Tentative analysis of Swirl defects in silicon crystals

Swirl defects in dislocation-free Czochralski (CZ) silicon crystals have been investigated by preferential etching, transmission electron microscopy (TER I) and electron energy loss spectroscopy (EELS) mode of a scanning transmission electron microscope (STEM). Two kinds of Swirl defects have been found with a good correspondence between striated pattern consisting of hillocks and the buried micro-defects. The Swirl defects were identified as perfect dislocation loop cluster and tetrahedral precipitate, respectively. In addition, a kind of tiny micro-defects is found to be distributed preferentially in the vicinity of the Swirl pattern although there is no detectable correspondence between hillocks and the micro-defects. The energy-filtered images have been obtained by the plasma peaks at different parts of a coherent precipitate with the Si matrix. The experimental results show some indications of the existence of oxygen and carbon in the core of the precipitate and suggest that oxygen and carbon may play important roles in the formation of Swirl defect. (C) 2000 Elsevier Science B.V. All rights reserved.

Polycrystalline silicon films prepared by improved pulsed rapid thermal annealing

An improved pulsed rapid thermal annealing (PRTA) has been used for the solid-phase crystallization (SPC) of a-Si films prepared by PECVD. The SPC can be completed with time-temperature budgets such as 10 cycles of 60-s 550 degrees C thermal bias/1-s 850 degrees C thermal pulse. The microstructure and surface morphology of the crystallized films are investigated by X-ray diffraction (XRD). The results indicate that this PRTA is a suitable post-crystallization technique for fabricating large-area poly-Si films on low-cost substrate. (C) 2000 Elsevier Science B.V. All rights reserved.

Raman scattering of nanocrystalline silicon embedded in SiO2

Raman scattering of nanocrystalline silicon embedded in SiO2 matrix is systematically investigated. It is found that the Raman spectra can be well fitted by 5 Lorentzian lines in the Raman shift range of 100-600 cm(-1). The two-phonon scattering is also observed in the range of 600-1100 cm(-1) The experimental results indicate that the silicon crystallites in the films consist of nanocrystalline phase and amorphous phase; both can contribute to the Raman scattering. Besides the red-shift of the first order optical phonon modes with the decreasing size of silicon nanocrystallites, we have also found an enhancement effect on the second order Raman scattering, and the size effect on their Raman shift.

Improvement of thin silicon on sapphire (SOS) film materials and device performances by solid phase epitaxy

The increased emphasis on sub-micron CMOS/SOS devices has placed a demand for high quality thin silicon on sapphire (SOS) films with thickness of the order 100-200 nm. It is demonstrated that the crystalline quality of as-grown thin SOS films by the CVD method can be greatly improved by solid phase epitaxy (SPE) process: implantation of self-silicon ions and subsequent thermal annealing. Subsequent regrowth of this amorphous layer leads to a greater improvement in silicon layer crystallinity and channel carrier mobility, evidenced, respectively, by double crystal X-ray diffraction and electrical measurements. We concluded that the thin SPE SOS films are suitable for application to high-performance CMOS circuitry. (C) 2000 Elsevier Science S.A. All rights reserved.

Absorption spectra of nanocrystalline silicon embedded in SiO2 matrix

Nanocrystalline silicon (nc-Si) embedded SiO2 matrix has been formed by annealing the SiOx films fabricated by plasma-enhanced chemical vapor deposition (PECVD) technique. Absorption coefficient and photoluminescence of the films have been measured at room temperature. The experimental results show that there is an "aUrbach-like" b exponential absorption in the spectral range of 2.0-3.0 eV. The relationship of (alpha hv)(1/2) proportional to(hv - E-g) demonstrates that the luminescent nc-Si have an indirect band structure. The existence of Stokes shift between photoluminescence and absorption edge indicates that radiative combination can take place not only between electron states and hole states but also between shallow trap states of electrons and holes. (C) 2000 Elsevier Science B.V. All rights reserved.

