Nd3+掺杂的氧化镧钇透明激光陶瓷的光谱性能研究

Nd3+-doped Y2-2x La-2x O-3 (x = 0.08) transparent ceramics were fabricated by conventional fabrication process. Spectroscopic properties of the samples were investigated. The absorption band of Nd3+ : Y1.84La0.16O3 was broad covering the wavelength range 780-850 nm. When doped with 1.5at% Nd3+, the cross sections of the sample at 820 nm and laser diode pumped 808 nm were 1.81 x 10(-20) cm(2) and 1.54 x 10(-20) cm(2), respectively. The strongest emission peak of the sample was centered at 1078 mn with long fluorescent lifetime, broad emission bandwidth and high quantum efficiency. Because of the additive La2O3, the spectroscopic quality parameter (X-Nd) of matrix was' decreased from 1.6 to 0.46, thus the fluorescence branch ratio of F-4(3/2) - (4) I-11/2 transition was increased to 56.82%. These properties of Nd3' : Y1.84La0.16O3 transparent ceramic are benefitial to achieve high efficient laser output and ultrashort modelocked pulse.

铬、钕双掺钆镓石榴石（Cr^4＋，Nd^3＋）：Gd3Ga5O12激光晶体光学性能的研究

用提拉法生长了掺铬、钕的钆镓石榴石(Cr^4+，Nd^3+：GGG)自调Q激光品体。报道了室温下的吸收光谱和荧光光谱特性。分析了Cr离子浓度对光谱性质的影响。比较了Cr^4+：GGG，Nd^3+：GGG和(Cr^4+，Nd^3+)：GGG晶体吸收光谱的关系。测量了(Cr^4+，Nd^3+)：GGG晶体和Nd^3+：GGG晶体的荧光寿命，它们分别是33μs和250μs。实验表明，(Cr^4+，Nd^3+)：GGG晶体是一种非常有潜力的自调Q激光晶体，可以实现大功率激光器的小型化和全固态化。

Effect of La2O3 on microstructure and transmittance of transparent alumina ceramics

Optically transparent alumina ceramics were fabricated by conventional process and sintered without pressure in H-2 atmosphere. The results indicate that relative densities of alumina specimens increase to theoretical densities (T. D.) with increasing content of La2O3. With increasing holding time during sintering, much less pores and larger grains were found in the sintered alumina samples. Higher transmittance was achieved in alumina codoped with MgO and La2O3 as compared with that doped with MgO only. The total-transmittance of alumina sample is up to 86% at a wavelength range of 300 - 800 nm.

激光二极管抽运Na，Yb共掺CaF2晶体自调Q激光特性的研究

利用激光二极管（LD）抽运新型Na．Yb共掺CaF2（Na．Yb：CaF2）晶体，获得了1．05μm的自调Q激光输出。利用透射率1％的耦合输出镜，得到最低激光输出的抽运阈值功率仅为70mW。在透射率为2％的输出镜条件下，得到最大输出激光功率为390mw，此时激光的斜度效率达到20%。实验详细记录了自调Q脉冲的周期和宽度随抽运功率的变化关系，随着抽运功率的增加，自调Q脉冲的周期和宽度呈指数衰减。同时，还采用单棱镜进行光谱调谐实验，获得了1036～1059nm的自调Q激光调谐输出。

Growth and spectroscopic characteristics of Yb : LPS single crystal

For the first time, a high optical quality Yb3+-doped lutetium pyrosilicate laser crystal Lu2Si2O7 (LPS) was grown by the Czochralski (Cz) method. The segregation coefficient of ytterbium ion in Yb:LPS crystal detected by the inductively coupled plasma atomic emission spectrometer (TCP-AES) method is equal to 0.847. X-ray powder diffraction result confirms the C2/m phase monoclinic space group of the grown crystal and the peaks corresponding to different phases were indexed. The absorption and fluorescence spectra, as well as fluorescence decay lifetime of Yb3+ ion in LPS have been investigated. The absorption and fluorescence cross-sections of the transitions F-2(7/2) <-> F-2(5/2) of Yb3+ ion in LPS crystal have been determined. The advantages of the Yb:LPS crystal including high crystal quality, quasi-four-level laser operating scheme, high absorption cross-sections (1.33 x 10(-2) cm(2)) and particularly broad emission bandwidth (similar to 62 nm) indicated that the Yb:LPS crystal seemed to be a promising candidate used as compact, efficient thin chip lasers when LD is pumped at 940 and 980 nm due to its low-symmetry monoclinic structure and single crystallographic site. (c) 2007 Elsevier B.V. All rights reserved.

Passively Q-switched Yb3+ laser with Yb3+-doped CaF2 crystal as saturable absorber

Passive Q-switching of a diode-pumped Yb:LYSO laser at 1060 nm with a Yb3+ ions-doped CaF2 crystal without the excited-state absorption (ESA) was demonstrated. An average output power of 174 mW with pulse duration of 5.6 mu s and repetition rate of 27 kHz have been obtained under the unoptimized conditions. And the Q-switching conversion efficiency was as high as 51.7%. (c) 2007 Optical Society of America.

