Improved purity of long-wavelength InAsSb epilayers grown by melt epitaxy in fused silica boats

In this study, we first present the process of the melt epitaxial (ME) growth method, and the improvement of low-temperature electron mobility of the long-wavelength InAsSb epilayers grown by ME in a fused silica boat. The electrical properties were investigated by van der Pauw measurement at 300 and 77 K. It is seen that the electron mobility of the InAsSb samples grown by graphite boat decreased from 55,700 to 26,600 cm(2)/V s when the temperature was reduced from 300 to 77 K, while for the samples grown by fused silica boat, the electron mobility increased from 52,600 at 300 K to 54,400 cm(2)/V s at 77 K. The electron mobility of 54,400cm(2)/Vs is the best result, so far, for the InAsSb materials with cutoff wavelength of 8-12 mum at 77 K. This may be attributed to the reduction of the carbon contamination by using a fused silica boat instead of a graphite boat. (C) 2002 Elsevier Science B.V. All rights reserved.

Liquid encapsulated-melt zone processing of GaAs

A liquid encapsulated melt Bone process has been developed for single crystal growth of GaAs. Single crystals of 40 mm long have been grown with this technique. To avoid unwanted nucleation events and maintain a constant crystal diameter, from top to bottom growth using a short zone with a convex zone surface was found to give the best results. An arsenic overpressure was used to in conjunction with a B2O3 encapsulant in order to suppress arsenic dissociation from the melt and maintain the stoichiometry of the crystal.

Electrical properties of semi-insulating GaAs grown from the melt under microgravity conditions

A technologically important undoped semi-insulating (SI) GaAs single crystal was successfully grown in the Chinese recoverable satellite as far as we know for the first time by using a similar growth configuration described previously. The experimental results proved that the space SI GaAs crystals have a lower density of defects and defect-impurity complexes as well as a better uniformity.

Crystallographic and electrochemical characteristics of melt-spun Ti–Zr–Ni–Y alloys

Ti45Zr30Ni25Yx (x = 1, 3, 5 and 7) alloys were prepared by melt-spinning at wheel velocity of 20 m s(-1). The effect of additive Y on phase structure and electrochemical performance of melt-spun alloys was investigated. Ti45Zr30Ni25Yx melt-spun alloys were composed of I-phase and amorphous phase. T

Crystallographic and electrochemical characteristics of melt-spun Ti-Zr-Ni-La alloys

Ti-based icosahedral quasicrystalline phase (I-phase) exhibited excellent hydrogen storage property for special structure. Unfortunately, the application as the negative electrode material of the nickel-metal hydride batteries was limited due to the poor electrochemical kinetics. Meanwhile, rare-earth element was beneficial to the electrochemical properties of Ti, Zr-based alloy.

Numerical Simulation of Reactive Extrusion Processes for Activated Anionic Polymerization

In order to deal with the complicated relationships among the variables of the reactive extrusion process for activated anionic polymerization, a three-dimensional equivalent model of closely intermeshing co-rotating twin screw extruders was established. Then the numerical computation expressions of the monomer concentration, the monomer conversion, the average molecular weight and the fluid viscosity were deduced, and the numerical simulation of the reactive extrusion process of Styrene was carried out. At last, our simulated results were compared with Michaeli's simulated results and experimental results. (C) 2007 Elsevier B.V. All rights reserved

Phase separation and crystallization in a melt-spun Ti45Zr35Ni17Cu3 alloy

Structure and crystallization behavior of amorphous and quasicrystalline Ti45Zr35Ni17Cu3 alloy have been studied. DSC trace of the amorphous alloy obtained during continuous heating to 1300 K shows distinctly an exothermic peak and two endothermic peaks.

Grafting acrylic acid onto polypropylene by reactive extrusion with pre-irradiated PP as initiator

In this paper, the modification of polypropylene (PP) with acrylic acid (AA) by reactive extrusion using pre-irradiated PP (rPP) as initiator was investigated. It was found the relatively high graft degree (Gd) and slight degradation of modified PP was obtained when 20 wt% rPP was used. This result can be explained in terms of effective concentration of free radicals.

Novel morphology of polyethylene crystals created upon melt crystallization of spin-coated film

We demonstrate a strikingly novel morphology of high-density polyethylene (HDPE) crystal obtained upon melt crystallization of spin-coated thin film. This crystal gives windmill-like morphology which contains a number of petals. A detailed inspection on this morphology reveals that each petal is actually composed of terrace-stacked PE lamellae, in which the polymer chains within crystallographic a-c planes adopt similar to 45 degrees tilting around b-axis. The surrounding domains associated with a petal of the windmill composed of twisted lamellar overgrowths with an identical orientation of their long axis, which is the crystallographic b-axis shared by the petal and its corresponding twisted lamellar overgrowths.

Crystallographic and electrochemical characteristics of Ti45Zr35Ni13Pd7 melt-spun alloys

Ti45Zr35Ni13Pd7 alloys are prepared by melt spinning at different cooling rates (v). The phase structure and electrochemical hydrogen storage performance are investigated. When U is 10 m/s, the alloy consists of icosahedral quasicrystalline phase (I-phase), C14 Laves phase and a little amorphous phase. When v increases to 20 or 30 m/s, a mixed structure of I-phase and amorphous phase is formed. Maximum discharge capacity of alloy electrode decreases from 156 mAh/g (v = 10 m/s) to 139 mAh/g (v = 30 m/s) with increasing v. High-rate discharge ability at the discharge current density of 240 mA/g decreases monotonically from 61.2% (v = 10 m/s) to 56.8% (v = 30 m/s).