Influence of ion energy and deposition temperature on the surface morphology of carbon films deposited by ion beams

Carbon films were deposited by mass-selected ion beam technique with ion energies 50-200eV at a substrate temperature from room temperature to 80 degreesC,. For the energies used, smooth diamond-like carbon films were deposited at room temperature. When the substrate temperature was 600 degreesC,rough graphitic films were produced. But highly oriented carbon tubes were observed when the energies were larger than 140eV at 800 degreesC. They were perpendicular to the surface and parallel to each other. preferred orientation of graphite basic plane was observed by high-resolution electron microscopy. Shallow ion implantation and stress are responsible for this orientation.

Surface roughness and high density of cubic twins and hexagonal inclusions in cubic GaN epilayers

Surface roughness and its correlation with the polarity of internal hexagonal inclusions and cubic twins have been investigated by atomic force microscopy (AFM), scanning electron microscopy (SEM), transmission electron microscopy (TEM) and X-ray diffraction (XRD). The surface roughness resulted from large amount of strips, which prolonged in [1 (1) over bar0] direction with small size in [110] or [110] direction. The sidestep of each strip is just the top of high density of hexagonal inclusions or cubic microtwins. Moreover, XRD shows that the amount of hexagonal inclusions and cubic microtwins measured in [110] direction are twice or more as much as in [110] direction. Therefore, it is hexagonal inclusions, cubic twins and their distributive polarity that is responsible to the surface characteristics of cubic GaN epilayers.

Annealing-induced evolution of defects in low-temperature-grown GaAs-related materials

Infrared absorption spectroscopy, optical transient current spectroscopy (OTCS), and photoluminescence (PL) spectroscopy are used to investigate the annealing induced evolution of defects in low-temperature (LT)-grown GaAs-related materials. Two LT samples of bulk GaAs (sample A) and GaAs/AlxGa1-xAs multiple-quantum-well. (MQW) structure (sample B) were grown at 220 and 320 degreesC on (001) GaAs substrates, respectively. A strong defect-related absorption band has been observed in both as-grown samples A and B. It becomes weaker in samples annealed at temperatures above 600 degreesC. In sample A, annealed in the range of 600-800 degreesC, a large negative decay signal of the optical transient current (OTC) is observed in a certain range of temperature, which distorts deep-level spectra measured by OTCS, making it difficult to identify any deep levels. At annealing temperatures of 600 and 700 degreesC, both As-Ga antisite and small As cluster-related deep levels are identified in sample B. It is found that compared to the As cluster, the As-Ga antisite has a larger activation energy and carrier capture rate. At an annealing temperature of 800 degreesC, the large negative decay signal of the OTC is also observed in sample B. It is argued that this negative decay signal of the OTC is related to large arsenic clusters. For sample B, transient PL spectra have also been measured to study the influence of the, defect evolution on optical properties of LT GaAs/AlxGa1-xAs MQW structures. Our results clearly identify a defect evolution from AS(Ga) antisites to arsenic clusters after annealing.

Investigation of defects in low-temperature-grown GaAs using optical transient spectroscopy

Optical transient current spectroscopy (OTCS) has been used to investigate defects in the low-temperature-grown GaAs after postgrowth rapid thermal annealing (RTA). Two samples A and B were grown at 220 degreesC and 360 degreesC on (001) GaAs substrates, respectively. After growth, samples were subjected to 30s RTA in the range of 500-800 degreesC. Before annealing, X-ray diffraction measurements show that the concentrations of the excess arsenic for samples A and B are 2.5 x 10(19) and 1 x 10(19) cm(-3), respectively. It is found that there are strong negative decay signals in the optical transient current (OTC) for the annealed sample A. Due to the influence of OTC strong negative decay signals, it is impossible to identify deep levels clearly from OTCS. For a comparison, three deep levels can be identified for sample B before annealing. They are two shallower deep levels and the so-called As-Ga antisite defect. At the annealing temperature of 600 degreesC, there are still three deep levels. However, their structures are different from those in the as-grown sample. OTC strong negative decay signals are also observed for the annealed sample B. It is argued that OTC negative decay signals are related to arsenic clusters. (C) 2000 Elsevier Science B.V. All rights reserved.

Design consideration and performance of high-power and high-brightness InGaAs-InGaAsP-AlGaAs quantum-well diode lasers (lambda=0.98 mu m)

In this paper, we conduct a theoretical analysis of the design, fabrication, and performance measurement of high-power and high-brightness strained quantum-well lasers emitting at 0.98 mum, The material system of interest consists of an Al-free InGaAs-InGaAsP active region and AlGaAs cladding layers. Some key parameters of the laser structure are theoretically analyzed, and their effects on the laser performance are discussed. The laser material is grown by metal-organic chemical vapor deposition and demonstrates high quality with low-threshold current density, high internal quantum efficiency, and extremely low internal loss. High-performance broad-area multimode and ridge-waveguide single-mode laser devices are fabricated. For 100-mum-wide stripe lasers having a cavity length of 800 mum, a high slope efficiency of 1.08 W-A, a low vertical beam divergence of 34 degrees, a high output power of over 4.45 W, and a very high characteristic temperature coefficient of 250 K were achieved. Lifetime tests performed at 1.2-1.3 W (12-13 mW/mum) demonstrates reliable performance. For 4-mum-wide ridge waveguide single-mode laser devices, a maximum output power of 394 mW and fundamental mode power up to 200 mW with slope efficiency of 0.91 mW/mum are obtained.

