Raman spectroscopy of apatite irradiated with swift heavy ions with and without simultaneous exertion of high pressure

Durango apatite was irradiated with energetic U ions of 2.64 GeV and Kr ions of 2.1 GeV, with and without simultaneous exposure to a pressure of 10.5 GPa. Analysis by confocal Raman spectroscopy gives evidence of vibrational changes being marginal for fluences below 5x10(11) ions/cm(2) but becoming dominant when increasing the fluence to 8x10(12) ions/cm(2). Samples irradiated with U ions experience severe strain resulting in crystal cracking and finally breakage at high fluences. These radiation effects are directly linked to the formation of amorphous tracks and the fraction of amorphized material increasing with fluence. Raman spectroscopy of pressurized irradiated samples shows small shifts of the band positions with decreasing pressure but without a significant change of the Gruneisen parameter. Compared to irradiations at ambient conditions, the Raman spectra of apatite irradiated at 10.5 GPa exhibit fewer modifications, suggesting a higher radiation stability of the lattice by the pressure applied.

Structural modification of C-doped SiO2 induced by swift heavy ion irradiations

Thermally grown amorphous SiO2 samples were implanted at room temperature (RT) with 120 keV C-ions to a dose ranging from 1.0 x 10(16) to 8.6 x 10(17)C ions/cm(2), then irradiated at RT with 950 MeV Pb, 345 or 1754 MeV Xe ions to a fluence in the region from 1.0 x 10(11) to 3.8 x 10(12) ions/cm(2), respectively. The irradiated samples were investigated using micro-FTIR and micro-Raman spectroscopes. It was found that new chemical bonds such as Si-C, C=C(O), C C and Si(C)-O-C bonds formed significantly in the C-doped SiO2 films after heavy ion irradiations. The evolution of Si-O-C bonds and possible mechanism of structural modification in C-doped SiO2 induced by swift heavy ion irradiations were discussed.

Melting of Au and Al in nanometer Fe/Au and Fe/Al multilayers under swift heavy ions: A thermal spike study

Knowing that Fe is sensitive to swift heavy ion irradiations whereas Au and Al are not, the behavior of nanometric metallic multilayer systems, like [Fe(3 nm)/Au(x)](y) and [Fe(3 nm)/Al(x)](y) with x ranging between 1 and 10 mn, were studied within the inelastic thermal spike model. In addition to the usual cylindrical geometry of energy dissipation perpendicular to the ion projectile direction, the heat transport along the ion path was implemented in the electronic and atomic sub-systems. The simulations were performed using three different values of linear energy transfer corresponding to 3 MeV/u of Pb-208, Xe-132 and Kr-84 ions. For the Fe/Au system, evidence of appearance of a molten phase was found in the entire Au layer, provided the Au thickness is less than 7 nm and 3 nm for Pb and Xe ions, respectively. For the Fe/Al(x) system irradiated with Pb ions, the Al layers with a thickness less than 4 nm melt along the entire ion track. Surprisingly, the Fe layer does not melt if the Al thickness is larger than 2 nm, although the deposited energy surpasses the electronic stopping power threshold of track formation in Fe. For Kr ions melting does not occur in any of the multilayer systems.

Materials research with swift heavy ions at the IMP accelerators

The main ion beams acceleration facilities and research fields of the Institute of Modern Physics (IMP) are briefly introduced. Some of the experimental instruments, typical works and the obtained results on the materials research with swift heavy ions at the IMP-accelerators are presented.

Preparation of Microporous Membranes by Swift Heavy Ion Irradiation and Impedance Characterization

Polypropylene (PP) microporous membranes were successfully prepared by swift heavy ion irradiation and track-etching. Polypropylene foils were irradiated with Au-197 ions of kinetic energy 11.4 MeV.u(-1) (total energy of 2245.8 MeV) and fluence 1x10(8) ions.cm(-2) at normal incidence. The damaged regions produced by the gold ions along the trajectories were etched in H2SO4 and K2Cr2O7 solutions leading to the formation of cylindrical pores in the membranes. The pore diameters of the PP microporous membranes increased from 380 to 1610 nm as the etching time increased from 5 to 30 min. The surface and cross-section morphologies of the porous membranes were characterized by scanning electron microscopy (SEM). The micropores in the membranes were found to be cylindrical in shape, homogeneous in distribution, and equal in size. Some mathematical relations of the porosity of the PP microporous membranes were established by analytic derivation. The microporous membranes were used in lithium-ion batteries to measure their properties as separators. The electrical conductivity of the porous membrane immersed in liquid electrolyte was found to be comparable to that of commercial separators by electrochemical impedance spectroscopy (EIS). The results showed that the porosity and electrical conductivity were dependent on the ion fluence and etching time. By adjusting these two factors, microporous membranes with good porosity and electrical conductivity were made that met the requirements for commercial use.

重离子辐照制备电池用微孔膜及其阻抗性质；Preparation of Microporous Membranes by Swift Heavy Ion Irradiation and Impedance Characterization

利用离子辐照结合径迹蚀刻方法制备聚丙烯(PP)微孔膜.用加速器产生的单核能为11.4MeV·u-1(总能量2245.8MeV)的197Au离子束辐照PP膜,剂量为1×108ions·cm-2.辐照后PP膜沿离子路径产生损伤区域,用硫酸与重铬酸钾的混合液进行蚀刻(5-30min),制备出孔径为380-1610nm的聚丙烯微孔膜.对膜的表面和断面形貌进行表征,微孔膜的孔径大小及空间分布均匀,孔道上下贯通,形状近似为圆柱形.给出了微孔膜的孔隙率理论公式.将制备的聚丙烯微孔膜用作锂离子电池隔膜,用电化学阻抗谱(EIS)测定浸满电解液的微孔膜的离子电导率,并与商用隔膜进行比较.分析表明辐照剂量和孔径大小均会影响膜的孔隙率和离子电导率,选择合适的辐照剂量和蚀刻时间,可以制备出孔隙率和离子电导率符合应用标准的聚丙烯微孔膜.

利用重离子辐照技术制备锂离子电池隔膜；Preparation Lithium-ion Battery Separator by Swift Heavy Ion Irradiation Methods

用能量11.4MeV/u和注量1×108ions/cm2的197Au离子垂直辐照聚丙烯薄膜,通过电导测量法监测温度、硫酸浓度和重铬酸钾浓度对径迹蚀刻速率的影响,得到合适的蚀刻条件;成功制备出孔径范围在600—1000nm的重离子径迹聚丙烯孔膜,并用场发射扫描电镜对孔的形状及孔径大小进行了表征,对孔洞锥角的形成进行了分析,为重离子辐照技术制备锂离子电池隔膜提供了实验数据。