Growth of high quality Cr, Yb codoped gadolinium gallium garnet (Gd3Ga5O12) crystal and its spectral properties

The Cr(0.1%),Yb(10%):GGG crystals have been grown by the Czochralski method. The chemical composition is: Yb0.33Gd2.47Cr0.005Ga5.2O12. There are no observed Yb3+ ions substituting Ga3+ ions, just like that of Yb:GGG crystals. The defects in Cr,Yb:GGG crystal were also investigated. The absorption and emission spectra of Cr,Yb:GGG crystal at room temperature have been measured. The 02 and H-2 annealing effect of Cr,Yb:GGG crystal have been compared. Cr3+ can greatly weak the visible luminescence of this crystal. The Cr-Yb-codoped crystals may be potential materials for compact, efficient, high stability LD pumped solid state lasers. (C) 2006 Elsevier B.V. All rights reserved.

室温下光纤耦合二极管泵浦Tm：YAP激光器

为实现室温下小型化、高效率的1.9μm激光输出,采用793.5 nm激光二极管泵浦Tm：YAP晶体,晶体采用热电制冷及风冷的方式控制在18℃,采用1∶1的聚焦耦系统,获得功率为2.2 W、中心波长为1928 nm的激光输出,光光转换效率为31%,斜率效率达41%。对影响激光输出的耦合输出率、腔型、腔长、晶体工作温度等因素进行了实验分析,实验结果表明：输出功率的变化与温度基本成线性关系,当增加激光谐振腔长时,由于高阶模式损耗加大以及晶体热透镜效应的加重导致腔内损耗加大,输出功率和斜率效率都有所下降。

Yb：YAG透明陶瓷的制备和激光输出

制备了高质量的Yb：YAG透明陶瓷．Yb：YAG透明陶瓷的晶粒尺寸为10μm左右且分布均匀，晶界处和晶粒中没有杂质、气孔的存在．Yb：YAG样品中所有元素分布均匀，不同的晶粒间，晶粒和晶界间成分是一致的，没有出现成分的偏析．4mm厚样品的透过率为80％．LD泵浦获得了波长为1030nm，最大功率为268mW的连续激光输出．

共掺Na^＋的Yb^3＋：CaF2晶体的荧光分析与低阈值激光运转

基于975nm激发的室温下荧光光谱测量，系统地研究了在新型钠、镱共掺的氟化钙晶体中钠离子的作用机理，分析了掺钠离子浓度与激光阈值的关系，获得了具有最低激光阈值的掺杂浓度优化配比．激光实验表明对于2％Yb^3＋离子浓度的氟化钙，掺入3％的钠离子能够获得最低阈值的激光运转，这与理论和荧光分析完全一致．

高效室温下激光二极管泵浦Tm:YAP激光器

文章报道了室温下二极管泵浦Tm：YAP激光器，最大输出功率5.2瓦，波长为1981nm，斜率效率是30％。实验测量800nm左右晶体的吸收谱以及1800nm附近的荧光发射谱。此外，讨论了输出功率随晶体工作温度关系。

Yb:YAP与Yb:YAG晶体光谱性能比较

应用中频感应提拉法生长出掺杂浓度为10 at.-%的Yb:YAG与Yb:YAP晶体，对比了室温下两种晶体的吸收和发射光谱特性。结果表明，Yb:YAG晶体比Yb:YAP晶体有更好的激光性能和低的阈值；同时对比发现，Yb:YAP晶体的吸收截面是Yb:YAG晶体的2.16倍，它容易实现LD泵；由于Yb:YAP晶体的各向异性，它有轴向效应明显，它可以产生偏振激光。

7.3 W of single-frequency output power at 2.09 μm from an Ho:YAG monolithic nonplanar ring laser

Single-frequency output power of 7.3 W at 2.09 mu m from a monolithic Ho:YAG nonplanar ring oscillator (NPRO) is demonstrated. Resonantly pumped by a Tm-doped fiber laser at 1.91 mu m, the Ho:YAG NPRO produces 71% of slope efficiency with respect to absorbed pump power and nearly diffraction-limited output with a beam quality parameter of M-2 approximate to 1.1. (c) 2008 Optical Society of America

Judd-Ofelt analysis of spectra and experimental evaluation of laser performance of Tm3+ doped Lu2SiO5 crystal

This paper reports that the TM3+:Lu2SiO5 (Tm:LSO) crystal is grown by Czochralski technique. The room-temperature absorption spectra of Tm:LSO crystal are measured on a b-cut sample with 4 at.% thulium. According to the obtained Judd-Ofelt intensity parameters Omega(2)=9.3155 x 10(-20) cm(2), Omega(4)=8.4103 x 10(-20) cm(2), Omega(6)=1.5908 x 10(-20) cm(2), the fluorescence lifetime is calculated to be 2.03 ms for F-3(4) -> H-3(6) transition, and the integrated emission cross section is 5.81 x 10(-18) cm(2). Room-temperature laser action near 2 mu m under diode pumping is experimentally evaluated in Tm:LSO. An optical-optical conversion efficiency of 9.1% and a slope efficiency of 16.2% are obtained with continuous-wave maximum output power of 0.67 W. The emission wavelengths of Tm:LSO laser are centred around 2.06 mu m with spectral bandwidth of similar to 13.6 nm.