Evolution from point defects to arsenic clusters in low-temperature grown GaAs/AlGaAs multiple quantum wells

Optical transient current spectroscopy (OTCS), photoluminescence (PL) spectroscopy and excitonic electroabsorption spectroscopy have been used to investigate the evolution of defects in the low-temperature grown GaAs/AlGaAs multiple quantum well structures during the postgrowth rapid thermal annealing. The sample was grown at 350 degrees C by molecular beam epitaxy on miscut (3.4 degrees off (001) towards (111)A) (001) GaAs substrate. After growth, the sample was subjected to 30s rapid thermal annealing in the range of 500-800 degrees C. It is found that the integrated PL intensity first decreases with the annealing temperature, then gets a minimum at 600 degrees C and finally recovers at higher temperatures. OTCS measurement shows that besides As,, antisites and arsenic clusters, there are several relatively shallower deep levels with excitation energies less than 0.3 eV in the as-grown and 500 degrees C-annealed samples. Above 600 degrees C, OTCS signals from As,, antisites and shallower deep levels become weaker, indicating the decrease of these defects. It is argued that the excess arsenic atoms group together to form arsenic clusters during annealing. (C) 2000 Elsevier Science B.V. All rights reserved.

Photoluminescence and Raman scattering of silicon nanocrystals prepared by silicon ion implantion into SiO2 films

Photoluminescence (PL) and Raman spectra of silicon nanocrystals prepared by Si ion implantion into SiO2 layers on Si substrate have been measured at room temperature. Their dependence on annealing temperature was investigated in detail. The PL peaks observed in the as-implanted sample originate from the defects in SiO2 layers caused by ion implantation. They actually disappear after thermal annealing at 800 degrees C. The PL peak from silicon nanocrystals was observed when thermal annealing temperatures are higher than 900 degrees C. The PL peak is redshifted to 1.7 eV and the intensity reaches maximum at the thermal annealing temperature of 1100 degrees C. The characterized Raman scattering peak of silicon nanocrystals was observed by using a right angle scattering configuration. The Raman signal related to the silicon nanocrystals appears only in the samples annealed at temperature above 900 degrees C. It further proves the formation of silicon nanocrystals in these samples. (C) 2000 American Institute of Physics. [S0021-8979(00)00215-2].

High power 980 nm Al-free strained quantum-well lasers for erbium-doped fiber amplifiers

In this paper, we reported on the fabrication of 980 nm InGaAs/InGaAsP strained quantum-well (QW) lasers with broad waveguide. The laser structure was grown by low-pressure metalorganic chemical vapor deposition on a n(+)- GaAs substrate. For 3 mu m stripe ridge waveguide lasers, the threshold current is 30 mA and the maximum output power and the output power operating in fundamental mode are 350 mW and 200 mW, respectively. The output power from the single mode fiber is up to 100 mW, the coupling efficiency is 50%. We also fabricated 100 mu m broad stripe coated lasers with cavity length of 800 mu m, a threshold current density of 170 A/cm(2), a high slope efficiency of 1.03 W/A and a far-field pattern of 40 x 6 degrees are obtained. The maximum output power of 3.5 W is also obtained for 100 mu m wide coated lasers. (C) 2000 Elsevier Science B.V. All rights reserved.

Optical properties of nanometer silicon prepared by silicon ion implanted into SiO2 layers

The samples of silicon nanocrystals (nc-Si) were prepared by Si ion implanted into SiO2 layers. Photoluminescence spectra were measured at room temperature and their dependence on thermal annealing was investigated. The experimental results show that PL peaks originate from the defects in SiO2 layers caused by ion implantation when the thermal annealing temperature is lower than 800 C. The PL peak from nc-Si was observed when the thermal annealing temperature was higher than 900 C, and PL intensity reached its maximum at the thermal annealing temperature of 1100 C. As the annealing temperature increases the red shift of PL peak from nc-Si shows the quantum size effect. The characterized Raman scattering peak of nc-Si was observed at the right angle scattering configuration for the first time. It provides further support for the PL measurements.

