Excellent antimicrobial properties of mesoporous anatase TiO2 and Ag/TiO2 composite films

Optically transparent, crack-free, mesoporous anatase TiO2 thin films were fabricated. The Ag/TiO2 composite films were prepared by incorporating Ag in the pores of TiO2 films with an impregnation method via photoreduction. The as-prepared composite films were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), X-ray photoelectronic spectra (XPS) and N-2 adsorption. The release behavior of silver ions in the mesoporous composite film was also studied. Moreover, the antimicrobial behaviors of the mesoporous film were also investigated by confocal laser scanning microscopy.

Preparation and properties of ternary polyimide/SiO2/polydiphenyisiloxane composite films

A series of novel ternary polyimide/SiO2/polydiphenylsiloxane (PI/SiO2/PDPhS) composite films were prepared through co-hydrolysis and condensation between tetramethoxysilane, diphenyldimethoxysilane (DDS) and aminopropyltriethoxysilane-terminated polyamic acid, using an in situ sol-gel method. The composite films exhibited good optical transparency up to 30 wt% of total content of DDS and SiO2. SEM analysis showed that the PDPhS and SiO2 were well dispersed in the PI matrix without macroscopic separation of the composite films. TGA analysis indicated that the introduction of SiO2 could improve the thermal stability of the composite films. Dynamic mechanical thermal analysis showed that the composite films with low DDS content (5 wt%) had a higher glass transition temperature (T-g) than pure PI matrix. When the content of DDS was above 10 wt%, the T-g of the composite decreased slightly due to the plasticizing effect of flexible PDPhS linkages on the rigid PI chains. The composite films with high SiO2 content exhibited higher values of storage modulus. Tensile measurements also showed that the modulus and tensile strength of the composite films increased with increasing SiO2 content, and the composite films still retained a high elongation at break due the introduction of DDS.

Morphology and thermal properties of conductive polyaniline/polyamide composite films

Polyaniline (PANI) in an emeraldine-base form, synthesized by chemical oxidation polymerization, was doped with camphor sulfonic acid (CSA). The conducting complex (PANI-CSA) and a matrix, polyamide-66, polyamide-11, or polyamide-1010, were dissolved in a mixed solvent, and the blend solution was dropped onto glass and dried for the preparation of PANI/polyamide composite films. The conductivity of the films ranged from 10(-7) to 10(0) S/cm when the weight fraction of PANI-CSA in the matrices changed from 0.01 to 0.09, and the percolation threshold was about 2 wt %. The morphology of the composite films before and after etching was studied with scanning electron microscopy, and the thermal properties of the composite films were monitored with differential scanning calorimetry. The results indicated that the morphology of the blend systems was in a globular form. The addition of PANI-CSA to the films resulted in a decrease in the melting temperature of the composite films and also affected the crystallinity of the blend systems.

Amperometric enzyme electrode for the determination of hydrogen peroxide based on sol-gel/hydrogel composite film

A new type of organic-inorganic composite material was prepared by sol-gel method, and a peroxidase biosensor was fabricated by simply dropping sor-gel-peroxidase mixture onto glassy carbon electrode surface. The sol-gel composite film and enzyme membrane were characterized by Fourier-transform infrared (FT-IR) spectroscopy and EQCM, the electrochemical behavior of the biosensor was studied with potassium hexacyanoferrate(II) as a mediator, and the effects of pH and operating potential were explored for optimum analytical performance by using amperometric method. The response time of the biosensor was about 10 s; the linear range was up to 3.4 mM with a detection limit of 5 x 10(-7) M. The sensor also exhibited high sensitivity (15 mu A mM(-1)) and good long-term stability. In addition, the performance of the biosensor was investigated using flow injection analysis (FIA), and the determination of hydrogen peroxide in real samples was discussed. (C)2000 Elsevier Science B.V. All rights reserved.

Studies on the room temperature conductivity of PEO-LiClO4-Al2O3 composite polymer electrolyte

A composite polymer electrolyte of Polyethylene oxide (PEO)-LiClO4 containing fine Al2O3 particles was studied by using differential scanning calorimetry, infrared spectroscopy and electrochemical impedance spectroscopy. Compared with the polymer electrolyte without Al2O3 particles, the glass transition temperature and the degree of crystallinity were decreased, and the room temperature conductivity of PEO-LiClO4-Al2O3 composite polymer electrolyte was considerably enhanced. Moreover, the equivalent circuits and the effect of dc potential on impedance spectroscopy were discussed.

Functionalized inorganic-organic composite material derivated by sol-gel for construction of mediated amperometric hydrogen peroxide biosensor

A novel functionalized inorganic-organic hybrid material with cation exchange property was prepared by sol-gel method. The H2O2 biosensor was fabricated by simply dipping the horseradish peroxidase-containing functionalized membrane modified electrode into Meldola's blue (MDB) solution. MDB was adsorbed and firmly immobilized within the membrane. The electrochemical behavior of MDB incorporated in the membrane was more reversible compared with that of the solution species and suitable as mediator for the horseradish peroxidase. The response time was less than 25 s. Linear range is up to 0.6 mM (COH. coeff. 0.9998) with detection Limit of 9 x 10(-7) M. High sensitivity of 75 nA mu M cm(-2) was obtained due to high MDB-loading. The biosensor exhibited a good stability. (C) 1999 Elsevier Science B.V. All rights reserved.

THE EFFECT OF LOADING PARAMETERS ON FATIGUE BEHAVIOR OF INJECTION-MOLDED COMPOSITE

Flexural fatigue tests were performed on an injection-moulded glass-fiber reinforced blend of polyphenylene ether ketone and polyphenylene sulfide composite using four-point bending at a series of fixed mean stress levels with varying stress amplitude. Attention was given to identifying the effects of mean stress and stress amplitude on the fatigue life and failure mechanisms. It was found that the fatigue life of the studied material decreased sharply with increasing stress amplitude at a constant mean stress level and also decreased at a fixed stress amplitude with increasing mean stress. However, analyses of the fatigue data and failure behaviour reveal that, for the studied material, fatigue failure mechanisms depend on the relative importance of mean stress and stress amplitude. At a mean stress level of 80% ultimate flexural strength, the failure results from accumulation of creep strain, while at mean stress levels of 40%, 50% and 60% ultimate flexural strength, the magnitude of stress amplitude influences the type of failure mechanism. As stress amplitude is reduced, the fatigue failure mechanism changes from matrix yielding dominated to crack growth dominated fracture.