Red laser-induced domain inversion in MgO-doped lithium niobate crystals

A laser beam at wavelength 647 nm is focused on a sample of 5 mol% MgO-doped lithium niobate crystal for domain inversion by a conventional external electric field. In this case, a reduction of 36% in the electric field required for domain nucleation (nucleation field) is observed. To the best of our knowledge, it is the longest wavelength reported for laser-induced domain inversion. This extends the spectrum of laser inducing, and the experimental results are helpful to understand the nucleation dynamics under laser illumination. The dependence of nucleation fields on intensities of laser beams is analysed in experiments.

Analysis on fluorescence intensity reverse photonic phenomenon between red and green fluorescence of oxyfluoride nanophase vitroceramics

An interesting fluorescence intensity reverse photonic phenomenon between red and green fluorescence is investigated. The dynamic range. of intensity reverse between red and green fluorescence of Er( 0.5) Yb( 3): FOV oxyfluoride nanophase vitroceramics, when excited by 378.5nm and 522.5nm light respectively, is about 4.32 x 10(2). It is calculated that the phonon- assistant energy transfer rate of the electric multi- dipole interaction of {(4)G(11/2)( Er3+) -> F-4(9/2)( Er3+), F-2(7/2)( Yb3+). F-2(5/2)( Yb3+)} energy transfer of Er( 0.5) Yb( 3): FOV is around 1.380 x 10(8) s(-1), which is much larger than the relative multiphonon nonradiative relaxation rates 3.20 x 10(5) s(-1). That energy transfer rate for general material with same rare earth ion's concentration is about 1.194 x 10(5) s(-1). These are the reason to emerge the unusual intensity reverse phenomenon in Er( 0.5) Yb( 3): FOV. (C) 2007 Optical Society of America.

Green and red upconversion luminescence in ytterbium-sensitized erbrium-doped novel lead-free germanium bismuth lanthanum glass

Structural and infrared-to-visible upconversion fluorescence properties in ytterbium-sensitized erbrium-doped novel lead-free germanium bismuth-lanthanum glass have been studied. The structure of lead-free germanium-bismuth-lanthanum glass was investigated by peak-deconvolution of Raman spectrum, and the structural information was obtained from the peak wavenumbers. Intense green and red emissions centered at 525, 546, and 657 nm, corresponding to the transitions 2H(11/2) -> I-4(15/2), S-4(3/2) -> I-4(15/2), and F-4(9/2) -> I-4(15/2), respectively, were observed at room temperature. The quadratic dependence of the 525, 546, and 657 nm emissions on excitation power indicates that a two-photon absorption process occurs under 975 nm excitation. This novel lead-free germanium-bismuth-lanthanum glass with low maximum phonon energy (similar to 751 cm(-1)) can be used as potential host material for upconversion lasers. (c) 2005 Published by Elsevier B.V.

Two-photon excited red upconversion luminescence of thulium ions doped GeS2-In2S3-CsI glass

We report a novel phenomenon in GeS2-In2S3-CsI chalcohalide glass doped with Tm3+ ions. Under irradiation with an 808 nm laser diode, a bright red emission centered at 700 nm is observed for the first time in this glass. The log-log correlation between integrated emission intensity and pump power reveals that a two-photon absorption process is involved in the phenomenon, suggesting that the F-3(3,2) -> H-3(6) transition of Tm3+ ions is responsible for the appearance of the red emission. The results indicate that the indium (In) based chalcohalide glass containing Tm3+ ions is expected to find applications in visible lasers, high density optical storage and three-dimensional color displays. (C) 2009 Elsevier B.V. All rights reserved.