High-performance 980-nm quantum-well lasers using a hybrid material system of an Al-free InGaAs-InGaAsP active region and AlGaAs cladding layers grown by metal-organic chemical vapor deposition

We report on the material growth and fabrication of high-performance 980-nm strained quantum-well lasers employing a hybrid material system consisting of an Al-free InGaAs-InGaAsP active region and AlGaAs cladding layers. The use of AlGaAs cladding instead of InGaP provides potential advantages in flexibility of laser design, simple epitaxial growth, and improvement of surface morphology and laser performance. The as-grown InGaAs-InGaAsP(1.6 eV)-AlGaAs(1.95 eV) lasers achieve a low threshold current density of 150 A/cm(2) (at a cavity length of 1500 mu m), internal quantum efficiency of similar to 95%, and low internal loss of 1.8 cm(-1). Both broad-area and ridge-waveguide laser devices are fabricated. For 100-mu m-wide stripe lasers with a cavity length of 800 Irm, a slope efficiency of 1.05 W/A and a characteristic temperature coefficient (T-0) of 230 K are achieved. The lifetime test demonstrates a reliable performance. The comparison with our fabricated InGaAs-InGaAsP(1.6 eV)-AlGaAs(1.87 eV) lasers and Al-free InGaAs-InGaAsP (1.6 eV)-InGaP lasers are also given and discussed. The selective etching between AlGaAs and InGaAsP is successfully used for the formation of a ridge-waveguide structure. For 4-mu m-wide ridge-waveguide laser devices, a maximum output power of 350 mW is achieved. The fundamental mode output power can be up to 190 mW with a slope efficiency as high as 0.94 W/A.

Influence of (001) vicinal GaAs substrates on the optical properties of defects in low-temperature grown GaAs/AlGaAs multiple quantum wells

Photoluminescence (PL) spectroscopy and carrier lifetime measurement has been used to characterize optical properties of defects in the low-temperature (LT) grown GaAs/AlGaAs multiple quantum well structures. Two sets of samples were grown at 400 degrees C by molecular beam epitaxy on nominal (001) and miscut [4 degrees off (001) towards (111) A] GaAs substrates, respectively. After growth, samples were subjected to 30 s rapid thermal annealing at 600-800 degrees C. It is found that after annealing, two defect-related PL features appear in the samples grown on nominal (001) GaAs substrates, but not in those grown on miscut (001) GaAs substrates. The carrier lifetimes are about 31 and 5 ps in as-grown samples grown on nominal and miscut (001) GaAs substrates, respectively. The different PL spectra and carrier lifetimes in two sets of samples are attributed to different structures of the As-Ga-like defects formed during LT growth. (C) 1999 American Institute of Physics. [S0003-6951(99)00230-2].

The effects of carbonized buffer layer on the growth of SiC on Si

Carbonized buffer layers were formed with C2H4 on Si(100) and Si(111) substrates using different methods and SIC epilayers were grown on each buffer layer at 1050 degrees C with simultaneous supply of C2H4 and Si2H6. The structure of carbonized and epitaxy layers was analyzed with in situ RHEED. The buffer layers formed at 800 degrees C were polycrystalline on both Si(100) and Si(111) substrates whereas they were single crystals, with twins on Si(100) and without tu ins on Si(111)substrates. when formed with a gradual rise in substrate temperature from 300 degrees C to growth temperature. Raising the substrate temperature slowly results in the formation of more twins. Epilayers grown on carbonized polycrystalline lavers are polycrystalline. Single crystal epilayers without twins grow on single crystalline buffer layers without twins or with a few twins. (C) 1999 Elsevier Science B.V. All rights reserved.

980nm InGaAs/InGaAsP quantum well lasers with AlGaAs cladding grown by metal organic chemical vapour deposition

The authors report on the fabrication of 980 nm InGaAs strained quantum well lasers with hybrid materials of InGaAsP as waveguide and AlGaAs as cladding grown by metal organic chemical vapour deposition. The InGaAs/InGaAsP/AlGaAs diode lasers (100 x 800 mu m) with broadened waveguide structure exhibit a threshold current of 180 mA, a slope efficiency of 1.0 W/A, and a high characteristic temperature coefficient (T-0) of 230 K.

Photoluminescence from Erbium-implanted silicon-rich SiO2

Si-rich SiO2 films were deposited by plasma-enhanced chemical vapor deposition on the silicon substrates, and then implanted with 1 x 10(15) cm(-2) 400 keV Er ions. After annealing at 800 degrees C for 5 min the samples show room temperature luminescence around 1.54 mu m, characteristic of intra-4f emission from Er3+, upon excitation using an Ar ion laser.

Zinc phthalocyanine (ZnPc) incorporated into silicon matrix grown by plasma enhanced chemical vapor deposition (PECVD)

Hybrid composites composed of zinc phthalocyanine embedded in silicon matrixes have attracted attention because of the potential for solar energy conversion. We produce hybrid composites by thermal evaporation for the plithalocyanine and PECVD (Plasma Enhanced Chemical Vapor Deposition) for the silicon matrix. Deposition of ZnPc/a-Si(amorphous silicon) composites was achieved in a sequential manner. The compound films were characterized by optical transmittance spectra and photoconductivity measurement. The optical transmittance measurements were carried out in the visible region (500 - 800 nm). Compared to pure silicon film, the photosensitivity of compound functional films was enhanced by one order of magnitude. This demonstrates the Si sensitized by adding ZnPc.