Deposition of GdVO4 : Eu3+ nanoparticles on silica nanospheres by a simple sol-gel method

The deposition and coating of GdVO4: Eu3+ nanoparticles on spherical silica was carried out using a simple sol - gel method at low temperature. The GdVO4: Eu3+-coated silica composites obtained were characterized by differential thermal analysis (DTA), thermogravimetric (TG) analysis, x-ray diffraction (XRD), Fourier-transform IR spectroscopy (FT-IR), transmission electron microscopy (TEM), x-ray photoelectron spectroscopy (XPS), photoluminescence spectra, and kinetic decay. It is found that the similar to 5 nm GdVO4: Eu3+ nanoparticles coating the silica spheres are crystal in the as-prepared samples and the crystallinity increases with increasing annealing temperature. The composites obtained are spherical in shape with an average size of 100 nm. The GdVO4: Eu3+ nanoparticles are linked with silica cores by a chemical bond. The photoluminescence spectra of the obtained GdVO4: Eu3+-coated silica composites are similar to those of the bulk GdVO4: Eu3+ phosphors. The strongest peak is near 617 nm, which indicates that Eu3+ is located in the low symmetry site with non-inversion centre.

Monodisperse spherical core-shell structured SiO2-CaTiO3 : Pr3+ phosphors for field emission displays

Nanocrystalline CaTiO3:Pr3+ phosphor layers were coated on nonaggregated, monodisperse, and spherical SiO2 particles by the sol-gel method, resulting in the formation of core-shell structured SiO2-CaTiO3:Pr3+ particles. X-ray diffraction, Fourier transform infrared spectroscopy, field emission scanning electron microscopy, transmission electron microscopy, photoluminescence, cathodoluminescence spectra, as well as lifetimes were utilized to characterize the core-shell structured SiO2-CaTiO3:Pr3+ phosphor particles. The obtained core-shell structured phosphors consist of well dispersed submicron spherical particles with a narrow size distribution. The thickness of the CaTiO3:Pr3+ shell could be easily controlled by changing the number of deposition cycles (about 70 nm for four deposition cycles). The core-shell SiO2-CaTiO3:Pr3+ particles show a strong red emission corresponding to D-1(2)-H-3(4) (612 nm) of Pr3+ under the excitation of ultraviolet (326 nm) and low voltage electron beams (1-5 kV). These particles may be used in field emission displays.

Core-shell structured SiO2@YVO4 : Dy3+/Sm3+ phosphor particles: Sol-gel preparation and characterization

Spherical SiO2 particles have been coated with YVO4:Dy3+/Sm3+ phosphor layers by a Pechini sol-gel process, leading to the formation of core-shell structured SiO2@YVO4:Dy3+/Sm3+ particles. X-ray diffraction (XRD), Fourier-transform IR spectroscopy, field emission scanning electron microscopy (FE-SEM), transmission electron microscopy (TEM), photoluminescence (PL) spectra as well as lifetimes were used to characterize the resulting SiO2 @YVO4:Dy3+/Sm3+ core-shell phosphors. The obtained core-shell phosphors have perfect spherical shape with narrow size distribution (average size ca. 300 nm), smooth surface and non-agglomeration. The thickness of shells could be easily controlled by changing the number of deposition cycles (20 nm for one deposition cycle). The core-shell particles show strong characteristic emission from Dy3+ for SiO2@YVO4:Dy3+ and from Sm3+ for SiO2@YVO4:Sm3+ due to an efficient energy transfer from YVO4 host to them. The PL intensity of Dy3+ and Sm3+ increases with raising the annealing temperature and the number of coating cycles.

