Preparation and characterization of Pd-Ag alloy composite membrane with magnetron sputtering

A Pd-Ag (24 wt%) alloy composite membrane was prepared by the magnetron sputtering. A gamma-Al2O3 membrane was synthesized by the sol-gel method and used as substrate of the Pd-Ag alloy film. The process parameters of the magnetron sputtering were optimized as a function of the compactness of the Pd-Ag alloy film. The best membrane with a thickness of 1 mu m was produced with a sputtering pressure of 2.7 Pa and a substrate temperature of 400 degrees C. The membrane had an H-2/N-2 permselectivity of 51.5-1000 and an H-2 permeation rate of 0.036-1.17 x 10(-5)cm(3)/cm(2).s. Pa, depending on operating conditions.

Preparation of a novel polysulfone/polyethylene oxide/silicone rubber multilayer composite membrane for hydrogen-nitrogen separation

A novel poly sulfone/polyethylene oxide/silicone rubber (PSOPEO/SR) multilayer composite membrane was fabricated by double coating polysulfone substrate membrane with polyethylene oxide and silicone rubber. Gas permeation experiments were performed at 30 degrees C for hydrogen and nitrogen. PSf(PEO/SR membrane displayed high and steady performance for H-2/N-2: permeances of H-2 and N-2 of 49.51 and 0.601 GPU, respectively, and H-2/N-2 ideal separation factor of 82.3. It was explained that layer interfaces due to the introduction of PEO layer act as the permselective media and are responsible for the higher H-2/N-2 ideal separation factor which has exceeded the intrinsic permselectivities of the three polymers used in this study. (c) 2005 Elsevier B.V. All rights reserved.

A novel PTFE-reinforced multilayer self-humidifying composite membrane for PEM fuel cells

A novel polytetrafluoroethylene (PTFE)-reinforced multilayer self-humidifying composite membrane is developed. The membrane is composed of Nafion-impregnated porous PTFE composite as the central layer and nanosized SiO2 supported Pt catalyst imbedded into Nafion as the two side layers. The proton exchange membrane (PEM) fuel cells employing the self-humidifying membrane (20 mu m thick) under dry H-2/O-2 gave a peak power density of 0.95 W/cm(2) and an open-circuit voltage of 1.032 V. The good membrane performance is attributed to hygroscopic Pt-SiO2 catalyst at the two side layers, which results in enhanced anode side self-humidification function and decreased cathode polarization. (c) 2005 The Electrochemical Society.

Investigation of LSM1.1-ScSZ composite cathodes for anode-supported solid oxide fuel cells

La0.8Sr0.2Mn1.1O3 (LSM1.1)-10 mol% Sc2O3-Stabilized ZrO2 co-doped with CeO2 (ScSZ) composite cathodes were investigated for anode-supported solid oxide fuel cells (SOFCs) with thin 8 mol% Y2O3-stabilized ZrO2 (YSZ) electrolyte. X-ray diffraction (XRD) results indicated that the ScSZ electrolytes displayed good chemical compatibility with the nonstoichiometric LSM1.1 against co-firing at 1300 degrees C. Increasing the CeO2 content in the ScSZ electrolytes dramatically suppressed the electrode polarization resistance, which may be related to the improved surface oxygen exchange or the enlarged active area of cathode. The 5Ce10ScZr was the best electrolyte for the composite cathodes, which caused a small ohmic resistance decrease and the reduced polarization resistance and brought about the highest cell performance. The cell performances at lower temperatures seemed to rely on the electrode polarization resistance more seriously, than the ohmic resistance. Compared with the cell impedance at higher temperatures, the higher the 5Ce10ScZr proportion in the composite cathodes, the smaller the increment of the charge transfer resistance at lower temperatures. The anode-supported SOFC with the LSM1.1-5Ce10ScZr (60:40) composite cathode achieved the maximum power densities of 0.82 W/cm(2) at 650 degrees C and 2.24 W/cm(2) at 800 degrees C, respectively. (c) 2005 Elsevier B.V. All rights reserved.