All rights reserved.

Crystallization kinetics of poly(ether ether ketone) (PEEK) from its metastable melt

After isothermal crystallization of the amorphous poly(ether ether ketone), double endothermic behaviour can be found through differential scanning calorimetry experiments. During the heating scan of semicrystalline PEEK, a metastable melt, which comes from the melt of the thinner lamellar crystal populations, can be obtained between these two endotherms. The metastable melt can recrystallize immediately just above the lower melting temperature and form slightly thicker lamellae than the original ones. The thickness and the perfection depend upon the crystallization time and the crystallization temperature. By comparing the TEM morphological observations of the samples before and after partial melting, it can be shown that lamellar crystals, having different thermodynamic stability, form during isothermal crystallization. After partial melting, only the type of lamellar crystal exhibiting the higher thermodynamic stability remains. Wide angle X-ray diffraction measurements shows a slightly change in the crystallinity of the samples before and after the partial melting. Small angle X-ray scattering results exhibit a change in the long period of the lamellar crystals before and after the partial melting process. The crystallization kinetics of the metastable melt can be determined by means of differential scanning calorimetry. The kinetic analysis showed that the isothermal crystallization of the metastable PEEK melt proceeds with an Avrami exponent of n = 1.0 similar to 1.4, reflecting that probably one-dimensional or an irregular line growth of the crystal occurred between the existing main lamellae with heterogeneous nucleation. (C) 1998 Elsevier Science Ltd. All rights reserved.

On morphology and the competition between crystallization and phase separation in polypropylene-polyethylene blends

Blends of polypropylene (PP) and low density polyethylene (LDPE) have been examined for a series of compositions using differential scanning calorimetry and permanganic etching followed by transmission electron microscopy. Thermal analysis of their melting and recrystallization behaviour suggests two possibilities, either that below 15 wt % PP the blends are fully miscible and that PP only crystallizes after LDPE because of compositional changes in the remaining melt, or else that the PP is separated, but in the form of droplets too small to crystallize at normal temperatures. Microscopic examination of the morphology shows that the latter is the case, but that a fraction of the PP is nevertheless dissolved in the LDPE. (C) 1998 Kluwer Academic Publishers.

Crystallization of micelles and matrix in dilute diblock copolymer/homopolymer solutions

The crystallization, morphology, and crystalline structure of dilute solid solutions of tetrahydrofuran-methyl methacrylate diblock copolymer (PTHF-b-PMMA) in poly(ethylene oxide) (PEO) and PTHF have been studied with differential scanning calorimetry (DSC), X-ray, and optical microscopy. This study provides a new insight into the crystallization behavior of block copolymers. For the dilute PTHF-b-PMMA/PEO system containing only 2 to 7 wt % of PTHF content, crystallization of the PTHF micellar core was detected both on cooling and on heating. Compared the crystallization of the PTHF in the dilute solutions with that in the pure copolymer, it was found that the crystallizability of the PTHF micellar core in the solution is much greater than that of the dispersed PTHF microdomain in the pure copolymer. The stronger crystallizability in the solution was presumably due to a softened PMMA corona formed in the solution of the copolymer with PEG. However, the "soft" micelles formed in the solution (meaning that the glass transition temperatures (T-g) of the micelle is lower than the T-m of the matrix phase) showed almost no effects on the spherulitic morphology of the PEO component, compared with that of the pure PEO sample. In contrast, significant effects of the micelles with a "hard" PMMA core (meaning that the T-g of the core is higher than the T-m of the PTHF homopolymer) on the nucleation, crystalline structure, and spherulitic morphology were observed for the dilute PTHF-b-PMMA/PTHF system. (C) 1998 John Wiley & Sons, Inc.