Applications of Heavy Ion Irradiation in Photonic Crystal Research

Photonic crystals (PC) have received extensive attention for the photonic band gap (PBG). The polystyrene (PS) particles bottom-up approach is a productive method for photonic crystal manufacture, this kind of photonic crystals having an unique PBG that depends on the particle's shape, sizes and defects. Heavy ion irradiation is a very useful method to induce defects in PC and change the shapes of the particles to tune the PBG. MeV heavy ion irradiation leads to an anisotropic deformation of the particles from spherical to ellipsoidal, the aspect ratio of which can be precisely controlled by using the ion energy and flux. Sub-micrometer PS particles were deposited on a Cu substrate and were irradiated at 230 K by using heavy ion energy and fluence in the range from 2 to 10 MeV and 1 x 10(14) cm(-2) to 1 x 10(15) cm(-2); respectively.

Luminescence functionalization of mesoporous silica with different morphologies and applications as drug delivery systems

Ordered mesoporous silica (MCM-41) particles with different morphologies were synthesized through a simple hydrothermal process. Then these silica particles were functionalized with luminescent YVO4:EU3+ layers via the Pechini sol-gel process. The obtained YVO4:Eu3+ and MCM-41 composites, which maintained the mesoporous structure of MCM-41 and the red luminescence property of YVO4:Eu3+ were investigated as drug delivery systems using ibuprofen (IBU) as model drug. The physicochemical properties of the samples were characterized by X-ray diffraction (XRD), Fourier transform-infrared spectroscopy (FT-IR), scanning electron microscopy (SEM), transmission electron microscopy (TEM), N-2 adsorption, and photoluminescence (PL) spectra, respectively.

Non-isothermal crystallisation kinetics of polyamide 6/mesoporous silica nanocomposites

Non-isothermal crystallisation kinetics of a polyamide 6/mesoporous silica nanocomposite (PA6-MS) has been investigated by differential scanning calorimetry (DSC) at different cooling rates. Mandelkern, Jeziorny-Ziabicki and Ozawa methods were applied to describe this crystallisation process. The analyses show that the mesoporous silica particles act as nucleating agents in the composite and that the Avrami exponent n varies from 3.0 to 4.6. The addition of mesoporous silica influenced the mechanism of nucleation and the growth of polyamide 6 (PA6) crystallites.

Sol-Gel Preparation of Zn2 Si04：Mn Phosphor Layers on Silica Spheres and Their Luminescent Properties

The synthesis and luminescence properties of Zn2SiO4:Mn phosphor layers on spherical silica spheres,i.e.,a kind of core-shell complex phosphor,Zn2SiO4:Mn@SiO2 were described.Firstly,monodisperse silica spheres were obtained via the Stober method by the hydrolysis of tetraethoxysilane(TEOS)Si(OC2H5)4 under base condition (using NH4OH as the catalyst).Secondly,the silica spheres were coated with a Zn2SiO4:Mn phosphor layer by a Pechini sol-gel process.X-ray diffraction(XRD),scanning electron microscope(SEM),energy-dispersive X-ray spectrum(EDS) and photoluminescence(PL) were employed to characterize the resulting complex phosphor.The results comfirm that 1000℃ annealed sample consists of crystalline Zn2SiO4:Mn shells and amorphous SiO2 cores.The phosphor show the green emission of Mn2+ at 521nm corresponding 4T1(4G)-6A1(6S) transition,and the possible luminescence mechanism is proposed.

Synthesis and characterization of functionalized mesoporous silica by aerosol-assisted self-assembly

An efficient, productive, and low-cost aerosol-assisted self-assembly process has been developed to produce organically modified mesoporous silica particles via a direct co-condensation of silicate species and organosilicates that contain nonhydrolyzable functional groups in the presence of templating surfactant molecules. Different surfactants including cetyltrimethylammonium bromide, nonionic surfactant Brij-56, and triblock copolymer P123 have been used as the structure-directing agents. The organosilanes used in this study include tridecafluoro-1, 1,2,2-tetrahydrooctyltriethoxysilane, methytriethoxysilane, vinyltrimethoxysilane, and 3-(trimethoxysilyl)propyl methacrylate. X-ray diffraction and transmission electron microscopy studies indicate the formation of particles with various mesostructures. Fourier transform infrared and solid-state nuclear magnetic resonance spectra confirm the organic ligands are covalently bound to the surface of the silica framework. The porosity, pore size, and surface area of the particles were characterized using nitrogen adsorption and desorption measurements.