The new exploration for proton-implanted silicon: the conversion of a surface-region-purification-induced p-n junction into a p-i-n electrical structure approaching silicon on insulator

A surface-region-purification-induced p-n junction, a puzzle discovered at Brookhaven National Laboratory, in a silicon-on-defect-layer (SODL) material has been explored by carrying out various annealing conditions and subsequent measurements on electrical properties. The origin of the pn junction has been experimentally investigated. Furthermore, the p-n junction has been transformed into a p-i-n electrical structure by adding a high temperature annealing process to the previously used SODL procedure, making the SODL material approach silicon on insulator (SOI). The control of the initial oxygen amount in the silicon material is suggested to be critical for the experimental results.

Microstructures of microcrystalline silicon thin films prepared by hot wire chemical vapor deposition

Undoped hydrogenated microcrystalline silicon (mu c-Si:H) thin films were prepared at low temperature by hot wire chemical vapor deposition (HWCVD). Microstructures of the mu c-Si:H films with different H-2/SiH4 ratios and deposition pressures have been characterized by infrared spectroscopy X-ray diffraction (XRD), Raman scattering, Fourier transform (FTIR), cross-sectional transmission electron microscopy (TEM) and small angle X-ray scattering (SAX). The crystallization of silicon thin film was enhanced by hydrogen dilution and deposition pressure. The TEM result shows the columnar growth of mu c-Si:H thin films. An initial microcrystalline Si layer on the glass substrate, instead of the amorphous layer commonly observed in plasma enhanced chemical vapor deposition (PECVD), was observed from TEM and backside incident Raman spectra. The SAXS data indicate an enhancement of the mass density of mu c-Si:H films by hydrogen dilution. Finally, combining the FTIR data with the SAXS experiment suggests that the Si--H bonds in mu c-Si:H and in polycrystalline Si thin films are located at the grain boundaries. (C) 2000 Elsevier Science S.A. All rights reserved.

Optical properties of nanometer silicon prepared by silicon ion implanted into SiO2 layers

The samples of silicon nanocrystals (nc-Si) were prepared by Si ion implanted into SiO2 layers. Photoluminescence spectra were measured at room temperature and their dependence on thermal annealing was investigated. The experimental results show that PL peaks originate from the defects in SiO2 layers caused by ion implantation when the thermal annealing temperature is lower than 800 C. The PL peak from nc-Si was observed when the thermal annealing temperature was higher than 900 C, and PL intensity reached its maximum at the thermal annealing temperature of 1100 C. As the annealing temperature increases the red shift of PL peak from nc-Si shows the quantum size effect. The characterized Raman scattering peak of nc-Si was observed at the right angle scattering configuration for the first time. It provides further support for the PL measurements.

Investigation of absorption of nanocrystalline silicon

Nanocrystalline silicon embedded SiO2 matrix is formed by annealing the SiO2 films fabricated by plasma enhanced chemical vapor deposition technique. In conjunction with the micro-Ramam spectra, the absorption spectra of the films have been investigated. The blue-shift of absorption edge with decreasing size of silicon crystallites is due to quantum confinement effect. It is found that nanocrystalline silicon is of an indirect band structure, and that the absorption presents an exponential dependance absorption coefficient on photon energy ii! the range of 2.0-3.0 eV, and a sub-band appears in the the range of 1.0-1.5 eV. We believe that the exponential absorption is due to the indirect band-to-band transition of electrons in silicon nanocrystallites, while the Sub-band absorption is ascribed to transitions between the amorphous silicon states existing in the films.

Arsenic clusters on the surface of vertically aligned InAs islands on GaAs substrate by annealing

The formation of arsenic clusters in a system of vertically aligned InAs quantum islands on GaAs during thermal annealing under As overpressure has been investigated by transmission electron microscopy (TEM) and Raman scattering. Semicoherent arsenic clusters, identified by TEM examination, have been formed on the surface of the GaAs capping layer. The existence of arsenic precipitates is also confirmed by Raman spectra, showing new peaks from the annealed specimen at 256 and 199 cm(-1). These peaks have been ascribed to A(1g) and E-g Raman active phonons of crystalline arsenic. The phenomenon can be understood by a model of strain-induced selected growth under As overpressure. (C) 1999 American Institute of Physics. [S0003-6951(99)02045-8].