An effective approach to synthesis of poly(methyl methacrylate)/silica nanocomposites

A novel synthetic route for nearly monodispersed poly(methyl methacrylate)/SiO2 composite particles (PMSCP) is reported. Silica nanoparticles modified with oleic acid were used as 'seeds'. Methyl methacrylate (MMA) monomer was copolymerized with oleic acid via in situ emulsion polymerization, in the presence of an initiator; it resulted finally in the formation of composites with core-shell morphology. The composite particles were examined by transmission electron microscopy (TEM), scanning electron microscopy (SEM), x-ray photoelectron spectroscopy (XPS) and thermogravimetric analysis (TGA). The number of silica particles inside the composite particles increases with an increase in the silica concentration. The effect of grafted silica concentration on the morphology of PMSCP is also reported in detail. It was found by thermogravimetric analysis that PMSCP show a potential application for fire retardance.

A NMR-STUDY OF THE INTERACTION OF SILICA WITH DIPALMITOYLPHOSPHATIDYLCHOLINE LIPOSOMES

The interaction of silica with dipalmitoylphosphatidylcholine (DPPC) liposomes has been studied by detecting H-1 and 2D NOESY NMR spectra and measuring proton spin-lattice relaxation time (T-1). The antagonistic effect of aluminium citrate on silica has also been studied by measuring the proton T-1 values, The results show that silica particles mainly bind to the phosphate moiety of the polar headgroup of DPPC bilayers through hydrogen bonds between Si-OH and O-P groups, but they have no significant effect on the conformation of the choline group of the polar headgroup, The addition of silica particles decreases the mobilities of the hydrocarbon chains slightly, Proton T-1 data also indicate that aluminium citrate reduces the effect of silica, A possible mechanism for the toxicity of silica and the antagonistic effect of aluminium titrate on silica is suggested. (C) 1995 Academic Press Inc.

Preparation and characteristic of a new class of silica/polyimide nanocomposites

A new class of silica/polyimide nanocomposites was successfully prepared by the sol-gel reaction, tetraethoxysilane, (TEOS), was hydrolyzed by the water released from imidization at low and high temperature. Silica particles with diameter of around 30-50 nm were observed in the hybrid films by scanning electron microscopy. The flame retardance, decomposition temperature and glass transition temperature of the film increased with increasing silica content. The tensile strength increased slightly while the elongation at break of the films decreased with increasing silica content. (C) 2002 Kluwer Academic Publishers.

Automated voltammetric system for shipboard determination of metal speciation in sea water

An automated and semi-intelligent voltammetric system is described for trace metal analysis. The system consists of a voltammeter interfaced with a personal computer, a sample changer, 2 peristaltic pumps, a motor burette and a hanging mercury drop electrode. The system carries out fully automatically approximately 5 metal determinations per hour (including at least 3 repetitive scans and calibration by standard addition) at trace levels encountered in clean sea water. The computer program decides what level of standard addition to use and evaluates the data prior to switching to the next sample. Alternatively, the system can be used to carry out complexing ligand titration with copper whilst recording the labile copper concentration; in this mode up to 8 full titrations are carried out per day. Depth profiles for chromium speciation in the Mediterranean Sea and a profile for copper complexing ligand concentrations in the North Atlantic Ocean measured on board-ship with the system are presented. The chromium speciation was determined using a new method to differentiate between Cr(III) and Cr(VI) utilizing adsorption of Cr(III) on silica particles.

Colloidal crystal heterostructures by a two-step vertical deposition method

A two-step template-induced vertical deposition technique was introduced to fabricate the colloidal crystal heterostructures due to wettability differences and spatial confinement of the templates structured with microchannels. The heterostructures exhibited a bi-frequency Bragg diffraction whose position was determined by the microsphere diameter of the opals. It was demonstrated that the channel width had an influence on the optical properties of the colloidal crystal heterostructures. The strategy proposed is suited for fabrication of different micron-sized opal architectures with complex form and designed optical functionality.