Optical properties of nanocrystalline silicon embedded in SiO2

Nanocrystalline silicon embedded SiO2 matrix has been formed by annealing the a-SiOx films fabricated by plasma enhanced chemical vapor deposition technique. Absorption and photoluminescence spectra of, the films have been studied in conjunction with micro-Raman scattering spectra. It is found that absorption presents an exponential dependence of absorption coefficient to photon energy in the range of 1.5-3.0 eV, and a sub-band appears in the range of 1.0-1.5 eV. The exponential absorption is due to the indirect band-to-band transition of electrons in silicon nanocrystallites, while the sub-band absorption is ascribed to transitions between surfaces and/or defect states of the silicon nanocrystallites. The existence of Stokes shift between absorption and photoluminescence suggests that the phonon-assisted luminescence would he enhanced due to the quantum confinement effects.

First charge collection and position-precision data on the medium-resistivity silicon strip detectors before and after neutron irradiation up to 2x10(14) n/cm(2)

Test strip detectors of 125 mu m, 500 mu m, and 1 mm pitches with about 1 cm(2) areas have been made on medium-resistivity silicon wafers (1.3 and 2.7 k Ohm cm). Detectors of 500 mu m pitch have been tested for charge collection and position precision before and after neutron irradiation (up to 2 x 10(14) n/cm(2)) using 820 and 1030 nm laser lights with different beam-spot sizes. It has been found that for a bias of 250 V a strip detector made of 1.3 k Ohm cm (300 mu m thick) can be fully depleted before and after an irradiation of 2 x 10(14) n/cm(2). For a 500 mu m pitch strip detector made of 2.7 k Ohm cm tested with an 1030 nm laser light with 200 mu m spot size, the position reconstruction error is about 14 mu m before irradiation, and 17 mu m after about 1.7 x 10(13) n/cm(2) irradiation. We demonstrated in this work that medium resistivity silicon strip detectors can work just as well as the traditional high-resistivity ones, but with higher radiation tolerance. We also tested charge sharing and position reconstruction using a 1030 nm wavelength (300 mu m absorption length in Si at RT) laser, which provides a simulation of MIP particles in high-physics experiments in terms of charge collection and position reconstruction, (C) 1999 Elsevier Science B.V. All rights reserved.

High-frequency hydrogen-related infrared modes in silicon grown in a hydrogen atmosphere

High-frequency vibrational modes have been observed at liquid-helium temperature in silicon samples grown in a H-2 or D-2 atmosphere. The highest-frequency ones are due to the overtones and combination modes of SiH fundamentals. Others are CH modes due to (C,H) complexes, but the simultaneous presence of NH modes due to (N,H) complexes cannot be excluded. The present results seem to show also the existence of centers including both SiH and CH or NH bonds. One sharp mode at 4349 cm-l is related to a weak SiH fundamental at 2210 cm(-1). The related center is ascribed to a vacancy fully decorated with hydrogen with a nearest-neighbor C atom. [S0163-1829(99)00911-X].

New annealing processes and explanation for novel silicon pn junctions formed by proton implantation

Proton-implanted n-type Si wafers were annealed at 950 degrees C to achieve novel pn junctions. The novel pn junctions are explained by the combined use of four models. The background (e.g. oxygen impurity) of an Si wafer is suggested to play a key role in creating the novel pn junction.

Neutron irradiation-infrared based measurement method for interstitial oxygen in heavily boron-doped silicon

A novel method, based on an infrared absorption and neutron irradiation technique, has been developed for the determination of interstitial oxygen in heavily boron-doped silicon. The new procedure utilizes fast neutron irradiated silicon wafer specimens. On fast neutron irradiation, the free carriers of high concentration in silicon can be trapped by the irradiated defects and the resistivity increased. The resulting calibration curve for the measurement of interstitial oxygen in boron-doped silicon has been established on the basis of the annealing behaviour of irradiated boron-doped CZ silicon.